CN102108171A - Formula of high-strength fluororubber product material - Google Patents
Formula of high-strength fluororubber product material Download PDFInfo
- Publication number
- CN102108171A CN102108171A CN 201110086462 CN201110086462A CN102108171A CN 102108171 A CN102108171 A CN 102108171A CN 201110086462 CN201110086462 CN 201110086462 CN 201110086462 A CN201110086462 A CN 201110086462A CN 102108171 A CN102108171 A CN 102108171A
- Authority
- CN
- China
- Prior art keywords
- nanometers
- viton
- formula
- calcium carbonate
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of a high-strength fluororubber product material. The formula of the high-strength fluororubber product material comprises the following components in part by mass: 100 parts of fluororubber (2603), 2.5 parts of bisphenol AF, 0.5 part of tert-butyl peroxypivalate (BPP), 3.0 parts of magnesium oxide, 6.0 parts of calcium hydroxide, 15 to 22 parts of nano calcium carbonate (less than 80 nanometers) and a proper amount of coloring agent. In the formula, the nano calcium carbonate (50 nanometers to 100 nanometers) serves as a reinforcing agent. The reinforcing performance of the nano calcium carbonate (less than 80 nanometers) is high. The fluororubber product prepared by the invention has relatively high strength which can be up to 14MPa, can take full use of the excellent performance of the fluororubber and meets the requirements on use.
Description
Technical field
The present invention relates to a kind of light viton goods sizing compound formula, the strengthening agent in particularly a kind of light viton goods sizing compound formula.
Background technology
Viton is a kind of excellent performance, the specialty elastomer that price is higher.Common rubber item is to be the rubber item of the black of strengthening agent with carbon black.In order to allow excellent performance, the higher viton goods of price are from being different from common black rubber goods in appearance significantly, and the color of viton goods is generally made the light color of non-black more.In order to make the light viton goods of non-black, in the light viton goods sizing compound formula of non-black, can not be strengthening agent with the good black carbon black of reinforcing property.In the prior art, strengthening agent in the light color viton goods sizing compound formula is the inorganic supporting material of diatomite, light calcium carbonate or other light color of light color, also has an amount of tinting material in the light color viton goods sizing compound formula, an amount of tinting material makes the light viton goods of making have certain color, as light viton goods are made blue look.Diatomite, light calcium carbonate or other inorganic supporting material are not fine to the reinforcing property of viton, is not very high with diatomite, light calcium carbonate or other inorganic supporting material as the viton product strength of strengthening agent, common intensity is no more than 9Mpa, is difficult to make the higher light viton goods of intensity.In the performance index of rubber item, intensity is most important basic property index, and intensity not higher position can not have been given play to the excellent properties of viton fully, even can not satisfy the requirement of use.
Summary of the invention
The objective of the invention is in order to overcome above-mentioned deficiency, propose a kind of high strength viton goods sizing compound formula that can make the higher light viton goods of intensity.
The present invention is achieved using the following method.
The composition of high strength viton goods sizing compound formula and each composition and mass parts are:
Viton (2603) 100,
Bisphenol AF 2.5,
BPP 0.5,
Magnesium oxide 3.0,
Calcium hydroxide 6.0,
Nano-calcium carbonate (50 nanometers ~ 100 nanometers) 15 ~ 22
Tinting material is an amount of.
The present invention is with nano-calcium carbonate 50 nanometers ~ 100 nanometers) be strengthening agent, the reinforcing property of nano-calcium carbonate (50 nanometers ~ 100 nanometers) is good, higher with the viton product strength that the present invention makes, intensity can reach 14 Mpa, the higher viton goods of intensity can have been given play to the excellent properties of viton fully, satisfy the requirement of using.
The nano-calcium carbonate calcium product that strengthening agent nano-calcium carbonate (50 nanometers ~ 100 nanometers) in the above-mentioned high strength viton goods sizing compound formula can use Jilin Tian Ze nano material company limited to produce.
In the above-mentioned high strength viton goods sizing compound formula an amount of tinting material is arranged, according to the required color of high strength viton goods, the those of ordinary skill of rubber industry can determine the kind of tinting material and the consumption of tinting material at an easy rate.
Below in conjunction with embodiment, the present invention is further described.
Embodiment
Embodiment 1
The composition of high strength viton goods sizing compound formula and each composition and mass parts are:
Viton (2603) 100,
Bisphenol AF 2.5,
BPP 0.5,
Magnesium oxide 3.0,
Calcium hydroxide 6.0,
Nano-calcium carbonate (50 nanometers ~ 100 nanometers) 18 ~ 20,
Tinting material is an amount of.
Claims (2)
1. high strength viton goods sizing compound formula is characterized in that: the composition of described high strength viton goods sizing compound formula and each composition and mass parts are:
Viton (2603) 100,
Bisphenol AF 2.5,
BPP 0.5,
Magnesium oxide 3.0,
Calcium hydroxide 6.0,
Nano-calcium carbonate (50 nanometers ~ 100 nanometers) 15 ~ 22
Tinting material is an amount of.
2. by the described high strength viton of claim 1 goods sizing compound formula, it is characterized in that: the mass parts of described nano-calcium carbonate (50 nanometers ~ 100 nanometers) is 18 ~ 20.