CN103014891A - Process for producing bamboo charcoal viscose fibers - Google Patents
Process for producing bamboo charcoal viscose fibers Download PDFInfo
- Publication number
- CN103014891A CN103014891A CN2012104991273A CN201210499127A CN103014891A CN 103014891 A CN103014891 A CN 103014891A CN 2012104991273 A CN2012104991273 A CN 2012104991273A CN 201210499127 A CN201210499127 A CN 201210499127A CN 103014891 A CN103014891 A CN 103014891A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo charcoal
- viscose fibers
- spinning solution
- viscose fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for producing bamboo charcoal viscose fibers. The process comprises the steps of dispersing bamboo charcoal micro-powder and porphine cobalt micro-particles into an organic solvent, and stirring the mixture to obtain a mixed emulsion; soaking, squeezing and ageing pulps of the emulsion to obtain cellulose derived from natural plants; dissolving and defoaming the cellulose in the mixed emulsion to obtain a spinning solution; extruding the spinning solution from a spinning pump; and solidifying the spinning solution in solidification liquid to obtain the bamboo charcoal viscose fibers. Therefore, the process for producing the bamboo charcoal viscose fibers is simple in production process, and with the process, the workload of manual operation is reduced, and the production cost is greatly reduced, so that the process is suitable for large-scale popularization and application, a fabric made of the bamboo charcoal viscose fibers has good air permeability, is suitable for wearing at high temperature in summer, has high strength and elasticity, is difficult to deform, and is comfortable to wear by people, and the added porphine cobalt has the functional characteristics of deodorization, antibiosis and the like.
Description
Technical field
The present invention relates to the weaving face fabric field, particularly relate to a kind of production technology of bamboo-carbon viscose fibre.
Background technology
Along with the progress of the development of human society and science and technology, people are gradually to decorating and clothes attractive in appearance had higher requirement.Manufacturers also pay attention to the development and application of fiber more, generally be by means such as physical modification, chemical modification and MOLECULE DESIGN the functional of fiber to be improved, obtain having the fiber of particular characteristic, make that original chemical fibre is stable at photo-thermal, there is larger improvement conduction, fire-retardant, dyeing, antistatic, moisture absorption, fluffy, ANTIPILLING, the aspect such as antifouling.The bamboo resource of China is very abundant, and bamboo is drawn materials conveniently, is easy to processing, is widely used.As raw material, it is carried out charing with old bamboo, obtain bamboo charcoal, the bamboo charcoal carbonaceous is fine and close, and than great, hole is flourishing, contains simultaneously abundant mineral matter element, and bamboo charcoal is processed into microfine, can be prepared into bamboo-carbon fibre.
The complex manufacturing of general bamboo-carbon viscose fibre, cost is high, is not suitable for large-scale production, and is bad with the fabric gas permeability that bamboo-carbon viscose fibre is made, intensity is little, breaks easily, and elasticity is little, the people puts on uncomfortable, and is antibacterial, deodorizing effect is bad, can not satisfy the requirement of people's life.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of production technology of bamboo-carbon viscose fibre, and this technique preparation is simple, can mass production.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of production technology of bamboo-carbon viscose fibre is provided, comprises that step is:
(1) with bamboo charcoal micropowder and porphines cobalt microparticulate in organic solvent and stir, obtain mixing serum, with pulp flood, squeezing and the experienced cellulose that obtains deriving from natural plants;
(2) described cellulose is joined in the described mixing serum dissolving and deaeration and obtain spinning solution, spinning solution is extruded by Spinning pumps, solidifies to obtain bamboo-carbon viscose fibre in solidification liquid.
In a preferred embodiment of the present invention, the mass ratio of bamboo charcoal micropowder described in the step (1) and described porphines cobalt particulate is 1:1.
In a preferred embodiment of the present invention, organic solvent comprises one or more in methyl alcohol, the ethanol described in the step (1).
In a preferred embodiment of the present invention, the temperature of solidification liquid is 10-20 ℃ described in the step (2).
The invention has the beneficial effects as follows: the production technology of bamboo-carbon viscose fibre of the present invention, this production technology production process is simple, reduce manually-operated workload, greatly reduce production cost, be fit to large-scale promotion and application, the fabric good permeability that obtains with the bamboo-carbon viscose fibre that makes, be adapted at wearing under the summer high-temperature, intensity and elasticity are large, are not easy distortion, the people puts on comfortable, and the porphines cobalt that adds simultaneously also has deodorizing, the functional characteristic such as antibiotic.
The specific embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Embodiment one:
(1) with 50g bamboo charcoal micropowder and 50g porphines cobalt microparticulate in methyl alcohol and stir, obtain mixing serum, with pulp flood, squeezing and the experienced cellulose that obtains deriving from natural plants;
(2) described cellulose is joined in the described mixing serum dissolving and deaeration and obtain spinning solution, spinning solution is extruded by Spinning pumps, solidifies to obtain bamboo-carbon viscose fibre in 10 ℃ of solidification liquids.
Embodiment two:
(1) with 100g bamboo charcoal micropowder and 100g porphines cobalt microparticulate in ethanol and stir, obtain mixing serum, with pulp flood, squeezing and the experienced cellulose that obtains deriving from natural plants;
(2) described cellulose is joined in the described mixing serum dissolving and deaeration and obtain spinning solution, spinning solution is extruded by Spinning pumps, solidifies to obtain bamboo-carbon viscose fibre in 15 ℃ of solidification liquids.
Embodiment three:
(1) with 200g bamboo charcoal micropowder and 200g porphines cobalt microparticulate in the mixed solution of methyl alcohol and ethanol and stir, obtain mixing serum, with pulp flood, squeezing and the experienced cellulose that obtains deriving from natural plants;
(2) described cellulose is joined in the described mixing serum dissolving and deaeration and obtain spinning solution, spinning solution is extruded by Spinning pumps, solidifies to obtain bamboo-carbon viscose fibre in 20 ℃ of solidification liquids.
The production technology of the bamboo-carbon viscose fibre that the present invention discloses, this production technology production process is simple, reduce manually-operated workload, greatly reduce production cost, be fit to large-scale promotion and application, the fabric good permeability that obtains with the bamboo-carbon viscose fibre that makes, be adapted at wearing under the summer high-temperature, intensity and elasticity are large, are not easy distortion, the people puts on comfortable, and the porphines cobalt that adds simultaneously also has deodorizing, the functional characteristic such as antibiotic.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (4)
1. the production technology of a bamboo-carbon viscose fibre is characterized in that, comprises that step is:
(1) with bamboo charcoal micropowder and porphines cobalt microparticulate in organic solvent and stir, obtain mixing serum, with pulp flood, squeezing and the experienced cellulose that obtains deriving from natural plants;
(2) described cellulose is joined in the described mixing serum dissolving and deaeration and obtain spinning solution, spinning solution is extruded by Spinning pumps, solidifies to obtain bamboo-carbon viscose fibre in solidification liquid.
2. the production technology of bamboo-carbon viscose fibre according to claim 1 is characterized in that, the mass ratio of bamboo charcoal micropowder described in the step (1) and described porphines cobalt particulate is 1:1.
3. the production technology of bamboo-carbon viscose fibre according to claim 1 is characterized in that, organic solvent comprises one or more in methyl alcohol, the ethanol described in the step (1).
4. the production technology of bamboo-carbon viscose fibre according to claim 1 is characterized in that, the temperature of solidification liquid is 10-20 ℃ described in the step (2).