CN102294717B - Multiple-effect wood protective agent based on metal oxide - Google Patents
Multiple-effect wood protective agent based on metal oxide Download PDFInfo
- Publication number
- CN102294717B CN102294717B CN 201110242949 CN201110242949A CN102294717B CN 102294717 B CN102294717 B CN 102294717B CN 201110242949 CN201110242949 CN 201110242949 CN 201110242949 A CN201110242949 A CN 201110242949A CN 102294717 B CN102294717 B CN 102294717B
- Authority
- CN
- China
- Prior art keywords
- oxide
- protective agent
- agent based
- metal oxide
- wood protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a multiple-effect wood protective agent based on metal oxide, the preparation method comprises the following steps: weighting zinc oxide, titanium dioxide, copper oxide, magnesium oxide, stannic oxide, molybdenum trioxide, neodymium oxide, lanthana and yttrium oxide according to weight part, uniformly mixing the raw materials and grinding for 30 minutes to obtain the product with particle size less than 80 meshes; drying a mixture accord with the granularity requirement under the temperature lower than 120 DEG C until the moisture less than 1%; acquiring the multiple-effect wood protective agent based on metal oxide. The present invention has the advantages of simple process, easy industrialization, and cleanness without pollution.
Description
Technical field
The present invention relates to timber protective agent, be specially a kind of multiple-effect wood protective agent based on metal oxide.
Background technology
At present, in the manufacturing enterprise of timber, in the process of converted timber, need to adopt the repeatedly processing of various medicaments just can reach the kinds of protect effect such as fire-retardant, anticorrosion to timber.
Summary of the invention
Technical problem solved by the invention is to provide a kind of multiple-effect wood protective agent based on metal oxide, to solve the shortcoming in the above-mentioned background technology.
Technical problem solved by the invention realizes by the following technical solutions:
A kind of multiple-effect wood protective agent based on metal oxide comprises the component of following weight portion:
Zinc oxide 20%-25%
Titanium dioxide 15%-20%
Cupric oxide 10%-15%
Magnesia 10%-15%
Tin ash 10%-15%
Molybdenum trioxide 7%-9%
Neodymia 7%-9%
Lanthana 7%-9%
Yittrium oxide 7%-9%.
A kind of preparation method of multiple-effect wood protective agent based on metal oxide may further comprise the steps:
The first step: the percentage by parts by weight of raw materials takes by weighing zinc oxide, titanium dioxide, cupric oxide, magnesia, tin ash, molybdenum trioxide, neodymia, lanthana, yittrium oxide, and raw material mixed and grinds 30min to particle diameter less than 80 orders;
Second step: the mixed material that will meet granularity requirements is dried to moisture less than 1% being lower than under 120 ℃ of conditions; Namely obtain a kind of multiple-effect wood protective agent based on metal oxide.
Know-why of the present invention is: fire-retardant, the smoke suppressant of preparation timber take Multimetal oxide as main component, various materials are by different mechanism performance fire retardations, such as tin ash energy catalysis timber alkylation process, the oxidation state of the molybdenum ion of molybdenum trioxide and ligancy mutability can generate novel substance with timber, cupric oxide by the reductive coupling mechanism can with timber on hydroxyl reaction etc., each component is mixed the different catalytic action of generation when using, have synergistic, flame retardant effect is better during than single use; Metal oxide reduces producing flammable tar component and other volatile matters in the combustion of wood process by catalytic action among the present invention, has smoke effect, has guaranteed the smoke suppressing that fire retardant of the present invention is good; Fire retardant not only has good flame retarding and smoke suppressing properties among the present invention, also has good mildew-resistant, mothproof, photocatalysis, automatic cleaning action.
Beneficial effect
Protective agent not only has good flame retarding and smoke suppressing properties among the present invention, also has good mildew-resistant, mothproof, photocatalysis, automatic cleaning action, and technique of the present invention is simple, easily industrialization, cleanliness without any pollution.Be uniformly applied to timber protective agent of the present invention in adhesive, the coating or be paved in wooden shavings, the lumber fibre, the basic production technique of other Wood-based composite is constant, can a step finish high efficient protected and press down cigarette timber Wood-based composite.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
Embodiment 1
Take by weighing zinc oxide 200 grams, titanium dioxide 150 grams, cupric oxide 100 grams, magnesia 150 grams, tin ash 120 grams, molybdenum trioxide 70 grams, neodymia 80 grams, lanthana 70 grams, yittrium oxide 80 grams by the percentage of parts by weight of raw materials, and raw material mixed and grinds 30min to particle diameter less than 80 orders; The mixed material that will meet granularity requirements is dried to moisture less than 1% being lower than under 120 ℃ of conditions; Namely obtain a kind of multiple-effect wood protective agent based on metal oxide.
Embodiment 2
Take by weighing zinc oxide 230 grams, titanium dioxide 160 grams, cupric oxide 130 grams, magnesia 100 grams, tin ash 130 grams, molybdenum trioxide 80 grams, neodymia 80 grams, lanthana 80 grams, yittrium oxide 80 grams by the percentage of parts by weight of raw materials, and raw material mixed and grinds 30min to particle diameter less than 80 orders; The mixed material that will meet granularity requirements is dried to moisture less than 1% being lower than under 120 ℃ of conditions; Namely obtain a kind of multiple-effect wood protective agent based on metal oxide.
Embodiment 3
Take by weighing zinc oxide 240 grams, titanium dioxide 170 grams, cupric oxide 120 grams, magnesia 130 grams, tin ash 120 grams, molybdenum trioxide 80 grams, neodymia 80 grams, lanthana 70 grams, yittrium oxide 80 grams by the percentage of parts by weight of raw materials, and raw material mixed and grinds 30min to particle diameter less than 80 orders; The mixed material that will meet granularity requirements is dried to moisture less than 1% being lower than under 120 ℃ of conditions; Namely obtain a kind of multiple-effect wood protective agent based on metal oxide.
Above demonstration and described basic principle of the present invention and principal character and advantage of the present invention; the technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications; these changes and improvements all fall in the claimed scope of the invention, and the claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (2)
1. a multiple-effect wood protective agent based on metal oxide is characterized in that, comprises the component of following weight portion:
Zinc oxide 20%-25%
Titanium dioxide 15%-20%
Cupric oxide 10%-15%
Magnesia 10%-15%
Tin ash 10%-15%
Molybdenum trioxide 7%-9%
Neodymia 7%-9%
Lanthana 7%-9%
Yittrium oxide 7%-9%.
2. the preparation method of a multiple-effect wood protective agent based on metal oxide as claimed in claim 1 is characterized in that, may further comprise the steps:
The first step: the percentage by parts by weight of raw materials takes by weighing zinc oxide, titanium dioxide, cupric oxide, magnesia, tin ash, molybdenum trioxide, neodymia, lanthana, yittrium oxide, and raw material mixed and grinds 30min to particle diameter less than 80 orders;
Second step: the mixed material that will meet granularity requirements is dried to moisture less than 1% being lower than under 120 ℃ of conditions; Namely obtain a kind of multiple-effect wood protective agent based on metal oxide.