CN102251676A - Construction method of joint-free heat-insulating, decorative and waterproof integrated composite plate - Google Patents
Construction method of joint-free heat-insulating, decorative and waterproof integrated composite plate Download PDFInfo
- Publication number
- CN102251676A CN102251676A CN2011101022447A CN201110102244A CN102251676A CN 102251676 A CN102251676 A CN 102251676A CN 2011101022447 A CN2011101022447 A CN 2011101022447A CN 201110102244 A CN201110102244 A CN 201110102244A CN 102251676 A CN102251676 A CN 102251676A
- Authority
- CN
- China
- Prior art keywords
- plate
- polymer
- decoration
- integrated composite
- seam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a construction method of a joint-free heat-insulating, decorative and waterproof integrated composite plate. The construction method comprises the following steps: plastering polymer bonding mortar on the surface sprayed with an interface agent, of the seamless integrated composite plate by adopting the point-frame method, sticking on the wall surface with the need of heat insulation, adopting seamless splicing of plate joints of the seamless integrated composite plate and mounting an auxiliary anchoring piece in a region; using a polymer cement adhesive to perform smearing, solid covering, smearing, shaving and leveling on a glass fiber gridding cloth and the anchoring piece which are interleaved mutually in the spliced positions of the plate joints; and sticking a veneer through a polymer waterproof adhesive and then compacting after curing the polymer cement adhesive, thereby enabling a veneer layer of a heat insulation system of the seamless integrated composite plate to be a continuous whole and enabling the whole system to integrate heat insulation, decoration and waterproofing into a whole. The construction method has the beneficial effects of greatly improving waterproof, anti-cracking and anti-impact performances of the plate joints and using the polymer waterproof adhesive for sticking and then compacting so as to enable the veneer layer of the heat insulation system of the seamless integrated composite plate to be the continuous whole and enable the whole system to integrate heat insulation, decoration and waterproofing into a whole.
Description
One, technical field:
The present invention relates to a kind of thermal insulating composite panel job practices that is used for skin, particularly a kind of job practices of not having seam insulation, decoration, waterproof integrated composite plate.
Two, background technology:
At present outside the building in the wall outer heat preservation system, insulation, decoration, waterproof " composite board integrating " heat insulation system commonly used have the simple superiority of job practices, this plate that will reserve certain width of edge that " composite board integrating " anchoring device when sticking construction is located at sheet material usually stitches, and uses the fluid sealant jointing at last with polyethylene foam bar tamponade plate seam then.The common fault of this job practices is: 1. what plate stitched is arranged so that the blocking-up of heat insulation system insulation layer is discontinuous, produces " cold and hot bridge " and has reduced heat insulation effect; The anchoring device be located at composite board integrating around and to insert and make anchoring strength reduce in the heat insulation core material; 3. because the existence of warming plate plate seam brings great hidden danger for the water-proof function of heat insulation system." the thin heat insulation system of plastering " overcomes above-mentioned 3 common faults, but wet construction is long in time limit, method is tired of lock, efficiency of construction is low, construction cost is high.
Three, summary of the invention:
Purpose of the present invention is exactly the above-mentioned defective that exists at prior art, a kind of job practices of not having seam insulation, decoration, waterproof integrated composite plate is provided, this method efficiency of construction height, insulation, decoration, good water-proof effect, no seam composite board integrating heat insulation system of the present invention has kept " composite board integrating heat insulation system commonly used " and " the thin heat insulation system of plastering " superiority, has overcome their weak point separately.
A kind of job practices of not having seam insulation, decoration, waterproof integrated composite plate is: with the face that is sprayed with interfacial agents of seamless composite board integrating, adopt some frame method to spread polymer bonding mortar, stick on the metope that needs insulation, seamless composite board integrating plate seam adopts seamless spliced, the part of simultaneously glass fiber reticular cloth on two seamless composite board integratings being longer than edges of boards 10cm-15cm is in splicing place of plate seam, in interleaved relation with each other and pressure pats whole, and in this zone the piggy-back anchor firmware is installed; After the piggy-back anchor firmware is installed and is finished, glass fiber reticular cloth in interleaved relation with each other and anchoring piece are coated with in splicing place of plate seam with the polymer cement bonding adhesive and face reality also wiping is smooth, its smearing thickness is identical with the thickness of seamless composite board integrating original copolymer cement gel stick, makes polymer cement bonding adhesive float coat and grid enhancement Layer on the seamless composite board integrating of being pasted form continuous jointless integral body; After treating the polymer cement adhesive solidification, will with the facing plate of the identical material of seamless composite board integrating finish coat, size is with the on-the-spot polymer cement adhesive areas size of smearing, with compacting after the glue of polymer water-proof binding, make the continuous one of finish coat of seamless composite board integrating heat insulation system, the insulation of whole system collection, decoration, waterproof are one.
Polymer cement bonding adhesive of the present invention is with inorganic powder and aqueous polymer glue 2-3 by weight proportion: 1 ratio stirs in container and forms, and this bonding adhesive has high-strength, water resistance.
Above-mentioned inorganic powder part by weight is the PO425 cement 45%-55% on quartz sand 35%-45%, powdered whiting 7%-12%, the existing market.
Above-mentioned aqueous polymer collagen material part by weight is that emulsion polymerization 75%-85%, fire retardant 8%-13%, deionized water 5%-10%, thickener 1%-3% material compounded combination form.
Above-mentioned thickener can adopt at least a in the following commercially available thickener model: UH-420, TE-936, TT935, ASE-60.
Above-mentioned emulsion polymerization is: one or more compound ligands of commercially available pure-acrylic emulsion GD-3400, pure-acrylic emulsion GD-3600, pure-acrylic emulsion BA-310T, pure-acrylic emulsion BA-310Ts.
Above-mentioned fire retardant can adopt at least a in the following raw materials according: polymer phosphate ammonium, TCEP, chlorinated paraffin wax.
Polymer water-proof binding collagen material part by weight of the present invention is: short fiber 2%-5%, quartz sand 25%-35%, powdered whiting 10%-12%, PO425 cement 25%-35%, composite the combining of emulsion polymerization 20%-30% material.Glass fiber reticular cloth of the present invention is commercially available alkali resistant glass fibre open weave cloth.Warming plate of the present invention is commercially available Rigid foam polyurethane, polystyrene extruded sheet or expansion polyphenyl plate.Interfacial agents of the present invention is commercially available cement based interfacial agents.Facing plate of the present invention is that commercially available 1mm～3mm is thick: the inorganic plate of plastic-aluminum decorative panel, fluorine carbon lacquer facing, flexible imitative slabstone, flexible clay facing tile.
The invention has the beneficial effects as follows: the waterproof, cracking resistance, the shock resistance that have improved the plate seam greatly.After treating the polymer cement adhesive solidification, will with compacting after the glue of the facing plate of the identical material of seamless composite board integrating finish coat (size is with the on-the-spot polymer cement adhesive areas size of smearing) usefulness polymer water-proof binding, make the continuous one of finish coat of seamless composite board integrating heat insulation system, the insulation of whole system collection, decoration, waterproof are one.
Four, the specific embodiment:
Embodiment 1: it is standby to make the polymer cement bonding adhesive in advance; The alkali resistant glass fibre open weave cloth that cuts length and width and be 70cm * 70cm unit mass and be 160g/m2 is standby; Select the XPS plastic extrusion heated board that 4cm is thick, length and width are 60cm * 60cm and spray the cement based interfacial agents standby on the two sides of plate; Select 1.8mm flexible clay facing tile thick, that length and width are 29.7cm * 29.7cm standby; It is standby to make polymer water-proof binding glue in advance.On the composite board integrating production line, introduce the XPS plastic extrusion heated board, after the surrounding of XPS plastic extrusion heated board is coated with the polymer cement bonding adhesive of scraping 2mm in the 11cm of center, immediately with the glass fiber reticular cloth of 70cm * 70cm apart from be pressed in the thick polymer cement bonding adhesive slurry of 2mm on the XPS extruded sheet (having 20.5cm not have the polymer cement bonding adhesive around 70cm * 70cm glass fiber reticular cloth) and with the surface be coated with scrape smooth, system enters curing through device transmission, dehydration, behind the baking operation, again with polymer water-proof binding glue 30cm * 30cm place in XPS plastic extrusion heated board distance, be coated with to scrape and be pressed on the polymer cement adhesive faec of glass fiber reticular cloth, before not solidifying, polymer water-proof binding glue flattens pasting thereon also compacting in the flexible clay facing tile of the 29.7cm * 29.7cm distance, through solidifying, behind the baking operation, use the flexible clay facing tile facing, the XPS extruded sheet is that the no seam composite board integrating of heat insulating material finishes with regard to making.
Polymer cement bonding adhesive of the present invention is inorganic powder and 3: 1 by weight proportion ratio of aqueous polymer glue to be stirred form in container.The inorganic powder part by weight is quartz sand (80 orders-120 order) 40%, powdered whiting 10%, PO425 cement 50%.Aqueous polymer collagen material part by weight is that BA-310Ts pure-acrylic emulsion 40%, GD-3400 pure-acrylic emulsion 38% fire retardant TCEP 10%, deionized water 10%, ASE-60 thickener 2% material compounded combination form.Polymer water-proof binding collagen material part by weight of the present invention is: short fiber 3%, (80 orders-120 order), quartz sand 25%, powdered whiting 12%, PO425 cement 30%, composite the combining of GD-3400 pure-acrylic emulsion 30% material.
The job practices of seamless composite board integrating of the present invention is: with the face that is sprayed with the cement based interfacial agents of the seamless composite board integrating of above-mentioned flexible clay facing tile facing, after adopting some frame method wiping polymer bonding mortar (the polymer bonding mortar bonding area is greater than 40%), stick on the metope that needs insulation.Every seamless composite board integrating plate seam adopts " seamless spliced ", and the glass fiber reticular cloth of seamless composite board integrating being longer than edges of boards 10cm at plate seam place in interleaved relation with each other and press pat whole, and in no flexible clay facing tile zone or glass fiber reticular cloth zone, punch with Churn drill, piggy-back anchor firmware (every square meter quantity of piggy-back anchor firmware is determined by designing requirement) is installed, after the piggy-back anchor firmware is installed and is finished, with the polymer cement bonding adhesive glass fiber reticular cloth and anchoring piece be coated with face real and wiping smooth, the smearing thickness of bonding adhesive is identical with the thickness of seamless composite board integrating original copolymer cement gel stick, make polymer cement bonding adhesive float coat and grid enhancement Layer on the seamless composite board integrating of being pasted form continuous jointless integral body, improved the waterproof of plate seam greatly, cracking resistance, shock resistance.After treating the polymer cement adhesive solidification, the flexible clay facing tile of 29.7cm * 29.7cm with polymer water-proof binding glue, in having the space of flexible clay facing tile, 30.3cm * 30.3cm is not pasted compacting as filling (need not bullet extension control line during patch block).This just form lattice be 29.7cm * 29.7cm seam wide be the no seam composite board integrating heat insulation system of heat insulating material for the flexible clay facing tile facing of 6mm, XPS extruded sheet.
Embodiment 2: it is standby to make the polymer cement bonding adhesive in advance; The alkali resistant glass fibre open weave cloth that cuts length and width and be 75cm * 75cm unit mass and be 160g/m2 is standby; Select 2cm PU composite insulation boards thick, that length and width are 60cm * 60cm standby; The thick length and width of selection 2mm are that the two-sided plastic-aluminum facing plate of 29.7cm * 29.7cm is standby; It is standby to make polymer water-proof binding glue in advance.On the composite board integrating production line, introduce the PU composite insulation boards, after the surrounding of warming plate is coated with the polymer cement bonding adhesive of scraping 2mm in the 16cm of center, immediately with the glass fiber reticular cloth of 75cm * 75cm apart from be pressed in the thick polymer cement bonding adhesive slurry of 2mm on the PU composite insulation boards, (like this having 30cm not have the polymer cement bonding adhesive around 75cm * 75cm glass fiber reticular cloth) and with the surface be coated with scrape smooth, system enters curing through device transmission, dehydration, behind the baking operation, again with polymer water-proof binding glue on the PU composite insulation boards apart from 30cm * 30cm place scribble to be coated with on the face of polymer cement bonding adhesive and scrape gluing, before not solidifying, polymer water-proof binding glue flattens pasting thereon also compacting in the two-sided plastic-aluminum facing plate distance of 29.7cm * 29.7cm, through solidifying, behind the baking operation, with two-sided plastic-aluminum facing plate facing, PU polyurethane is that the no seam composite board integrating of heat insulating material finishes with regard to making.
Polymer cement bonding adhesive of the present invention is inorganic powder and 2: 1 by weight proportion ratio of aqueous polymer glue to be stirred form in container.
Above-mentioned inorganic powder part by weight is quartz sand (80 orders-120 order) 35%, powdered whiting 10%, PO425 cement 55%.Above-mentioned aqueous polymer collagen material part by weight is that BA-310T pure-acrylic emulsion 40%, GD-3600 pure-acrylic emulsion 42% fire retardant chlorinated paraffin wax 12%, deionized water 5%, ASE-60 thickener 1% material compounded combination form.
Polymer water-proof binding collagen material part by weight of the present invention is: short fiber 5%, (80 orders-120 order) quartz sand 35%, powdered whiting 10%, PO425 cement 25%, composite the combining of GD-3600 pure-acrylic emulsion 25% material.
The job practices of no seam composite board integrating of the present invention is: with the face that is sprayed with the cement based interfacial agents of the no seam composite board integrating of above-mentioned two-sided plastic-aluminum facing plate facing, after adopting some frame method wiping polymer bonding mortar (the polymer bonding mortar bonding area is greater than 40%), stick on the metope that needs insulation.Every no seam composite board integrating plate seam adopts " seamless spliced " and with seamless composite board integrating, the glass fiber reticular cloth of being longer than edges of boards 15cm at plate seam place in interleaved relation with each other and press pat whole, and in no two-sided plastic-aluminum facing plate zone or glass fiber reticular cloth zone, change punching with impacting, piggy-back anchor firmware (every square meter quantity of piggy-back anchor firmware is determined by designing requirement) is installed, after the piggy-back anchor firmware is installed and is finished, with the polymer cement bonding adhesive glass fiber reticular cloth and anchoring piece be coated with face real and wiping smooth, the smearing thickness of bonding adhesive is identical with the thickness of seamless composite board integrating original copolymer cement gel stick, make polymer cement bonding adhesive float coat and grid enhancement Layer on the seamless composite board integrating of being pasted form continuous jointless integral body, improved the waterproof of plate seam greatly, cracking resistance, shock resistance.After treating the polymer cement adhesive solidification, the two-sided plastic-aluminum facing plate of 29.7cm * 29.7cm with polymer water-proof binding glue, in having the space of two-sided plastic-aluminum facing plate, 35.3cm * 35.3cm is not pasted compacting as filling (need not bullet extension control line during pasting board).This just form lattice be the wide two-sided plastic-aluminum facing plate facing for 6mm of 29.7cm * 29.7cm seam be the no seam composite board integrating heat insulation system of heat insulating material with the hard polyurethane foam.
Claims (9)
1. job practices of not having seam insulation, decoration, waterproof integrated composite plate is characterized in that:
The face that is sprayed with interfacial agents with seamless composite board integrating, adopt some frame method to spread polymer bonding mortar, stick on the metope that needs insulation, seamless composite board integrating plate seam adopts seamless spliced, the part of simultaneously glass fiber reticular cloth on two seamless composite board integratings being longer than edges of boards 10cm-15cm is in splicing place of plate seam, in interleaved relation with each other and pressure pats whole, and in this zone the piggy-back anchor firmware is installed; After the piggy-back anchor firmware is installed and is finished, glass fiber reticular cloth in interleaved relation with each other and anchoring piece are coated with in splicing place of plate seam with the polymer cement bonding adhesive and face reality also wiping is smooth, its smearing thickness is identical with the thickness of seamless composite board integrating original copolymer cement gel stick, makes polymer cement bonding adhesive float coat and grid enhancement Layer on the seamless composite board integrating of being pasted form continuous jointless integral body; After treating the polymer cement adhesive solidification, will with the facing plate of the identical material of seamless composite board integrating finish coat, size is with the on-the-spot polymer cement adhesive areas size of smearing, with compacting after the glue of polymer water-proof binding, make the continuous one of finish coat of seamless composite board integrating heat insulation system, the insulation of whole system collection, decoration, waterproof are one.
2. the job practices of no seam insulation according to claim 1, decoration, waterproof integrated composite plate is characterized in that: described polymer cement bonding adhesive is with inorganic powder and aqueous polymer glue 2-3 by weight proportion: 1 ratio stirs in container and forms.
3. the job practices of no seam insulation according to claim 2, decoration, waterproof integrated composite plate is characterized in that: the part by weight of described inorganic powder is quartz sand 35%-45%, powdered whiting 7%-12%, PO425 cement 45%-55%; Described aqueous polymer collagen material part by weight is that emulsion polymerization 75%-85%, fire retardant 8%-13%, deionized water 5%-10%, thickener 1%-3% material compounded combination form.
4. the job practices of no seam insulation according to claim 3, decoration, waterproof integrated composite plate is characterized in that: described thickener adopts at least a in the following raw materials according: UH-420, TE-936, TT935, ASE-60.
5. the job practices of no seam insulation according to claim 3, decoration, waterproof integrated composite plate, it is characterized in that: described emulsion polymerization is: one or more compound ligands of commercially available pure-acrylic emulsion GD-3400, pure-acrylic emulsion GD-3600, pure-acrylic emulsion BA-310T, pure-acrylic emulsion BA-310Ts.
6. the job practices of no seam insulation according to claim 3, decoration, waterproof integrated composite plate is characterized in that: described fire retardant adopts at least a in the following raw materials according: polymer phosphate ammonium, TCEP, chlorinated paraffin wax.
7. the job practices of no seam insulation according to claim 1, decoration, waterproof integrated composite plate is characterized in that: the raw material weight ratio of described polymer water-proof binding glue is: short fiber 2%-5%, quartz sand 25%-35%, powdered whiting 10%-12%, PO425 cement 25%-35%, composite the combining of emulsion polymerization 20%-30% material.
8. the job practices of no seam insulation according to claim 1, decoration, waterproof integrated composite plate is characterized in that: described glass fiber reticular cloth is commercially available alkali resistant glass fibre open weave cloth; Described warming plate is commercially available Rigid foam polyurethane, polystyrene extruded sheet or expansion polyphenyl plate; Described interfacial agents is commercially available cement based interfacial agents.
9. the job practices of no seam insulation according to claim 1, decoration, waterproof integrated composite plate is characterized in that: described facing plate is that commercially available 1mm～3mm is thick: the inorganic plate of plastic-aluminum decorative panel, fluorine carbon lacquer facing, flexible imitative slabstone, flexible clay facing tile.