CN102167959B - 一种光锥与ccd耦合粘接用胶及其制备方法 - Google Patents

一种光锥与ccd耦合粘接用胶及其制备方法 Download PDF

Info

Publication number
CN102167959B
CN102167959B CN201110053666A CN201110053666A CN102167959B CN 102167959 B CN102167959 B CN 102167959B CN 201110053666 A CN201110053666 A CN 201110053666A CN 201110053666 A CN201110053666 A CN 201110053666A CN 102167959 B CN102167959 B CN 102167959B
Authority
CN
China
Prior art keywords
ccd
light cone
glue
polyisobutene
petroleum resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201110053666A
Other languages
English (en)
Other versions
CN102167959A (zh
Inventor
句红兵
郑林涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YUNNAN PHOTOELECTRIC AUXILIARY MATERIAL CO Ltd
Original Assignee
YUNNAN PHOTOELECTRIC AUXILIARY MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YUNNAN PHOTOELECTRIC AUXILIARY MATERIAL CO Ltd filed Critical YUNNAN PHOTOELECTRIC AUXILIARY MATERIAL CO Ltd
Priority to CN201110053666A priority Critical patent/CN102167959B/zh
Publication of CN102167959A publication Critical patent/CN102167959A/zh
Application granted granted Critical
Publication of CN102167959B publication Critical patent/CN102167959B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及光电化工辅料领域，尤其是一种光锥与CCD耦合粘接用胶及其制备方法。这种光锥与CCD耦合粘接用胶的特征在于，由一定重量份比的数均分子量为1000～2000及2000～3500的两种聚异丁烯、碳五石油树脂、癸二酸二异辛酯、2，6—二叔丁基对甲酚混合制备而成。以此胶粘剂将光锥与CCD耦合粘接在一起，粘接效果好。经高温低温循环试验、振动试验，胶层无变化，光透过率损失小。

Description

一种光锥与CCD耦合粘接用胶及其制备方法
技术领域
本发明涉及光电化工辅料领域，尤其是一种光锥与CCD耦合粘接用胶及其制备方法。
背景技术
光锥作为一种硬光纤锥形传像器件，具有放大或缩小并无畸变传输图像的功能，在相同分辨率下，光锥与电荷耦合器件(Charge Coupled Device，CCD)耦合后可缩短焦距，从而减小仪器的体积和重量。此技术已经在微光夜视技术、空间遥感探测、导弹电视跟踪系统、医学视频成像、荧光学等领域得到应用。
光锥与CCD耦合连接一般都采用粘接。发明专利CN 101051107及CN1887227中都提及，光锥与CCD耦合对准后采用粘接剂进行粘合。其中CN1887227中更提及，光锥与CCD耦合粘接采用光敏胶。
由于光锥像元与CCD像元在尺寸、排列、形状上不同像素间不可避免地会产生几何对准误差，为保证器件的成像质量必须在粘接前通过仪器进行仔细的校对，然后才能粘接。光敏胶接触光线特别是紫外线后即发生反应，快速形成粘接，不利于光锥与CCD的校对。
发明内容
本发明的目的在于，解决现有光敏胶粘接光锥与CCD固化速度过快，不利于校对的问题。提供一种固化速度不快易于光锥与CCD的校对，粘接后成像质量高的光锥与CCD耦合粘接用胶。
本发明公开了一种光锥与CCD耦合粘接用胶，其特征在于这种胶粘剂由两种不同分子量分布的聚异丁烯、增粘树脂、增塑剂、抗老剂混合制备而成，上述各组分的重量份比如下：
Figure BSA00000445247300011
所述两种不同分子量的聚异丁烯，其数均分子量分别为1000～2000及2000～3500。增粘树脂可选用松香及其衍生物、萜烯类树脂、石油树脂中的一种或几种的混合物，优选与聚异丁烯相溶性好、色泽较浅的石油树脂。增塑剂可选用癸二酸酯类、苯二甲酸酯类、脂肪酸酯类、磷酸酯类、聚酯类中的一种或几种的混合物，优选与聚异丁烯相溶性好、色泽较浅的癸二酸酯类，如癸二酸二异辛酯。抗老剂可选用酚类、胺类、亚磷酸酯类中的一种或几种的混合物，优选与聚异丁烯相溶性好、色泽较浅的酚类，如2，6-二叔丁基对甲酚。
本发明光锥与CCD耦合粘接用胶制备方法如下：
1、按配比将两种不同分子量的聚异丁烯、增粘树脂、增塑剂加入溶解釜中，并于50℃～80℃下分散混合均匀；
2、溶解釜内温度降至室温度后，高速搅拌下加入抗老剂，并分散混合均匀；
3、过滤、出料、分装、备用；
具体实施方式
下面结合具休实施事例，进一步阐述本发明。
实施例1
配方(份数比)：
6130聚异丁烯    40    癸二酸二异辛酯         20份
6240聚异丁烯    15    2，6-二叔丁基对甲酚    0.5份
碳五石油树脂    0
制备时按配比将6130聚异丁烯、6240聚异丁烯、碳五石油树脂、癸二酸二异辛酯加入溶解釜中，并于50℃～80℃下分散混合均匀。溶解釜内温度降至室温度后，高速搅拌下加入2，6-二叔丁基对甲酚，并分散混合均匀，过滤、出料、分装、备用。
以此胶粘剂将1/2″光锥与F-20CW黑白CCD耦合粘接在一起。经高温60℃2小时，低温-45℃2小时各三次循环试验、振动试验，胶层无变化，光透过率损失＜3％。
实施例2
配方(份数比)：
6130聚异丁烯    20        癸二酸二异辛酯         30份
6230聚异丁烯    30        2，6-二叔丁基对甲酚    0.5份
碳五石油树脂    0
制备时按配比将6130聚异丁烯、6230聚异丁烯、碳五石油树脂、癸二酸二异辛酯加入溶解釜中，并于50℃～80℃下分散混合均匀。溶解釜内温度降至室温度后，高速搅拌下加入2，6-二叔丁基对甲酚，并分散混合均匀，过滤、出料、分装、备用。
以此胶粘剂将1/2″光锥与F-20CW黑白CCD耦合粘接在一起。经高温60℃2小时，低温-45℃2小时各三次循环试验、振动试验，胶层无变化，光透过率损失＜3％。
实施例3
配方(份数比)：
6130聚异丁烯    40        癸二酸二异辛酯         20份
6240聚异丁烯    10        2，6-二叔丁基对甲酚    0.5份
碳五石油树脂    20
制备时按配比将6130聚异丁烯、6240聚异丁烯、碳五石油树脂、癸二酸二异辛酯加入溶解釜中，并于50℃～80℃下分散混合均匀。溶解釜内温度降至室温度后，高速搅拌下加入2，6-二叔丁基对甲酚，并分散混合均匀，过滤、出料、分装、备用。
以此胶粘剂将1/2″光锥与F-20CW黑白CCD耦合粘接在一起。经高温60℃2小时，低温-45℃2小时各三次循环试验、振动试验，胶层无变化，光透过率损失＜4％。

Claims (2)

1.一种光锥与CCD耦合粘接用胶，其特征在于这种胶粘剂由两种不同分子量的聚异丁烯、碳五石油树脂、癸二酸二异辛酯、2，6—二叔丁基对甲酚混合制备而成，上述各组分的重量份比如下：
数均分子量为1000～2000的聚异丁烯              20～40份
数均分子量为2000～3500的聚异丁烯              15～30份
碳五石油树脂                                              0～25份
癸二酸二异辛酯                                           10～30份
2，6—二叔丁基对甲酚                                     0.5～1份。
2.一种制备如权利要求1所述的光锥与CCD耦合粘接用胶方法，其特征在于具体步骤如下：
步骤1、按配比将两种不同分子量分布的聚异丁烯、碳五石油树脂、癸二酸二异辛酯剂加入溶解釜中，并于50℃～80℃下分散混合均匀；
步骤2、溶解釜内温度降至室温度后，高速搅拌下加入2，6—二叔丁基对甲酚，并分散混合均匀； 
步骤3、过滤、出料、分装、备用。
                                                 
CN201110053666A 2011-03-07 2011-03-07 一种光锥与ccd耦合粘接用胶及其制备方法 Expired - Fee Related CN102167959B (zh)