CN1021029C - 高速焊剂 - Google Patents
高速焊剂 Download PDFInfo
- Publication number
- CN1021029C CN1021029C CN 88103994 CN88103994A CN1021029C CN 1021029 C CN1021029 C CN 1021029C CN 88103994 CN88103994 CN 88103994 CN 88103994 A CN88103994 A CN 88103994A CN 1021029 C CN1021029 C CN 1021029C
- Authority
- CN
- China
- Prior art keywords
- present
- welding
- welding flux
- castings
- positions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于一种新型的用于铝热焊的高速焊剂,其有效材料由铝粉、氧化铁粉、锆石粉、萤石、硝酸钠均匀混合组成干粉。其用在冶金行业钢锭模、方渣罐、大底板、中心铸管等大铸件的破损部位的修补以及新铸铁件的焊接,经过40-60秒时间,温度达到1400-1500℃,速焊剂将缺陷部位局部铸件熔化而被速接在一起。用途广,在实践中取得很好的效果。
Description
本发明属于用于铝热焊的焊剂,特别是铝热焊的高速焊剂。
目前的焊剂,如对比文献1980年8月12日公开的美国专利US.4.216.816介绍的:焊接高锰铁的铝热剂,到于含锰14-17%,碳0.7-0.8(均按重量计%)的低碳高锰钢,在铸模中呈液态的焊剂成份:铝粉,氧化铁(例如氧化铁和三氧化二铁),软钢颗料,锰合金和/或电解锰,镍颗粒和/或镍合金和/或氧化镍,微量碳,使用这种焊剂可以对低碳高锰钢铸件焊接,但是被焊工件需根据含锰量成分高低,来选择焊剂成分配比,工艺繁杂。在实施过程中,组成铝热剂的成分要尽可能选择低的磷和硅,但作为杂质必竟还是存在的,因此易导致焊件裂纹和热撕裂。
本发明的目的是为了克服现有的铝热焊剂的不足而提出一种新型的用于铝热焊的高速焊剂。
本发明有如下优点:
本申请的高速焊剂成分配比与现有焊剂不同,用途也不同。其可以用于冶金行业钢锭模、方渣罐、大底板、中心铸管等大铸件的破损部位的修补以及新铸铁件的焊接,并取得很好的效果。
本发明的成分配比如下:
高速焊剂有效材料由铝粉14%,氧化铁粉77%,锆石粉7%,萤石1.6%,硝酸钠0.4%,(均按重量%计),均匀混合组成干粉。
实施例1:
焊接时将破损部位四周用耐火砖紧密围成,首先将助燃剂填充其底部,厚层为2mm,其次,将均匀混合的干粉再填入助燃剂上面,其厚度高于破损高度40-50mm,将装好的干粉用点燃器点着,点燃时间为40-60秒,干粉燃烧温度为1400-1500℃时,将破损部位周围局部铸件熔化,经5分钟后自然凝固,将破损部位速焊接在一起,去除上面残渣。如高出破损位可用砂轮打平。
实施例2:
点燃时间为40秒时,温度为1400-1500℃;
点燃时间为50秒时,温度为1400-1500℃。
Claims (1)
1、一种新型的用于铝热焊的高速焊剂,其特征是有效材料由铝粉14%,氧化铁粉77%,锆石粉7%,萤虫1,6%,硝酸钠0.4%,(均按重量%计),均匀混合组成干粉。