CN102162064A - 一种铁铬铝合金及其钢卷 - Google Patents
一种铁铬铝合金及其钢卷 Download PDFInfo
- Publication number
- CN102162064A CN102162064A CN2011101203160A CN201110120316A CN102162064A CN 102162064 A CN102162064 A CN 102162064A CN 2011101203160 A CN2011101203160 A CN 2011101203160A CN 201110120316 A CN201110120316 A CN 201110120316A CN 102162064 A CN102162064 A CN 102162064A
- Authority
- CN
- China
- Prior art keywords
- strip
- coil
- chromium
- iron
- strip coil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种铁铬铝合金及其钢卷，铁铬铝合金与钢卷的成分的质量百分比均为：C≤0.015％；Si≤1.0％； Mn≤1.0％；Al 5.0％-6.0％；Cr 19.0％-21.0％；La 0.06％-0.12％；Ti 0.10-0.30％；Y 0.05％-0.07％；Zr 0.15％-0.25％；Co 0.10％-0.30％；其余含量主要为Fe，P、S以及其它不可避免的杂质元素含量总和低于0.1％。钢卷的厚度为0.20mm-0.15mm，宽度为300-600mm。本铁铬铝合金及其钢卷的耐高温性能较好，最高使用温度提高到1350℃，并延长其产品在1350℃下的使用寿命。
Description
技术领域
本发明涉及一种铁铬铝合金及其钢卷。
背景技术
铁铬铝合金即FeCrAl是铁素体组织的电热合金，主要牌号有：
0Cr13Al4、0Cr21Al5、0Cr25Al5和0Cr27Al7Mo2等钢种，其产品应用领域遍及国民经济和日常生活的各个方面。该材料是通过焦耳热的方式实现电能一热能的转换，达到对某一区域(如炉膛)或某些物品(如食品)加热的目的，现有的铁铬铝合金轧制的钢卷一般使用温度在1300℃以下，使用温度高于1300℃就发生脆断等。
发明内容
为了克服现有铁铬铝合金及其钢卷的上述不足，本发明提供一种使用温度高达1350℃的铁铬铝合金，并提供一种使用温度高达1350℃的铁铬铝合金钢卷。
现有的铁铬铝合金成分的质量百分比为：
C≤0.015％； Si≤1.0％； Mn≤1.0％； Al 5.0％-6.0％；Cr 19.0％-21.0％； La 0.06％-0.12％；
其余含量主要为Fe，P、S以及其它不可避免的杂质元素含量总和低于0.1％。
以上述成分轧制的厚度0.2mm产品，在1350℃-1400℃，使用寿命不超过20小时。
为了提高产品的高温使用寿命，本发明在现有铁铬铝合金成分的基础上，添加了Ti、Y、Zr与Co元素，本FeCrAl合金成分的质量百分比为：
C≤0.015％； Si≤1.0％； Mn≤1.0％； Al 5.0％-6.0％；Cr 19.0％-21.0％； La 0.06％-0.12％； Ti 0.10-0.30％； Y 0.05％-0.07％；Zr 0.15％-0.25％； Co 0.10％-0.30％；
其余含量主要为Fe，P、S以及其它不可避免的杂质元素含量总和低于0.1％。
本FeCrAl钢卷的成分的质量百分比为：
C≤0.015％； Si≤1.0％； Mn≤1.0％； Al 5.0％-6.0％；Cr 19.0％-21.0％； La 0.06％-0.12％； Ti 0.10-0.30％； Y 0.05％-0.07％；Zr 0.15％-0.25％； Co 0.10％-0.30％；
其余含量主要为Fe，P、S以及其它不可避免的杂质元素含量总和低于0.1％。
厚度为0.15mm-0.20mm。
以本发明的FeCrAl合金轧制的钢卷产品(厚度≤0.2mm)，在1350℃-1400℃使用寿命超过40小时，可达60小时。显著提高产品高温性能，满足了电阻带产品在1350-1400℃长时间使用需要。
具体实施方式
下面结合实施例对本铁铬铝合金及其钢卷的具体实施方式进行详细说明，但本发明的具体实施方式不局限于下述的实施例。
合金实施例一
铁铬铝合金成分的质量百分比为：
C 0.008％； Si 0.21％； Mn 0.10％； Al 5.2％； Cr 19.8％；La 0.07％； Ti 0.11％； Y 0.054％； Zr 0.17％； Co 0.11％；P 0.021％； S 0.001％ 其余为Fe及其它不可避免的杂质，其它不可避免的杂质元素低于0.078。
钢卷实施例一
铁铬铝合金钢卷的成分的质量百分比为：
C 0.008％； Si 0.21％； Mn 0.10％； Al 5.2％； Cr 19.8％；La 0.07％； Ti 0.11％； Y 0.054％； Zr 0.17％； Co 0.11％；P 0.021％； S 0.001％； 其余为Fe及其它不可避免的杂质，其它不可避免的杂质元素低于0.078。
钢卷的规格为0.2(厚度)×350(宽度)mm钢卷，本实施例的钢卷在1380℃下使用寿命达到52小时。
合金实施例二
铁铬铝合金成分的质量百分比为：
C 0.009％； Si 0.17％； Mn 0.12％； Al 5.8％； Cr 20.2％； La 0.07％；Ti 0.13％； Y 0.058％； Zr 0.17％； Co 0.13％； P 0.018％； S 0.001％；其余为Fe及其它不可避免的杂质，其它不可避免的杂质元素低于0.081。
钢卷实施例二
铁铬铝合金钢卷的成分的质量百分比为：
C 0.009％； Si 0.17％； Mn 0.12％； Al 5.8％； Cr 20.2％； La 0.07％；Ti 0.13％； Y 0.058％； Zr 0.17％； Co 0.13％； P 0.018％； S 0.001％；其余为Fe及其它不可避免的杂质，其它不可避免的杂质元素低于0.078。
钢卷的规格为0.18(厚度)×350(宽度)mm，本实施例的钢卷在1380℃下使用寿命达到48小时。
Claims (2)
1.一种铁铬铝合金，它的成分的质量百分比为：
C≤0.015％； Si≤1.0％； Mn≤1.0％； Al 5.0％-6.0％；Cr 19.0％-21.0％； La 0.06％-0.12％； Ti 0.10-0.30％； Y 0.05％-0.07％；Zr 0.15％-0.25％； Co 0.10％-0.30％；其余含量主要为Fe，P、S以及其它不可避免的杂质元素含量总和低于0.1％。
2.一种铁铬铝合金钢卷，它的成分的质量百分比为：
C≤0.015％； Si≤1.0％； Mn≤1.0％； Al 5.0％-6.0％；Cr 19.0％-21.0％； La 0.06％-0.12％； Ti 0.10-0.30％； Y 0.05％-0.07％；Zr 0.15％-0.25％； Co 0.10％-0.30％；
其余含量主要为Fe，P、S以及其它不可避免的杂质元素含量总和低于0.1％；
厚度为0.20mm-0.15mm，宽度为300-600mm。