CN102382559A - Fire retardant coating for bamboo floor - Google Patents
Fire retardant coating for bamboo floor Download PDFInfo
- Publication number
- CN102382559A CN102382559A CN201110311145XA CN201110311145A CN102382559A CN 102382559 A CN102382559 A CN 102382559A CN 201110311145X A CN201110311145X A CN 201110311145XA CN 201110311145 A CN201110311145 A CN 201110311145A CN 102382559 A CN102382559 A CN 102382559A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo floor
- retardant coating
- fire retardant
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a fire retardant coating for a bamboo floor, which is prepared by stirring the following raw materials in parts by weight: 70 to 78 parts of n-butyl acetate, 50 to 55 parts of alkyd resin, 30 to 40 parts of novolac epoxy resin, 15 to 25 parts of water glass, 40 to 60 parts of hydroxyethyl cellulose, 5 to 7 parts of sodium fluosilicate, 16 to 24 parts of methanal, 9 parts of trioxypurine, 14 parts of phosphoric acid and 145 to 155 parts of water. The formula can also comprise 10 parts of chlorinated terphenyls. Industrial experiments prove that a formed coating has the obvious characteristics of strong bonding strength and hydrocarbon fire resistance when a product of the fire retardant coating for the bamboo floor is coated on the surface of the bamboo floor.
Description
Technical field
The present invention relates to a kind of bamboo floor and use frie retardant coating, belong to the chemistry painting industry technical field.
Technical background
At present, the bamboo floor is a kind of new decorative material for building, and it is a raw material with natural high-quality bamboo; Because raw material sources are extensive, safe, wearing quality is strong; So the bamboo floor is to begin to rise in these several years, but bamboo is a nature material, material own belongs to inflammable material; So the bamboo floor must be carried out fire prevention and handle, not so presence of fire, consequence is hardly imaginable.And the fire prevention processing is done on the bamboo floor generally all is to be coated with the last layer frie retardant coating at its skin; But coating on the market is to be directed against solid wood mostly; Because there is certain difference in the material of solid wood and bamboo wood, so that coating on the market is used for the effect on bamboo floor is not so good.
Summary of the invention
The object of the invention provides the high bamboo floor of a kind of resistivity against fire and uses frie retardant coating.
In order to achieve the above object, the present invention adopts a technical scheme to be: a kind of bamboo floor is stirred according to weight proportion by following raw material with frie retardant coating and is processed: 70-78 part n-butyl acetate, 50-55 part Synolac; 30-40 phenolic aldehyde part epoxy resin, 15-25 part water glass, 40-60 part Natvosol; 5-7 part Sodium Silicofluoride 98min, 16-24 part formaldehyde, 9 parts of uric acid; 14 parts of phosphoric acid, 145-155 part water.
Above-mentioned prescription can also contain 10 parts of arochlors.
Product of the present invention proves through commerical test, and the bamboo floor surface is covered with paint, lacquer, colour wash, etc. processing, and the coating of formation has the distinguishing feature of cohesive strength height, anti-hydro carbons fire.
Embodiment
Embodiment 1
A kind of bamboo floor is stirred according to weight proportion by following raw material with frie retardant coating and is processed: 70-78 part n-butyl acetate, 50-55 part Synolac, 30-40 phenolic aldehyde part epoxy resin; 15-25 part water glass, 40-60 part Natvosol, 5-7 part Sodium Silicofluoride 98min; 16-24 part formaldehyde; 9 parts of uric acid, 14 parts of phosphoric acid, 145-155 part water.
Embodiment 2
A kind of bamboo floor is stirred according to weight proportion by following raw material with frie retardant coating and is processed: 70-78 part n-butyl acetate, 50-55 part Synolac, 30-40 phenolic aldehyde part epoxy resin; 15-25 part water glass, 40-60 part Natvosol, 5-7 part Sodium Silicofluoride 98min; 16-24 part formaldehyde, 9 parts of uric acid, 14 parts of phosphoric acid; 145-155 part water, 10 parts of arochlors.
Claims (2)
1. frie retardant coating is used on a bamboo floor, it is characterized in that it mainly is to be stirred according to weight proportion by following raw materials according to process: 70-78 part n-butyl acetate, 50-55 part Synolac; 30-40 phenolic aldehyde part epoxy resin, 15-25 part water glass, 40-60 part Natvosol; 5-7 part Sodium Silicofluoride 98min, 16-24 part formaldehyde, 9 parts of uric acid; 14 parts of phosphoric acid, 145-155 part water.
2. frie retardant coating is used on bamboo according to claim 1 floor, it is characterized in that also containing 10 parts of arochlors.