CN102251331B - 一种屏蔽布料及其制造方法 - Google Patents
一种屏蔽布料及其制造方法 Download PDFInfo
- Publication number
- CN102251331B CN102251331B CN201110202805.0A CN201110202805A CN102251331B CN 102251331 B CN102251331 B CN 102251331B CN 201110202805 A CN201110202805 A CN 201110202805A CN 102251331 B CN102251331 B CN 102251331B
- Authority
- CN
- China
- Prior art keywords
- yarn
- cotton
- stainless steel
- yarns
- shielding cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种屏蔽布料及其制造方法,包括经纱和纬纱,其特征在于:所述经纱和纬纱由不锈钢纤维混纺棉纱、棉包不锈钢微丝纱和棉纱包镀银涤纶长丝纱三种原纱并线而成。因此不会外露,不氧化,在外力作用下不断丝、不脱落,这样充分利用不锈钢纤维、不锈钢微丝、镀银涤纶长丝的优点相结合形成一个屏蔽厚网,使其屏蔽效果更强。
Description
技术领域
本发明涉及一种布料及其制造方法,尤其是一种屏蔽布料及其制造方法。
背景技术
随着人们对防辐射意识的不断增强,各种防辐射的产品也就随之而生,特别是纺织品,一些刮浆的、涂层的、并线的、外镀的防辐射、抗静电面料也应运而生。然而这些防辐射、抗静电面料都有两个缺点,一是不能水洗,遇水后涂层和刮浆脱落而减弱效果,甚至无效果;二是并线工艺金属丝外露容易氧化变色不但不能印花染色而且很刺眼让人看上去很不舒服,做屏蔽伪装容易被发现。
发明内容
本发明的目的是克服现有技术的缺陷,提供一种屏蔽布料及其制造方法,所述屏蔽布料可以水洗、抗氧化,永久屏蔽电磁波辐射、抗静电,而且染色隐蔽效果更好。
为解决上述技术问题,本发明提供了如下技术方案:一种屏蔽布料,包括经纱和纬纱,其中:所述经纱和纬纱由不锈钢纤维混纺棉纱、棉包不锈钢微丝纱和棉纱包镀银涤纶长丝纱三种原纱并线而成。
作为本发明所述的屏蔽布料的一种优选方案:所述不锈钢纤维混纺棉纱中不锈钢纤维含量可以从5%到50%。
作为本发明所述的屏蔽布料的一种优选方案:所述棉包不锈钢微丝纱可以从10S到40S。
作为本发明所述的屏蔽布料的一种优选方案:所述棉包不锈钢微丝纱包括不锈钢微丝,不锈钢微丝可以0.018mm到0.10mm。
作为本发明所述的屏蔽布料的一种优选方案:所述棉纱包镀银涤纶长丝纱中包括镀银涤纶长丝和棉纱,镀银涤纶长丝可以从30旦到1200旦,棉纱可以选择16S到80S。
本发明提供了一种屏蔽布料的制造方法,包括以下步骤:
步骤a.并线:
含不锈钢纤维的混纺棉纱 (A)
棉纱包不锈钢微丝纱 (B)
镀银涤纶长丝外包棉纱 (C)
(A)+(A)并线=(D),
(B)+(B)并线=(E),
(D)+(E)并线=(F),
(C)+(F)并线=(G);
步骤b.加捻:
将(G)经过加捻机加捻生成成品线;
步骤c.将成品线经整经,穿棕,上轴;
步骤d.在剑杆机上织造,再经过染色,制造出屏蔽布料。
作为本发明所述的屏蔽布料的制造方法的一种优选方案:
步骤a.并线:
30%含量不锈钢纤维混纺32S棉纱 (A)
32s棉纱包316L 0.035mm不锈钢微丝纱 (B)
700镀银涤纶长丝外包两根32s棉纱 (C)
(A)+(A)并线=(D),
(B)+(B)并线=(E),
(D)+(E)并线=(F),
(C)+(F)并线=(G);
步骤b.加捻:
将(G)经过加捻机加捻生成成品线;
步骤c.将成品线经整经,穿棕,上轴;
步骤d.在剑杆机上织造,再经过染色,制造出屏蔽布料。
采取上述技术措施后,具有以下优点:
不锈钢纤维混纺纱和棉纤维包不锈钢微丝再加上棉纱芯包镀银涤纶长丝纱经并线加捻及织布工艺织造而成,银离子在受水浸泡或受外力作用时不脱落。不锈钢微丝包进纱,因此不会外露,不氧化,在外力作用下不断丝、不脱落,这样充分利用不锈钢纤维、不锈钢微丝、镀银涤纶长丝的优点相结合形成一个屏蔽厚网,使其屏蔽效果更强。
将镀银涤纶长丝包入纱线内,增强了耐劳度和耐曲耐抗力,即使银离子脱落了也脱落在两根棉纱包裹之中,可以多次洗涤重复使用,水洗后屏蔽效果基本不受影响。
根据实验数据表明,原有C32s 30%含不锈钢纤维纱两根+C32s并两根不锈钢微丝0.035mm,两根棉纱并700镀银涤纶长丝一根,所织布料检测经过一次水洗。频率(MHz)=100透过屏蔽布料能屏蔽掉75.25%;原频率(MHz)=100透过屏蔽布料能屏蔽掉99.521%。而我们现在将不锈钢微丝和镀银涤纶长丝包芯起来后经测试未洗前在频率(MHz)=100时透过屏蔽材料布电磁波能量被屏蔽掉99.998%,经过两次洗涤后经测试在频率(MHz)=100时透过屏蔽材料布电磁波能量被屏蔽掉99.995%。
附图说明
图1是不锈钢纤维混纺棉纱示意图
图2是棉包不锈钢微丝纱示意图
图3是棉纱包镀银涤纶长丝纱示意图
图4是三种原纱并线后的示意图
图5是屏蔽布料示意图
图6是屏蔽布料剖面示意图
图7是屏蔽布料制造流程示意图
图8是生产棉纱包镀银涤纶长丝纱设备示意图
具体实施方式
下面结合附图和实施例作进一步说明。
图8中:31、紧定螺帽;32、调节捻度链轮,可根据要求调换大小;33、调节盘;34、固定支架;3、棉纱包镀银涤纶长丝纱;6、皮带盘一;6-1、链轮;7、传动轴;8、收线盘滚;9、导线管;10、棉纱;11、机架;12、马蹄锭子;13、棉纱余管;14、加捻转动盘;15、被动轮;16、传动轮;17、导丝管;18、皮带盘二;19、伞形齿轮一;20、伞形齿轮二;21、电机主动轮;21-1、皮带轮;22、镀银涤纶长丝;23、银纤维长丝轴;24、电动机;25、镀银涤纶长丝盘滚,26、开关。
如图1-8所示,在加捻转动盘14上安装马蹄锭子12两个,32支棉纱缠绕在棉纱余管13上,棉纱余管13装入马蹄锭子12,棉纱10经过固定支架34上的导线管9,再经过调节盘33,固定在收线盘滚8上。700旦镀银涤纶长丝缠绕在镀银涤纶长丝盘滚25上,镀银涤纶长丝盘滚25安装在银纤维长丝轴23上,根据要求可以装入多个。镀银涤纶长丝22穿过导丝管17,经过固定支架34上的导线管9,将其包入棉纱10内再经过调节盘33同棉纱10一起固定在收线盘滚8上,紧定螺帽31用于箍紧收线盘滚8,电动机24上的主动轮21通过皮带与皮带盘二18连接,皮带盘二18通过传动机构连接伞形齿轮一19,伞形齿轮一19与伞形齿轮二20相配合,伞形齿轮二20上的传动轮16与被动轮15通过皮带连接。被动轮15与加捻转动盘14连接,电动机24上的皮带轮21-1通过皮带与皮带盘一6连接,皮带轮一6通过传动轴7与链轮6-1连接,链轮6-1与调节捻度链轮32通过链条连接,调节捻度链轮32与收线盘滚连接。
工作时,电动机24转动,带动主动轮21、皮带轮21-1转动,带动皮带盘二18转动,皮带盘二18带动伞形齿轮一19转动,伞形齿轮一19与伞形齿轮二20配合,通过传动轮16,带被动轮15转动,从而使加捻转动盘14转动,使棉纱10包裹住镀银涤纶长丝22。同时,主动轮21带动皮带盘一6转动,皮带盘一6通过传动轴7带动链轮6-1转动,链轮6-1带动调节捻度链轮32转动,从而使收线盘滚8转动,将棉纱包镀银涤纶长丝纱3收集起来。这样棉纱包镀银涤纶长丝纱3就生产出来了。
屏蔽布料的制造方法的实施例1,如图1-6所示。
a.并线:
30%含量不锈钢纤维混纺32S棉纱1 (A)
32s棉纱包316L 0.035mm不锈钢微丝纱2 (B)
700旦镀银涤纶长丝外包两根32s棉纱3 (C)
(A)+(A)并线=(D),
(B)+(B)并线=(E),
(D)+(E)并线=(F),
(C)+(F)并线=(G)。
b.加捻:
将(G)经过加捻机加捻生成成品线4。
c.将成品线经整经,穿棕,上轴。
d.经纬密度我们采用68×36,纹路为斜纹二上二下工艺,在剑杆机上织造,再经过染色,制造出高强度、可以水洗、永久屏蔽电磁波辐射、抗静电屏蔽布料5。
所述不锈钢纤维混纺棉纱1,包括含5%~50%不锈钢纤维1-1,16s~40s棉或其它纤维混纺棉纱1-2。
所述棉包不锈钢微丝纱2,包括0.018mm~0.1mm 316L不锈钢微丝2-1,16s~40s包芯纱2-2。
所述棉纱包镀银涤纶长丝纱3,包括30旦~1200旦镀银涤纶长丝3-1,16s~80s棉纱3-2。
其它纤维是根据要求选择天然纤维、人造纤维、化学纤维。
实际生产中,银纤维长丝和镀银涤纶长丝为同一产品。
应说明的是,以上实施例仅用以说明本发明的技术方案而非限制,尽管参照较佳实施例对本发明进行了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的精神和范围,其均应涵盖在本发明的权利要求范围当中。
Claims (3)
1.一种屏蔽布料,包括经纱和纬纱,其特征在于:所述经纱和纬纱由不锈钢纤维混纺棉纱、棉包不锈钢微丝纱和棉纱包镀银涤纶长丝纱三种原纱并线而成,所述三种原纱并线,其通过先将两根30%含量不锈钢纤维混纺32s棉纱并线形成的纱与两根32s棉纱包316L0.035mm不锈钢微丝纱并线形成的纱再次并线,再次并线所形成的纱与700旦镀银涤纶长丝纱外包两根32s棉纱并线加捻生成成品线。
2.根据权利要求1所述的屏蔽布料,其特征在于:所述不锈钢纤维混纺棉纱中不锈钢纤维含量可以从5%到50%。
3.根据权利要求1所述的屏蔽布料,其特征在于:所述棉包不锈钢微丝纱可以从10S到40S。