CN102199387A - Preparation method of fluorocarbon roller painting stone-imitating coating - Google Patents
Preparation method of fluorocarbon roller painting stone-imitating coating Download PDFInfo
- Publication number
- CN102199387A CN102199387A CN 201110084519 CN201110084519A CN102199387A CN 102199387 A CN102199387 A CN 102199387A CN 201110084519 CN201110084519 CN 201110084519 CN 201110084519 A CN201110084519 A CN 201110084519A CN 102199387 A CN102199387 A CN 102199387A
- Authority
- CN
- China
- Prior art keywords
- coating
- fluorine carbon
- preparation
- stone material
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a fluorocarbon roller painting stone-imitating coating. The method comprises the following steps: (1) mixing and dispersing fluorocarbon varnish, a 3175 curing agent, isophorone, a delustering agent, inorganic ceramic pigment, solvent oil and butanone, and grinding until the fineness is 15-25 micron; (2) carrying out roller painting and baking on coiled aluminum: coating polyester system base paint and then baking, and middle coating fluorocarbon finish paint and then baking; and (3) three coating; spraying various stone-imitating paints on the coiled aluminum according to the size and color of pattern by using a spray device and a spray gun, and baking in a furnace at the temperature of 240-245 DGE C, wherein the spray speed of the spray device is 18m/min, and the spray flow is 200cc/min. By using the preparation method, the radiation and water absorption properties of the surface of the prepared fluorocarbon roller painting stone-imitating coating can be improved; bulge and deformation are not easy to occur for a long-term use; and the coating on the surface is not easy to fall out; and the weather resistance is good.
Description
Technical field
The present invention relates to the field of coating, the preparation method of the imitative stone material coating of especially a kind of fluorine carbon roller coat.
Background technology
Fast development along with Building Trade in China, people more and more pursue the effect of nature to the building decoration aspect at present, the outer wall coating of the diversification low power consuming environment-friendly type of external wall more and more is subjected to building the favor of manufacturer, the product of stone material has just reached such requirement, and its natural texture and different surface effects are subjected to the welcome in market very much.Particularly in western countries, high-grade building nearly all be unable to do without stone material.At stone material the inside marble and grouan is most popular, and natural granite has luxurious dignified decorative effect and superior barrier propterty.
The restricted use of present external wall of high-rise building ceramic tile and marble coating requires the lithotome curtain wall should not be applied in the Highrise buildings in big cities such as Beijing and Chongqing, if when design requirements is adopted, the measure of stone material chip resistant be arranged.The stone curtain wall of non-seismic design, stone material must not be damaged under wind effect; The stone curtain wall of seismic design, curtain wall still can use after repairing under the fortification intensity earthquake action; Curtain wall frame must not come off under rare earthquake action, because tellurian resource is limited, and in the face of constantly consuming the condition that makes resource deficient more, the soil erosion vegetation havoc that over-drastic exploitation causes has brought irreparable damage to ecology, also forbids or reduces the such price that has also raised stone material of exploitation in a lot of countries in recent years.
At this growth requirement, occurred the imitative stone material coating of a kind of aluminium-plastic panel in the market, the imitative stone material coating of this aluminium-plastic panel all is that heat transfer film is made, can only be as indoor design, weathering resistance is relatively poor, and transfer film uses back bulge distortion easily for a long time.
Summary of the invention
The technical problem to be solved in the present invention is: overcome the deficiencies in the prior art, the preparation method of the imitative stone material coating of a kind of fluorine carbon roller coat is provided, the imitative stone material coating of the fluorine carbon roller coat that adopts its preparation method to prepare has stone effect true to nature and super weatherable coating and good repeatability, and the top coat difficult drop-off.
The technical solution adopted for the present invention to solve the technical problems is: the preparation method of the imitative stone material coating of a kind of fluorine carbon roller coat has following steps:
(1) preparation fluorine carbon finishing paint coating: with weight proportion
Fluorine carbon varnish: 60～70%,
3175 solidifying agent: 0.5～1.5%,
Different fluorine that ketone: 2～8%,
Matting agent: 0.1～0.5%,
Inorganic ceramic pigment: 17～27%,
Solvent oil: 2～8%,
Butanone: 1.2～2.2%
Blending dispersion 20～30 minutes, mesh-of-grind to 15～25 micron form fluorine carbon finishing paint coating;
(2) volume aluminium roller coat baking: be coated with fluorine carbon finishing paint coating and baking during application polyester system priming paint and baking reach;
(3) three are coated with: adopt flusher and spray gun that size and the color of all kinds of imitative stone material coating by decorative pattern is sprayed on the volume aluminium, advance stove and toast under 240～245 ℃ of temperature.
Particularly, described preparation fluorine carbon finishing paint coating: with weight proportion
Fluorine carbon varnish: 65%,
3175 solidifying agent: 1%,
Different fluorine that ketone: 5%,
Matting agent: 0.3%,
Inorganic ceramic pigment: 22%,
Solvent oil: 5%,
Butanone: 1.7%
Blending dispersion 20～30 minutes, mesh-of-grind to 15～25 micron form fluorine carbon finishing paint coating.
Particularly, the spray rate of described flusher is 18m/min, and the sprinkling flow is 200cc/min.
Particularly, described jitter time is 25 minutes.
Particularly, described mesh-of-grind is 20 microns.
The invention has the beneficial effects as follows: the imitative stone material coating of fluorine carbon roller coat that adopts preparation method's preparation of the imitative stone material coating of fluorine carbon roller coat of the present invention, can increase the radiation and the water-absorbent of coatingsurface, the long-time use is difficult for the bulge distortion, and the effect of imitative stone material, degree height true to nature, thickness standard and easy construction.Imitative stone material decorative pattern in the imitative stone material coating of fluorine carbon roller coat of the present invention obtains after spraying baking by flusher, therefore, the top coat difficult drop-off, weathering resistance is better.
Embodiment
The preparation method of the imitative stone material coating of a kind of fluorine carbon roller coat has following steps:
(1) preparation fluorine carbon finishing paint coating: with weight proportion
Fluorine carbon varnish: 65%,
3175 solidifying agent: 1%,
Different fluorine that ketone: 5%,
Matting agent: 0.3%,
Inorganic ceramic pigment: 22%,
Solvent oil: 5%,
Butanone: 1.7%
Blending dispersion 20～30 minutes, mesh-of-grind to 15～25 micron form fluorine carbon finishing paint coating;
(2) volume aluminium roller coat baking: be coated with fluorine carbon finishing paint coating and baking during application polyester system priming paint and baking reach;
(3) three are coated with: adopt flusher and spray gun that size and the color of all kinds of imitative stone material coating by decorative pattern is sprayed on the volume aluminium, advancing stove advances stove in baking under 240～245 ℃ of temperature and toasts under 240～245 ℃ of temperature, the spray rate of flusher is 18m/min, and the sprinkling flow is 200cc/min.
Whole coating process is 3 to be coated with 3 roastingly, and the spray rate of the speed of whole streamline and spray gun will have good collocation when application for the third time.General imitative stone color is that 3～4 colors are formed.
Imitative stone material decorative pattern in the imitative stone material coating of fluorine carbon roller coat of the present invention obtains after spraying baking by flusher, therefore, the top coat difficult drop-off, weathering resistance is better.
Adopt the imitative stone material coating of fluorine carbon roller coat of preparation method's preparation of the imitative stone material coating of fluorine carbon roller coat of the present invention, can increase the radiation and the water-absorbent of coatingsurface, the long-time use is difficult for the bulge distortion, and the effect of imitative stone material, degree height true to nature, thickness standard and easy construction.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must determine its technical scope according to the claim scope.
Claims (5)
1. a fluorine carbon roller coat is imitated the preparation method of stone material coating, it is characterized in that: have following steps:
(1) preparation fluorine carbon finishing paint coating: with weight proportion
Fluorine carbon varnish: 60～70%,
3175 solidifying agent: 0.5～1.5%,
Different fluorine that ketone: 2～8%,
Matting agent: 0.1～0.5%,
Inorganic ceramic pigment: 17～27%,
Solvent oil: 2～8%,
Butanone: 1.2～2.2%
Blending dispersion 20～30 minutes, mesh-of-grind to 15～25 micron form fluorine carbon finishing paint coating;
(2) volume aluminium roller coat baking: be coated with fluorine carbon finishing paint coating and baking during application polyester system priming paint and baking reach;
(3) three are coated with: adopt flusher and spray gun that size and the color of all kinds of imitative stone material coating by decorative pattern is sprayed on the volume aluminium, advance stove and toast under 240～245 ℃ of temperature.
2. the preparation method of the imitative stone material coating of fluorine carbon roller coat according to claim 1 is characterized in that: described preparation fluorine carbon finishing paint coating: with weight proportion
Fluorine carbon varnish: 65%,
3175 solidifying agent: 1%,
Different fluorine that ketone: 5%,
Matting agent: 0.3%,
Inorganic ceramic pigment: 22%,
Solvent oil: 5%,
Butanone: 1.7%
Blending dispersion 20～30 minutes, mesh-of-grind to 15～25 micron form fluorine carbon finishing paint coating.
3. the preparation method of the imitative stone material coating of fluorine carbon roller coat according to claim 1, it is characterized in that: the spray rate of described flusher is 18m/min, the sprinkling flow is 200cc/min.
4. the preparation method of the imitative stone material coating of fluorine carbon roller coat according to claim 1, it is characterized in that: described jitter time is 25 minutes.
5. the preparation method of the imitative stone material coating of fluorine carbon roller coat according to claim 1, it is characterized in that: described mesh-of-grind is 20 microns.