CN102206453A - Method for producing external wall latex paint - Google Patents
Method for producing external wall latex paint Download PDFInfo
- Publication number
- CN102206453A CN102206453A CN2010101425975A CN201010142597A CN102206453A CN 102206453 A CN102206453 A CN 102206453A CN 2010101425975 A CN2010101425975 A CN 2010101425975A CN 201010142597 A CN201010142597 A CN 201010142597A CN 102206453 A CN102206453 A CN 102206453A
- Authority
- CN
- China
- Prior art keywords
- parts
- latex paint
- wall latex
- exterior wall
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing an external wall latex paint. The product in the invention is a top-quality external wall latex paint which is made of high grade raw materials by adopting an advanced production process. The latex paint has excellent properties, and good decoration property, color retention, stain resistance and weatherability. When being in use, the latex paint has the characteristics of flat, rich and bright paint film, strong durability, fast drying, firm adhesion, good scrub-resistance, dense and thick paint liquid, strong covering power, no toxicity and odor and lustrousness, so the latex paint belongs to an environment-friendly product. The raw materials adopted for producing the external wall latex paint are as follows: water, AMP-95 (a 2-amino-2-methyl-1-propanol containing 5 percent of water), acrylic ester copolymer, dodecanol ester, a defoaming agent, mildew preventive, rutile titanium pigment, mica powder, zinc oxide, pure acrylic emulsion, calcium carbonate, calcined kaolin, alkali-swelling thickening agent, bactericide, a covering emulsion and a polyurethane thickener.
Description
Affiliated technical field:
Product of the present invention belongs to building materials field.
Background technology:
The major function of exterior wall latex paint is to decorate and the protection external surface of buildings, makes the buildings appearance neat and artistic, can play the effect of protection skin simultaneously, prolongs its work-ing life.Its service requirements following points: good decorative property, require the exterior wall latex paint rich color, select variation, tint retention is good, can the long period keep good decorate properties; Water-tolerant, exterior wall long-term exposure will often be subjected to rainwash, thereby exterior wall latex paint must possess good water resistance in atmosphere; After dust in the atmosphere and other materials stain coating, coating can lose original aesthetic, thereby exterior wall latex paint must be difficult for being stain or stain the back easy cleaning by these materials; Good weatherability is exposed to coating in the atmosphere and is subjected to the influence of many weather environment factors and effect down, and phenomenons such as general coating can occur ftractureing, peels off, shedding, variable color make it lose original ornamental and protectiveness.Therefore, the exterior wall latex paint coating requires in the time limit of regulation above-mentioned breakoff phenomenon to take place, and it must possess good weather resistance.A kind of high-grade exterior wall latex paint that product of the present invention is selected high-quality raw material for use, adopted advanced production technique to produce.This coats with lacquer excellent property, can satisfy good decorative property, conditions such as tint retention is good, contamination resistance is good, good weatherability.In use strong, dry rapidly, the adhere firmly of smooth, plentiful, bright, the weather resistance of paint film, scrubbing resistance, lacquer liquid stiff, strong covering power, nonpoisonous and tasteless, light arranged, belong to environmentfriendly products.Along with causing day of Building Trade in China developed with progressive, China is also more and more higher to the requirement of outdoor wall.The various defectives that exist at the exterior wall latex paint of former production, original technology and prescription have been carried out improving and having developed this product, this lacquer is to be filmogen, to be added high-quality pigment, filler and auxiliary agent by pure-acrylic emulsion, the environmental protection and economy type coating that processes meticulously through the science design.Product has good weathering resistance, alkali resistance, abrasion resistance, good decorating effect, and is harmless, environmental.
Summary of the invention:
The invention provides a kind of method of suitability for industrialized production exterior wall latex paint, this product has good ornamental, water tolerance, weathering resistance and washing property certainly.The raw material of producing this emulsion paint use has: 155 parts in water, 1.5 parts of AMP-95,15 parts of acrylate copolymers, 25 parts of 12 carbon alcohol esters, 10 parts of defoamers, 7.5 parts of mould inhibitors, 170 parts in rutile titanium white powder, 10 parts of mica powders, 5 parts in zinc oxide, 480 parts of pure-acrylic emulsions, 40 parts in lime carbonate, 40 parts of calcined kaolins, 4 parts of alkali swelling property thickening materials, 2 parts in sterilant, 25 parts of opacifying property emulsions, 10 parts of polyurethane thickeners.
A kind of production method of exterior wall latex paint, its beneficial effect is: product has good weathering resistance, alkali resistance, abrasion resistance, good decorating effect, and coating is harmless, and is environmental.
Embodiment:
Embodiment:
The first step: water is added chemical reaction kettle for 155 parts, start stirrer, rotating speed is 35 rev/mins, and temperature is brought up to 35 ℃, adds 1.5 parts of AMP-95 slowly, is stirred to dissolving; Add 15 parts of acrylate copolymers more slowly, be stirred to dissolving, insulation reaction 30 minutes.
Second step: 25 parts of 12 carbon alcohol esters, 10 parts of defoamers, mould inhibitor are added reactor for 7.5 parts slowly, stir, insulation reaction 30 minutes.
The 3rd step: 170 parts in rutile titanium white powder, 10 parts of mica powders, 5 parts of adding reactors of zinc oxide, speed drop to 10 rev/min stirs.
The 4th step: be cooled to normal temperature, add 480 parts of pure-acrylic emulsions, rotating speed with 10 rev/mins stirs, rotating speed is brought up to 30 rev/mins, add 40 parts in lime carbonate, 40 parts of calcined kaolins, 4 parts of alkali swelling property thickening materials, 2 parts in sterilant, 25 parts of opacifying property emulsions, 10 parts of polyurethane thickeners successively, stirring promptly gets exterior wall latex paint.
Claims (5)
1. the production method of an exterior wall latex paint is characterized in that with 155 parts in water, AMP-951.5 part, 15 parts of acrylate copolymers, 25 parts of 12 carbon alcohol esters, 10 parts of defoamers, 7.5 parts of mould inhibitors, 170 parts in rutile titanium white powder, 10 parts of mica powders, 5 parts in zinc oxide, 480 parts of pure-acrylic emulsions, 40 parts in lime carbonate, 40 parts of calcined kaolins, 4 parts of alkali swelling property thickening materials, 2 parts in sterilant, 25 parts of opacifying property emulsions, 10 parts of polyurethane thickeners.Obtain finished product by following step.
2. the production method of an exterior wall latex paint, the feature of its first step is: water is added chemical reaction kettle for 155 parts, start stirrer, rotating speed is 35 rev/mins, and temperature is brought up to 35 ℃, adds AMP-951.5 part slowly, is stirred to dissolving; Add 15 parts of acrylate copolymers more slowly, be stirred to dissolving, insulation reaction 30 minutes.
3. the production method of an exterior wall latex paint, the feature in its second step is: 25 parts of 12 carbon alcohol esters, 10 parts of defoamers, mould inhibitor are added reactor for 7.5 parts slowly, stir, insulation reaction 30 minutes.
4. the production method of an exterior wall latex paint, the feature in its 3rd step is: 170 parts in rutile titanium white powder, 10 parts of mica powders, 5 parts of adding reactors of zinc oxide, speed drop to 10 rev/min stirs.
5. the production method of an exterior wall latex paint, the feature in its 4th step is: be cooled to normal temperature, add 480 parts of pure-acrylic emulsions, rotating speed with 10 rev/mins stirs, rotating speed is brought up to 30 rev/mins, add 40 parts in lime carbonate, 40 parts of calcined kaolins, 4 parts of alkali swelling property thickening materials, 2 parts in sterilant, 25 parts of opacifying property emulsions, 10 parts of polyurethane thickeners successively, stirring promptly gets exterior wall latex paint.