CN102133530A - 一种香烟过滤嘴用纳米催化剂的制备方法 - Google Patents

一种香烟过滤嘴用纳米催化剂的制备方法 Download PDF

Info

Publication number
CN102133530A
CN102133530A CN201010602751.2A CN201010602751A CN102133530A CN 102133530 A CN102133530 A CN 102133530A CN 201010602751 A CN201010602751 A CN 201010602751A CN 102133530 A CN102133530 A CN 102133530A
Authority
CN
China
Prior art keywords
mixture
cigarettes
catalyst
aqueous solution
nanocatalyst
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201010602751.2A
Other languages
English (en)
Other versions
CN102133530B (zh
Inventor
郭凌华
刘保健
姚宝晶
宋蕊
卜宇
王峥
杨琳琳
焦旭英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi University of Science and Technology
Original Assignee
Shaanxi University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi University of Science and Technology filed Critical Shaanxi University of Science and Technology
Priority to CN2010106027512A priority Critical patent/CN102133530B/zh
Publication of CN102133530A publication Critical patent/CN102133530A/zh
Application granted granted Critical
Publication of CN102133530B publication Critical patent/CN102133530B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种香烟过滤嘴用纳米催化剂的制备方法，本发明旨在降低在吸食香烟过程中的有害物质的比例，首先将纳米二氧化钛、铁与铜、钴或锌混合，然后将混合物加入水中得混合物水溶液，再向混合物水溶液中加入表面活性剂和聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。将制的催化剂均匀的喷洒在过滤嘴的纤维中，该催化剂可以在很短的时间将有害分解为无害的物质，将其的比例降低65-85％。可以有效的降低香烟对人体健康带来的危害。

Description

一种香烟过滤嘴用纳米催化剂的制备方法
技术领域
本发明涉及用于香烟过滤嘴的纳米材料，具体涉及一种可以短时间内分解吸食香烟分解出有害物质的香烟过滤嘴用纳米催化剂的制备方法。
背景技术
吸烟是危害人体健康的一种习惯，为了降低其对人体带来的危害商家采取了许多手段，例如添加过滤嘴等。但是都不能从根本上解决问题。研究证明吸烟分解出的有害物质能够引起肺癌等致命的疾病。每年我国由于吸烟导致的损失高达千亿元以上。
发明内容
本发明的目的在于解决上述现有领域内的存在的问题，提供了一种成本低廉、制备简便的香烟过滤嘴用纳米催化剂的制备方法。
为达到上述目的，本发明采用的技术方案是：按纳米二氧化钛∶铁∶铜、钴或锌为100∶(5-10)∶(5-10)的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂和混合物1-4倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
所述的表面活性剂为十二烷基磺酸钠，脂肪醇聚氧乙烯醚或氨基酸。
在香烟过滤嘴中添加了本发明的纳米催化剂作为降解剂，本发明的纳米催化剂能够分解有害物质，能有效地降低吸烟对人体带来的危害。这样就解决了香烟对于人体带来的危害，该催化剂可以在很短的时间将有害分解为无害的物质，将其的比例降低65-85％。
将制的催化剂涂敷在玻璃玻片的表面，然后将香烟燃烧后废气导入，经过30秒，使用气相色谱测试，产生的废气含量降低65-85％。
具体实施方式
实施例1：按纳米二氧化钛∶铁∶铜为100∶5∶5的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂十二烷基磺酸钠和混合物1倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。然后就可以将制的催化剂均匀的喷洒在过滤嘴的纤维中，就可以将65-85％的吸烟产生的有害物质降解。
实施例2：按纳米二氧化钛∶铁∶铜为100∶8∶8的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂脂肪醇聚氧乙烯醚和混合物2倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
实施例3：按纳米二氧化钛∶铁∶铜为100∶10∶10的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂氨基酸和混合物4倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
实施例4：按纳米二氧化钛∶铁∶钴为100∶6∶9的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂十二烷基磺酸钠和混合物3倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。然后就可以将质的催化剂均匀的喷洒在过滤嘴的纤维中，就可以将75-85％的吸烟产生的有害物质降解。
实施例5：按纳米二氧化钛∶铁∶钴为100∶9∶5的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂脂肪醇聚氧乙烯醚和混合物2倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
实施例6：按纳米二氧化钛∶铁∶钴为100∶7∶8的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂氨基酸和混合物1倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
实施例7：按纳米二氧化钛∶铁∶锌为100∶10∶6的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂十二烷基磺酸钠和混合物4倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。然后就可以将质的催化剂均匀的喷洒在过滤嘴的纤维中，就可以将75-85％的吸烟产生的有害物质降解。
实施例8：按纳米二氧化钛∶铁∶锌为100∶5∶7的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂脂肪醇聚氧乙烯醚和混合物3倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
实施例9：按纳米二氧化钛∶铁∶锌为100∶8∶6的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂氨基酸和混合物1倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。

Claims (2)

1.一种香烟过滤嘴用纳米催化剂的制备方法，其特征在于：首先按纳米二氧化钛∶铁∶铜、钴或锌为100∶(5-10)∶(5-10)的质量比混合得混合物，然后将混合物与水按1∶25的质量比加入水中得混合物水溶液，再向混合物水溶液中加入混合物等量的表面活性剂和混合物1-4倍质量的聚丙烯酸粘合剂，在90℃下搅拌4小时得到香烟过滤嘴用纳米催化剂。
2.根据权利要求1所述的香烟过滤嘴用纳米催化剂的制备方法，其特征在于：所述的表面活性剂为十二烷基磺酸钠，脂肪醇聚氧乙烯醚或氨基酸。
CN2010106027512A 2010-12-23 2010-12-23 一种香烟过滤嘴用纳米催化剂的制备方法 Expired - Fee Related CN102133530B (zh)