CN102212281A - 环保耐水、耐擦洗内墙涂料 - Google Patents
环保耐水、耐擦洗内墙涂料 Download PDFInfo
- Publication number
- CN102212281A CN102212281A CN2010101415812A CN201010141581A CN102212281A CN 102212281 A CN102212281 A CN 102212281A CN 2010101415812 A CN2010101415812 A CN 2010101415812A CN 201010141581 A CN201010141581 A CN 201010141581A CN 102212281 A CN102212281 A CN 102212281A
- Authority
- CN
- China
- Prior art keywords
- water
- resistant
- interior wall
- scrub
- wall paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种内墙涂料，尤其是涉及一种耐水、耐擦洗内墙涂料。其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝45～75∶15～30∶50～80∶10～20∶3.5～5.5∶2.0～4.0∶90～120。本发明经过大量实验，研制出一种具有极高的附着力、耐水和耐擦洗性能，耐擦洗次数达上万次。性能优良，安全无毒、施工方便、干燥迅速，不起泡，不易脱皮剥落，储存期长而稳定，而且原料易得，价格低廉，工艺简单极大的满足了使用者的需求。
Description
技术领域
本发明涉及一种内墙涂料，尤其是涉及一种耐水、耐擦洗内墙涂料。
背景技术
目前.国内外建筑涂料生产发展非常迅速，以每年2.5～3％的速度增长.在我国增长速度将更侠。涂捌的品种分为无机有机、复合三大类。
有机建筑涂料以各种有机高分子聚合物为主要成膜物.再添加一些填料.颜料.消泡剂.固化剂等经研磨.配制而成。这类涂料具有色彩艳丽.漆膜丰满、表面光洁、耐擦洗、装饰性好等优点·但因价格太高、且原料来源紧张、麓工索业化程度要求较高等.故多用于高级建筑装饰，推广.直用较为困难。
无机建筑椽料多以水溶性碱金属硅酸盐或磷酸盐为主要成膜物。虽然这类涂料价格低廉、成膜性好，但饰面的耐水性、耐擦洗性、装饰性等均较差.且产品质量不稳定.使其应用受到了一定的限制。用无机酸、缩磷酸盐改性的硅酸钠涂料.虽然成本不报高.但其装饰性、实用性、麓工性等均欠佳.故仍不很理想。
发明内容
本发明经过大量实验，研制出一种性能优良，安全无毒、施工方便、干燥迅速、耐水、耐擦洗，且附着力强的内墙涂料。
本发明的技术方案是：
环保耐水、耐擦洗内墙涂料，其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝45～75∶15～30∶50～80∶10～20∶3.5～5.5∶2.0～4.0∶90～120。
所述的环保耐水、耐擦洗内墙涂料，其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝55～65∶17～26∶60～70∶12～17∶4.0～5.0∶2.2～3.5∶100～110。
所述的环保耐水、耐擦洗内墙涂料，其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝60∶28∶65∶15∶4.5∶3.0∶105。
所述的交联剂为氯化聚乙烯。
制备所述的环保耐水、耐擦洗内墙涂料的方法，采用常规方法进行混合搅拌即可。
本发明与现有技术相比具有如下的优点效果：
本发明经过大量实验，研制出一种具有极高的附着力、耐水和耐擦洗性能，耐擦洗次数达上万次。性能优良，安全无毒、施工方便、干燥迅速，不起泡，不易脱皮剥落，储存期长而稳定，而且原料易得，价格低廉，工艺简单极大的满足了使用者的需求。
具体实施方式
实施例1
环保耐水、耐擦洗内墙涂料，由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶氯化聚乙烯∶水＝60∶28∶65∶15∶4.5∶3.0∶105。
制备所述的环保耐水、耐擦洗内墙涂料的方法，采用常规方法进行混合搅拌即可。
实施例2
环保耐水、耐擦洗内墙涂料，由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝45∶30∶80∶20∶5.5∶4.0∶120。其它同实施例1。
实施例3
环保耐水、耐擦洗内墙涂料，由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝75∶15∶50∶10∶3.5∶2.0∶90。其它同实施例1。
实施例4
环保耐水、耐擦洗内墙涂料，由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝55∶26∶70∶17∶5.0∶3.5∶110。其它同实施例1。
实施例5
环保耐水、耐擦洗内墙涂料，由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝65∶17∶60∶12∶4.0∶2.2∶100。其它同实施例1。
实施例6
环保耐水、耐擦洗内墙涂料，由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝58∶25∶72∶15∶4.5∶2.55∶110。其它同实施例1。
具体使用时：本发明涂料在使用前要搅拌均匀；本发明涂料可采用喷、辊或刷涂，一般涂两遍，待第一遍干燥后，在涂第二遍，通常间隔在2～4小时；涂刷温度不低于5℃。
Claims (4)
1.环保耐水、耐擦洗内墙涂料，其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝45～75∶15～30∶50～80∶10～20∶3.5～5.5∶2.0～4.0∶90～120。
2.根据权利要求1所述的环保耐水、耐擦洗内墙涂料，其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝55～65∶17～26∶60～70∶12～17∶4.0～5.0∶2.2～3.5∶100～110。
3.根据权利要求1所述的环保耐水、耐擦洗内墙涂料，其特征在于是由下述原料按重量份数比组成：硅灰石粉∶凹凸棒土∶轻质碳酸钙∶膨润土∶改性剂∶交联剂∶水＝60∶28∶65∶15∶4.5∶3.0∶105。
4.根据权利要求1、2或3所述的环保耐水、耐擦洗内墙涂料，其特征在于所述的交联剂为氯化聚乙烯。