CN102127258A - 一种煤矿用聚乙烯管材专用磷系阻燃母料 - Google Patents
一种煤矿用聚乙烯管材专用磷系阻燃母料 Download PDFInfo
- Publication number
- CN102127258A CN102127258A CN2010106223448A CN201010622344A CN102127258A CN 102127258 A CN102127258 A CN 102127258A CN 2010106223448 A CN2010106223448 A CN 2010106223448A CN 201010622344 A CN201010622344 A CN 201010622344A CN 102127258 A CN102127258 A CN 102127258A
- Authority
- CN
- China
- Prior art keywords
- special
- pipe
- phosphorous
- colliery
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明为一种煤矿用聚乙烯管材专用磷系阻燃母料,其原料组分的重量配比为:红磷15-40%,机油5-20%,氧化钙0.1-10%,LLDPE30-80%。有益效果:使用本发明煤矿用聚乙烯管材专用磷系阻燃母料生产出的煤矿用聚乙烯管材,其高分散性使管材质量稳定、使阻燃性能超过国标V0标准、提高管材表面光亮度、拉伸强度>18MPa、断裂伸长率>450%等,管材具有极佳的使用性。使用机型:双螺杆挤出机。
Description
技术领域
本发明涉及塑料,具体为一种煤矿用聚乙烯管材专用磷系阻燃母料,解决矿用管材的抗阻燃性。
背景技术.
目前,现国内没有专业适用于煤矿用聚乙烯管材专用磷系阻燃母料,现生产煤矿用聚乙烯管材所使用的阻燃母料,只是溴系阻燃母料或不是专业用到聚乙烯管材的阻燃母料,其缺点是分散性差、阻燃性能差、管材表面不光滑、影响管材内部性能指标等。
发明内容
本发明的目的是为了克服现有技术存在的缺陷,提高原料组分的分散性、使阻燃性能超过国标V0标准、并能提高管材表面光亮度、拉伸强度>18Mpa、断裂伸长率>450%等,生产出高性能的矿用聚乙烯管材的一种煤矿用聚乙烯管材专用磷系阻燃母料。
本发明所采取的方案是:一种煤矿用聚乙烯管材专用磷系阻燃母料,其原料组分的重量配比为:红磷15-40%,机油5-20%,氧化钙0.1-10%,LLDPE30-80%。
具体地,其原料组分的重量配比为:红磷25%,机油12%,氧化钙5%,LLDPE68%。
所述红磷为磷含量70-100%。
所述机油为15-80号。
所述氧化钙为活性氧化钙≥93%、白度≥85%、325目筛余物≤3.0%、活性≥60℃3min。
所述LLDPE为低密度线性聚乙烯拉伸强度≥10Mpa、断裂伸长率≥600%、维卡软化点≥95℃、熔体流动速率2g/10min以上。
配方中采用红磷可以达到阻燃效果;优质机油达到好的分散性及润滑性;优质国产LLDPE做主料,在保证提高分散性、使阻燃性能超过国标V0标准、提高管材表面光亮度、拉伸强度>18Mpa、断裂伸长率>450%等情况下;工艺采用同向双螺杆挤出机加工工艺来解决易起火问题。
本发明的有益效果:使用本发明煤矿用聚乙烯管材专用磷系阻燃母料生产出的煤矿用聚乙烯管材,其高分散性使管材质量稳定、使阻燃性能超过国标V0标准、提高管材表面光亮度、拉伸强度>18Mpa、断裂伸长率>450%等,管材具有极佳的使用性。
具体实施方式
一种煤矿用聚乙烯管材专用磷系阻燃母料,其原料组分的重量配比为:红磷25%,机油12%,氧化钙5%,LLPE68%。
其中,红磷为磷含量70-100%,机油为15-80号,氧化钙为活性氧化钙≥93%、白度≥85%、325目筛余物≤3.0%、活性≥60℃3min;LLDPE为低密度线性聚乙烯拉伸强度≥10Mpa、断裂伸长率≥600%、维卡软化点≥95℃、熔体流动速率2g/10min以上。
使用机型:双螺杆挤出机。
Claims (6)
1.一种煤矿用聚乙烯管材专用磷系阻燃母料,其原料组分的重量配比为:红磷15-40%,机油5-20%,氧化钙0.1-10%,LLDPE 30-80%。
2.如权利要求1所述的一种煤矿用聚乙烯管材专用磷系阻燃母料,其特征在于:其原料组分的重量配比为:红磷25%,机油12%,氧化钙5%,LLDPE68%。
3.如权利要求1或2所述的一种煤矿用聚乙烯管材专用磷系阻燃母料,其特征在于:所述红磷为磷含量70-100%。
4.如权利要求1或2所述的一种煤矿用聚乙烯管材专用磷系阻燃母料,其特征在于所述机油为15-80号。
5.如权利要求1或2所述的一种煤矿用聚乙烯管材专用磷系阻燃母料,其特征在于所述氧化钙为活性氧化钙≥93%、白度≥85%、325目筛余物≤3.0%、活性≥60℃3min。
6.如权利要求1或2所述的一种煤矿用聚乙烯管材专用磷系阻燃母料,其特征在于所述LLDPE为低密度线性聚乙烯,拉伸强度≥10Mpa、断裂伸长率≥600%、维卡软化点≥95℃、熔体流动速率2g/10min以上。