CN102249636A - 水泥基无收缩灌浆砂浆 - Google Patents
水泥基无收缩灌浆砂浆 Download PDFInfo
- Publication number
- CN102249636A CN102249636A CN2011101286322A CN201110128632A CN102249636A CN 102249636 A CN102249636 A CN 102249636A CN 2011101286322 A CN2011101286322 A CN 2011101286322A CN 201110128632 A CN201110128632 A CN 201110128632A CN 102249636 A CN102249636 A CN 102249636A
- Authority
- CN
- China
- Prior art keywords
- cement
- mortar
- grout
- agent
- contraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水泥基无收缩灌浆砂浆,其特征在于,按重量百分比其包括:硅酸盐水泥35%~42%;铝酸盐水泥5%~12%;石膏6%~10%;骨料40%~50%;高效减水剂0.8%~1.4%;调凝剂0.05%~0.2%;消泡剂0.4%~1.0%;防泌水剂1%~3%。本发明水泥基无收缩灌浆砂浆采用硅酸盐水泥-铝酸盐水泥-石膏复合成胶凝材料配制,其性能稳定,可根据用户的需求来调整流动度,凝结时间和膨胀率。该灌浆砂浆用水拌合后,自流性好、不沉降、不泌水。具有塑性微膨胀性能,不产生缝隙,早期强度高,后期强度不倒缩,且具有很好的耐久性、抗渗性、抗冻性、抗震动性,材料价格低廉,其原料来源广泛,操作灵活,使用简单。
Description
技术领域
本发明涉及建筑材料领域,特别涉及一种基础工程用灌浆砂浆。
背景技术
无收缩灌浆砂浆最早起源于美国,是为加固军事设施而研制的一种高强快速凝固材料。至50年代,西方国家将其应用于工业部门,主要用于机械设备安装和加固修补工程,经过多年的发展,高强无收缩灌浆料从传统用于机械设备安装的二次灌浆发展到用于地脚螺栓锚固,钢结构柱脚底板的二次灌浆,混凝土结构改造、加固及后张预应力混凝土结构预留孔道灌浆与封锚等新的领域。
随着我国经济的发展和基础设施的大量建设,许多拥有大型设备的工厂、企业不断出现,冶金、石化和电力企业各种大型设备的安装,桥梁、铁路的建设,对灌浆材料提出了更大的需求。为此,20世纪70年代,为了满足进口设备的需要,我国开始了灌浆砂浆的研制工作,并于1977年研制成功,开始在冶金设备安装中大量应用。经过30多年的研究实践,我国灌浆砂浆的技术性能逐步提高。但是,目前使用的灌浆砂浆成本偏高,体积收缩较大,强度发展慢,耐久性差,影响结构稳定性和使用寿命。
当前国内配制灌浆砂浆主要有两大途径:一是在普通硅酸盐水泥中加早强剂和膨胀剂,二是使用特性水泥。第一种途径应用广泛,但配制的灌浆砂浆存在性能不稳定的缺点。原因有二:一是国内市场上膨胀剂稳定性不理想,二是使用的早强剂虽然获得一定的早期强度但后期强度和耐久性能受到很大的影响。因此,采用该方法配制灌浆砂浆质量不易控制,且难以实现批量生产。第二种途径主要是利用特性水泥配制灌浆砂浆。考虑到水泥成本较高且膨胀性能不足,配制的灌浆砂浆只能在一些重点工程中应用,不宜推广。
发明内容
针对上述现有技术的不足,本发明要解决的技术问题是提供一种性能优良,具有早强、高强、大流动性、微膨胀性能的灌浆砂浆。
为解决上述技术问题,本发明采用如下技术方案:
一种水泥基无收缩灌浆砂浆,其特征在于,按重量百分比其包括:
硅酸盐水泥35%~42%;
铝酸盐水泥5%~12%;
石膏6%~10%;
骨料40%~50%;
高效减水剂0.8%~1.4%;
调凝剂0.05%~0.2%;
消泡剂0.4%~1.0%;
防泌水剂1%~3%。
优选的,所述硅酸盐水泥为普通硅酸盐水泥。
优选的,所述硅酸盐水泥为PO42.5R型水泥。
优选的,所述铝酸盐水泥为CA-50型水泥。
优选的,所述石膏为天然生石膏。
优选的,所述骨料为中粗黄砂,所述中粗黄砂的细度为2.5~3.3。
优选的,所述高效减水剂为萘磺酸盐甲醛缩合物减水剂或氨基磺酸盐减水剂,或者两者复合使用。
优选的,所述调凝剂中含有缓凝剂或促凝剂,所述缓凝剂为葡萄糖酸钠和酒石酸复合使用,所述促凝剂为细度较小的碳酸锂。
优选的,所述消泡剂为有机硅消泡剂。
优选的,所述防泌水剂为熟石灰粉。
上述技术方案具有如下有益效果:本发明水泥基无收缩灌浆砂浆采用硅酸盐水泥-铝酸盐水泥-石膏复合成胶凝材料配制,其性能稳定,可根据用户的需求来调整流动度,凝结时间和膨胀率。该灌浆砂浆用水拌合后,自流性好、不沉降、不泌水。具有塑性微膨胀性能,不产生缝隙,早期强度高,后期强度不倒缩,且具有很好的耐久性、抗渗性、抗冻性、抗震动性,材料价格低廉,其原料来源广泛,操作灵活,使用简单。
具体实施方式
实施例一:
一种水泥基无收缩灌浆砂浆,按重量百分比,其包括:
胶凝材料:PO42.5R水泥38%,CA-50水泥5%,天然生石膏6%;
骨料:中粗黄砂48.5%;
高效减水剂:萘磺酸盐甲醛缩合物1%;
调凝剂:碳酸锂0.01%,葡萄糖酸钠0.05%,酒石酸0.04%;
硅消泡剂:有机硅消泡剂0.4%;
防泌水剂:熟石灰粉1%。
实施例二:
一种水泥基无收缩灌浆砂浆,按重量百分比,其包括:
胶凝材料:PO42.5R水泥35%,CA-50水泥8%,天然生石膏7.4%;
骨料:中粗黄砂45%;
高效减水剂:萘磺酸盐甲醛缩合物减水剂和氨基磺酸盐减水剂混合物1.4%;
调凝剂:碳酸锂0.02%,葡萄糖酸钠0.1%,酒石酸0.08%;
硅消泡剂:有机硅消泡剂1%;
防泌水剂:熟石灰粉2%。
实施例三:
一种水泥基无收缩灌浆砂浆,按重量百分比,其包括:
胶凝材料:PO42.5R水泥42%,CA-50水泥5%,天然生石膏8%;
骨料:中粗黄砂40%;
高效减水剂:氨基磺酸盐减水剂混合物1.2%;
调凝剂:碳酸锂0.02%,葡萄糖酸钠0.05%,酒石酸0.08%;
硅消泡剂:有机硅消泡剂0.65%;
防泌水剂:熟石灰粉3%。
该水泥基无收缩灌浆砂浆所用的硅酸盐水泥-铝酸盐水泥-石膏复合胶凝材料本身就具有早强、高强、微膨胀的性能,且性能具有可调节性。可以根据不同的用户要求调节原材料的比例,达到不同的要求。如1d的强度可高可低(20MPA~40MPA),28d的强度(70MPA~100MPA),流动性可大可小(260mm~340mm),1d的膨胀率可高可低(0.01%~0.5%)。
本发明水泥基无收缩灌浆砂浆经过各种性能测试,具有如下的特点:
1)凝结时间可通过调凝剂来调节,初凝(1h~8h)。可以满足不同的施工要求。
2)具有大流动性,通过减水剂来调节灌浆砂浆的流动性(260~340mm),对强度没有不良的影响,
3)早强,高强:1d(20MPA~40MPA),28d(70MPA~100MPA)。
4)微膨胀性,可以通过控制石膏的掺量来控制1d的竖向膨胀率(0.01~0.5)。
5)耐久性好,对钢筋无锈蚀。
6)钢筋握裹强度高,圆钢大于6.0MPA。
7)(7)成本低,原材料来源广泛,有利于批量生产。
以实施例一为例,将采用实施例一所得的水泥基无收缩灌浆砂浆拌合15%,使其用于工业设备的安装的二次灌浆和建筑结构的加固和抢修。其具体性能如下表所示:
该水泥基无收缩灌浆砂浆采用价格低廉的原材料,原材料来源广泛。如使用PO42.5R型水泥,天然生石膏粉,普通中粗黄砂,萘磺酸盐甲醛缩合物减水剂,熟石灰粉等。所以本发明的水泥基无收缩灌浆砂浆和同类产品相比还具有性能好,成本低的优势。
以上对本发明实施例所提供的一种水泥基无收缩灌浆砂浆进行了详细介绍,对于本领域的一般技术人员,依据本发明实施例的思想,在具体实施方式及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制,凡依本发明设计思想所做的任何改变都在本发明的保护范围之内。
Claims (10)
1.一种水泥基无收缩灌浆砂浆,其特征在于,按重量百分比其包括:
a)硅酸盐水泥35%~42%;
b)铝酸盐水泥5%~12%;
c)石膏6%~10%;
d)骨料40%~50%;
e)高效减水剂0.8%~1.4%;
f)调凝剂0.05%~0.2%;
g)消泡剂0.4%~1.0%;
h)防泌水剂1%~3%。
2.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述硅酸盐水泥为普通硅酸盐水泥。
3.根据权利要求2所述的水泥基无收缩灌浆砂浆,其特征在于:所述硅酸盐水泥为PO42.5R型水泥。
4.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述铝酸盐水泥为CA-50型水泥。
5.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述石膏为天然生石膏。
6.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述骨料为中粗黄砂,所述中粗黄砂的细度为2.5~3.3。
7.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述高效减水剂为萘磺酸盐甲醛缩合物减水剂或氨基磺酸盐减水剂,或者两者复合使用。
8.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述调凝剂中含有缓凝剂或促凝剂,所述缓凝剂为葡萄糖酸钠和酒石酸复合使用,所述促凝剂为细度较小的碳酸锂。
9.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述消泡剂为有机硅消泡剂。
10.根据权利要求1所述的水泥基无收缩灌浆砂浆,其特征在于:所述防泌水剂为熟石灰粉。