CN102249693B - Process for preparing Hussein stone - Google Patents
Process for preparing Hussein stone Download PDFInfo
- Publication number
- CN102249693B CN102249693B CN 201110105718 CN201110105718A CN102249693B CN 102249693 B CN102249693 B CN 102249693B CN 201110105718 CN201110105718 CN 201110105718 CN 201110105718 A CN201110105718 A CN 201110105718A CN 102249693 B CN102249693 B CN 102249693B
- Authority
- CN
- China
- Prior art keywords
- carrying
- powder
- grid
- compression moulding
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a process for preparing a Hussein stone, and the process is characterized by comprising the following steps: a, carrying out slurry melting, carrying out material conveying, carrying out powder hitting, carrying out blanking from multiple main material pipes, and then carrying out secondary opposite-washing permeation; b, carrying out powder conveying, carrying out material distribution, and laying one or more layers of micro powder in a grille by using a roller; c, transferring the micro powder in the grille to a mould, then sequentially carrying out compression moulding, drying and sintering on the micro powder; and d, polishing. The product prepared by using the process disclosed by the invention is random and fluent in appearance, unique in style, bright and tender in color and distinct in gradation.
Description
Technical field
The present invention relates to the ceramic production technology field, relate in particular the preparation technology of a kind of Hai Shanshi.
Background technology
Hai Shanshi is divided into two plate face, is divided into red plate plate and green plate face, is combined by generation glomerocryst, butterfly stone, the perfection of non-hole cave stove texture, presents the graceful texture as beautiful matter, and texture combines together, and is very popular.
Summary of the invention
It is smooth at random that purpose of the present invention is exactly a kind of plate face that provides for the deficiency that solves prior art, unique style, and color and luster is fresh and tender soft, the preparation technology of well-bedded Hai Shanshi.
The present invention adopts following technical solution to realize above-mentioned purpose: the preparation technology of a kind of Hai Shanshi, it is characterized in that, and it comprises the steps:
A, change slurry, feeding, beat powder, divide the blanking of many major ingredient pipes, then carry out the secondary infiltration that liquidates;
B, powder feeding, cloth utilize roller to be distributed into one or more layers micro mist in grid;
C, the differential in grid is transferred in mould, compression moulding, drying is burnt till;
D, polishing.
As further illustrating of such scheme, in described processing step a process, powder is beaten powder fineness below 5%, allows fine powder material condense one.
In described processing step b process, cloth adopts snake twill grid.
In described processing step c process, compression moulding is in press compression moulding.
In described processing step c process, firing is to fire at kiln, and firing temperature is the 1100-1300 degree.
The beneficial effect that the present invention adopts above-mentioned technical solution to reach is:
The present invention adopts the large grid of snake twill, the infiltration that liquidates of the unique ultra-fine micropowder secondary of a new generation, and the product of production presents the graceful texture as beautiful matter, texture combine together " come from stone material, more be better than stone material ".
Embodiment
The preparation technology of a kind of Hai Shanshi of the present invention, it comprises the steps:
A, change slurry, feeding, beat powder, powder is beaten powder fineness below 5%, allows one of fine powder material cohesion, every kind of material transition nature, and natural texture silk silk permeates.Mainly minute 6 major ingredient pipes blanking, the lower transparent material of 1#3#5# pipe, the lower super-white marerial of 2#4# pipe, the lower red material of 6# pipe/green material, by 2 auxiliary tubes billot that rolls off the production line, the then secondary infiltration that liquidates;
Powder title per-cent fineness
Technical recipe: super-white marerial: 25% 5%
Transparent material: 50% 5%
Red material/green material: 25% 5%
Zirconium white lines material: 20% 5%
Be popular in the open-wire line billot: 19% 5%
B, powder feeding, cloth utilize roller to be distributed into one or more layers micro mist in grid, and cloth adopts snake twill grid;
C, the differential in grid is transferred in mould, adopts in press compression moulding, drying is fired at kiln, and firing temperature is 1200 degree;
D, polishing.
Hai Shanshi of the present invention is divided into two plate face, is divided into red plate face and green plate face.
The happy elegance of feeling that the red version of Hai Shanshi is given the people, red plate face white touched with red sends a some light under light, set off out especially noble elegant makings.
Sea coral malachite green plate is just as nature, and gracefulness is rich in infectivity, the plate face that stereoscopic sensation is more intense.
Above-described is only the preferred embodiment of the present invention, should be pointed out that for the person of ordinary skill of the art, under the prerequisite that does not break away from the invention design, can also make some distortion and improvement, and these all belong to protection scope of the present invention.
Claims (3)
1. the preparation technology of an extra large coral stone, is characterized in that, it comprises the steps:
A, change slurry, feeding, beat powder, powder is beaten powder fineness below 5%, allows one of fine powder material cohesion, divides the blanking of many major ingredient pipes, then carries out the secondary infiltration that liquidates;
B, powder feeding, cloth, cloth adopt snake twill grid, utilize roller to be distributed into one or more layers micro mist in grid;
C, the differential in grid is transferred in mould, compression moulding, drying is burnt till;
D, polishing.
2. the preparation technology at a kind of Hai Shanshi according to claim 1, is characterized in that, in described processing step c process, compression moulding is in press compression moulding.
3. the preparation technology at a kind of Hai Shanshi according to claim 1, is characterized in that, in described processing step c process, firing is to fire at kiln, and firing temperature is the 1100-1300 degree.