CN102295439A - 矿用快硬高强混凝土外加剂 - Google Patents
矿用快硬高强混凝土外加剂 Download PDFInfo
- Publication number
- CN102295439A CN102295439A CN 201010219535 CN201010219535A CN102295439A CN 102295439 A CN102295439 A CN 102295439A CN 201010219535 CN201010219535 CN 201010219535 CN 201010219535 A CN201010219535 A CN 201010219535A CN 102295439 A CN102295439 A CN 102295439A
- Authority
- CN
- China
- Prior art keywords
- concrete
- reducing agent
- component
- strength
- quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了矿用快硬高强混凝土外加剂,其特征在于,其组成及其质量百分含量包括:高效减水剂:10%~15%碱性早强组份:1%~5%金属引气组份铝粉:0.5%~5%促凝早强组份:75%~80%其中,高效减水剂由萘系高效减水剂和氨基磺酸盐高效减水剂复合,促凝早强组份由525快硬水泥和525速凝水泥组成。可以使混凝土具有较高的流动性能满足泵送施工,又可以明显缩短混凝土的凝结时间,并具有较高的后期强度。
Description
技术领域
本发明涉及一种用于煤矿低温施工的快凝混凝土外加剂,具体说是一种在低温条件下使混凝土具有较高流动性能进行泵送施工,并能在较短的时间内凝结硬化的混凝土外加剂,属于混泥土外加剂技术领域。
背景技术
煤矿混凝土是一种在低温下施工的特种混凝土,首先由于混凝土浇筑地点位于井下混凝土泵送距离长,因此要求混凝土具有较高的流动性以满足施工要求。与此同时矿井下温度低,使用普通外加剂的混凝土凝结时间过长,且有可能影响后期强度。因此,要求混凝土尽可能缩短凝结时间,来提高施工效率,保证工程质量。而在现在广泛使用的各种混凝土外加剂均不能很好的同时满足以上两种要求,以普通有机和无机早强组份复配的普通早强减水剂对混凝土3天、7天强度有一定提高,但对于混凝土的凝结时间和小时抗压强度却没有明显的提高作用。而采用特种水泥和速凝剂配制的混凝土虽然能很好的满足对凝结时间的要求,但混凝土施工性能差,且部分使用铝酸盐水泥配制的混凝土虽然早期强度较高,但后期强度下降明显,只能用于临时性的抢修工程,无法用于永久性建筑物。
发明内容
本发明目的是针对普通早强剂对缩短凝结时间无明显效果而特种水泥又不能很好的满足施工性和耐久性的要求,而提供了一种既可以满足混凝土具有较高的流动性能满足泵送施工,又可以明显缩短混凝土的凝结时间,并具有较高的后期强度的混凝土外加剂超早强泵送剂,主要采用萘系高效减水剂、氨基磺酸盐高效减水剂、碱性早强组份、金属引气组份和促凝早强剂。
本发明的ADD-M-KY矿用快硬高强混凝土外加剂,其特征在于,其组成及其质量百分含量包括:
高效减水剂:10%~15%
碱性早强组份:1%~5%
金属引气组份铝粉:0.1%~5%
促凝早强组份:75%~80%
其中,高效减水剂由萘系高效减水剂和氨基磺酸盐高效减水剂复合,促凝早强组份由525快硬水泥和525速凝水泥组成。
上述所述碱性早强组份为碳酸钠。
本发明中,萘系高效减水剂、氨基磺酸盐高效减水剂用于提高混凝土的流动性,来改善混凝土的施工性能,并通过降低混凝土单位体积用水量的方式来缩短混凝土的凝结时间,提高混凝土耐久性。金属引气组份提高混凝土和易性,碱性早强组份则主要用于提高新拌混凝土夜相中的PH值,提高混凝土的早期强度缩短混凝土凝结时间。促凝早强组份(硫铝酸盐水泥)则起到较快水化反应速度,在早期大量生成水化产物,从而缩短混凝土凝结时间。
本发明的外加剂可以使混凝土具有较高的流动性能满足泵送施工,又可以明显缩短混凝土的凝结时间,并具有较高的后期强度。
具体实施方式
下面以实施例对本发明作进一步说明,但本发明不限于以下实施例。
实施例1
一种ADD-M-KY矿用快硬高强混凝土外加剂,以重量百分比包括:
高效减水剂:15%
碱性早强组份(碳酸钠):4.5%
金属引气组份铝粉:0.5%
促凝早强组份:80%
其中:高效减水剂中萘系高效减水剂和氨基磺酸盐高效减水剂质量比为2∶1,促凝早强组份中525快硬水泥和525速凝水泥质量比为1∶1。
本实施例的制备方法是,按配比称量各种原料,然后在搅拌机内混合,搅拌均匀即可。使用时,采用外掺法,掺量范围:10%~20%,最佳掺量:15%,试验结果如下表所示。
ADD-M-KY矿用快凝高强混凝土外加剂(C30混凝土为准)
名称 | 4h抗压强度 | 28d抗压强度 | 减水率 | 初始坍落度 | 半小时后坍落度 |
ADD-M-KY | ≥3MPa | ≥36MPa | ≥18% | ≥180mm | ≥150mm |
Claims (2)
1.ADD-M-KY矿用快硬高强混凝土外加剂,其特征在于,其组成及其质量百分含量包括:
高效减水剂:10%~15%
碱性早强组份:1%~5%
金属引气组份铝粉:0.5%~5%
促凝早强组份:75%~80%
其中,高效减水剂由萘系高效减水剂和氨基磺酸盐高效减水剂复合,促凝早强组份由525快硬水泥和525速凝水泥组成。
2.权利要求1的ADD-M-KY矿用快硬高强混凝土外加剂,其特征在于,所述碱性早强组份为碳酸钠。