CN105017589A - Heat-resistant chloroprene rubber formula - Google Patents

Heat-resistant chloroprene rubber formula Download PDF

Info

Publication number
CN105017589A
CN105017589A CN201510367985.6A CN201510367985A CN105017589A CN 105017589 A CN105017589 A CN 105017589A CN 201510367985 A CN201510367985 A CN 201510367985A CN 105017589 A CN105017589 A CN 105017589A
Authority
CN
China
Prior art keywords
chloroprene rubber
parts
thermotolerance
formula
rubber formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510367985.6A
Other languages
Chinese (zh)
Inventor
袁庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHANGJIAGANG DANENG PLASTIC PRODUCT Co Ltd
Original Assignee
ZHANGJIAGANG DANENG PLASTIC PRODUCT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHANGJIAGANG DANENG PLASTIC PRODUCT Co Ltd filed Critical ZHANGJIAGANG DANENG PLASTIC PRODUCT Co Ltd
Priority to CN201510367985.6A priority Critical patent/CN105017589A/en
Publication of CN105017589A publication Critical patent/CN105017589A/en
Pending legal-status Critical Current

Abstract

The invention discloses a heat-resistant chloroprene rubber formula. The heat-resistant chloroprene rubber formula comprises 100 parts of chloroprene rubber, 30 parts of high abrasion-resistant furnace black, 50 parts of activated calcium carbonate, 10 parts of plasticizer TCP, 1 part of anti-aging agent PA, 1 part of anti-aging agent NBC, 4 parts of magnesium oxide, 1 part of stearic acid, 5 parts of a processing agent, and 0.5 part of promoter Na-22. The heat-resistant chloroprene rubber formula can be used for producing high-quality rubber low in cost and wide in application range.

Description

A kind of thermotolerance Chloroprene rubber formula
Technical field
The present invention relates to a kind of thermotolerance Chloroprene rubber formula, belong to rubber compounding technical field.
Background technology
How chloroprene rubber, as the widely used product of one, is designed and can be met product performance requirement, has again the rubber compounding of lower cost simultaneously, for improving the quality of products, reduces production cost, significant.
Summary of the invention
According to above-mentioned requirements, the object of this invention is to provide a kind of thermotolerance Chloroprene rubber formula, to produce, there is lower cost, there is again applicable widely used high-quality rubber.
For achieving the above object, the present invention is realized by following technique means:
A kind of thermotolerance Chloroprene rubber formula, is characterized in that: comprise chloroprene rubber 100 parts, high abrasion furnace black(HAF) 30 parts, activated Calcium carbonate 50 parts, softening agent TCP10 part, antioxidant PA 1 part, antioxidant NBC 1 part, 4 parts, magnesium oxide, stearic acid 1 part, processing aid 5 parts, accelerant N a-22 be 0.5 part.
Further:
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: du pont company's product selected by described chloroprene rubber.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: described high abrasion furnace black(HAF) adopts Japanese East Sea carbon black Products.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: described antiozonant NBC plays heat-resisting anti-aging agent in formula.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: described magnesium oxide adopts No. 1 magnesium oxide.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: the hardness of described formulation product 60 °, tensile strength 17 more than MPa.
The invention has the beneficial effects as follows: a kind of thermotolerance Chloroprene rubber formula provided by the invention, can produce and there is lower cost, there is again applicable widely used high-quality rubber.
Embodiment
A kind of thermotolerance Chloroprene rubber formula, is characterized in that: comprise chloroprene rubber 100 parts, high abrasion furnace black(HAF) 30 parts, activated Calcium carbonate 50 parts, softening agent TCP10 part, antioxidant PA 1 part, antioxidant NBC 1 part, 4 parts, magnesium oxide, stearic acid 1 part, processing aid 5 parts, accelerant N a-22 be 0.5 part.
Further:
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: du pont company's product selected by described chloroprene rubber.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: described high abrasion furnace black(HAF) adopts Japanese East Sea carbon black Products.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: described antiozonant NBC plays heat-resisting anti-aging agent in formula.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: described magnesium oxide adopts No. 1 magnesium oxide.
Described a kind of thermotolerance Chloroprene rubber formula, is characterized in that: the hardness of described formulation product 60 °, tensile strength 17 more than MPa.
In CR, use high abrasion furnace black(HAF), if consider mixing in heat-dissipating, can say and more or less hold.Its consumption limit is 30 parts.
The thermotolerance of softening agent TCP is better than process oil (naphthene series), because the characteristic of its 120 DEG C of weight loss on heating is good.If carry out formulating of recipe, then preferably use full-bodied paraffin series process oil.
The object using 5 parts of processing aids is in order to supplementary dispersion agent and softening agent.Common consumption is 1 ~ 2 part.Because of carbon black, weighting agent, softening agent (tenderizer) with the use of sometimes produce ooze out phenomenon.What is called is oozed out (bleeding) is exactly softening agent, tenderizer and lubricant etc. migrate to phenomenon (bloom) on rubber surface.
Antiozonant NBC plays heat-resisting anti-aging agent in CR formula.
More than show and describe ultimate principle of the present invention, principal character and advantage.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (6)

1. a thermotolerance Chloroprene rubber formula, is characterized in that: comprise chloroprene rubber 100 parts, high abrasion furnace black(HAF) 30 parts, activated Calcium carbonate 50 parts, softening agent TCP10 part, antioxidant PA 1 part, antioxidant NBC 1 part, 4 parts, magnesium oxide, stearic acid 1 part, processing aid 5 parts, accelerant N a-22 be 0.5 part.
2. a kind of thermotolerance Chloroprene rubber formula as claimed in claim 1, is characterized in that: du pont company's product selected by described chloroprene rubber.
3. a kind of thermotolerance Chloroprene rubber formula as claimed in claim 1, is characterized in that: described high abrasion furnace black(HAF) adopts Japanese East Sea carbon black Products.
4. a kind of thermotolerance Chloroprene rubber formula as claimed in claim 1, is characterized in that: described antiozonant NBC plays heat-resisting anti-aging agent in formula.
5. a kind of thermotolerance Chloroprene rubber formula as claimed in claim 1, is characterized in that: described magnesium oxide adopts No. 1 magnesium oxide.
6. a kind of thermotolerance Chloroprene rubber formula as claimed in claim 1, is characterized in that: the hardness of described formulation product 60 °, tensile strength 17 more than MPa.
CN201510367985.6A 2015-06-29 2015-06-29 Heat-resistant chloroprene rubber formula Pending CN105017589A (en)