CN102337112A - 油井用固体生化缓蚀棒及其制备方法 - Google Patents

油井用固体生化缓蚀棒及其制备方法 Download PDF

Info

Publication number
CN102337112A
CN102337112A CN201110184247XA CN201110184247A CN102337112A CN 102337112 A CN102337112 A CN 102337112A CN 201110184247X A CN201110184247X A CN 201110184247XA CN 201110184247 A CN201110184247 A CN 201110184247A CN 102337112 A CN102337112 A CN 102337112A
Authority
CN
China
Prior art keywords
corrosion
solid
rod
oil well
oil wells
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110184247XA
Other languages
English (en)
Inventor
陈富林
孙叶芳
陈文刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NORTHWEST UNIVERSITY
XI'AN REJE BIOLOGICAL TECHNOLOGY Co Ltd
Original Assignee
NORTHWEST UNIVERSITY
XI'AN REJE BIOLOGICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NORTHWEST UNIVERSITY, XI'AN REJE BIOLOGICAL TECHNOLOGY Co Ltd filed Critical NORTHWEST UNIVERSITY
Priority to CN201110184247XA priority Critical patent/CN102337112A/zh
Publication of CN102337112A publication Critical patent/CN102337112A/zh
Pending legal-status Critical Current

Abstract

本发明所述的油井固体生化缓蚀棒及其制备方法涉及一种施加在油井中能抑制油管、套管腐蚀的固体生化复合缓蚀棒及其制备方法。该缓蚀棒由下述质量百分含量的组分组成：硬脂酸4％～8％、硬脂酸钙8％～16％、缓蚀剂38％～44％、表面活性剂38％～44％和微生物，其中微生物的质量是前四种组分总质量的2％。本发明的油井固体生化缓蚀棒能有效增长防腐有效期，延长油井寿命。操作工艺简单，使用方便、安全、环保，不会对原油造成污染，是一种长效的固体缓蚀剂。不合格产品可重新回锅生产，生产过程中不会产生废弃物。该产品缓蚀率≥80％，有效期≥360天。

Description

油井用固体生化缓蚀棒及其制备方法
【技术领域】
本发明涉及一种施加在油井中能抑制油管、套管腐蚀的固体生化复合缓蚀棒及其制备方法。
【背景技术】
很多油田由于多年的开采，有相当部分的油井已经进入采油后期。随着不断的开采，油井含水率逐渐增大，加之油井产出液中含有大量的腐蚀性阴离子、金属阳离子和硫化氢气体等，这些因素直接或间接地对油泵、油管、套管和抽油杆造成不同程度的腐蚀，直接引起油泵密封不严、油管穿孔甚至抽油杆断裂，直接影响油田的正常生产。
【发明内容】
本发明的目的是解决现有技术中防腐周期短和油井底部存在防腐死角的问题，提供一种有效期长、使用方便的油井用固体生化缓蚀棒，该油井用固体生化缓蚀棒在油井液中缓慢溶解、释放并通过油管进入原油传输系统，在整个采集过程起到缓蚀作用。
本发明还提供了一种制备上述缓蚀棒的方法，其操作简单，成本低廉。
本发明所述的油井用固体生化缓蚀棒是由下述质量百分含量的组分组成：
硬脂酸      4％～8％、
硬脂酸钙    8％～16％、
缓蚀剂      38％～44％、
表面活性剂  38％～44％、
和抗菌肽，其中抗菌肽的质量是上述四种组分总质量的2％。
其中优选地，所述的缓蚀剂为咪唑啉季铵盐。
更优选地，所述的表面活性剂为十二烷基磺酸钠。
一种制备上述油井用固体生化缓蚀棒的方法，包括以下步骤：
(1)按质量比准备硬脂酸、硬脂酸钙、缓蚀剂和表面活性剂，并在室温条件下混合均匀；
(2)边搅拌边按1℃/分钟的速度升温到115℃，并在115℃条件下搅拌45分钟，然后倒入专用模具，自然冷却2小时；
(3)然后在其上均匀地钻孔，向孔中均匀地加入抗菌肽即可，其中所加入的抗菌肽总质量是步骤(1)中四种组分总质量的2％。
本发明的有益效果是：本发明的油井固体生化缓蚀棒能有效增长防腐有效期，延长油井寿命。操作工艺简单，使用方便、安全、环保，不会对原油造成污染，是一种长效的固体缓蚀剂。不合格产品可重新回锅生产，生产过程中不会产生废弃物。该产品缓蚀率≥80％，有效期≥12个月。
【具体实施方式】
实施例一
(1)按质量比准备4公斤硬脂酸、8公斤硬脂酸钙、44公斤双咪唑啉季铵盐和44公斤十二烷基磺酸钠，并在室温条件下混合均匀；
(2)边搅拌边按1℃/分钟的速度升温到115℃，并在115℃条件下搅拌45分钟使其完全反应，然后平均地倒入100个专用模具，自然冷却2小时；
(3)冷却成型后在每个缓蚀棒上均匀地钻孔，向孔中均匀地加入0.02公斤抗菌肽即可。
(4)使用《油田采出水用缓蚀剂评价方法》SY/T5237-2000所述的测试方法测试，其缓蚀率为85.2％，防腐有效期为13个月。
实施例二
(1)按质量比准备6公斤硬脂酸、12公斤硬脂酸钙、41公斤环烷基阳离子咪唑啉季铵盐和41公斤十二烷基磺酸钠，并在室温条件下混合均匀；
(2)边搅拌边按1℃/分钟的速度升温到115℃，并在115℃条件下搅拌45分钟使其完全反应，然后平均地倒入100个专用模具，自然冷却2小时；
(3)冷却成型后在每个缓蚀棒上均匀地钻孔，向孔中均匀地加入公斤抗菌肽即可。
(4)使用《油田采出水用缓蚀剂评价方法》SY/T5237-2000所述的测试方法测试，其缓蚀率为83.6％，防腐有效期为14个月。
实施例三
(1)按质量比准备8公斤硬脂酸、16公斤硬脂酸钙、38公斤油酸基阳离子咪唑啉季铵盐和38公斤十二烷基本磺酸钠，并在室温条件下混合均匀；(2)边搅拌边按1℃/分钟的速度升温到115℃，并在115℃条件下搅拌45分钟使其完全反应，然后平均地倒入100个专用模具，自然冷却2小时；
(3)冷却成型后在每个缓蚀棒上均匀地钻孔，向孔中均匀地加入0.02公斤抗菌肽即可。
(4)使用《油田采出水用缓蚀剂评价方法》SY/T5237-2000所述的测试方法测试，其缓蚀率为82％，防腐有效期为13个月。

Claims (4)

1.油井用固体生化缓蚀棒，其特征在于由下述质量百分含量的组分组成：
硬脂酸      4％～8％、
硬脂酸钙    8％～16％、
缓蚀剂      38％～44％、
表面活性剂  38％～44％、
和抗菌肽，其中抗菌肽的质量是上述四种组分总质量的2％。
2.如权利要求1所述的油井用固体生化缓蚀棒，其特征在于所述的缓蚀剂为咪唑啉季铵盐。
3.如权利要求1或2所述的油井用固体生化缓蚀棒，其特征在于所述的表面活性剂为十二烷基磺酸钠。
4.一种制备如权利要求1或2所述油井用固体生化缓蚀棒的方法，其特征在于包括以下步骤：
(1)按质量比准备硬脂酸、硬脂酸钙、缓蚀剂和表面活性剂，并在室温条件下混合均匀；
(2)边搅拌边按1℃/分钟的速度升温到115℃，并在115℃条件下搅拌45分钟，然后倒入专用模具，自然冷却2小时；
(3)然后在其上均匀地钻孔，向孔中均匀地加入抗菌肽即可，其中所加入的抗菌肽总质量是步骤(1)中四种组分总质量的2％。
CN201110184247XA 2011-07-01 2011-07-01 油井用固体生化缓蚀棒及其制备方法 Pending CN102337112A (zh)