CN102329566A - High-permeability liquid rubber spray coating - Google Patents
High-permeability liquid rubber spray coating Download PDFInfo
- Publication number
- CN102329566A CN102329566A CN201110195825A CN201110195825A CN102329566A CN 102329566 A CN102329566 A CN 102329566A CN 201110195825 A CN201110195825 A CN 201110195825A CN 201110195825 A CN201110195825 A CN 201110195825A CN 102329566 A CN102329566 A CN 102329566A
- Authority
- CN
- China
- Prior art keywords
- component
- rubber
- hypertonicity
- spray
- liquid rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-permeability liquid rubber spray coating, and relates to the technical field of spray coatings. The high-permeability liquid rubber spray coating comprises a component A and a component B, wherein the component A is anionic liquid rubber asphalt emulsion; the component B is a coagulant solution; the component A has the solid content of liquid rubber asphalt emulsion of 50-75 weight percent, and comprises the following components in percentage by mass: 1 to 35 percent of rubber emulsion, 10 to 50 percent of asphalt emulsion, 0.01 to 2 percent of anionic dispersing agent, 0.01 to 2 percent of anionic surfactant, 0.1 to 10 percent of fatty alcohol-polyoxyethylene ether, 0.1 to 10 percent of alkali resistant wetting agent OEP-70 and 0.1 to 10 percent of alkali resistant wetting agent AEP; and the component B is an aqueous solution at the concentration of 3-18 percent, which is prepared by mixing calcium chloride and composite aluminum-iron polymer in percentage by mass. The wetting agents are added into the spray coating, and the coating has high permeability and wider application range.
Description
Technical field
The present invention relates to the spray material technical field, specifically be meant a kind of liquid rubber spray-coating material with hypertonicity.
Background technology
Spray material is used and extensively, is not only related to building field, also relates to each technical fields such as chemical industry, daily life.People hope to provide and multi-functional novel spraying material such as a kind of anticorrosion, waterproof, protection, adiabatic heat-insulation, thin sound noise reduction occur.Though CN101235252 discloses a kind of spray material, solved some technical barriers among the US4287242, its side or performance do not reach the ideal effect, have brought very big resistance to practical application, make the scope of application of its spray material seriously limited.
Summary of the invention
The present invention is in order to solve above-mentioned technical barrier; Providing a kind of can solidify rapidly; And the coating after solidifying not only has certain antiseepage, rot-resistant effect; And have hypertonicity, can be applied to the liquid rubber spray-coating material with hypertonicity of the steelwork of buildings such as ocean, sluice, port engineering and the antiseepage of concrete structure, anticorrosion mask.
The present invention to achieve these goals, the technical scheme that is adopted does, a kind of liquid rubber spray-coating material with hypertonicity is provided, said liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; Said A component is an anion liquid body rubber bitumen emulsion; Said B component is a coagulant solution;
Said A component is represented with mass percent, and fluid rubber bitumen emulsion weight solid content is 50-75%; Wherein, rubber latex 1-35%, bitumen emulsion 10-50%; Anionic dispersing agents 0.01-2%, AS 0.01-2%, AEO 0.1-10%; OEP-70 0.1-10%, AEP 0.1-10%;
Said B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
Said have the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
Rubber in the rubber latex of said A component is tree elastomer or viton; Said viton is selected from (co) polychloroprene rubber, butadienestyrene copolymer rubber, the fine copolymer rubber of divinyl propylene, iso-butylene, isoprene copolymer rubber, one or more in the polybutadiene rubber;
Pitch in the bitumen emulsion of said A component is selected from petroleum pitch, coal-tar pitch, shale tar pitch, one or more in the transformation of the way pitch;
The anionic dispersing agents of said A component is selected from vitriol, TH-904, Acumer940 polymkeric substance, CD-4, naphthalene sulfonate salt polycondensate, one or more in the naphthalenesulfonate formaldehyde condensation compound;
The AS of said A component is selected from rosined soap, synthetic fatty acid soap, AS, sodium alkyl benzene sulfonate, alkyl-sulphate, alkyl aryl sulfate, one or more in α-sodium naphthalene sulfonate.
Said B component is preferably, and representes with mass percent, is 3-18% the aqueous solution by 93-99.7% calcium chloride, the formulated concentration of 0.3-7% compound ferro-aluminum mixed with polymers.
Said B component also contains sodium-chlor, representes with mass percent, is 3-18% the aqueous solution by 90-99.2% calcium chloride, 0.5-3% sodium-chlor, the formulated concentration of 0.3-7% compound ferro-aluminum mixed with polymers.
Said compound ferro-aluminum polymkeric substance is one or both in Poly aluminum Chloride (PAC), the bodied ferric sulfate.
Said A component is represented with mass percent, also contains carbon black 0-3%, fine powder material 0-3%.
Pitch in the bitumen emulsion of said A component is preferably 60-120 petroleum pitch and emulsion thereof.
Rubber in the rubber latex of said A component is preferably one or both in (co) polychloroprene rubber, the butadienestyrene copolymer rubber.
The carbon black of said A component is that fineness is not less than 600 purpose carbon powders or WHITE CARBON BLACK powder;
The fine powder material of said A component is that fineness is not less than 800 porcelain powder or dicalcium powder.
A kind of its beneficial effect of liquid rubber spray-coating material with hypertonicity of the present invention is: coating of the present invention adds nonionogenic tenside AEO and alkali-resistant penetrant OEP-70 and alkali-resistant penetrant AEP for improving its performance; Permeate agent is as the term suggests be osmosis; Also be to have fixed hydrophilic and oleophilic group; Surface energy at solution aligns, and the material that surface tension is significantly descended.Coating of the present invention has following advantage: water proof anti-seepage is effective; Cohesive strength is high, can be integrally formed with structure; Resistance to corrosion is strong, the acid-and base-resisting of mortar ability, salt and the corrosion of other chemical; Anti-high humidity, ageing-resistant, frost resistance good; The product aqueous non-toxic, compliance with environmental protection requirements.
Coating of the present invention has excellent bonding, cracking resistance, freeze proof, antiseepage, anticorrosion, chloride-penetration resistance, ageing-resistant and corrosion resisting property, is applicable to steelwork and the antiseepage of skeleton construction, anticorrosion mask and repairing works such as ocean, sluice, waterfall, port engineering, highway, bridge, metallurgy, chemical industry, industry ground slab and covil construction.Has fabulous sticking power, the fluent material that seepage force is extremely strong, fast drying; Wear resistance is strong, and good anti-chemical and water tolerance are arranged, and makes it to produce effective infiltration through adding permeate agent; Have an effect with the composition in concrete and the solid, make concrete each composition be solidified into a firm entity, and blocked concrete each big or small pore; Obtain the integral body of a dustless densification, thereby improve concrete wear resistance, crushing resistance, compactness and impermeability.Can satisfy various user demand and environmental difference, the application of the processing of cement floorings such as suitable factory, warehouse, harbour, parking and the anti-brine corrosion of road both sides cement block etc., and also color can unrestrictedly be allocated.
Embodiment
Below in conjunction with embodiment a kind of liquid rubber spray-coating material with hypertonicity of the present invention is described.
1 one kinds of liquid rubber spray-coating materials of embodiment with hypertonicity.
A kind of prescription with liquid rubber spray-coating material of hypertonicity is:
A kind of liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; The A component is an anion liquid body rubber bitumen emulsion, the water-based spray material; The B component is a coagulant solution;
A component anion liquid body rubber bitumen emulsion adds up to 100kg, wherein, and (co) polychloroprene rubber emulsion 25kg; No. 80 petroleum pitch emulsion 30kg; Anionic dispersing agents TH-904 is that 0.15kg, naphthalenesulfonate formaldehyde condensation compound 0.15kg, CD-4 are 0.15kg, AS rosined soap 1kg, synthetic fatty acid soap 0.5kg, AS 0.2kg, AEO 2%; OEP-70 3%, and AEP 4%; Carbon black 1.5kg, fineness is not less than 800 purpose porcelain powder 0.75kg, and water is surplus.
The B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
The B component is represented with mass percent, is 10% the aqueous solution by 95% calcium chloride, 1.5% sodium-chlor, the formulated concentration of 5% compound ferro-aluminum mixed with polymers, and compound ferro-aluminum polymkeric substance is a Poly aluminum Chloride (PAC).
Having the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
The preparation of A component anion liquid body rubber bitumen emulsion:
(1) producing of nature rubber latex or synthetic rubber latex: with the rubber latex of buying if solid content is lower than 48-65%; Need pass through extract at low temperature; Extract solid content at 48-65% nature rubber latex or synthetic rubber latex, with its be warming up to 20--40 ℃ subsequent use.
(2) bitumen emulsion produces
In emulsified bitumen equipment, add the pitch of 1000 weight parts, and remain on 130 ℃, add 20-45% water and anionic part tensio-active agent, temperature will be 40-70 ℃, and carrying out high speed shear, to stir worth solid content be 50-75% anionic emulsified bitumen.
(3) carbon black is produced
Get a certain amount of dispersion agent (consumption be carbon black mass 0.2-30%); Elder generation's water is transferred and is opened; Add the carbon black powder then, disperse fully (it is abundant together to put into grinding in ball grinder) to form stable and flowability carbon black dispersion preferably, it is subsequent use to make liquid carbon black.It is subsequent use that liquid carbon black also can be processed carbon powder.The system carbon powder takes the electrically heated oven dry to handle, and preferably adopts spray drying treatment, and the carbon black that the electrically heated oven dry is handled also need carry out the dry grinding powdering.
(4) fine powder material is produced preparation method and is produced with carbon black.
(5) white lake is processed fineness and is not less than 800 purpose powders.
(6) produce anion liquid body rubber bitumen emulsion
The emulsified bitumen that (2) make is reduced to 20--40 ℃; Add the carbon black of (3) producing, the fine powder material that produce (4), the white lake powder that produce (5) therein; Nature rubber latex or the synthetic rubber latex (1) produced slowly add again; Stir at adding anionic dispersing agents, remaining AS, red phosphorus (powder), silane coupling agent, make anion liquid body rubber bitumen emulsion.
The preparation of B component condensing agent:
90% (mass ratio) water that is accounted for 10% (mass ratio) and the B component total amount of B component by calcium chloride, compound ferro-aluminum polymkeric substance, sodium-chlor mixes fully, produces the B component.
A kind of spraying coating process: the A for preparing, B component are respectively charged in the proportion container separately with liquid rubber spray-coating material of hypertonicity; Under the promotion of power system; A component and B component run to spray gun separately respectively through two pipelines; Two muzzle slope inwardly during spraying, and spray angle is aimed at the same district of the object basal plane face that needs spraying simultaneously, and the moment of material ejection forms atomization process; Two components are carried out thorough mixing before arriving basal plane or when arriving basal plane, film thereby form more uniformly rubber asphalt.Two components are 350-600mm in the joint distance of mixing the spraying face of arrival.
The glued membrane checking.
Have a certain amount of moisture that gets to separate out in the glued membrane that generates, behind the 24h, coating is dry, and the surface is evenly smooth, thickness 2.3mm.Do adhesive test behind the 168h, according to the ASTM standard, material can't be peeled off from body of wall.Use the same method, coat releasing agent at spraying money, with the drawing machine test, tension set is 200% behind the 168h that films that makes.Detect anti-pierceability test, do not seep water, detect impermeability test, waterproof.
2 one kinds of liquid rubber spray-coating materials of embodiment with hypertonicity.
A kind of prescription with liquid rubber spray-coating material of hypertonicity is:
A kind of liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; The A component is an anion liquid body rubber bitumen emulsion, the water-based spray material; The B component is a coagulant solution;
A component anion liquid body rubber bitumen emulsion adds up to 100kg, wherein, and butadienestyrene copolymer rubber 15kg; No. 90 petroleum pitch emulsion 25kg; Anionic dispersing agents vitriol is that 0.5kg, naphthalenesulfonate formaldehyde condensation compound 0.15kg, CD-4 are 0.15kg, AS rosined soap 0.5kg, synthetic fatty acid soap 1kg, α-sodium naphthalene sulfonate 0.2kg, AEO 1%; OEP-70 9%, and AEP 2%; Water is surplus.
The B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
The B component is represented with mass percent, is 10% the aqueous solution by 95% calcium chloride, the formulated concentration of 5% compound ferro-aluminum mixed with polymers, and compound ferro-aluminum polymkeric substance is a Poly aluminum Chloride (PAC).
Having the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
The preparation of A component anion liquid body rubber bitumen emulsion, the preparation of B component condensing agent and to have a spraying coating process of liquid rubber spray-coating material of hypertonicity identical with embodiment 1.
The glued membrane checking.
Have a certain amount of moisture that gets to separate out in the glued membrane that generates, behind the 24h, coating is dry, and the surface is evenly smooth, thickness 2.0mm.Do adhesive test behind the 168h, according to the ASTM standard, material can't be peeled off from body of wall.Use the same method, coat releasing agent at spraying money, with the drawing machine test, tension set is 200% behind the 168h that films that makes.Detect anti-pierceability test, do not seep water, detect impermeability test, waterproof.
3 one kinds of liquid rubber spray-coating materials of embodiment with hypertonicity.
A kind of prescription with liquid rubber spray-coating material of hypertonicity is:
A kind of liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; The A component is an anion liquid body rubber bitumen emulsion, the water-based spray material; The B component is a coagulant solution;
A component anion liquid body rubber bitumen emulsion adds up to 100kg, wherein, and the fine copolymer rubber emulsion of divinyl propylene 15kg; No. 100 petroleum pitch emulsion 30kg; Anionic dispersing agents TH-904 is that 0.25kg, naphthalenesulfonate formaldehyde condensation compound 0.25kg, Acumer940 polymkeric substance are 0.15kg, AS AS 2.2kg, AEO 0.2%; OEP-70 4%, and AEP 10%; Carbon black 0.3kg, fineness is not less than 800 purpose porcelain powder 0.75kg, and water is surplus.
The B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
The B component is represented with mass percent, is 10% the aqueous solution by 97% calcium chloride, 2% sodium-chlor, the formulated concentration of 5% compound ferro-aluminum mixed with polymers, and compound ferro-aluminum polymkeric substance is a bodied ferric sulfate.
Having the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
The preparation of A component anion liquid body rubber bitumen emulsion, the preparation of B component condensing agent and to have a spraying coating process of liquid rubber spray-coating material of hypertonicity identical with embodiment 1.
The glued membrane checking.
Have a certain amount of moisture that gets to separate out in the glued membrane that generates, behind the 24h, coating is dry, and the surface is evenly smooth, thickness 1.8mm.Do adhesive test behind the 168h, according to the ASTM standard, material can't be peeled off from body of wall.Use the same method, coat releasing agent at spraying money, with the drawing machine test, tension set is 200% behind the 168h that films that makes.Detect anti-pierceability test, do not seep water, detect impermeability test, waterproof.
4 one kinds of liquid rubber spray-coating materials of embodiment with hypertonicity.
A kind of prescription with liquid rubber spray-coating material of hypertonicity is:
A kind of liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; The A component is an anion liquid body rubber bitumen emulsion, the water-based spray material; The B component is a coagulant solution;
A component anion liquid body rubber bitumen emulsion adds up to 100kg, wherein, and isoprene copolymer rubber latex 20kg; Coal-tar pitch emulsion 15kg; Anionic dispersing agents naphthalene sulfonate salt polycondensate is that 0.25kg, naphthalenesulfonate formaldehyde condensation compound 0.55kg, CD-4 are 0.15kg, AS rosined soap 1kg, sodium alkyl benzene sulfonate 1.2kg, AEO 9%; OEP-70 2%, and AEP 0.6%; Water is surplus.
The B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
The B component is represented with mass percent, is 10% the aqueous solution by 95% calcium chloride, 2% sodium-chlor, the formulated concentration of 5% compound ferro-aluminum mixed with polymers, and compound ferro-aluminum polymkeric substance is Poly aluminum Chloride (PAC) and bodied ferric sulfate.
Having the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
The preparation of A component anion liquid body rubber bitumen emulsion, the preparation of B component condensing agent and to have a spraying coating process of liquid rubber spray-coating material of hypertonicity identical with embodiment 1.
The glued membrane checking.
Have a certain amount of moisture that gets to separate out in the glued membrane that generates, behind the 24h, coating is dry, and the surface is evenly smooth, thickness 2.8mm.Do adhesive test behind the 168h, according to the ASTM standard, material can't be peeled off from body of wall.Use the same method, coat releasing agent at spraying money, with the drawing machine test, tension set is 200% behind the 168h that films that makes.Detect anti-pierceability test, do not seep water, detect impermeability test, waterproof.
5 one kinds of liquid rubber spray-coating materials of embodiment with hypertonicity.
A kind of prescription with liquid rubber spray-coating material of hypertonicity is:
A kind of liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; The A component is an anion liquid body rubber bitumen emulsion, the water-based spray material; The B component is a coagulant solution;
A component anion liquid body rubber bitumen emulsion adds up to 100kg; Wherein, polybutadiene rubber emulsion 20kg, transformation of the way bitumen emulsion 30kg; Anionic dispersing agents TH-904 is 0.25kg, naphthalenesulfonate formaldehyde condensation compound 1.5kg; AS synthetic fatty acid soap 1.5kg, AS 0.2kg AEO 5%, OEP-708%, AEP 1%; Carbon black.1kg, fineness is not less than 800 purpose porcelain powder 2.5kg, and water is surplus.
The B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
The B component is represented with mass percent, is 10% the aqueous solution by 95% calcium chloride, 1.5% sodium-chlor, the formulated concentration of 5% compound ferro-aluminum mixed with polymers, and compound ferro-aluminum polymkeric substance is a Poly aluminum Chloride (PAC).
Having the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
The preparation of A component anion liquid body rubber bitumen emulsion, the preparation of B component condensing agent and to have a spraying coating process of liquid rubber spray-coating material of hypertonicity identical with embodiment 1.
The glued membrane checking.
Have a certain amount of moisture that gets to separate out in the glued membrane that generates, behind the 24h, coating is dry, and the surface is evenly smooth, thickness 3.3mm.Do adhesive test behind the 168h, according to the ASTM standard, material can't be peeled off from body of wall.Use the same method, coat releasing agent at spraying money, with the drawing machine test, tension set is 200% behind the 168h that films that makes.Detect anti-pierceability test, do not seep water, detect impermeability test, waterproof.
6 one kinds of liquid rubber spray-coating materials of embodiment with hypertonicity.
A kind of prescription with liquid rubber spray-coating material of hypertonicity is:
A kind of liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; The A component is an anion liquid body rubber bitumen emulsion, the water-based spray material; The B component is a coagulant solution;
A component anion liquid body rubber bitumen emulsion adds up to 100kg, wherein, and isobutene polymer rubber latex 15kg; Shale tar pitch emulsion 50kg, anionic dispersing agents vitriol 2kg, AS synthetic fatty acid soap 2.5kg; AEO 8%, OEP-70 4%, and AEP 10%; Carbon black 2kg, fineness is not less than 800 purpose porcelain powder 0.75kg, and water is surplus.
The B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
The B component is represented with mass percent, is 10% the aqueous solution by 95% calcium chloride, 2% sodium-chlor, the formulated concentration of 3% compound ferro-aluminum mixed with polymers, and compound ferro-aluminum polymkeric substance is a Poly aluminum Chloride (PAC).
Having the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
The preparation of A component anion liquid body rubber bitumen emulsion, the preparation of B component condensing agent and to have a spraying coating process of liquid rubber spray-coating material of hypertonicity identical with embodiment 1.
The glued membrane checking.
Have a certain amount of moisture that gets to separate out in the glued membrane that generates, behind the 24h, coating is dry, and the surface is evenly smooth, thickness 2.5mm.Do adhesive test behind the 168h, according to the ASTM standard, material can't be peeled off from body of wall.Use the same method, coat releasing agent at spraying money, with the drawing machine test, tension set is 200% behind the 168h that films that makes.Detect anti-pierceability test, do not seep water, detect impermeability test, waterproof.
The above; Be merely the preferable embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any technician who is familiar with the present technique field is equal to replacement or change according to technical scheme of the present invention and inventive concept thereof in the technical scope that the present invention discloses, all should be encompassed within protection scope of the present invention.
Claims (9)
1. liquid rubber spray-coating material with hypertonicity, it is characterized in that: said liquid rubber spray-coating material with hypertonicity is divided into A, two kinds of components of B; Said A component is an anion liquid body rubber bitumen emulsion; Said B component is a coagulant solution;
Said A component is represented with mass percent, and fluid rubber bitumen emulsion weight solid content is 50-75%; Wherein, rubber latex 1-35%, bitumen emulsion 10-50%; Anionic dispersing agents 0.01-2%, AS 0.01-2%, AEO 0.1-10%; OEP-70 0.1-10%, AEP 0.1-10%;
Said B component is represented with mass percent, is 3-18% the aqueous solution by calcium chloride, the formulated concentration of compound ferro-aluminum mixed with polymers;
Said have the liquid rubber spray-coating material B component of hypertonicity and the spraying volume ratio of A component is 1/15-1/3.5.
2. a kind of liquid rubber spray-coating material with hypertonicity according to claim 1 is characterized in that:
Rubber in the rubber latex of said A component is tree elastomer or viton; Said viton is selected from the chlorine polybutadiene rubber, butadienestyrene copolymer rubber, the fine copolymer rubber of divinyl propylene, iso-butylene, isoprene copolymer rubber, one or more in the polybutadiene rubber;
Pitch in the bitumen emulsion of said A component is selected from petroleum pitch, coal-tar pitch, shale tar pitch, one or more in the transformation of the way pitch;
The anionic dispersing agents of said A component is selected from vitriol, TH-904, Acumer940 polymkeric substance, CD-4, naphthalene sulfonate salt polycondensate, one or more in the naphthalenesulfonate formaldehyde condensation compound;
The AS of said A component is selected from rosined soap, synthetic fatty acid soap, AS, sodium alkyl benzene sulfonate, alkyl-sulphate, alkyl aryl sulfate, one or more in α-sodium naphthalene sulfonate.
3. a kind of liquid rubber spray-coating material according to claim 1 with hypertonicity; It is characterized in that: said B component is preferably; Representing with mass percent, is 3-18% the aqueous solution by 93-99.7% calcium chloride, the formulated concentration of 0.3-7% compound ferro-aluminum mixed with polymers.
4. a kind of liquid rubber spray-coating material according to claim 1 with hypertonicity; It is characterized in that: said B component also contains sodium-chlor; Representing with mass percent, is 3-18% the aqueous solution by 90-99.2% calcium chloride, 0.5-3% sodium-chlor, the formulated concentration of 0.3-7% compound ferro-aluminum mixed with polymers.
5. according to claim 1 or 3 or 4 described a kind of liquid rubber spray-coating materials with hypertonicity, it is characterized in that: said compound ferro-aluminum polymkeric substance is one or both in Poly aluminum Chloride (PAC), the bodied ferric sulfate.
6. a kind of liquid rubber spray-coating material with hypertonicity according to claim 1 is characterized in that: it is characterized in that: said A component, represent with mass percent, and also contain carbon black 0-3%, fine powder material 0-3%.
7. a kind of liquid rubber spray-coating material with hypertonicity according to claim 2, it is characterized in that: the pitch in the bitumen emulsion of said A component is preferably 60-120 petroleum pitch and emulsion thereof.
8. a kind of liquid rubber spray-coating material with hypertonicity according to claim 1 is characterized in that: the rubber in the rubber latex of said A component is preferably one or both in (co) polychloroprene rubber, the butadienestyrene copolymer rubber.
9. a kind of liquid rubber spray-coating material with hypertonicity according to claim 6 is characterized in that: the carbon black of said A component is that fineness is not less than 600 purpose carbon powders or WHITE CARBON BLACK powder; The fine powder material of said A component is for carefully being not less than 800 purpose porcelain powder or dicalcium powders.