CN102260439A - 一种亮光面底漆 - Google Patents
一种亮光面底漆 Download PDFInfo
- Publication number
- CN102260439A CN102260439A CN2011102354488A CN201110235448A CN102260439A CN 102260439 A CN102260439 A CN 102260439A CN 2011102354488 A CN2011102354488 A CN 2011102354488A CN 201110235448 A CN201110235448 A CN 201110235448A CN 102260439 A CN102260439 A CN 102260439A
- Authority
- CN
- China
- Prior art keywords
- accounts
- priming paint
- account
- primer
- weight percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明的亮光面底漆,该底漆的组分及重量百分比为:丙烯酸树脂占30%-35%、氧化铁红占12%-16%、滑石粉占22%-30%、醋酸丁脂占3%、附着力助剂占2%-3%和二甲苯占10%-14%;上述组分研磨搅拌,再加占16%-20%固体含量50的固定剂形成底漆,再按与底漆1∶1重量加入稀释剂完成。相对于现有技术来说,具有以下优点:1、附着力好,可以牢固附着于光滑的平面,达到小于或等于2级;2、干燥速度快,表干达到5分钟,实干只需要1小时;3、耐冲击,正冲50kg/cm、反冲50kg/cm;4、遮盖率高,小于或等于30g/m2。5、光泽度小于或等于30。
Description
技术领域
本发明涉及一种亮光面底漆。
背景技术
汽车外板部、家电制品及家具等的部件大多为了提高面漆涂膜与成型品的附着性,这些成型品常常预先需要涂覆一层底漆。然而,现有的底漆不易附着于光滑的平面,容易出现脱落的现象,严重影响产品的品质和外观,且干燥速度慢,生产效率低;同时,耐冲击力、遮盖率、硬度和光泽度等都较差。
发明内容
本发明要解决的技术问题是提供一种附着力好、快干、耐冲击、遮盖率高的亮光面底漆。本发明是通过以下技术方案来实现的:
为解决上述技术问题,本发明采用如下技术方案:该底漆的组分及重量百分比为:丙烯酸树脂占30%-35%、氧化铁红占12%-16%、滑石粉占22%-30%、醋酸丁脂占3%、附着力助剂占2%-3%和二甲苯占10%-14%;上述组分研磨搅拌,再加占16%-20%固体含量50的固定剂形成底漆,再按与底漆1:1重量加入稀释剂完成。
进一步的,所述丙烯酸树脂的组分及重量百分比为:丙烯酸丁脂占20%、羟丁脂占15%、羟丙脂占15%、月桂酯占10%、甲甲酯占20%和苯乙烯占20%。
进一步的,所述附着力助剂为聚酯基因极性的酸或氨、有机硅偶联或未改性的氨单体、氯化聚合物或钛酸酯偶联物。
进一步的,所述稀释剂的组分及重量百分比为:二甲笨占60%、醋酸丁酯占30%和环已酮占10%。
进一步的,该底漆的组分及重量百分比为:丙烯酸树脂占30%、氧化铁红占13%、滑石粉占23%、醋酸丁脂占3%、附着力助剂占3%、二甲苯占11%和固体含量50的固定剂占17%。
进一步的,该底漆的组分及重量百分比为:丙烯酸树脂占35%、氧化铁红占12%、滑石粉占22%、醋酸丁脂占3%、附着力助剂占2%、二甲苯占10%和固体含量50的固定剂占16%。
进一步的,该底漆的组分及重量百分比为:丙烯酸树脂占31%、氧化铁红占13%、滑石粉占23%、醋酸丁脂占3%、附着力助剂占3%、二甲苯占11%和固体含量50的固定剂占16%。
本发明的亮光面底漆,相对于现有技术来说,具有以下优点:1、附着力好,可以牢固附着于光滑的平面,达到小于或等于2级;2、干燥速度快,表干达到5分钟,实干只需要1小时;3、耐冲击,正冲50kg/cm、反冲50kg/cm;4、遮盖率高,小于或等于30g/m2。5、光泽度小于或等于30。
具体实施方式
所述亮光面底漆,该底漆的组分及重量百分比为:丙烯酸树脂占30%-35%、氧化铁红占12%-16%、滑石粉占22%-30%、醋酸丁脂占3%、附着力助剂占2%-3%和二甲苯占10%-14%;上述组分研磨搅拌,再加占16%-20%固体含量50的固定剂形成底漆,再按与底漆1:1重量加入稀释剂完成。其附着力好、快干、耐冲击、遮盖率高。
其中,所述丙烯酸树脂的组分及重量百分比为:丙烯酸丁脂占20%、羟丁脂占15%、羟丙脂占15%、月桂酯占10%、甲甲酯占20%和苯乙烯占20%。所述附着力助剂为聚酯基因极性的酸或氨、有机硅偶联或未改性的氨单体、氯化聚合物或钛酸酯偶联物。所述稀释剂的组分及重量百分比为:二甲笨占60%、醋酸丁酯占30%和环已酮占10%。
实施例1:
该底漆的组分及重量百分比为:丙烯酸树脂占30%、氧化铁红占13%、滑石粉占23%、醋酸丁脂占3%、附着力助剂占3%和二甲苯占11%,上述组分研磨搅拌,再加占17%固体含量50的固定剂形成底漆,再按与底漆1:1重量加入稀释剂完成;其中,所述丙烯酸树脂的组分及重量百分比为:丙烯酸丁脂占20%、羟丁脂占15%、羟丙脂占15%、月桂酯占10%、甲甲酯占20%和苯乙烯占20%。所述附着力助剂为聚酯基因极性的酸或氨,当然也可为有机硅偶联或未改性的氨单体、氯化聚合物或钛酸酯偶联物;所述稀释剂的组分及重量百分比为:二甲笨占60%、醋酸丁酯占30%和环已酮占10%。
经广东省东莞市质量监督检测中心,按HG/T 2454-2006《溶剂型聚氨酯涂料(双组分)》检验,本次抽样检验合格。得出的数据为:光泽:≤30;表干:5min;实干:1h(室温);附着力:≤2级;硬度:≥H;遮盖率g/m2:≤30;耐冲击:正冲50kg/cm、反冲50kg/cm。
实施例2:
与实施例1不同之处在于:该底漆的组分及重量百分比为:丙烯酸树脂占35%、氧化铁红占12%、滑石粉占22%、醋酸丁脂占3%、附着力助剂占2%和二甲苯占10%,上述组分研磨搅拌,再加占16%固体含量50的固定剂形成底漆,再按与底漆1:1重量加入稀释剂完成;经广东省东莞市质量监督检测中心,按HG/T 2454-2006《溶剂型聚氨酯涂料(双组分)》检验,本次抽样检验合格。得出的数据为:光泽:≤30;表干:5min;实干:1h(室温);附着力:≤2级;硬度:≥H;遮盖率g/m2:≤30;耐冲击:正冲50kg/cm、反冲50kg/cm。
实施例3:
与实施例1不同之处在于:该底漆的组分及重量百分比为:丙烯酸树脂占31%、氧化铁红占13%、滑石粉占23%、醋酸丁脂占3%、附着力助剂占3%和二甲苯占11%,上述组分研磨搅拌,再加占16%固体含量50的固定剂形成底漆,再按与底漆1:1重量加入稀释剂完成;经广东省东莞市质量监督检测中心,按HG/T 2454-2006《溶剂型聚氨酯涂料(双组分)》检验,本次抽样检验合格。得出的数据为:光泽:≤30;表干:5min;实干:1h(室温);附着力:≤2级;硬度:≥H;遮盖率g/m2:≤30;耐冲击:正冲50kg/cm、反冲50kg/cm。
本发明的亮光面底漆,相对于现有技术来说,具有以下优点:1、附着力好,可以牢固附着于光滑的平面;2、干燥速度快;3、耐冲击强;4、遮盖率高;5、光泽度高;6、硬度好。
以上已将本发明做一详细说明,以上所述,仅为本发明之较佳实施例而已,当不能限定本发明实施范围,即凡依本申请范围所作均等变化与修饰,皆应仍属本发明涵盖范围内。
Claims (7)
1. 一种亮光面底漆,其特征在于:该底漆的组分及重量百分比为:丙烯酸树脂占30%-35%、氧化铁红占12%-16%、滑石粉占22%-30%、醋酸丁脂占3%、附着力助剂占2%-3%和二甲苯占10%-14%;上述组分研磨搅拌,再加占16%-20%固体含量50的固定剂形成底漆,再按与底漆1:1重量加入稀释剂完成。
2.根据权利要求1所述的一种亮光面底漆,其特征在于:所述丙烯酸树脂的组分及重量百分比为:丙烯酸丁脂占20%、羟丁脂占15%、羟丙脂占15%、月桂酯占10%、甲甲酯占20%和苯乙烯占20%。
3.根据权利要求1所述的一种亮光面底漆,其特征在于:所述附着力助剂为聚酯基因极性的酸或氨、有机硅偶联或未改性的氨单体、氯化聚合物或钛酸酯偶联物。
4.根据权利要求1所述的一种亮光面底漆,其特征在于:所述稀释剂的组分及重量百分比为:二甲笨占60%、醋酸丁酯占30%和环已酮占10%。
5.根据权利要求1所述的一种亮光面底漆,其特征在于:该底漆的组分及重量百分比为:丙烯酸树脂占30%、氧化铁红占13%、滑石粉占23%、醋酸丁脂占3%、附着力助剂占3%、二甲苯占11%和固体含量50的固定剂占17%。
6.根据权利要求1所述的一种亮光面底漆,其特征在于:该底漆的组分及重量百分比为:丙烯酸树脂占35%、氧化铁红占12%、滑石粉占22%、醋酸丁脂占3%、附着力助剂占2%、二甲苯占10%和固体含量50的固定剂占16%。
7.根据权利要求1所述的一种亮光面底漆,其特征在于:该底漆的组分及重量百分比为:丙烯酸树脂占31%、氧化铁红占13%、滑石粉占23%、醋酸丁脂占3%、附着力助剂占3%、二甲苯占11%和固体含量50的固定剂占16%。