CN102367574A - 一种低温快速无渣磷化剂的制备方法 - Google Patents

一种低温快速无渣磷化剂的制备方法 Download PDF

Info

Publication number
CN102367574A
CN102367574A CN2011103128465A CN201110312846A CN102367574A CN 102367574 A CN102367574 A CN 102367574A CN 2011103128465 A CN2011103128465 A CN 2011103128465A CN 201110312846 A CN201110312846 A CN 201110312846A CN 102367574 A CN102367574 A CN 102367574A
Authority
CN
China
Prior art keywords
preparation
pouring
phosphating
uniform solution
low temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103128465A
Other languages
English (en)
Inventor
邹益坚
刘炳焕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI FUTONG ENVIRONMENTAL PROTECTION NEW ENERGY TECHNOLOGY CO LTD
Original Assignee
HEFEI FUTONG ENVIRONMENTAL PROTECTION NEW ENERGY TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI FUTONG ENVIRONMENTAL PROTECTION NEW ENERGY TECHNOLOGY CO LTD filed Critical HEFEI FUTONG ENVIRONMENTAL PROTECTION NEW ENERGY TECHNOLOGY CO LTD
Priority to CN2011103128465A priority Critical patent/CN102367574A/zh
Publication of CN102367574A publication Critical patent/CN102367574A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种低温快速无渣磷化剂的制备方法，包括将肌醇六磷酸(C6H18O24P6)投入去离子水中，在搅拌的条件下，投入氧化锌(ZnO)和硝酸锌[Zn(NO3)26H2O]搅拌不停得到第一均匀溶液；再将硝酸镍[Ni(NO3)26H2O]和硫酸铬[Cr(OH)SO4]，投入第一均匀溶液搅拌至均匀得到第二均匀溶液；最后将苯骈三氮唑(BTA)和氟钛酸钾(K2TiF6)投入第二均匀溶液搅拌均匀得到该发明产品的磷化剂，本发明具有使用方便，低温磷化而减少能耗、磷化膜致密，导电性好，耐蚀性优良，漆膜附着力强，极少沉渣，无环境污染，磷化成本低等优点。

Description

一种低温快速无渣磷化剂的制备方法
技术领域
本发明涉及化工生产领域，尤其涉及一种低温快速无渣磷化剂的制备方法。
背景技术
传统的磷化工艺，无论高温，中温还是低温，一般多为锰盐、钙盐等形式，这些磷酸盐结晶转化膜的共同特点是随着膜重、膜厚的增加，表面绝缘电阻值增大。导致导电性能不好，同时抗腐蚀能力很弱。
发明内容
本发明所要解决的技术问题是克服现有技术的缺陷，提供一种使用方便，低温磷化而减少能耗、磷化膜致密，导电性好，耐蚀性优良，漆膜附着力强，极少沉渣，无环境污染，磷化成本低的一种低温快速无渣磷化剂的制备方法。
为解决上述技术问题，本发明提供了一种低温快速无渣磷化剂的制备方法，包括下列工艺步骤：
步骤1、将肌醇六磷酸(C6H18O24P6)投入去离子水中，在搅拌的条件下，投入氧化锌(ZnO)和硝酸锌[Zn(NO3)26H2O]搅拌不停得到第一均匀溶液；
步骤2、将硝酸镍[Ni(NO3)26H2O]和硫酸铬[Cr(OH)SO4]，投入第一均匀溶液搅拌至均匀得到第二均匀溶液；
步骤3、将苯骈三氮唑(BTA)和氟钛酸钾(K2TiF6)投入第二均匀溶液搅拌均匀得到该发明产品的磷化剂。
本发明在锌系成膜的机理上，将PA盐应用于磷化成膜领域，PA盐有极强的螯合能力，它有18个解离氢离子，能在很宽的PH值范围内，与不同价的金属进行螯合，PA盐为主组分形成的膜具有薄形化，品位高，晶格排列有序、致密，且工作液清澈透明，常温磷化(20-35℃)，工作能力强，处理量大(每L工作液处理4m2补加原液)不挂灰，无沉渣(＜0.5g/m2)操作简单易控，无三废排出，无环境污染，省去了排渣解毒、清堵等工作，性能优于日本帕卡和德国凯米特尔，磷化成本低于进口同类品，经济和社会效益显著。SP系列磷化液是以天然化合物——肌醇六磷酸为主要成分制成的新一代磷化液，植酸(phyticacid.PA)广泛地存在于植物界和动物的血液、心脏、肝脏、脑、目、生殖器等脏器中，分子式C6H18O24P6WV，分子量660.04，它的分子结构为对称的肌醇六磷酸，具有12个可解离的酸性氢离子。是很强的阴极负荷，可在很宽的PH值范围内，与不同价的金属具有极强的螯合能力。
在锌系成膜的机理上，将PA盐应用于磷化成膜领域，发挥了本品优势(PA盐有极强的螯合能力)解决了磷化成膜过程中沉渣多之难题，而得到的转化膜具有成膜薄形化。品质高，晶格排列有序、致密。
为适应汽车产品质量不断提高的要求，确立了漆前磷化基底金属能成倍的提高漆膜的质量。油漆前的磷化处理工艺，配方繁多，但低温(＜40℃)、低渣(＜0.5g/m2)、快速磷化(＜5分钟)集一体的磷化产品未见报送。
应用试验证明：SP磷化液具有操作简单，使用方便，低温磷化而减少能耗、磷化膜致密，导电性好，耐蚀性优良，漆膜附着力强，极少沉渣，无环境污染，磷化成本低等优点，具有广阔前景。其中SP-I多功能磷化液性能及指标如下：
一、浓缩液
1、外观    绿色粘稠液体
2、总酸    200±30点
3、游离酸  13-18点
二、工作液
由于采用上述技术方案，本发明具有以下的有益效果：
本发明使用方便，低温磷化而减少能耗、磷化膜致密，导电性好，耐蚀性优良，漆膜附着力强，极少沉渣，无环境污染，磷化成本低。
具体实施方式
以制得1000公斤无渣磷化剂，本发明一种低温快速无渣磷化剂的制备方法，包括下列工艺步骤：
步骤1、将肌醇六磷酸(C6H18O24P6)500公斤投入去离子水中，在搅拌的条件下，投入氧化锌(ZnO)200公斤和硝酸锌[Zn(NO3)26H2O]100公斤搅拌不停得到第一均匀溶液；
步骤2、将硝酸镍[Ni(NO3)26H2O]50公斤和硫酸铬[Cr(OH)SO4]50公斤，投入第一均匀溶液搅拌至均匀得到第二均匀溶液；
步骤3、将苯骈三氮唑(BTA)50公斤和氟钛酸钾(K2TiF6)50公斤投入第二均匀溶液搅拌均匀得到该发明产品的磷化剂1000公斤。
最后应说明的是：以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案；因此，尽管本说明书参照上述的各个实施例对本发明已进行了详细的说明，但是，本领域的普通技术人员应当理解，仍然可以对本发明进行修改或等同替换；而一切不脱离本发明的精神和范围的技术方案及其改进，其均应涵盖在本发明的权利要求范围中。

Claims (1)

1.一种低温快速无渣磷化剂的制备方法，其特征在于：包括下列工艺步骤：
步骤1、将肌醇六磷酸投入去离子水中，在搅拌的条件下，投入氧化锌和硝酸锌搅拌不停得到第一均匀溶液；
步骤2、将硝酸镍和硫酸铬投入第一均匀溶液搅拌至均匀得到第二均匀溶液；
步骤3、将苯骈三氮唑和氟钛酸钾投入第二均匀溶液搅拌均匀得到该发明产品的磷化剂。
CN2011103128465A 2011-10-14 2011-10-14 一种低温快速无渣磷化剂的制备方法 Pending CN102367574A (zh)