CN102071442A - 一种用于铝件预镀铜电镀液 - Google Patents
一种用于铝件预镀铜电镀液 Download PDFInfo
- Publication number
- CN102071442A CN102071442A CN2009102200923A CN200910220092A CN102071442A CN 102071442 A CN102071442 A CN 102071442A CN 2009102200923 A CN2009102200923 A CN 2009102200923A CN 200910220092 A CN200910220092 A CN 200910220092A CN 102071442 A CN102071442 A CN 102071442A
- Authority
- CN
- China
- Prior art keywords
- parts
- nacn
- electroplating solution
- copper electroplating
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种铜电镀液，尤其是涉及一种用于铝件预镀铜电镀液，属于金属加工领域。所含各成分按重量份数比为：CuCN 26～52份，NaCN 40～67份，NaCN(游离)2～9份，Na2CO3 18～45份，酒石酸钾那43～68份，光亮剂0.5～1.5份。本发明经过大量的科学实验得到一种配方简单、合理，无毒害气体逸出，废水处理简单，本发明有利于保护环境、减少投资和节约经费，操作容易，通过化学镀得到的金属镀层的化学、机械、磁性等性能优良。
Description
技术领域
本发明涉及一种铜电镀液，尤其是涉及一种用于铝件预镀铜电镀液，属于金属加工领域。
背景技术
铜是导电性、导热性好的红色金属，而且柔软容易抛光，但在空气中易受湿气、二氧化碳和含硫气体的腐蚀，生成氧化膜、硫化物和碱式碳酸铜。因此镀铜是一种重要的预镀层，铝件、锌压铸件、锡焊件、铝锡合金件等，在电镀前预镀铜，铍青铜、磷铜等铜合金也常预镀铜，用来提高镀层的结合强度，镀铜层用于局部防渗碳，印刷板孔金属化、印刷辊表面层、电极和电刷等，因此镀铜液的好坏将直接关系各种零件及设备的性能，用以镀层的化学、机械、磁性等性能。
发明内容
本发明的目的是提供一种废水处理简单，有利于保护环境、减少投资和节约经费，操作容易，铝件金属镀层的化学、机械、磁性等性能较好的铜电镀液。
为了实现以上目的，本发明的技术方案是：
一种用于铝件预镀铜电镀液，其特征在于所含各成分按重量份数比为：CuCN26～52份，NaCN 40～67份，NaCN(游离)2～9份，Na2CO3 18～45份，酒石酸钾那43～68份，光亮剂0.5～1.5份。
所述的用于铝件预镀铜电镀液，其特征在于所含各成分按重量份数比为：CuCN 29～50份，NaCN 45～62份，NaCN(游离)3～8份，Na2CO3 20～41份，酒石酸钾那46～63份，光亮剂0.6～1.2份。
所述的用于铝件预镀铜电镀液，其特征在于所含各成分按重量份数比为：CuCN 39份，NaCN 53份，NaCN(游离)7.5份，Na2CO3 32份，酒石酸钾那55份，光亮剂1.0份。
所述的光亮剂为呋喃、香豆素中的一种或两种。
上述用于铝件预镀铜电镀液的配制方法是采用常规的方法，其工艺条件为：镀液温度为60～70℃，阴极电流密度1.6～6.5A/dm2，阳极电流密度0.8～3.3A/dm2，光亮剂采用25s：(2～5)s换向电流可得到光亮铜镀层。
本发明与现有技术相比具有下列优点效果：本发明经过大量的科学实验得到一种配方简单、合理，无毒害气体逸出，废水处理简单，本发明有利于保护环境、减少投资和节约经费，操作容易，通过化学镀得到的金属镀层的化学、机械、磁性等性能优良。
具体实施方式
实施例1
用于铝件预镀铜电镀液，其所含各成分按重量份数比为：CuCN 39份，NaCN53份，NaCN(游离)7.5份，Na2CO3 32份，酒石酸钾那55份，呋喃1.0份。
用于铝件预镀铜电镀液的配制方法是采用常规的方法，其工艺条件为：镀液温度为60～70℃，阴极电流密度1.6～6.5A/dm2，阳极电流密度0.8～3.3A/dm2，光亮剂采用25s：(2～5)s换向电流可得到光亮铜镀层。
实施例2
用于铝件预镀铜电镀液，其所含各成分按重量份数比为：CuCN 26份，NaCN67份，NaCN(游离)9份，Na2CO3 45份，酒石酸钾那68份，香豆素1.5份。其它同实施例1。
实施例3
用于铝件预镀铜电镀液，其所含各成分按重量份数比为：CuCN 52份，NaCN40份，NaCN(游离)2份，Na2CO3 18份，酒石酸钾那43份，光亮剂0.5份。其它同实施例1。
实施例4
用于铝件预镀铜电镀液，其所含各成分按重量份数比为：CuCN 29份，NaCN62份，NaCN(游离)8份，Na2CO3 41份，酒石酸钾那63份，呋喃和香豆素1.2份。其它同实施例1。
实施例5
用于铝件预镀铜电镀液，其所含各成分按重量份数比为：CuCN 50份，NaCN45份，NaCN(游离)3份，Na2CO3 20份，酒石酸钾那46份，呋喃0.6份。其它同实施例1。
实施例5
用于铝件预镀铜电镀液，其所含各成分按重量份数比为：CuCN 36份，NaCN58份，NaCN(游离)6份，Na2CO3 35份，酒石酸钾那56份，香豆素0.7份。其它同实施例1。
Claims (4)
1.一种用于铝件预镀铜电镀液，其特征在于所含各成分按重量份数比为：CuCN 26～52份，NaCN 40～67份，NaCN(游离)2～9份，Na2CO3 18～45份，酒石酸钾那43～68份，光亮剂0.5～1.5份。
2.根据权利要求1所述的用于铝件预镀铜电镀液，其特征在于所含各成分按重量份数比为：CuCN 29～50份，NaCN 45～62份，NaCN(游离)3～8份，Na2CO3 20～41份，酒石酸钾那46～63份，光亮剂0.6～1.2份。
3.根据权利要求1所述的用于铝件预镀铜电镀液，其特征在于所含各成分按重量份数比为：CuCN 39份，NaCN 53份，NaCN(游离)7.5份，Na2CO3 32份，酒石酸钾那55份，光亮剂1.0份。
4.根据权利要求1所述的用于铝件预镀铜电镀液，其特征在于所述的光亮剂为呋喃、香豆素中的一种或两种。