CN108005027A - A kind of cesspool construction of waterproof layer method - Google Patents

A kind of cesspool construction of waterproof layer method Download PDF

Info

Publication number
CN108005027A
CN108005027A CN201711311596.7A CN201711311596A CN108005027A CN 108005027 A CN108005027 A CN 108005027A CN 201711311596 A CN201711311596 A CN 201711311596A CN 108005027 A CN108005027 A CN 108005027A
Authority
CN
China
Prior art keywords
waterproof layer
spray
waterproof
component
components
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711311596.7A
Other languages
Chinese (zh)
Inventor
马庆海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Meichente Environmental Protection And Energy Conservation Product Co L
Original Assignee
Dalian Meichente Environmental Protection And Energy Conservation Product Co L
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Meichente Environmental Protection And Energy Conservation Product Co L filed Critical Dalian Meichente Environmental Protection And Energy Conservation Product Co L
Priority to CN201711311596.7A priority Critical patent/CN108005027A/en
Publication of CN108005027A publication Critical patent/CN108005027A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of cesspool construction of waterproof layer method, include the following steps：（1）Base treatment；（2）Spray waterproof layer；（3）Repeat step（2）2 to 3 times.Two kinds of components of A, B are mixing cured rapidly during spraying application, antiseptic, silver powder and zinc powder are wrapped in the waterproof layer to be formed, effective antimicrobial component is gradually discharged from film, play the role of a sustained release, antimicrobial component, which has not only been effectively ensured, to be washed away by flowing water easily, and can ensure that will not adhere on waterproof coating, cooperating microorganisms and algae, reduce the possibility that antiseptic produces water body secondary pollution.Nano-silver powder and antiseptic in formula, can effectively inhibit bacteria growth, prevent microorganism in waterproof coating surface attachment, grow, prevent waterproof material from occurring biodegradable, avoid the antibacterial and mouldproof that waterproof layer fails from gathering；Further antibacterial Eradicates tastes are mould proof for nano zinc powder energy.

Description

A kind of cesspool construction of waterproof layer method
Technical field
The invention belongs to rubber coating technical field, and in particular to a kind of cesspool construction of waterproof layer method.
Background technology
With the raising of living standards of the people and flourishing for industrial sector, the eutrophication of water resource caused by sewage Problem is increasingly severe.Artificial water lake, pond, offal treatment field and settling tank, for a long time in underground by the underground of eutrophication When water soaks, bacterium and algae may be attached on waterproof layer, so as to cause waterproof coating to suffer erosion, or even biology occurs Degraded produces leakage, loses waterproof effect.It would therefore be highly desirable to produce a kind of special waterproof that can be contacted for a long time with nutritive water Corrosion-inhibiting coating product.
The content of the invention
For above-mentioned technical problem existing in the prior art, present invention technical solution used to achieve the above object It is：A kind of cesspool construction of waterproof layer method, includes the following steps：
（1）Base treatment：After top board structure concreting, hydraulic pressure reality should be received repeatedly, makes substrate surface smooth, it is flat Whole degree is checked that the gap of one basic unit of ruler is no more than 5mm, and only allows smooth variation with 2m guiding rulers；The gas of substrate surface Hole, uneven, honeycomb, gap, dusting etc., answer repairing treatment, basal plane must totally, without laitance, without droplet, impermeable；
（2）Spray waterproof layer：After enhancement layer is done solid work, liquid rubber spray-coating material is begun to use to spray waterproof layer, the twice of contact apply Layer spray paint direction should be orthogonal；When film coated surface is fully cured（It is tack-free）Afterwards, lower road spraying application can just be carried out；
（3）Repeat step（2）2 to 3 times.
Further, the specific component of the liquid rubber spray-coating material is：The liquid rubber spray-coating material is divided into two kinds of A, B Component；The A components are anion liquid body rubber asphalt emulsion；The B components are coagulant solution；The component A, with matter Percentage to be measured to represent, liquid rubber asphalt emulsion weight solid content is 50-75%, wherein, rubber latex 1-35%, asphalt emulsion 10-50%, anionic dispersing agents 0.01-2%, anion surfactant 0.01-2%, fatty alcohol polyoxyethylene ether 0.1- 10%, OEP-70 0.1-10%, AEP 0.1-10%, carbon black 0-3%, fine powder material 0-3%, antiseptic 0.3-1%, Nano-Zinc Powder 0.1-0.5%, nano-silver powder 0.1-0.5%；The B component, is represented with mass percent, is gathered by calcium chloride, Complex aluminium-iron The concentration that compound mixed preparing forms is 3-18% aqueous solution, and the Complex aluminium-iron polymer is aluminium polychloride, polymerised sulphur One or both of sour iron；The spraying Capacity Ratio with liquid rubber spray-coating material B component and component A is 1/15-1/ 3.5。
Compared with prior art, the beneficial effects of the invention are as follows：Spraying process is easy for construction, moment after efficient, spraying Shaping, rapid hardening film forming.Liquid rubber spray-coating material has excellent chemical resistance, acidproof, alkali, salt and chlorine, especially suitable The anti-corrosion waterproofs such as artificial water lake, pond, offal treatment field and settling tank for accommodating eutrophic water body.A during spraying application, Two kinds of components of B are mixing cured rapidly, and antiseptic, silver powder and zinc powder are wrapped in the waterproof layer to be formed, effective antimicrobial component by Gradually discharged from film, play the role of a sustained release, antimicrobial component has not only been effectively ensured will not be easily by flowing water Wash away, and can ensure that will not adhere on waterproof coating, cooperating microorganisms and algae, reduce antiseptic and two produced to water body The possibility of secondary pollution.Nano-silver powder and antiseptic in formula, can effectively inhibit bacteria growth, prevent microorganism to be applied in waterproof Film surface attachment, grow, and prevents waterproof material from occurring biodegradable, avoids the antibacterial and mouldproof that waterproof layer fails from gathering；Nano zinc powder Further antibacterial Eradicates tastes are mould proof for energy.
Embodiment
The technical solution in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation Example is only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this area is common Technical staff's all other embodiments obtained without making creative work, belong to the model that the present invention protects Enclose.
Embodiment：
Liquid rubber spray-coating material is prepared, the liquid rubber spray-coating material is divided into two kinds of components of A, B；The A components are anion Liquid rubber asphalt emulsion；The B components are coagulant solution；
A component anion liquid body rubber asphalt emulsions add up to 100kg, wherein, (co) polychloroprene rubber lotion 25kg, No. 80 stones Oil asphalt lotion 30kg, anionic dispersing agents TH -904 are 0.15kg, naphthalenesulfonate formaldehyde condensation compound 0.15kg, CD -4 is 0.15kg, anion surfactant rosin soap 1kg, synthetic fatty acid soap 0.5kg, alkylsulfonate 0.2kg, fatty alcohol polyoxy Vinethene 2%, OEP-70 3%, AEP 4%；Carbon black 1.5kg, fineness are not less than the porcelain powder 0.75kg of 800 mesh, dodecyl two Methyl-benzyl ammonium chloride 2.5kg, nano zinc powder 0.3kg, nano-silver powder 0.1kg, water is surplus.B component, with mass percent table Show, the aqueous solution that the concentration being formulated by calcium chloride, Complex aluminium-iron mixed with polymers is 3-18%；B components, with quality hundred Divide than representing, the concentration being formulated by 95% calcium chloride, 1.5% sodium chloride, 5% Complex aluminium-iron mixed with polymers is 10% Aqueous solution, Complex aluminium-iron polymer are aluminium polychloride.The spraying Capacity Ratio of liquid rubber spray-coating material B components and A components For 1/15-1/3.5.
Base treatment：After concreting, hydraulic pressure reality should be received repeatedly, makes substrate surface smooth, its flatness 2m Guiding ruler is checked that the gap of one basic unit of ruler is no more than 5mm, and only allows smooth variation；The stomata of substrate surface, it is concavo-convex not Flat, honeycomb, gap, dusting etc., answer repairing treatment, basal plane must totally, without laitance, without droplet, impermeable；Spray waterproof layer： After basic unit's layer is done solid work, liquid rubber spray-coating material is begun to use to spray waterproof layer, the twice coating spraying material direction of contact should be mutual Vertically；When film coated surface is fully cured（It is tack-free）Afterwards, lower road spraying application can just be carried out；By prepared A, B component point It is not encased in respective proportion container, under the promotion of dynamical system, A components and B components are transported respectively by two pipelines Row arrive respective spray gun, and two muzzle slope inwardly during spraying, and spray angle is directed at the same area of object basal plane that needs spray at the same time Face, material spray moment formed atomization process, two components to reach basal plane before or arrival basal plane when be sufficiently mixed so that Form rubber asphalt film evenly.Two components be mixed into up to spray-coating surface joint distance be 350-600mm；Repeat Spraying 2 to 3 times.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of changes, modification, replace And modification, the scope of the present invention is defined by the appended.

Claims (2)

  1. A kind of 1. cesspool construction of waterproof layer method, it is characterised in that include the following steps：
    （1）Base treatment：After concreting, hydraulic pressure reality should be received repeatedly, makes substrate surface smooth；
    （3）Spray waterproof layer：After basic unit's layer is done solid work, liquid rubber spray-coating material is begun to use to spray waterproof layer, the twice of contact apply Layer spray paint direction should be orthogonal；
    （3）Repeat step（2）2 to 3 times.
  2. A kind of 2. cesspool construction of waterproof layer side as claimed in claim 1, it is characterised in that the liquid rubber spray-coating material Specifically component is：The liquid rubber spray-coating material is divided into two kinds of components of A, B；The A components are anion liquid body rubber pitch Lotion；The B components are coagulant solution；The component A, is represented with mass percent, and liquid rubber asphalt emulsion weight is consolidated Content is 50-75%, wherein, rubber latex 1-35%, asphalt emulsion 10-50%, anionic dispersing agents 0.01-2%, anion Surfactant 0.01-2%, fatty alcohol polyoxyethylene ether 0.1-10%, OEP-70 0.1-10%, AEP 0.1-10%, charcoal Black 0-3%, fine powder material 0-3%, antiseptic 0.3-1%, nano zinc powder 0.1-0.5%, nano-silver powder 0.1-0.5%；The B groups Point, represented with mass percent, the concentration being formulated by calcium chloride, Complex aluminium-iron mixed with polymers be 3-18% it is water-soluble Liquid, the Complex aluminium-iron polymer are one or both of aluminium polychloride, bodied ferric sulfate；It is described that there is liquid rubber spray The spraying Capacity Ratio of coating B component and component A is 1/15-1/3.5.
CN201711311596.7A 2017-12-11 2017-12-11 A kind of cesspool construction of waterproof layer method Withdrawn CN108005027A (en)