CN102226224A - 一种矿渣助磨剂及其制备方法 - Google Patents

一种矿渣助磨剂及其制备方法 Download PDF

Info

Publication number
CN102226224A
CN102226224A CN2011101002180A CN201110100218A CN102226224A CN 102226224 A CN102226224 A CN 102226224A CN 2011101002180 A CN2011101002180 A CN 2011101002180A CN 201110100218 A CN201110100218 A CN 201110100218A CN 102226224 A CN102226224 A CN 102226224A
Authority
CN
China
Prior art keywords
water glass
grinding aid
water
slag grinding
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011101002180A
Other languages
English (en)
Other versions
CN102226224B (zh
Inventor
徐福明
邱瑜铭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Feng Tai Tools Co., ltd
Original Assignee
Jiangsu Fengtai Building Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Fengtai Building Material Technology Co Ltd filed Critical Jiangsu Fengtai Building Material Technology Co Ltd
Priority to CN2011101002180A priority Critical patent/CN102226224B/zh
Publication of CN102226224A publication Critical patent/CN102226224A/zh
Application granted granted Critical
Publication of CN102226224B publication Critical patent/CN102226224B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：10-20wt％；水玻璃改性剂：2-5wt％；甘油：12-15wt％；丙三醇：5-15wt％；三乙醇胺：5-12wt％；乙二醇：3-8wt％；尿素：3-12wt％；和余量的水。加入0.03wt％-0.12wt％的上述矿渣助磨剂至矿渣中，可以显著的提高矿渣粉磨的效率10-35％左右。

Description

一种矿渣助磨剂及其制备方法
技术领域
本发明涉及一种矿渣微粉制造领域的添加剂，具体地，本发明涉及一种矿渣助磨剂，另外本发明还涉及该矿渣助磨剂的制备方法。
背景技术
矿渣是钢铁冶炼过程产生的一种副产品，为了有效利用资源，通常将其磨成细粉后作为矿渣微粉使用。矿渣微粉是新型绿色环保产品，不仅能有效利用高炉冶金渣，变废为宝，还对缩减矿渣占地、减少环境污染起到促进作用。矿渣微粉已成为生产高品质水泥、配置高性能、长寿命混凝土的首选物料之一。掺有矿渣微粉的混凝土具有水化热低、耐腐蚀、流动性好、后期强度高、防微缩、可使混凝土界面粘结性能改善等特点，被国家建设部确定为建筑业十项新技术之一。由于矿渣非常硬，细磨过程中需要消耗大量的能量和生产时间。现有液体矿渣助磨剂的配方组成主要采用乙二醇或者含有乙二醇的混合物作为助磨剂。但是由于矿渣的玻璃体结构原因，现有技术中的助磨剂加入到矿渣粉磨过程中，虽然能够解除矿渣颗粒周围的团聚现象，但不能提高矿渣颗粒本身的易磨性，所以助磨效果还是不够理想。为此，寻求一种有效的矿渣助磨剂产品是国内助磨剂行业急需要解决的问题。
发明内容
本发明的目的之一在于提供一种矿渣助磨剂，其能提高磨机粉磨效率、矿渣微粉的活性指数。
本发明的目的还在于提供一种制造上述矿渣助磨剂的制备方法。
为了实现上述目的，本发明采用的技术方案如下：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：10-20wt％；水玻璃改性剂：2-5wt％；甘油：12-15wt％；丙三醇：5-15wt％；三乙醇胺：5-12wt％；乙二醇：3-8wt％；尿素：3-12wt％；和余量的水。
优选的，水玻璃的含量为10-16wt％；尿素的用量为3-5wt％。
优选的，所述的水玻璃的模数为1.6-1.8。
优选的，所述的水玻璃的波美度为40-60度。
所述的水玻璃改性剂可以使用现有技术中公知的改性剂，优选的水玻璃改性剂(标记为M1)的组成和含量如下：钾明矾：0.2wt％；硫酸钠：0.3wt％；重铬酸钾：0.2wt％；硫酸亚铁：0.3wt％；元明粉：1.0wt％；大苏打：3.0wt％；和余量的水。使用该水玻璃改性剂可以有效阻止水玻璃的老化、有效细化凝胶基本颗粒，添加到矿渣助磨剂中可以方便助磨剂的配制、存储和运输；另外其还能进一步提高对矿渣的粉磨效率。
另一方面，本发明还提供了一种上述矿渣助磨剂的制备方法，其包括以下步骤：在反应釜中注入45-60℃的水，加入水玻璃、水玻璃改性剂和尿素，搅拌均匀；然后加入加入甘油、丙三醇、三乙醇胺、乙二醇，搅拌均匀，得到矿渣助磨剂产品。
应用时，使用液体计量设备，加入0.03wt％-0.12wt％的上述矿渣助磨剂至矿渣中，可以显著的提高矿渣粉磨的效率10-35％左右。
具体实施方式
下面结合实施例对本发明作进一步详细说明。
一、矿渣助磨剂的制备
依据上述本申请已经公开的方法制备实施例1-实施例8的矿渣助磨剂。
实施例1：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：10wt％；水玻璃改性剂：2wt％；甘油：12wt％；丙三醇：8wt％；三乙醇胺：6wt％；乙二醇：3wt％；尿素：5wt％；和余量的水。所述的改性剂为聚丙烯酰胺。
实施例2：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：10wt％；水玻璃改性剂：2wt％；甘油：12wt％；丙三醇：8wt％；三乙醇胺：6wt％；乙二醇：3wt％；尿素：5wt％；和余量的水。所述的改性剂为本申请优选的水玻璃改性剂M1。
实施例3：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：12wt％；水玻璃改性剂：3wt％；甘油：12wt％；丙三醇：5wt％；三乙醇胺：6wt％；乙二醇：5wt％；尿素：8wt％；和余量的水。所述的改性剂为聚丙烯酰胺。
实施例4：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：12wt％；水玻璃改性剂：3wt％；甘油：12wt％；丙三醇：5wt％；三乙醇胺：6wt％；乙二醇：5wt％；尿素：8wt％；和余量的水。所述的改性剂为本申请优选的水玻璃改性剂M1。
实施例5：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：15wt％；水玻璃改性剂：4wt％；甘油：15wt％；丙三醇：10wt％；三乙醇胺：8wt％；乙二醇：5wt％；尿素：6wt％；和余量的水。所述的改性剂为聚丙烯酰胺。
实施例6：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：15wt％；水玻璃改性剂：4wt％；甘油：15wt％；丙三醇：10wt％；三乙醇胺：8wt％；乙二醇：5wt％；尿素：6wt％；和余量的水。所述的改性剂为本申请优选的水玻璃改性剂M1。
实施例7：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：16wt％；水玻璃改性剂：5wt％；甘油：15wt％；丙三醇：8wt％；三乙醇胺：8wt％；乙二醇：8wt％；尿素：8wt％；和余量的水。所述的改性剂为聚丙烯酰胺。
实施例8：
一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：16wt％；水玻璃改性剂：5wt％；甘油：15wt％；丙三醇：8wt％；三乙醇胺：8wt％；乙二醇：8wt％；尿素：8wt％；和余量的水。所述的改性剂为本申请优选的水玻璃改性剂M1。
二、高炉炉渣粉磨实验
选用以下成分的炼钢渣在矿渣粉磨机上进行实验，助磨剂的添加量为0.05wt％，所得的实验结果如表1所示。
钢渣：CaO 42wt％、MgO 9wt％、SiO2 38wt％、Al2O3 15wt％，其余为MnO、FeO等。
Figure BSA00000478302800041
本产品的助磨剂基本呈现为液态，方便存储和运输，使用的时候，工厂仅仅需要增加一个储料罐和一个液体计量泵，就可以顺利加入。外观为棕褐色液体，密度(20℃)：1.10～1.25g/cm3，粘度(20℃)为30～80cps。使用矿渣助磨剂的时候，当入磨的矿渣含水量在0.5～1.0％之间，矿渣的粉磨效率最高。

Claims (9)

1.一种矿渣助磨剂，由水玻璃、水玻璃改性剂、甘油、丙三醇、三乙醇胺、乙二醇、尿素和水组成，各组分的含量分别为：水玻璃：10-20wt％；水玻璃改性剂：2-5wt％；甘油：12-15wt％；丙三醇：5-15wt％；三乙醇胺：5-12wt％；乙二醇：3-8wt％；尿素：3-12wt％；和余量的水。
2.权利要求1所述的矿渣助磨剂，其特征在于所述的水玻璃的模数为1.6-1.8。
3.权利要求1所述的矿渣助磨剂，其特征在于所述的水玻璃的波美度为40-60度。
4.权利要求1所述的矿渣助磨剂，其特征在于所述的水玻璃的含量为10-16wt％。
5.权利要求1所述的矿渣助磨剂，其特征在于尿素的用量为3-5wt％。
6.权利要求1-3任一项所述的矿渣助磨剂，其特征在于所述的水玻璃改性剂的组成和含量如下：钾明矾：0.2wt％；硫酸钠：0.3wt％；重铬酸钾：0.2wt％；硫酸亚铁：0.3wt％；元明粉：1.0wt％；大苏打：3.0wt％；和余量的水。
7.权利要求1-6任一项所述的矿渣助磨剂的制备方法，其包括以下步骤：在反应釜中注入45-60℃的水，加入水玻璃、水玻璃改性剂和尿素，搅拌均匀；然后加入甘油、丙三醇、三乙醇胺、乙二醇，搅拌均匀，得到矿渣助磨剂产品。
8.权利要求1-6任一项所述的矿渣助磨剂的使用方法，在待粉磨的矿渣中加入0.03wt％-0.12wt％的所述矿渣助磨剂。
9.权利要求8所述的矿渣助磨剂的使用方法，其特征在于所述的矿渣的含水率为0.5-1.0wt％。
CN2011101002180A 2011-04-21 2011-04-21 一种矿渣助磨剂及其制备方法 Expired - Fee Related CN102226224B (zh)