CN102294846B - Cf网片强化型碳纤维预浸料及其生产工艺 - Google Patents
Cf网片强化型碳纤维预浸料及其生产工艺 Download PDFInfo
- Publication number
- CN102294846B CN102294846B CN201110155600.1A CN201110155600A CN102294846B CN 102294846 B CN102294846 B CN 102294846B CN 201110155600 A CN201110155600 A CN 201110155600A CN 102294846 B CN102294846 B CN 102294846B
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- net sheet
- glued membrane
- prepreg
- release liners
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及CF网片强化型碳纤维预浸料及其生产工艺,CF网片强化型预浸料包括单向碳纤维层、CF网片、上层胶膜和下层胶膜,CF网片强化型预浸料包括单向碳纤维层、CF网片、上层胶膜和下层胶膜,所述的CF网片压合在单向碳纤维层上面,所述的CF网片上面是上层胶膜,所述下层胶膜在单向碳纤维层的下面,通过制胶膜、放丝排纱、压合网片、试运转、正常运行生产等工艺生产出CF网片强化型碳纤维预浸料。本发明改变了单向预浸料经向强度高、纬向强度低,甚至没有纬向强度的现状,可使预浸料横向强度提高20%,复合材料横向强度提高20%以上。
Description
一、技术领域
本发明涉及CF网片强化型碳纤维预浸料及其生产工艺。
二、背景技术
随着科学技术水平的不断发展和社会经济发展的强烈需求,碳纤维以其高比强度、高比模量、耐腐蚀、抗疲劳、质量轻、导电、隔热、耐高温等一系列综合优异性能被世界各国高度关注,碳纤维已广泛应用于航空、航天、车辆制造、舰船工业、风力发电、电子通讯、医疗器械、文体休闲器材等军工和民用的众多领域。
目前,碳纤维70%以上的用量都是通过碳纤维预浸料的应用方式实现,无论是航天器材、体育休闲器材等,还是大型风力发电叶片,医疗器材、体育休闲器材等领域,为了充分发挥碳纤维的超高强度性,都是将碳纤维做成单向纤维的预浸料来制造各种产品,而这种只有径向纤维没有纬向纤维的预浸料具有很多缺陷:1、经向强度高、纬向强度低;2、使用时幅面容易裂开,操作不方便;3、铺层后易出现折皱、缝隙等质量隐患。
三、发明内容
为了克服以上缺陷,本发明提供一种CF网片强化型碳纤维预浸料及生产工艺。
本发明的技术方案是:CF网片强化型碳纤维预浸料的生产工艺,其特征是:CF网片强化型碳纤维预浸料包括单向碳纤维层、CF网片、上层胶膜和下层胶膜,所述的CF网片压合在单向碳纤维层上面,所述的CF网片上面是上层胶膜,所述下层胶膜在单向碳纤维层的下面。
本发明CF网片强化型碳纤维预浸料的生产工艺为:一、制胶膜,将涂胶辊的温度升到50℃-90℃,将胶液预热后倒入胶辊上,将离型纸穿过胶辊间隙,然后进行预涂胶,调整两支涂胶辊的间隙,待含胶量达标后正式开机涂制胶膜,将涂制好的离型纸由卷辊按照每分钟2m-30m的速度卷成筒状,然后进入下道工序待用;
二、放丝排纱,在丝架上安装碳纤维纱筒,将成束的单向碳纤维纱束按顺序依次穿过布纱器和张力控制装置,放置在已升温的压合辊上;
三、压合网片,将CF网片引出压合在单向碳纤维纱的上面,再将上胶膜离型纸牵引到CF网片的上面,同时把下胶膜离型纸牵引到碳纤维的下面。
四、试运转,将各组压合辊升起来,将上述单向碳纤维、CF网片、上胶膜离型纸和下胶膜离型纸的前端对齐,然后进行人工牵引,将上离型纸和下离型纸收卷在辊轴上,上胶膜和下胶膜分别融入单向碳纤维和CF网片中,随后将离型膜覆盖在预浸料的上面,将CF网片强化预浸料卷绕在收卷辊的纸筒上,让含浸压合机低速运行;
五、正常运行生产,在低速运行中,调整产品的宽度,碳纤维的均匀度,各组辊筒的温度、压力、间隙和运行速度,根据设定长度将预浸料产品裁断,封装入库。
本发明所述的CF网片是网状无序的碳纤维网片。
本发明所述的CF网片为宽度0.8-1.2m、厚度为0.01-0.09mm,重为5g-12g/m2。
本发明所述的辊筒温度为50℃-100℃、压力为2 kg/cm2-15 kg/cm2、间隙为0.03mm-0.25mm、运行速度为每分钟0.5m-10m。
本发明所述的单向碳纤维与CF网片的强度为3500MPa以上、弹性模量为230GPa以上。
本发明的有益效果是:本发明改变了单向预浸料经向强度高、纬向强度低,甚至没有纬向强度的现状,可使预浸料横向强度提高20%,复合材料横向强度提高20%以上。 四、具体实施方式
本发明涉及CF网片强化型碳纤维预浸料及其生产工艺,其特征是:CF网片强化型碳纤维预浸料包括单向碳纤维层1、CF网片2、上层胶膜3和下层胶膜4,所述的CF网片2压合在单向碳纤维层1上面,所述的CF网片2上面是上层胶膜3,所述下层胶膜4在单向碳纤维层1的下面。
本发明CF网片强化型碳纤维预浸料的生产工艺为:一、制胶膜,将涂胶辊的温度升到50℃-90℃,将胶液预热后倒入胶辊上,将离型纸穿过胶辊间隙,然后进行预涂胶,调整两支涂胶辊的间隙,待含胶量达标后正式开机涂制胶膜,将涂制好的离型纸由卷辊按照每分钟2m-30m的速度卷成筒状,然后进入下道工序待用;
二、放丝排纱,在丝架上安装碳纤维纱筒,将成束的单向碳纤维纱束按顺序依次穿过布纱器和张力控制装置,放置在已升温的压合辊上;
三、压合网片,将CF网片引出压合在单向碳纤维纱的上面,再将上胶膜离型纸牵引到CF网片的上面,同时把下胶膜离型纸牵引到碳纤维的下面。
四、试运转,将各组压合辊升起来,将上述单向碳纤维、CF网片、上胶膜离型纸和下胶膜离型纸的前端对齐,然后进行人工牵引,将上离型纸和下离型纸收卷在辊轴上,上胶膜和下胶膜分别融入单向碳纤维和CF网片中,随后将离型膜覆盖在预浸料的上面,将CF网片强化预浸料卷绕在收卷辊的纸筒上,让含浸压合机低速运行;
五、正常运行生产,在低速运行中,调整产品的宽度,碳纤维的均匀度,各组辊筒的温度、压力、间隙和运行速度,根据设定长度将预浸料产品裁断,封装入库。
实施例1
所述的辊筒温度为50℃、压力为2kg/cm2、间隙为0.03mm-0.25mm、运行速度为每分钟0.5m。
实施例2
所述的辊筒温度为70℃、压力为6 kg/cm2、间隙为0.08mm、运行速度为每分钟2.5m。
实施例3
所述的辊筒温度为80℃、压力为10 kg/cm2、间隙为0.15mm、运行速度为每分钟4m。
实施例4
所述的辊筒温度为90℃、压力为12 kg/cm2、间隙为0.20mm、运行速度为每分钟6.5m。
实施例5
所述的辊筒温度为100℃、压力为15 kg/cm2、间隙为 0.25mm、运行速度为每分钟10m。
Claims (2)
1.生产一种CF网片强化型碳纤维预浸料的工艺,其特征是:CF网片强化型碳纤维预浸料包括单向碳纤维层、CF网片、上层胶膜和下层胶膜,所述的CF网片压合在单向碳纤维层上面,所述的CF网片上面是上层胶膜,所述下层胶膜在单向碳纤维层的下面,所述的CF网片是网状无序的碳纤维网片,所述的CF网片为宽度0.8-1.2m、厚度为0.01-0.09mm,重为5g/m2-12g/m2,工艺依次包括以下步骤:
一、制胶膜,将涂胶辊的温度升到50℃-90℃,将胶液预热后倒入胶辊上,将离型纸穿过胶辊间隙,然后进行预涂胶,调整两支涂胶辊的间隙,待含胶量达标后正式开机涂制胶膜,将涂制好胶的离型纸由卷辊按照每分钟2m-30m的速度卷成筒状,然后进入下道工序待用;
二、放丝排纱,在丝架上安装碳纤维纱筒,将成束的单向碳纤维纱束按顺序依次穿过布纱器和张力控制装置,放置在已升温的压合辊上;
三、压合网片,将CF网片引出压合在单向碳纤维纱的上面,再将上胶膜离型纸牵引到CF网片的上面,同时把下胶膜离型纸牵引到碳纤维的下面;
四、试运转,将各组压合辊升起来,将上述单向碳纤维、CF网片、上胶膜离型纸和下胶膜离型纸的前端对齐,然后进行人工牵引,将上离型纸和下离型纸收卷在辊轴上,上胶膜和下胶膜分别融入单向碳纤维和CF网片中,随后将离型纸覆盖在预浸料的上面,将CF网片强化预浸料卷绕在收卷辊的纸筒上,让含浸压合机低速运行;正常运行生产,在低速运行中,调整产品的宽度,碳纤维的均匀度,各组辊筒的温度、压力、间隙和运行速度,根据设定长度将预浸料产品裁断,封装入库。
2.根据权利要求1所述的生产一种CF网片强化型碳纤维预浸料的生产工艺,其特征是:所述的辊筒温度为50℃-100℃、压力为2kg/cm2-15kg/cm2、间隙为0.03mm-0.25mm、运行速度为每分钟0.5m-10m。