CN102311691A - 一种新型多彩墙漆 - Google Patents
一种新型多彩墙漆 Download PDFInfo
- Publication number
- CN102311691A CN102311691A CN201110211406A CN201110211406A CN102311691A CN 102311691 A CN102311691 A CN 102311691A CN 201110211406 A CN201110211406 A CN 201110211406A CN 201110211406 A CN201110211406 A CN 201110211406A CN 102311691 A CN102311691 A CN 102311691A
- Authority
- CN
- China
- Prior art keywords
- paint
- novel colorful
- wall paint
- colorful wall
- glue solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及油漆领域,具体涉及一种新型多彩墙漆,含有色漆40~60%、保护胶水溶液35~50%,硅丙乳液5~10%,其生产工艺为:(1)制备基础白漆:按照基础白漆各物质的配比称取,往水中加入各物质后搅拌均匀;(2)配色:根据实际需要,将色浆与基础白漆按照配比混合后搅拌均匀,即制成色漆;c、制备保护胶水溶液,按照保护胶水溶液的各物质的配比混合后搅拌均匀;d、配制多彩涂料:将制成的色漆、保护胶水溶液与硅丙乳液按照配比混合后搅拌均匀,即得到成品,该墙漆饰面纹理观感与天然石材极为相似,观感较好;造价仅为天然的十分之一左右,物美价廉。
Description
技术领域
本发明涉及油漆领域,具体涉及一种新型多彩墙漆。
背景技术
目前市面上的漆大都存在纹理观感较差,成本较高的特点,导致建筑成本也同步提高。
实用新型内容
本发明的目的是提供一种新型多彩墙漆,纹理观感较好,成本低。
本发明的目的是这样实现的,一种新型多彩墙漆,在有机硅超耐候外墒漆的基础上,利用带电凝胶同性相斥互不相溶的原理制成。
一种新型多彩墙漆,含有色漆40~60%、保护胶水溶液35~50%,硅丙乳液5~10%。
所述色漆含有基础白漆85~100%、色浆0~15%。
所述基础白漆含有水30~50%,合成锂皂石0.2~0.5%,分散剂0.2~0.5%,消泡剂O.3~0.5%,防腐剂0.1~0.3%,防霉剂0.2~0.5%,改性纤维素0.5~1.0%,钛白粉O~20%,碳酸钙10~40%,弹性硅丙乳液20~40%,所述合成锂皂石为细度45-100目的粉末。
所述保护胶水溶液含有水70~80%,稳定剂5~10%,交联剂5~10%,合成锂皂石3~10%。
其生产工艺为:(1)制备基础白漆:按照基础白漆各物质的配比称取,往水中加入各物质后搅拌均匀;(2)配色:根据实际需要,将色浆与基础白漆按照配比混合后搅拌均匀,即制成色漆;c、制备保护胶水溶液,按照保护胶水溶液的各物质的配比混合后搅拌均匀;d、配制多彩涂料:将制成的色漆、保护胶水溶液与硅丙乳液按照配比混合后搅拌均匀,即得到成品。
该墙漆饰面纹理观感与天然石材极为相似,观感较好;造价仅为天然的十分之一左右,物美价廉。
具体实施方式
实施例1
新型多彩墙漆生产工艺为:(1)制备基础白漆:按比例称取水30~50%,合成锂皂石0.2~0.5%,分散剂0.2~0.5%,消泡剂O.3~0.5%,防腐剂0.1~0.3%,防霉剂0.2~0.5%,改性纤维素0.5~1.0%,钛白粉O~20%,碳酸钙10~40%,弹性硅丙乳液20~40%,往水中加入各物质后搅拌均匀;(2)配色:根据实际需要,按比例称取基础白漆85~100%、色浆0~15%,将色浆与基础白漆按照配比混合后搅拌均匀,即制成色漆;c、制备保护胶水溶液,按比例称取水70~80%,稳定剂5~10%,交联剂5~10%,合成锂皂石3~10%,混合后搅拌均匀;d、配制多彩涂料:按比例称取色漆40~60%、保护胶水溶液35~50%,硅丙乳液5~10%,混合后搅拌均匀即得到成品。
实施例2
新型多彩墙漆生产工艺为:(1)制备基础白漆:按比例称取水45%,合成锂皂石0.5%,分散剂0.5%,消泡剂0.5%,防腐剂0.2%,防霉剂0.5%,改性纤维素0.8%,钛白粉10%,碳酸钙21%,弹性硅丙乳液21%,往水中加入各物质后搅拌均匀;(2)配色:根据实际需要,按比例称取基础白漆90%、色浆10%,将色浆与基础白漆按照配比混合后搅拌均匀,即制成色漆;c、制备保护胶水溶液,按比例称取水77%,稳定剂9%,交联剂9%,合成锂皂石5%,混合后搅拌均匀;d、配制多彩涂料:按比例称取色漆56%、保护胶水溶液39%,硅丙乳液5%,混合后搅拌均匀即得到成品。
实施例3
新型多彩墙漆生产工艺为:(1)制备基础白漆:按比例称取水22.68千克,合成锂皂石0.252千克,分散剂0.252千克,消泡剂0.252千克,防腐剂0.1008千克,防霉剂0.252千克,改性纤维素0.4032千克,钛白粉0.5.04千克,碳酸钙10.584千克,弹性硅丙乳液10.584千克,往水中加入各物质后搅拌均匀;(2)配色:根据实际需要,按比例称取基础白漆50.4千克、色浆5.6千克,将色浆与基础白漆按照配比混合后搅拌均匀,即制成色漆;c、制备保护胶水溶液,按比例称取水30.03千克,稳定剂3.51千克,交联剂3.51千克,合成锂皂石1.95千克,混合后搅拌均匀;d、配制多彩涂料:按比例称取色漆56千克、保护胶水溶液39千克,硅丙乳液5千克,混合后搅拌均匀即得到成品。所述合成锂皂石(硅酸镁锂)是一种人工合成的三八面体层状胶体材料,在水体系中具极强的成胶性能,具有优异的触变性、分散性、悬浮性和增稠性。
Claims (5)
1.一种新型多彩墙漆,其特征在于:含有色漆40~60%、保护胶水溶液35~50%,硅丙乳液5~10%。
2.根据权利要求1所述的一种新型多彩墙漆,其特征在于:所述色漆含有基础白漆85~100%、色浆0~15%。
3.根据权利要求1所述的一种新型多彩墙漆,其特征在于:所述基础白漆含有水30~50%,合成锂皂石0.2~0.5%,分散剂0.2~0.5%,消泡剂O.3~0.5%,防腐剂0.1~0.3%,防霉剂0.2~0.5%,改性纤维素0.5~1.0%,钛白粉O~20%,碳酸钙10~40%,弹性硅丙乳液20~40%,所述合成锂皂石为细度45-100目的粉末。
4.根据权利要求1所述的一种新型多彩墙漆,其特征在于:所述保护胶水溶液含有水70~80%,稳定剂5~10%,交联剂5~10%,合成锂皂石3~10%。
5. 根据权利要求1所述的一种新型多彩墙漆,其特征在于:其生产工艺为:(1)制备基础白漆:按照基础白漆各物质的配比称取,往水中加入各物质后搅拌均匀;(2)配色:根据实际需要,将色浆与基础白漆按照配比混合后搅拌均匀,即制成色漆;c、制备保护胶水溶液,按照保护胶水溶液的各物质的配比混合后搅拌均匀;d、配制多彩涂料:将制成的色漆、保护胶水溶液与硅丙乳液按照配比混合后搅拌均匀,即得到成品。