CN102167559B - Quick-setting cement mortar and preparation method thereof - Google Patents
Quick-setting cement mortar and preparation method thereof Download PDFInfo
- Publication number
- CN102167559B CN102167559B CN 201110030886 CN201110030886A CN102167559B CN 102167559 B CN102167559 B CN 102167559B CN 201110030886 CN201110030886 CN 201110030886 CN 201110030886 A CN201110030886 A CN 201110030886A CN 102167559 B CN102167559 B CN 102167559B
- Authority
- CN
- China
- Prior art keywords
- cement mortar
- parts
- emulsion
- rapid hardening
- hardening cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to quick-setting cement mortar and a preparation method thereof. The quick-setting cement mortar is concretely prepared from materials such as sulphate aluminium cement, styrene butadiene rubber emulsion, polyurethane emulsion, a water reducer, trolamine, droxyethylcellulose, fibre, river sand, water and the like according to a certain weight ratio. The quick-setting cement mortar has the characteristics of quickness in setting at normal temperature, high strength in the early stage, crack resistance, good durability and the like, can be widely applied to the fields such as embankment reinforcement, channel impermeability, soil and water conservation, side slope protection, quick repair of concrete road surfaces, and the like.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of construction work with rapid hardening cement mortar and preparation method thereof.
Background technology
The aluminosulfate cement mortar has outstanding does powerful feature early soon, and has performances such as volume microdilatancy, anticorrosive and low basicity, is normally used for making anticorrosion impervious material, fast repairing material etc.But, the anticorrosion impervious and patching material of only making with the aluminosulfate cement mortar, its later strength porosity lower, that be prone to shrinkage cracking, hydration and hardening slurry causes the resistance to corrosion can not engineering demands more greatly.In sand-cement slurry, add a small amount of organic high molecular polymer and fiber; Can effectively reduce the hole in the sand-cement slurry; Make sand-cement slurry obtain highly dense solidity; Be unlikely to make the fragility of sand-cement slurry to strengthen again, obtain dried, high-strength, impervious, corrosion resistant soon cement mortar material, thus the use field of having widened sand-cement slurry.
It is the polyacrylate modified cement of stablizer with the Z 150PH that US5753036 discloses a kind of, is that 5000~45000 Z 150PH, polyacrylic ester, cement and filler constitute by molecular-weight average.CN1730908 discloses a kind of method for reinforcing and protecting to inner surface of tunnel; Improve the surface strength of inner surface of tunnel through in cement waterproofing mortar, adding ROHM emulsion and polypropylene fibre, solved crack, infiltration and the high temperature explosion problem of inner surface of tunnel.CN1483692 discloses a kind of cement concrete mixture that adds polyacrylonitrile fibre.CN1415572 discloses a kind of polymer modification mortar patching material, is made up of Portland cement or short-term strength cement, styrene-butadiene rubber(SBR), yellow soda ash, trolamine.Polymkeric substance to the sand-cement slurry modification is mainly polyacrylate emulsion, EVA emulsion or styrene-butadiene emulsion at present.Polymer emulsion can effectively improve the impervious and anti-shrinkage cracking performance of sand-cement slurry; But in the process of preparation polymer cement mortar; Because of polymkeric substance and the cement consistency is relatively poor and reason such as polymkeric substance breakdown of emulsion; Cause prolong and the intensity reduction time of coagulation of sand-cement slurry, thereby influenced the net effect of sand-cement slurry.
Summary of the invention
The objective of the invention is to solve the problem of the rate of set that exists in the present use polymer modification rapid hardening cement mortar, a kind of rapid hardening cement mortar and preparation method thereof is provided.
The rapid hardening cement mortar that the present invention proposes is the liquid form mixt that is formed according to a certain weight ratio by materials such as aluminosulfate cement, SBR emulsion, polyaminoester emulsion, water reducer, trolamine, Natvosol, fiber, river sand, water.Comprising of raw material:
100 parts of aluminosulfate cements
2~10 parts of SBR emulsions
2~10 parts of polyaminoester emulsions
0.5~2 part of water reducer
0.5~2 part of trolamine
0.2~1 part of Natvosol
1~5 part of fiber
50~150 parts of river sands
150~250 parts in water
Described SBR emulsion, the solid content of said SBR emulsion are 20~40%.
Described polyaminoester emulsion, said polyaminoester emulsion are the cation type polyurethane emulsion, and its solid content is 30~60%.Second-order transition temperature is-30 ℃~-10 ℃.
Said water reducer is a kind of in poly carboxylic acid, the naphthalene sulfonic salt or their mixture.
Described fiber, said fiber are a kind of in polypropylene fibre or the thomel or their mixture.
Described polymer cement waterproof preparation methods is characterized in that comprising the steps:
(1) takes by weighing the material of following deal: 100 parts aluminosulfate cement, 0.5~2 part water reducer, 1~5 part fiber and 50~150 parts river sand, thorough mixing;
(2) take by weighing the material of following deal: 2~10 parts SBR emulsion, 2~10 parts polyaminoester emulsion, 0.5~2 part trolamine, 0.2~1 part Natvosol, 150~250 parts water, thorough mixing;
(3) material in the step (1) adds the material in the step (2) gradually under whipped state, and churning time is 1~6 minute, forms the rapid hardening cement mortar.
Confirming of the selected and proportioning content of the present invention through above composition promptly improves the elasticity of sand-cement slurry through adding SBR emulsion, adds the consistency that polyaminoester emulsion improves itself and cement; Add the rate of set of trolamine raising cement; Add the stability of Natvosol raising polymer cement mortar, cooperatively interact acting in conjunction between each composition; And the effective checking through embodiment, efficiently solve the problem of the rate of set that exists in the present sand-cement slurry.
The practical implementation method
Following examples are intended to explain the present invention rather than to further qualification of the present invention.
Embodiment 1.
The proportioning of this routine polymer cement waterproof paint is:
100 parts of aluminosulfate cements
2 parts of SBR emulsions
5 parts of polyaminoester emulsions
0.5 part of water reducer
0.5 part of trolamine
0.2 part of Natvosol
1 part of fiber
80 parts of river sands
200 parts in water
Concrete preparation method comprises the steps:
(1) takes by weighing the material of following deal: 100 parts aluminosulfate cement, 0.5 part water reducer, 1 part fiber and 80 parts river sand, thorough mixing;
(2) take by weighing the material of following deal: 2 parts SBR emulsion, 5 parts polyaminoester emulsion, 0.5 part trolamine, 0.2 part Natvosol, 200 parts water, thorough mixing;
(3) material in the step (1) adds the material in the step (2) gradually under whipped state, and churning time is 6 minutes, forms the rapid hardening cement mortar.
Employed aluminosulfate cement is 42.5 quick hardening sulphoaluminate cements that Tangshan six or nine cement ltds produce; Employed SBR emulsion is the PR 215 type SBR emulsions of Shanghai and assistant officer Industrial Co., Ltd.; Employed polyaminoester emulsion closes the PUA-102 type cation aqueous polyurethane of sincere polyurethane production for Taizhou Huangyan.
The technical target of the product that present embodiment obtains:
Embodiment 2
The proportioning of this routine polymer cement waterproof paint is:
100 parts of aluminosulfate cements
5 parts of SBR emulsions
5 parts of polyaminoester emulsions
1 part of water reducer
0.5 part of trolamine
0.2 part of Natvosol
1 part of fiber
80 parts of river sands
200 parts in water
Concrete preparation method comprises the steps:
(1) takes by weighing the material of following deal: 100 parts aluminosulfate cement, 1 part water reducer, 1 part fiber and 80 parts river sand, thorough mixing;
(2) take by weighing the material of following deal: 5 parts SBR emulsion, 5 parts polyaminoester emulsion, 0.5 part trolamine, 0.2 part Natvosol, 200 parts water, thorough mixing;
(3) material in the step (1) adds the material in the step (2) gradually under whipped state, and churning time is 6 minutes, forms the rapid hardening cement mortar.
Employed aluminosulfate cement is 42.5 quick hardening sulphoaluminate cements that Tangshan six or nine cement ltds produce; The PR 215 type SBR emulsions of big Shanghai of employed SBR emulsion and assistant officer Industrial Co., Ltd.; Employed polyaminoester emulsion closes the PUA-102 type cation aqueous polyurethane of sincere polyurethane production for Taizhou Huangyan.
The technical target of the product that present embodiment obtains:
Claims (6)
2. a kind of rapid hardening cement mortar according to claim 1, the solid content that it is characterized in that said SBR emulsion is 20~40%.
3. a kind of rapid hardening cement mortar according to claim 1 is characterized in that said polyaminoester emulsion is the cation type polyurethane emulsion, and its solid content is 30~60%.
4. a kind of rapid hardening cement mortar according to claim 1 is characterized in that said water reducer is a kind of in poly carboxylic acid, the naphthalene sulfonic salt or their mixture.
5. a kind of rapid hardening cement mortar according to claim 1 is characterized in that said fiber is a kind of in polypropylene fibre or the thomel or their mixture.
6. the preparation method of each described rapid hardening cement mortar of claim 1-5 is characterized in that comprising the steps:
(1) takes by weighing the material of following deal: 100 parts aluminosulfate cement, 0.5~2 part water reducer, 1~5 part fiber and 50~150 parts river sand, thorough mixing;
(2) take by weighing the material of following deal: 2~10 parts SBR emulsion, 2~10 parts polyaminoester emulsion, 0.5~2 part trolamine, 0.2~1 part Natvosol, 150~250 parts water, thorough mixing;
(3) material in the step (1) adds the material in the step (2) gradually under whipped state, and churning time is 1~6 minute, forms the rapid hardening cement mortar.