CN102206474A - 用于cpvc材料的溶剂型胶粘剂 - Google Patents
用于cpvc材料的溶剂型胶粘剂 Download PDFInfo
- Publication number
- CN102206474A CN102206474A CN 201010529839 CN201010529839A CN102206474A CN 102206474 A CN102206474 A CN 102206474A CN 201010529839 CN201010529839 CN 201010529839 CN 201010529839 A CN201010529839 A CN 201010529839A CN 102206474 A CN102206474 A CN 102206474A
- Authority
- CN
- China
- Prior art keywords
- solvent
- cpvc
- based adhesive
- resin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及溶剂型胶粘剂,具体是用于CPVC材料的溶剂型胶粘剂。该胶粘剂包括以下重量份数的组分:CPVC树脂15-28,低毒性溶剂120-165,增稠树脂0-15。一方面,本发明胶粘剂的粘接性能和耐热性能较佳,且各组分成本较低,具有较强的产品竞争力。另一方面,本发明的胶粘剂采用低毒性溶剂,可以用于给水CPVC管道系统粘接,固化后不影响水质,符合健康环保趋势。
Description
技术领域
本发明涉及溶剂型胶粘剂,具体是用于CPVC材料的溶剂型胶粘剂。
背景技术
CPVC(氯化聚氯乙烯)是由PVC(聚氯乙烯)氯化改性制得的一种介于橡胶和塑料之间的新型高分子弹性体材料。该产品为白色或淡黄色无味、无臭、无毒的疏松颗粒或粉末。PVC经过氯化后,分子键的不规则性增加,极性增加,使得溶解性增大,化学稳定性增加,从而提高了材料的耐热性、耐酸、碱、盐、氧化剂等的腐蚀。因此,CPVC是一种应用前景广阔的新型工程塑料。
CPVC管道连接通常采用粘接方式。这种方式采用溶剂型胶粘剂分别涂覆在需粘接的管材外表面和管件内表面,软化腐蚀需粘接表面,然后再通过一定的作用力使两表面融合在一起。此外,胶粘剂中的树脂有助于填充间隙,加速凝固,减少收缩和内应力,增强管材和管件的粘合力。然而目前并没有关于专门用于CPVC管道连接的溶剂型胶粘剂的公开资料。
另一方面,关于适用于硬质PVC的胶粘剂则有较多的报道。例如:《PVC-U管材胶粘剂的研制》(胡爱珠、杨建平,浙江化工,2000,31卷,第4期)介绍了以丁酮、环己酮、二氯己烷为混合溶剂溶解CPVC和PVC基料得到一种强度好的PVC-U管材用溶剂型胶粘剂。《改性硬质PVC胶粘剂的研制》(褚衡陈绪煌等,湖北化工,1999年第4期)介绍了采用二氯乙烷、四氢呋喃、三氯乙烯、环己酮、二甲苯等溶剂溶解EVA、CPE、CEPDM改性的CPVC而制得一种性能优良的硬质PVC胶粘剂。中国专利CN 200610035322.5公开了一种用于硬聚氯乙烯塑料管道系统粘接的低毒性溶剂型胶粘剂。
虽然上述胶粘剂也可以用于CPVC管道连接,但也存在一些不足:
(1)PVC类的溶剂型胶粘剂的粘接性能较差,因此采用这类胶粘剂来粘接CPVC管材和管件效果不是很理想。
(2)部分产品忽视了溶剂毒性对所输送水质的污染,广泛使用二氯乙烷、二氯己烷、甲苯、三氯乙烯等有毒产品做溶剂。
(3)这些PVC类溶剂型胶粘剂还有个缺陷就是不耐热。由于其填充的树脂粉以PVC树脂粉或改性PVC树脂粉为主,固化后软化点低,不适合CPVC管道系统用于输送热水的场合。
因此提供一种毒性低、专门适用于CPVC材料的溶剂型胶粘剂是一个需要解决的技术问题。
发明内容
本发明解决的第一技术问题是提供一种专门适用于CPVC材料的溶剂型胶粘剂,该胶粘剂不仅毒性较低,且具有较佳的粘结性能、耐热性能,使得使用该胶粘剂的CPVC管道系统更加安全可靠。
为解决上述技术问题,本发明采用技术方案是:
一种用于CPVC材料的溶剂型胶粘剂,该胶粘剂包括以下重量份数的组分:CPVC树脂15-28,低毒性溶剂120-165,增稠树脂0-15。
作为改进之一:所述低毒性溶剂包括环己酮、丁酮、乙酸乙酯中的一种或多种。
作为改进之二:所述低毒性溶剂各组分的重量份数为:环己酮60-70,丁酮55-80,乙酸乙酯5-15。
作为改进之三:该胶粘剂还包括填充料,该填充料为碳酸钙、高岭土、蒙脱土中的一种或多种混合物。
作为改进之四:所述填充料的重量份数比例小于10%
作为改进之五:所述增稠树脂为改性酚醛树脂、萜烯树脂、改性松香树脂中的一种或一种以上混合物。
与现有技术相比,本发明的有益效果是:
(1)本发明胶粘剂的粘接性能和耐热性能较佳,且各组分成本较低,具有较强的产品竞争力。
(2)本发明的胶粘剂采用低毒性溶剂,可以用于给水CPVC管道系统粘接,固化后不影响水质,符合健康环保趋势。
具体实施方式
将各组分按重量比例均匀混合后使之成为溶液或胶体,即可制得本发明的用于CPVC材料的溶剂型胶粘剂。实施例1-3的具体组分和重量比例如表1所示。
表1
分别将上述三个实施例的组分均匀混合制作成具有一定粘度的液体即可得到适用于CPVC材料,尤其是CPVC管道粘接的胶粘剂。由于上述各实施例采用的组分中没有采用毒性较高的物质,而且各组分不会反应生成剧毒物质,因此最终得到的胶粘剂毒性较低。
在上述实施例中,除了可以适用叔丁基酚醛树脂和改性松香树脂作为增稠剂以外,还可以使用萜烯树脂、其他类型的改性酚醛树脂作为增稠剂。这些增稠树脂既可以单独使用可以多种混合使用。另外,在上述实施例中还可以使用其他常用的填充料,例如高岭土、蒙脱土等。这些填充料同样既可以单独使用,也可以混合使用,但是混合的比例最好不要超过10%。
表2是分别使用上述三个实施例的胶粘剂来粘接的CPVC管材和管件所测得力学性能数据。
表2
[1]CPVC管材、管件用胶粘剂粘接好后,在23±2℃条件下调节2小时后立即开始实验。
[2]CPVC管材、管件用胶粘剂粘接好后,在80±2℃条件下调节2小时后立即开始实验。
[3]CPVC管材、管件用胶粘剂粘接好后,至少要在常温下静置1天,然后在80±2℃条件下静置4天后才开始实验。
力学性能实验结果表明,本发明的CPVC管材、管件采用实施例1-3的胶粘剂,具有较高的强度和耐热性能,符合行业技术标准要求,也满足实际使用要求。另一方面,实施例1-3配方的成本低,符合实用性和经济行要求,具有较高性价比,有很强的市场推广前景。
Claims (6)
1.一种用于CPVC材料的溶剂型胶粘剂,其特征在于包括以下重量份数的组分:CPVC树脂15-28,低毒性溶剂120-165,增稠树脂0-15。
2.根据权利要求1所述的用于CPVC材料的溶剂型胶粘剂,其特征在于:所述低毒性溶剂包括环己酮、丁酮、乙酸乙酯中的一种或多种。
3.根据权利要求2所述的用于CPVC材料的溶剂型胶粘剂,其特征在于:所述低毒性溶剂各组分的重量份数为:环己酮60-70,丁酮55-80,乙酸乙酯5-15。
4.根据权利要求1至3任一所述的用于CPVC材料的溶剂型胶粘剂,其特征在于:该胶粘剂还包括填充料,该填充料为碳酸钙、高岭土、蒙脱土中的一种或多种混合物。
5.根据权利要求4所述的用于CPVC材料的溶剂型胶粘剂,其特征在于:所述填充料的重量份数比例小于10%。
6.根据权利要求1至3任一所述的用于CPVC材料的溶剂型胶粘剂,其特征在于:所述增稠树脂为改性酚醛树脂、萜烯树脂、改性松香树脂中的一种或一种以上混合物。