CN102211901B - Sculpture mud for student and preparation method thereof - Google Patents
Sculpture mud for student and preparation method thereof Download PDFInfo
- Publication number
- CN102211901B CN102211901B CN2011101098357A CN201110109835A CN102211901B CN 102211901 B CN102211901 B CN 102211901B CN 2011101098357 A CN2011101098357 A CN 2011101098357A CN 201110109835 A CN201110109835 A CN 201110109835A CN 102211901 B CN102211901 B CN 102211901B
- Authority
- CN
- China
- Prior art keywords
- preparation
- vaseline
- toner
- kaolin
- talcum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses sculpture mud for a student and a preparation method thereof. The sculpture mud comprises the following raw material components in parts by weight: 30-45 of olefin, 45-55 of ozocerite, 5-15 of vaseline, 2-5 of glycerin, 20-40 of kaolin, 80-120 of talcum powder and 0.5-0.8 of toner. The preparation method comprises the following steps: adding the olefin, ozocerite and vaseline in a reaction kettle for heating and fusion; and adding the glycerin and toner for evenly stirring, adding the talcum powder and kaolin while stirring, continuously stirring until no particles are generated; and pouring out slurry, cooling to 35 DEG C-45 DEG C, and then carrying out extrusion molding in a pug mill. The finished sculpture mud prepared by using the unique raw material formula and preparation process has the advantages of hard and fine texture, bright color, no toxicity and no pollution, does not stick the hand, can be finely curved and can be softened by being warmed by a hand, and the shaping is convenient.
Description
Technical field
The present invention relates to a kind of carving material and preparation method thereof, especially relate to special-purpose sculpture clay of a kind of student and preparation method thereof.
Background technology
Sculpture clay is a kind of mud that the student is used for making the intention moulding; It can improve students ' practical ability, also can cultivate aesthetic quality such as moulding, color, the wing that lets them launch to imagine; Give full play to their initiative chui, create the important materials of the works of oneself audaciously.In order to improve student's interest, the manufacturer also provides sculpture clay model miscellaneous, but utilizes model straight forming clay sculpture spare, and is life-like and liked by the student.
Previous sculpture clay major ingredient comprises old powder, terra alba, sealing wax and rubber etc., and it exists, and color is gloomy, temperature difference bad adaptability, and cold day is pinched motionless firmly; The sticking hand of soft and easy paste in hot day; Pollute, main is to have the certain toxicity that is caused by its component, bans use of.Existing sculpture clay normally is made up of talcum powder, Paris white, breeze, butter, pigment and paraffin.Talcum powder, Paris white and breeze with can not form the mineral colloid after water mixes, be to depend on grease and be bonded together fully.The plastic poor-performing of this greasy filth, the finished product after the making are easy to generate drying, cracking, distortion, mouldy and rotten, in making processes, also can make the operator that a kind of greasy feeling is arranged on hand, and duration of service, long can the stimulation pointed, and influenced sense of touch, and touched with one's hand.
Summary of the invention
The defective that The present invention be directed to the existence of above-mentioned background technology provides special-purpose sculpture clay of a kind of student and preparation method thereof, and quality is hard careful, bright in luster under its sculpture clay finished product normal temperature of making; Can work with great care, can soften with the hand temperature, moulding easy; Tack-free, nontoxic, pollution-free.
For realizing above-mentioned purpose, the invention discloses special-purpose sculpture clay of a kind of student and preparation method thereof, the special-purpose sculpture clay of said student comprises the feed composition of following part by weight: paraffin: 30 ~ 45; Ceresine: 45 ~ 55; Vaseline: 5 ~ 15, glycerine: 2 ~ 5, kaolin: 20 ~ 40; Talcum powder: 80 ~ 120, toner: 0.5 ~ 0.8.The preparation method of the special-purpose sculpture clay of said student comprises the steps: at first, places in the reaction kettle paraffin, ceresine, Vaseline and heating; Secondly, when the material in the reaction kettle is heated to molten state, glycerine and toner are added in the said reaction kettle, and be stirred to and be evenly distributed; The 3rd, add kaolin and talcum powder while stirring; At last, when continue stirring in reaction kettle no particle, the slip in the reaction kettle is poured out and is cooled between 35 ℃ ~ 45 ℃, just get final product with the pug mill extrusion molding.
Further, the special-purpose sculpture clay of student comprises the feed composition of following part by weight: paraffin: 35 ~ 40, and ceresine: 48 ~ 53, Vaseline: 8 ~ 12, glycerine: 3 ~ 4, kaolin: 25 ~ 35, talcum powder: 90 ~ 110, toner: 0.6 ~ 0.7.
Further, the special-purpose sculpture clay of student comprises the feed composition of following part by weight: paraffin: 38, and ceresine: 50, Vaseline: 10, glycerine: 3.5, kaolin: 30, talcum powder: 100, toner: 0.65.
Further, last step of said preparation method is: when continue stirring in reaction kettle no particle, 40 ℃ are poured out and be cooled to the slip in the reaction kettle, just use the pug mill extrusion molding.
In sum, quality is hard careful, bright in luster under the sculpture clay finished product normal temperature that the present invention makes through the composition of raw materials and the manufacture craft of above-mentioned uniqueness, can work with great care, and can soften with the hand temperature, and is moulding easy, tack-free, nontoxic, pollution-free.
Embodiment
For further understanding characteristic of the present invention, technique means and the specific purposes that reached, function, the present invention is described in further detail below in conjunction with embodiment.
Embodiment 1: the special-purpose sculpture clay of student of the present invention comprise following part by weight feed composition (unit: kilogram): paraffin: 30, ceresine: 45, Vaseline: 5, glycerine: 2, kaolin: 20, talcum powder: 80, toner: 0.5.The preparation method of the special-purpose sculpture clay of said student comprises the steps: at first, places in the reaction kettle paraffin, ceresine, Vaseline and heating; Secondly, when the material in the reaction kettle is heated to molten state, glycerine and toner are added in the said reaction kettle, and be stirred to and be evenly distributed; The 3rd, add kaolin and talcum powder while stirring; At last, when continue stirring in reaction kettle no particle, 40 ℃ are poured out and be cooled to the slip in the reaction kettle, just get final product with the pug mill extrusion molding.
Embodiment 2, and the preparation method of present embodiment is identical with embodiment 1, and its difference is that the special-purpose sculpture clay raw material of student provided by the invention is prepared from (unit: kilogram) following components by weight percent; Paraffin: 45, ceresine: 55, Vaseline: 15; Glycerine: 5; Kaolin: 40, talcum powder: 120, toner: 0.8.
Embodiment 3, and the preparation method of present embodiment is identical with embodiment 1, and its difference is that the special-purpose sculpture clay raw material of student provided by the invention is prepared from (unit: kilogram) following components by weight percent; Paraffin: 38, ceresine: 50, Vaseline: 10; Glycerine: 3.5; Kaolin: 30, talcum powder: 100, toner: 0.65.
In sum, quality is hard careful, bright in luster under the sculpture clay finished product normal temperature that the present invention makes through the composition of raw materials and the manufacture craft of above-mentioned uniqueness, can work with great care, and can soften with the hand temperature, and is moulding easy, tack-free, nontoxic, pollution-free.Meet the requirement of GB6675-86 (Chinese toy safety standards) standard, EN7 1 (European toy safety standard) and ASTM-F963 (U.S. test association toy safety standard).
The above embodiment has only expressed one embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as limitation of the scope of the invention.Should be pointed out that for the person of ordinary skill of the art under the prerequisite that does not break away from the present invention's design, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with accompanying claims.
Claims (7)
1. the special-purpose sculpture clay of a student is characterized in that: the feed composition that comprises following part by weight: paraffin: 30 ~ 45, and ceresine: 45 ~ 55, Vaseline: 5 ~ 15, glycerine: 2 ~ 5, kaolin: 20 ~ 40, talcum powder: 80 ~ 120, toner: 0.5 ~ 0.8.
2. the special-purpose sculpture clay of student according to claim 1 is characterized in that: the feed composition that comprises following part by weight: paraffin: 35 ~ 40, and ceresine: 48 ~ 53; Vaseline: 8 ~ 12, glycerine: 3 ~ 4, kaolin: 25 ~ 35; Talcum powder: 90 ~ 110, toner: 0.6 ~ 0.7.
3. the special-purpose sculpture clay of student according to claim 1 and 2 is characterized in that: the feed composition that comprises following part by weight: paraffin: 38, and ceresine: 50, Vaseline: 10, glycerine: 3.5, kaolin: 30, talcum powder: 100, toner: 0.65.
4. the preparation method of the special-purpose sculpture clay of student is characterized in that, comprises the steps: at first; Prepare the feed composition of following part by weight: paraffin: 30 ~ 45, ceresine: 45 ~ 55, Vaseline: 5 ~ 15; Glycerine: 2 ~ 5, kaolin: 20 ~ 40, talcum powder: 80 ~ 120; Toner: 0.5 ~ 0.8, place in the reaction kettle paraffin, ceresine, Vaseline and heating; Secondly, when the material in the reaction kettle is heated to molten state, glycerine and toner are added in the said reaction kettle, and be stirred to and be evenly distributed; The 3rd, add kaolin and talcum powder while stirring; At last, when continue stirring in reaction kettle no particle, the slip in the reaction kettle is poured out and is cooled between 35 ℃ ~ 45 ℃, just get final product with the pug mill extrusion molding.
5. the preparation method of the special-purpose sculpture clay of student according to claim 4 is characterized in that: the feed composition that comprises following part by weight: paraffin: 35 ~ 40, and ceresine: 48 ~ 53; Vaseline: 8 ~ 12, glycerine: 3 ~ 4, kaolin: 25 ~ 35; Talcum powder: 90 ~ 110, toner: 0.6 ~ 0.7.
6. the preparation method of the special-purpose sculpture clay of student according to claim 5 is characterized in that: the feed composition that comprises following part by weight: paraffin: 38, and ceresine: 50; Vaseline: 10, glycerine: 3.5, kaolin: 30; Talcum powder: 100, toner: 0.65.
7. the preparation method of the special-purpose sculpture clay of student according to claim 6; It is characterized in that: last step of said preparation method is: when continue stirring in reaction kettle no particle; 40 ℃ are poured out and be cooled to slip in the reaction kettle, just use the pug mill extrusion molding.