CN109467377A - 一种超早强单组份注浆材料 - Google Patents
一种超早强单组份注浆材料 Download PDFInfo
- Publication number
- CN109467377A CN109467377A CN201811390452.XA CN201811390452A CN109467377A CN 109467377 A CN109467377 A CN 109467377A CN 201811390452 A CN201811390452 A CN 201811390452A CN 109467377 A CN109467377 A CN 109467377A
- Authority
- CN
- China
- Prior art keywords
- component
- injecting paste
- paste material
- super hardening
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超早强单组份注浆材料，包含如下组分：铝酸盐水泥、普硅水泥、石膏、矿渣微粉、粉煤灰、微硅粉、减水剂、缓凝剂、消泡剂、保水增稠剂、偏硅酸钠、黄沙和水。本发明提供的道路注浆加固用的超早强单组份注浆材料，具有较高的早期和后期力学性能和耐久性，极低的导热系数，无收缩开裂，良好的耐酸性和耐水性，在各种恶劣气候环境下均能够具有极强的耐久性。
Description
技术领域
本发明涉及一种注浆材料，尤其涉及一种超早强单组份注浆材料。
背景技术
注浆材料指在压力作用下注入地层、岩石或构筑物的缝隙、孔洞中，达到增加承载能力、防止渗漏及提高构筑物整体性能等效果的流体材料。
注浆材料，具有粘度低、流动度大、渗透性好等特点，由于施工和注浆设备的要求及注浆材料自身特点，常见的早强型注浆材料多为双组份有机灌浆料，需现场进行混合配置，双组份比例和混合均匀性较难控制，固化后其后期强度易倒缩，且体系的耐久性较差；常见的单组份注浆材料工厂预混后，现场直接加水即可施工，但存在凝结时间较长，早期强度低的缺点。因此，提供超早强单组份注浆材料在建筑工程应用领域具有较为广阔的前景。
发明内容
本发明所要解决的技术问题是提供一种超早强单组份注浆材料，在具备较长开放时间的同时，能够大幅度提高注浆材料的早期强度，并克服早强型注浆材料后期力学性能下降等问题。
本发明为解决上述技术问题而采用的技术方案是提供一种超早强单组份注浆材料，包含如下组分：铝酸盐水泥、普硅水泥、石膏、矿渣微粉、粉煤灰、微硅粉、减水剂、缓凝剂、消泡剂、保水增稠剂、偏硅酸钠、黄沙和水。
上述的道路超早强单组份注浆材料，其中，各组分按重量份数配比如下：
上述的道路超早强单组份注浆材料，其中，所述铝酸盐水泥为CA-50、CA-60、CA-70和CA-80中的一种；所述普硅水泥为普通硅酸盐水泥42.5和普通硅酸盐水泥52.5中的一种；所述石膏为无水石膏、半水石膏和二水石膏中的一种。
上述的道路超早强单组份注浆材料，其中，所述矿渣微粉为活性指数95％以上的矿渣微粉；所述粉煤灰为活性指数70％以上的二级粉煤灰或一级粉煤灰；所述微硅粉目数为600～2000目。
上述的道路超早强单组份注浆材料，其中，所述减水剂为聚羧酸减水剂或萘系减水剂；所述缓凝剂为柠檬酸、酒石酸和葡萄糖酸钠中的一种。
上述的道路超早强单组份注浆材料，其中，所述消泡剂为有机硅类消泡剂和聚醚类消泡剂中的一种。
上述的道路超早强单组份注浆材料，其中，所述保水增稠剂为纤维素醚和瓜尔胶中的一种。
上述的道路超早强单组份注浆材料，其中，还包含流变剂、表面活性剂、早强剂、胶黏剂、增韧材料和细集料中的任意一种或其混合物。
上述的道路超早强单组份注浆材料，其中，各组分混合均匀后，控制胶凝材料的初始流锥流动度为14～20s，开放时间15～30min，终凝时间为60～120min，4h抗压强度为5～20MPa，1d抗压强度30～45MPa，28d强度为60～100MPa。
本发明对比现有技术有如下的有益效果：本发明提供的超早强单组份注浆材料，具有较长的开放时间，同时具有较高的早期和后期力学性能，具有良好的耐久性，无收缩开裂。
具体实施方式
下面结合实施例对本发明作进一步的描述。
本发明提供的道道路超早强单组份注浆材料，包含如下组分：铝酸盐水泥、普硅水泥、石膏、矿渣微粉、粉煤灰、微硅粉、减水剂、缓凝剂、消泡剂、保水增稠剂、偏硅酸钠、黄沙和水；其中，各组分按重量份数配比如下：
应当理解的是，本发明上述配方组分中还可以加入还可以加入流变剂、表面活性剂、早强剂、胶黏剂、增韧材料和细集料中的任意一种或其混合物。
本发明提供的超早强单组份地聚合物，组分中的铝酸盐水泥为CA-50、CA-60、CA-70和CA-80中的一种；普硅水泥为普通硅酸盐水泥42.5和普通硅酸盐水泥52.5中的一种；石膏为无水石膏、半水石膏和二水石膏中的一种；矿渣微粉为活性指数95％以上的矿渣微粉；煤灰为活性指数70％以上的二级粉煤灰或一级粉煤灰；微硅粉目数为600～2000目；减水剂为聚羧酸减水剂和萘系减水剂中的一种；缓凝剂为柠檬酸、酒石酸和葡萄糖酸钠中的一种；消泡剂为有机硅类消泡剂和聚醚类消泡剂中的一种；保水增稠剂为纤维素醚和瓜尔胶中的一种。
下面通过具体实施例对本发明进行详细和具体的介绍，以使更好的理解本发明，但是下述实施例并不限制本发明范围。
实施例1
超早强单组份注浆材料各组分重量比为：
实施例2
超早强单组份注浆材料各组分重量比为：
实施例3
加气膨胀型地聚合物材料各组分重量比为：
本发明上述实施例制备的一种超早强单组份注浆材料，与现有普通注浆材料和灌浆料相比，具有更高的早期强度和后期强度，无收缩开裂，同时具有良好耐腐蚀性，在各种恶劣气候环境下均能够具有极好的耐久性。参照《铁路后张法预应力混凝土梁管道压浆技术条件》(TB/T 3192)、《城镇道路改性地聚合物注浆加固技术规程》(DGJ32/TJ225-2017)、《道路注浆加固技术规程》(DG/TJ 08-2240-2017)、等标准进行试验，本发明的超早强单组份注浆材料与普通注浆材料理化性能比较如下：
由上可见，本发明的超早强单组份注浆材料与现有普通注浆材料和灌浆料相比，体系具有更高的早期和后期力学性能，具有更好的耐久性。本发明通过调整各组分比例和缓凝剂的掺量，可以得到不同凝结时间的超早强单组份注浆材料。体系在各种恶劣气候环境下均能够具有极强的耐久性；是一种环保无污染的高性能注浆材料。
虽然本发明已以较佳实施例揭示如上，然其并非用以限定本发明，任何本领域技术人员，在不脱离本发明的精神和范围内，当可作些许的修改和完善，因此本发明的保护范围当以权利要求书所界定的为准。
Claims (9)
1.一种超早强单组份注浆材料，其特征在于，包含如下组分：铝酸盐水泥、普硅水泥、石膏、矿渣微粉、粉煤灰、微硅粉、减水剂、缓凝剂、消泡剂、保水增稠剂、偏硅酸钠、黄沙和水。
2.如权利要求1所述的超早强单组份注浆材料，其特征在于，各组分按重量份数配比如下：
3.如权利要求1所述的超早强单组份注浆材料，其特征在于，所述铝酸盐水泥为CA-50、CA-60、CA-70和CA-80中的一种；所述普硅水泥为普通硅酸盐水泥42.5和普通硅酸盐水泥52.5中的一种；所述石膏为无水石膏、半水石膏和二水石膏中的一种。
4.如权利要求1所述的超早强单组份注浆材料，其特征在于，所述矿渣微粉为活性指数95％以上的矿渣微粉；所述粉煤灰为活性指数70％以上的二级粉煤灰或一级粉煤灰；所述微硅粉目数为600～2000目。
5.如权利要求1所述的超早强单组份注浆材料，其特征在于，所述减水剂为聚羧酸减水剂或萘系减水剂；所述缓凝剂为柠檬酸、酒石酸和葡萄糖酸钠中的一种。
6.如权利要求1所述的超早强单组份注浆材料，其特征在于，所述消泡剂为有机硅类消泡剂和聚醚类消泡剂中的一种。
7.如权利要求1所述的注浆加固用的超早强单组份注浆材料，其特征在于，所述保水增稠剂为纤维素醚和瓜尔胶中的一种。
8.如权利要求1所述的超早强单组份注浆材料，其特征在于，还包含流变剂、表面活性剂、早强剂、胶黏剂、增韧材料和细集料中的任意一种或其混合物。
9.如权利要求1所述的超早强单组份注浆材料，其特征在于，各组分混合均匀后，控制胶凝材料的初始流锥流动度为14～20s，开放时间15～30min，终凝时间为60～120min，4h抗压强度为5～20MPa，1d抗压强度30～45MPa，28d强度为60～100MPa。