CN102167922A - 一种金属防腐水溶性涂料添加剂及其使用方法 - Google Patents

一种金属防腐水溶性涂料添加剂及其使用方法 Download PDF

Info

Publication number
CN102167922A
CN102167922A CN 201110006579 CN201110006579A CN102167922A CN 102167922 A CN102167922 A CN 102167922A CN 201110006579 CN201110006579 CN 201110006579 CN 201110006579 A CN201110006579 A CN 201110006579A CN 102167922 A CN102167922 A CN 102167922A
Authority
CN
China
Prior art keywords
water
phytate
coating
soluble
phytic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110006579
Other languages
English (en)
Other versions
CN102167922B (zh
Inventor
管从胜
马希骋
刘士明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong University
Original Assignee
Shandong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong University filed Critical Shandong University
Priority to CN 201110006579 priority Critical patent/CN102167922B/zh
Publication of CN102167922A publication Critical patent/CN102167922A/zh
Application granted granted Critical
Publication of CN102167922B publication Critical patent/CN102167922B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于金属防腐领域，涉及一种金属防腐水溶性涂料添加剂及其使用方法。该添加剂是由植酸、植酸盐、促进剂和pH调节剂组成的水溶液，各组分的含量为：植酸300～500g/dm3，植酸盐50～300g/dm3，促进剂20～50g/dm3；植酸盐为植酸锌、植酸铝、植酸钠中的两种或三种，促进剂味钨酸盐、钼酸盐中的一种或两种。该添加剂的使用方法为：用氢氧化钠或乙醇胺调整溶液的pH为3.0～10.0，添加量为10～20g/dm3，与水溶性丙烯酸树脂涂料、水溶性环氧树脂涂料和水溶性聚氨酯树脂涂料配合用于钢铁、铝及合金、锌及合金等的防腐处理。

Description

一种金属防腐水溶性涂料添加剂及其使用方法
技术领域
本发明属于金属防腐领域，特别是涉及一种金属防腐水溶性涂料添加剂及其使用方法。
背景技术
水性涂料是指以水为溶剂或者作分散介质的涂料，分为水溶性涂料、水稀释性涂料、水分散性涂料(乳胶涂料)3种。水性涂料具有污染小和施工方便等优点广泛应用于建筑结构和木制品防护与防腐处理，但是水性涂料存在耐水性和防腐性能差等缺点，达不到同类树脂的溶剂型涂料的性能，在金属防腐中受到一定限制，如何提高水性涂料的防腐性和耐水性能是涂料及涂装行业的研究热点。植酸为淡黄色或红褐色透明糖浆状液体，易溶于水、丙二醇、甘油等，难溶于醚、苯、氯仿，受强热可水解为肌醇和磷脂。与乙二胺四乙酸相比，植酸的络合能力更强和应用范围更广。植酸分子中有12个活泼氢而呈强酸性，与基体金属反应可在金属表面形成化学转化膜，该化学转化膜既有良好的防腐抑制作用，又改进了基体与涂层之间的结合强度。申请号为200910187640.7和20091087641.7的中国专利将植酸用于涂装前处理，代替传统磷化工艺，这两个专利都是将植酸金属表面处理和涂料的涂覆分步进行，不足之处是无法将植酸金属表面处理和涂料的涂覆合为一步完成。
发明内容
本发明目的在于克服上述现有技术的不足，提供一种金属防腐水溶性涂料添加剂及其使用方法。
本发明是通过以下方式实现的：
一种金属防腐水溶性涂料添加剂，其特征是：该添加剂是由植酸、植酸盐、促进剂和pH调节剂组成的水溶液，各组分的含量为：植酸300～500g/dm3，植酸盐50～300g/dm3，促进剂20～50g/dm3；植酸盐为植酸锌、植酸铝和植酸钠中的两种或三种；促进剂为钨酸盐和钼酸盐中的一种或两种。
上述添加剂的使用方法：用氢氧化钠或乙醇胺调整pH为3.0～10.0，添加量为添加量为10～20g/dm3，与水溶性涂料混合均匀即可；与水溶性丙烯酸涂料、水溶性环氧树脂涂料和水溶性聚氨酯树脂涂料配合用于钢铁、铝及合金、锌及合金等的防腐处理。涂料的涂装工艺流程如下：
工件→除油→水洗→除锈→水洗→涂料涂覆→烘干→固化(根据涂料性质而定)→产品。
该添加剂的优点体现在：
1)可以替代传统的磷化处理，将金属基体表面表面处理和涂料涂覆两个过程合并，简化工艺和提高效率
2)对于无油和轻锈工件可进→步省去除油和除锈工序；
3)植酸盐化学转化膜和有机涂层有机地结合为一体，提高涂层的性能，特别是附着力和耐蚀性。
具体实施方式
下面给出本发明的三个最佳实施例：
实施例1
一种铝合金防腐水溶性丙烯酸树脂涂料添加剂，其组成为：植酸350g/dm3，植酸锌150g/dm3，植酸铝50g/dm3，钼酸钠30g/dm3；用氢氧化钠调节pH为4.0，添加量为20g/dm3；在搅拌条件下，将该添加剂加入水性丙烯酸树脂涂料中，搅拌均匀得到铝合金防腐水性丙烯酸树脂涂料，涂料的涂装工艺流程如下：
工件→除油→水洗→除锈→水洗→涂料涂覆→烘干→固化(根据涂料性质而定)→产品。
实施例2
一种钢铁防腐水溶性环氧树脂涂料添加剂，其组成为：植酸400g/dm3，植酸锌80g/dm3，植酸钠60g/dm3，钨酸钠40g/dm3；用氢氧化钠调节pH为6.0，添加量为15g/dm3；在搅拌条件下，将该添加剂加入水性环氧树脂涂料中，搅拌均匀得到钢铁防腐水性环氧树脂涂料，涂料的涂装工艺流程同实施例1。
实施例3
一种镀锌钢板防腐水溶性聚氨酯树脂涂料添加剂，其组成为：植酸300g/dm3，植酸锌150g/dm3，钨酸钠20g/dm3，钼酸钠20g/dm3；用乙醇胺调节pH为8.0，添加量为10g/dm3；在搅拌条件下，将该添加剂加入水性聚氨酯树脂涂料中，搅拌均匀得到镀锌钢板防腐水性聚氨酯树脂涂料，涂料的涂装工艺流程同实施例1。

Claims (3)

1.一种金属防腐水溶性涂料添加剂，其特征是它是由植酸、植酸盐、促进剂和pH调节剂组成的水溶液，各组分的体积含量为：植酸300～500g/dm3，植酸盐50～300g/dm3，促进剂20～50g/dm3。
2.根据权利要求1所述的一种水溶性金属防腐涂料添加剂，其特征是植酸盐为植酸锌、植酸铝、植酸钠中的两种或三种；促进剂是钨酸盐、钼酸盐中的一种或两种。
3.根据权利要求1所述的一种金属防腐水溶性涂料添加剂的使用方法，其特征是：用氢氧化钠或乙醇胺调整pH为3.0～10.0，添加量为10～20g/dm3，与水溶性丙烯酸树脂涂料、水溶性环氧树脂和水溶性聚氨酯树脂涂料配合用于钢铁、铝及合金、锌及合金的防腐处理。 
CN 201110006579 2011-01-13 2011-01-13 一种金属防腐水溶性涂料添加剂及其使用方法 Expired - Fee Related CN102167922B (zh)