CN102269681A - Eva中va含量的测试方法 - Google Patents
Eva中va含量的测试方法 Download PDFInfo
- Publication number
- CN102269681A CN102269681A CN 201110111711 CN201110111711A CN102269681A CN 102269681 A CN102269681 A CN 102269681A CN 201110111711 CN201110111711 CN 201110111711 CN 201110111711 A CN201110111711 A CN 201110111711A CN 102269681 A CN102269681 A CN 102269681A
- Authority
- CN
- China
- Prior art keywords
- eva
- vinyl acetate
- content
- pyrolysis
- measuring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及光伏行业组件使用材料EVA中VA含量的测试方法，先对EVA进行称重，EVA升温热解，在热解结束后对固体物质称重，热解失重部分为产生的乙酸气体，乙酸与乙酸乙烯酯的摩尔比为1∶1，可快速计算出EVA中的乙酸乙烯酯的含量，本发明能解决现有存在着明显的缺陷问题。
Description
技术领域
本发明涉及光伏行业组件使用材料EVA中VA含量的测试方法。
背景技术
EVA是晶体硅太阳能电池广泛使用的封装材料。EVA具有优良的柔韧性，耐冲击性，弹性、光学透明性、低温绕曲性、粘着性，耐环境应力开裂性、耐候性、耐化学药品性，热密封性以及电性能等。
EVA的性能主要取决于熔融指数(以MI表示)和醋酸乙烯酯(以VA表示)的含量。VA含量作为基本参数指标，直接影响EVA的粘结性、透明性等性能和太阳能组件的耐久性。同时，VA含量影响EVA的软硬，对工艺生产有很大影响。再者，在目前太阳能用EVA市场紧俏的情况下，各种牌号甚至无牌号母料在许多厂家被混合使用，因此控制EVA来料的VA含量大有必要。
目前已报导的EVA中VA含量的测定，主要有仪器分析法(红外光谱法)和化学分析法(皂化法)两种。前者需要配制一系列乙烯-醋酸乙烯酯的标准样品，分别打出标准红外光谱图，测定时将被测EVA的红外光谱图进行对照，即可得出被测样品的VA含量。这种方法虽然快捷但准确度不高且仪器使用专一。后者是将EVA将样品首先在碱性介质中发生皂化反应，然后采用酸滴回剩余的碱，从而计算出共聚物中VA的含量，但这种方法结果总是比实际值高或低，波动性大，需要对反应条件研究。
综上所述，传统测定的方法存在着明显的缺陷，对于光伏行业快速发展的大环境中，寻找一种快速、简便、准确的测量VA含量的方法至关重要。
发明内容
为了克服上述缺陷，本发明要解决的技术问题是：针对现有存在着明显的缺陷问题，提供一种EVA中VA含量的测试方法。
为了克服背景技术中存在的缺陷，本发明解决其技术问题所采用的技术方案是：一种EVA中VA含量的测试方法，先对EVA进行称重，EVA升温热解，在热解结束后对固体物质称重，热解失重部分为产生的乙酸气体，乙酸与乙酸乙烯酯的摩尔比为1∶1，可快速计算出EVA中的乙酸乙烯酯的含量。
在本发明中所述测试原理：
EVA中的醋酸乙烯酯会分解为醋酸和一个双键共聚物，剩余部分可认为是乙烯-乙炔共聚物，且反应中醋酸会首先释放出来，剩余的共聚物会在温度更高时继续降解。将样品置于氮气的气氛下，改变其温度，观测样品的分解情况。分解式如下所示：
由于乙酸与乙酸乙烯酯的摩尔比为1∶1，则VA含量表示为：
式中，VA％为乙酸乙烯酯的质量分数，WL％为乙酸的失重率，Mm为乙酸乙烯酯的相对分子量(86)，Ma为乙酸的相对分子量(60)，即VA％＝WL％×1.433。
有益效果：本发明具有较高的灵敏度以及热重精准性，而且在测试过程中具有无毒害、无污染、安全、快速等优点，可以用于生产线组件产品EVA中VA含量的抽检测试。
附图说明
图1为EVA分解曲线图；
图2为EVA膜与EVA母料热重曲线比较图；
具体实施方式
实施例一
EVA膜与EVA母料VA含量的区别
太阳能组件用EVA胶膜中含有极少量固化剂(一般约0.5％以下)，固化剂对VA含量的测定影响很小，EVA膜与EVA母料热重曲线的比较如图2所示。
实例二：重复性验证
采用同一厂家EVA的TGA重复实验如表1所示，可以看出10次实验的结果重复性好。
表1EVA的TGA重复性实验结果
Claims (1)
1.一种EVA中VA含量的测试方法，其特征在于：先对EVA进行称重，EVA升温热解，在热解结束后对固体物质称重，热解失重部分为产生的乙酸气体，乙酸与乙酸乙烯酯的摩尔比为1∶1，可快速计算出EVA中的乙酸乙烯酯的含量。