CN102260459A - 一种水性的黑色的防静电防腐蚀的金属涂料的配方及其制造工艺 - Google Patents

一种水性的黑色的防静电防腐蚀的金属涂料的配方及其制造工艺 Download PDF

Info

Publication number
CN102260459A
CN102260459A CN2010101961578A CN201010196157A CN102260459A CN 102260459 A CN102260459 A CN 102260459A CN 2010101961578 A CN2010101961578 A CN 2010101961578A CN 201010196157 A CN201010196157 A CN 201010196157A CN 102260459 A CN102260459 A CN 102260459A
Authority
CN
China
Prior art keywords
water
black
metallic paint
sbs
electrostatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010101961578A
Other languages
English (en)
Inventor
张文知
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China University of Petroleum East China
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010101961578A priority Critical patent/CN102260459A/zh
Publication of CN102260459A publication Critical patent/CN102260459A/zh
Pending legal-status Critical Current

Abstract

本发明具体涉及一种水性的黑色的防静电防腐蚀的金属涂料。其基料为热塑性弹性体(SBS)改性的乳化沥青，体质和功能填料为鳞片石墨和炭黑，助剂则特别加入环氧基的硅烷偶联剂。该涂料环境友好，对施工人员健康没有影响，涂层牢固，防静电、防腐蚀，附着力强，耐环境性能优良。

Description

一种水性的黑色的防静电防腐蚀的金属涂料的配方及其制造工艺
技术领域
本发明涉及一种水性的黑色的防静电防腐蚀的金属涂料。
背景技术
防腐蚀涂料有着庞大的应用领域，如机械、机床、汽车、农机造船、柴油机等等。目前国内仍主要使用溶剂性涂料，该种涂料不但溶剂的挥发严重污染环境，也严重危害着施工人员的身体健康。市面上虽有一些水性防腐涂料，但大多附着力差，涂层牢固度和耐环境性能欠佳，影响了推广应用。机械与交通行业静电危害严重，每年都发生众多人身和机械事故，甚至火灾。水性涂料有防静电功能的涂料市场急需。
发明内容
本发明旨在提供了水性的黑色的防静电防腐蚀的金属涂料，并公开了其配方和制造工艺。
为了实现上述目的，本发明的技术解决方案为：一种水性的黑色的防静电防腐蚀的金属涂料的配方，步骤可分为三步：第一步，制造SBS改性乳化沥青，使用的原料有10号沥青、60号沥青、粉状的SBS、水、氢氧化钠、水玻璃、聚乙烯醇、乳化剂X-102；制作工艺为：配制乳化剂、沥青乳化；第二步，制造填料和功能填料分散色浆，原材料有1000目石墨、粒状石墨、分散剂NNO、水，制作工艺为砂磨，过滤；第三步制造防静电防腐蚀涂料，原材料为第一步制造的SBS改性乳化沥青，第二步制造的填料功能填料色浆，以及环氧基硅烷偶联剂、增稠剂，工艺为超声均化。
具体实施方式
1、SBS改性乳化沥青的制作
配方：
组分名称                用量比例
10号沥青                15
60号沥青                70
SBS               10
水                100
氢氧化钠          0.5-2.0
水玻璃            1.0-2.0
聚乙烯醇          1.0-8.0
乳化剂X-102       0.5-3.0
工艺：
a、在聚乙烯醇中加入总水量的50％，加热至80℃-90℃，使聚乙烯醇溶解并随时补充蒸发的水分；其余水加热到40℃-50℃，加入如氢氧化钠溶解后加入水玻璃，加热至70℃-80℃；将两部分混合均匀，在高速搅拌下加入乳化剂X-102和SBS，SBS溶解分散后继续保温在70℃-80℃；
b、将沥青在180℃左右熔化脱水，并保温在180℃的已溶化的沥青在高速搅拌下慢慢倾入上述的乳化液中，倾注完毕后继续搅拌5-10分钟，冷却过滤后即为乳化沥青；
c、检测：制成的乳化沥青粒度应在10um以下。
2、填料与功能填料色浆的制作
配方：
组合名称                用量比例
1000目石墨              15-40
粒状炭黑                3-8
分散剂NNO               1-2
水                      100
工艺：
将上述组份加入立式球磨机或砂磨机中研磨1-3小时，放料后过200筛即为色浆。
3、防静电防腐蚀的金属涂料的制作
配方：
组分名称                用量比例
SBS改性乳化沥青         60
填料和功能填料色浆      40-60
环氧基硅烷偶联剂        0.3-0.6
增粘剂                  适量
工艺：
在超声匀化机中依次加入上述组分，加入完成后继续匀化1个小时，然后过滤包装即为成品。
以上述实施方式仅仅是对本发明的优选实施方式进行描述，并非对本明的范围进行限定，在不脱离本发明技术精神的前提下，本领域工程技术人员对本发明的技术方案作出的各种变形和改性，均应落入本发明的权利要求书确定的保护范围内。

Claims (4)

1.一种水性的黑色的防静电防腐蚀的金属涂料，其特征在于其配方为(按质量比)：
热塑性弹性体(SBS)改性乳化沥青    50-70
填料和功能填料色浆               30-70
环氧基硅烷偶联剂                 0.3-0.6
增稠剂                           适量
2.一种制备权利要求书1所述的一种水性的黑色的防静电防腐蚀的金属涂料的制造工艺，其特征在于，所述的方法包括以下步骤：
S1、制备热塑性弹性体(SBS)改性乳化沥青，使用的原料有10号沥青、60号沥青、粉状的SBS、水、氢氧化钠、水玻璃、聚乙烯醇、乳化剂X-102，将以上组分按照一定比例，经过制备乳化剂、沥青乳化等步骤制备成热塑性弹性体(SBS)改性乳化沥青。
S2、制备填料和功能填料色浆，将1000目石墨、粒状石墨、分散剂NNO、水按照一定的质量比混合研磨，然后过200筛制得填料和功能填料色浆。
S3、制备水性的黑色的防静电防腐蚀的金属涂料，将S1制得的热塑性弹性体(SBS)改性乳化沥青、S2制得的填料和功能填料色浆、环氧基硅烷偶联剂增稠剂按照一定的质量比混合，经过超声匀化，最终制得水性的黑色的防静电防腐蚀的金属涂料。
3.根据权利要求书2所述的一种制造权利要求书1所述的水性的黑色的防静电防腐蚀的金属涂料的工艺，其特征在于其基料使用了热塑性弹性体(SBS)改性乳化沥青。
4.根据权利要求书2所述的一种制造权利要求书1所述的水性的黑色的防静电防腐蚀的金属涂料的工艺，其特征在于特别加入了环氧基硅烷偶联剂。
CN2010101961578A 2010-05-31 2010-05-31 一种水性的黑色的防静电防腐蚀的金属涂料的配方及其制造工艺 Pending CN102260459A (zh)