CN101619424A - 一种奥氏体不锈钢 - Google Patents
一种奥氏体不锈钢 Download PDFInfo
- Publication number
- CN101619424A CN101619424A CN200810022607A CN200810022607A CN101619424A CN 101619424 A CN101619424 A CN 101619424A CN 200810022607 A CN200810022607 A CN 200810022607A CN 200810022607 A CN200810022607 A CN 200810022607A CN 101619424 A CN101619424 A CN 101619424A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- austenitic stainless
- percent
- nickel
- manganese
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种奥氏体不锈钢,尤其是一种离锰适量铜低镍奥氏体不锈钢,它的组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.50-4.00%铜、余为铁。本发明的优点:1)在室温下表现出良好的力学性能和良好的冷轧加工成形性能;2)以提高锰、适量铜含量来节约因资源贫乏而致价格昂贵的镍,从而使奥氏体不锈钢的价得以降低。
Description
技术领域
本发明涉及一种奥氏体不锈钢,尤其是一种离锰低镍奥氏体不锈钢。
背景技术
目前,国内、外不锈钢管及厨房用具、餐具等,仍大都使用300系和200系不锈钢制作,譬如不锈钢304和不锈钢201,这些牌号的不锈钢含有较高的铬和镍。304牌号的不锈钢的铬、镍含量分别为17.54%和8.86%;201牌号的不锈钢的铬、镍含量分别为16.91%和4.7%。然而,由于铬、镍资源在我国比较匮乏,因而导致前述不锈钢价格居高。因此,对于奥氏体不锈钢,尤其对于前述用途的奥氏体不锈钢,将其镍、铬成份,尤为镍成份进行合理降低,而对锰、铜的成份作适当提高,加上对其它成份的合理组配,不仅可以节约宝贵的镍资源、降低成本,而且还可以大大改善冷轧加工成形性能。
当然,高锰低镍奥氏体不锈钢领域中,出于用途的不同,各有不同的成份设计。譬如以公告号CN1128246C公布的“一种奥氏体不锈钢”,它含有≤2.0%Mo和0.2-1.5%AL、还加入0.02-0.05%的Re元素。不但要提高成本,而且因为Mo、AL均为铁素体形成元素,会给获得单一的奥氏体组织带来不利影响。
发明内容
本发明的目的是要提供一种可大大改善冷轧加工成形性能的奥氏体不锈钢。
本发明的目的是这样来达到的,一种奥氏体不锈钢,其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.50-4.00%铜、余为铁。
本发明所述的一种奥氏体不锈钢,其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.91%铜、余为铁。
本发明所述的一种奥氏体不锈钢,其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.85%铜、余为铁。
本发明所述的一种奥氏体不锈钢,其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.83%铜、余为铁。
本发明奥氏体不锈钢具有以下优点:1)在室温下表现出良好的力学性能和良好的冷轧加工成形性能;2)以提高锰、适量铜含量来节约因资源贫乏而致价格昂贵的镍,从而使奥氏体不锈钢的价得以降低。
具体实施方式
申请人叙述确定上述主要化学成份范围的理由如下:
1、碳:碳在奥氏体不锈钢中是强烈形成并稳定奥氏体且扩大奥氏体区的元素,因此碳对形成奥氏体组织起着重要作用。所以碳要有一定的百分比含量。但碳高时,不但影响冷加工时的塑性,而且对钢的耐腐蚀性能也有不利影响。
2、硅:硅是强烈形成铁素体的元素,因此为保证本发明不锈钢获得奥氏体组织,硅含量必须加以限制。
3、锰:锰是比较弱的奥氏体形成元素,但具有强烈的稳定奥氏体组织的作用,并提高氮在钢中的溶解度。在节镍奥氏体不锈钢中,锰是非常重要的合金元素之一,常与镍、氮等元素复合加入钢中,以节约镍或取代镍。本发明奥氏体不锈钢中锰含量范围是为获得奥氏体组织而设计的。
4、铬:铬是不锈钢中最主要的元素,是钢获得不锈性、耐腐蚀性的重要元素。本发明奥氏体不锈钢的铬含量范围,既保证钢有良好的不锈耐蚀性,又保证获得奥氏体组织。
5、镍:镍是强烈形成并稳定奥氏体且扩大奥氏体区的元素。本发明的目的是以锰、氮代替镍。因此本发明奥氏体不锈钢镍含量较低,但为了提高钢的冷、热加工性能,仍加入了≤1.20%镍。
6、氮:氮是非常强烈形成并稳定奥氏定且扩大奥氏体区的元素,氮在奥氏体不锈钢中可代替部分镍。氮属固溶强化元素,可提高奥氏体不锈钢的强度并不显著损害钢的塑性和韧性。但当氮含量超过0.20%(重量)时,对钢的生产加工工艺及冷成形性有不利影响。本发明氮含量控制在≤0.20(重量)。氮加入可延缓碳化物的析出,从而使其耐晶间腐蚀性能得到改善。
7、磷:磷视为有害元素,应尽量控制在0.05%(重量)以下。
8、硫:硫视为有害元素,应尽量控制在0.03%(重量)以下。
9、铜:铜作为合金元素,将其追加在本发明钢中,主要起降低冷作硬化倾向,进而提高冷加工成形性能。铜的含量应尽量控制在3.50-4.00%(重量)。
实施例:
本发明奥氏体不锈钢可用非真空感应炉、电弧炉冶炼。锭坯的热加工(锻造、热轧)温度范围1115-1180℃,固溶热处理温度1050℃-1120℃。
本发明奥氏体不锈钢主要生产热轧带材、冷轧带材、热轧板材和棒材等。
本发明奥氏体不锈钢的三个实施例归纳于表一,并且在该表中还给出了本发明奥氏体不锈钢的试样和对比钢的化学成份对比,其中:对比钢A为304、B为201。
表一(重量百分比)
本发明的上述三个实施例获得的奥氏体不锈钢所表现出的优异的力学性能由表二示出,明显优于对比钢,其中:对比钢A为304、B为201。
表二
Claims (4)
1、根据权利要求1所述的一种奥氏体不锈钢,其特征在于其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.50-4.00%铜、余为铁。
2、根据权利要求1所述的一种奥氏体不锈钢,其特征在于其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.91%铜、余为铁。
3、根据权利要求1所述的一种奥氏体不锈钢,其特征在于其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.85%铜、余为铁。
4、根据权利要求1所述的一种奥氏体不锈钢,其特征在于其组成为(按重量)≤0.10%碳、≤0.80%硅、8.50-10.00%锰、14.00-15.00%铬、≤1.20%镍、≤0.050%磷、≤0.030%硫、≤0.20%氮、3.83%铜、余为铁。