CN102061022A - Novel rubber activator and preparation method thereof - Google Patents
Novel rubber activator and preparation method thereof Download PDFInfo
- Publication number
- CN102061022A CN102061022A CN 201010575002 CN201010575002A CN102061022A CN 102061022 A CN102061022 A CN 102061022A CN 201010575002 CN201010575002 CN 201010575002 CN 201010575002 A CN201010575002 A CN 201010575002A CN 102061022 A CN102061022 A CN 102061022A
- Authority
- CN
- China
- Prior art keywords
- benzene tricarboxylic
- acid
- tricarboxylic acid
- under
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a novel rubber activator and a preparation method thereof. The rubber activator particularly comprises 20 to 80 percent of aromatic group-containing formic acid type metal salt and 20 to 80 percent of zinc oxide, wherein the aromatic group-containing formic acid type metal salt is mixed with the zinc oxide at normal temperature and the two are stirred for 5 to 15 minutes at the rotation speed of between 2,000 and 3,500rpm. Compared with the prior art, the problems of high zinc content and high heavy metal element content in the zinc oxide can be effectively solved, density is reduced, dispersibility is improved, and the novel rubber activator improves rubber tensile property, broken chain elongation rate and rubber cross-linking effect.
Description
Technical field
The present invention relates to a kind of rubber activator.
Background technology
In order to accelerate vulcanization rate and raising state of vulcanization, the rubber activator is absolutely necessary rubber ingredients in vulcanization of rubber process.From the eighties of last century twenty or thirty age, zinc oxide is used till today in rubber as activator always, is that consumption is maximum now, the rubber activator of market capacity maximum.Yet zinc oxide has zinc content height, contents of heavy metal elements height such as lead, manganese, copper, and density is big, inherent defects such as dispersing property difference, a large amount of uses of zinc oxide have constituted huge environmental protection and have threatened.Therefore, actively seek and research and develop zinc oxide substitute or upgrading products have become the problem that rubber industry is paid special attention to, low zinc content or do not have the zinc activator and will become trend of the times.Ai Teen has produced a kind of new type rubber activator of low zinc environment-friendly high-efficiency through scientific and technical innovation for many years and the research and development of a large amount of industrial performance test.
Purpose of the present invention is exactly that a kind of problem that can effectively solve zinc oxide environmental protection aspect will be provided, and can improve the rubber activator of the crosslinked action of rubber tensile property, chain rupture elongation and rubber again.
Summary of the invention
The objective of the invention is to solve traditional rubber activator---the shortcoming that zinc oxide exists, and the physicals of raising rubber.
The technical scheme that realizes the object of the invention is:
A kind of new type rubber activator, it consists of: 20%-80% contains the formic acid metalloid salt of aromatic group and the zinc oxide of 20%-80%.
The described formic acid metalloid salt that contains aromatic group can be calcium benzoate, magnesium benzoate, Zinc dibenzoate, potassium benzoate, Sodium Benzoate, Barium dibenzoate, lead benzoate, aluminum benzoate, phenylformic acid iron, calcium phthalate, magnesium phthalate, zinc phthalate, phthalic acid potassium, sodium phthalate, phthalic acid barium, the O-phthalic lead plumbate, phthalic acid aluminium, phthalic acid iron, m-phthalic acid calcium, m-phthalic acid magnesium, m-phthalic acid zinc, m-phthalic acid potassium, m-phthalic acid sodium, m-phthalic acid barium, m-phthalic acid iron, m-phthalic acid lead, m-phthalic acid aluminium, terephthalic acid calcium, terephthalic acid magnesium, terephthalic acid zinc, potassium terephthalate, para-phthalic sodium, terephthalic acid barium, terephthaldehyde's lead plumbate, terephthalic acid aluminium, terephthalic acid iron, 1,2,3-benzene tricarboxylic acid calcium, 1,2,3-benzene tricarboxylic acid magnesium, 1,2,3-benzene tricarboxylic acid zinc, 1,2,3-benzene tricarboxylic acid potassium, 1,2,3-benzene tricarboxylic acid sodium, 1,2,3-benzene tricarboxylic acid barium, 1,2,3-benzene tricarboxylic acid lead, 1,2,3-benzene tricarboxylic acid aluminium, 1,2,3-benzene tricarboxylic acid iron, 1,2,4-benzene tricarboxylic acid calcium, 1,2,4-benzene tricarboxylic acid magnesium, 1,2,4-benzene tricarboxylic acid zinc, 1,2,4-benzene tricarboxylic acid potassium, 1,2,4-benzene tricarboxylic acid sodium, 1,2,4-benzene tricarboxylic acid barium, 1,2,4-benzene tricarboxylic acid lead, 1,2,4-benzene tricarboxylic acid aluminium, 1,2,4-benzene tricarboxylic acid iron, 1,3,5-benzene tricarboxylic acid calcium, 1,3,5-benzene tricarboxylic acid magnesium, 1,3,5-benzene tricarboxylic acid zinc, 1,3,5-benzene tricarboxylic acid potassium, 1,3,5-benzene tricarboxylic acid sodium, 1,3,5-benzene tricarboxylic acid barium, 1,3,5-benzene tricarboxylic acid lead, 1,3,5-benzene tricarboxylic acid aluminium or 1,3,5-benzene tricarboxylic acid iron.
A kind of method for preparing the new type rubber activator: under the normal temperature condition, the formic acid metalloid salt that will contain aromatic group mixes with zinc oxide, stirs 5min-15min under the rotating speed of 2000rpm-3500rpm.
Because the formic acid metalloid salt pair zinc oxide that contains aromatic group among the present invention has good synergy to make whole activation performance not reduce, therefore new type rubber activator of the present invention can solve the shortcoming of zinc oxide, as reduce zinc content and contents of heavy metal elements, reduce density, self excellent dispersing property of new type rubber activator helps the dispersion in sizing material of carbon black or white carbon black, can also prevent the phenomenon such as gel, conglomeration of sizing material.In addition, new type rubber activator equivalent substitution zinc oxide of the present invention, not only physicals does not reduce, and characteristics such as rubber tensile property, elongation at break improve on the contrary, and the crosslinked action of rubber is also effectively improved.
Embodiment
Embodiment 1
Under the normal temperature condition, 40% m-phthalic acid magnesium is mixed with 60% zinc oxide, under the rotating speed of 3500rpm, stir 5min and promptly get rubber activator of the present invention.
Embodiment 2
Under the normal temperature condition, 50% terephthalic acid calcium is mixed with 50% zinc oxide, under the rotating speed of 3500rpm, stir 5min and promptly get rubber activator of the present invention.
Embodiment 3
Under the normal temperature condition, 20% Zinc dibenzoate is mixed with 80% zinc oxide, under the rotating speed of 3500rpm, stir 10min and promptly get rubber activator of the present invention.
Embodiment 4
Under the normal temperature condition, 30% sodium phthalate is mixed with 70% zinc oxide, under the rotating speed of 3000rpm, stir 15min and promptly get rubber activator of the present invention.
Embodiment 5
Under the normal temperature condition, with 60%1,2,3-benzene tricarboxylic acid potassium mixes with 40% zinc oxide, stirs 15min and promptly get rubber activator of the present invention under the rotating speed of 2000rpm.
Embodiment 6
Under the normal temperature condition, with 70%1,2,4-benzene tricarboxylic acid barium mixes with 30% zinc oxide, stirs 10min and promptly get rubber activator of the present invention under the rotating speed of 3500rpm.
Embodiment 7
Under the normal temperature condition, with 80%1,3, the plumbous zinc oxide with 20% of 5-benzene tricarboxylic acid mixes, and stirs 10min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 8
Under the normal temperature condition, 45% m-phthalic acid calcium is mixed with 55% zinc oxide, under the rotating speed of 3500rpm, stir 10min and promptly get rubber activator of the present invention.
Embodiment 9
Under the normal temperature condition, 55% terephthalic acid magnesium is mixed with 45% zinc oxide, under the rotating speed of 3000rpm, stir 12min and promptly get rubber activator of the present invention.
Embodiment 10
Under the normal temperature condition, 25% aluminum benzoate is mixed with 75% zinc oxide, under the rotating speed of 2000rpm, stir 15min and promptly get rubber activator of the present invention.
Embodiment 11
Under the normal temperature condition, 35% phthalic acid iron is mixed with 65% zinc oxide, under the rotating speed of 3500rpm, stir 8min and promptly get rubber activator of the present invention.
Embodiment 12
Under the normal temperature condition, with 65%1,2,3-benzene tricarboxylic acid zinc mixes with 35% zinc oxide, stirs 14min and promptly get rubber activator of the present invention under the rotating speed of 2500rpm.
Embodiment 13
Under the normal temperature condition, with 75%1,2,4-benzene tricarboxylic acid iron mixes with 25% zinc oxide, stirs 7min and promptly get rubber activator of the present invention under the rotating speed of 3500rpm.
Embodiment 14
Under the normal temperature condition, with 29%1,3,5-benzene tricarboxylic acid barium mixes with 71% zinc oxide, stirs 8min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 15
Under the normal temperature condition, 21% m-phthalic acid potassium is mixed with 79% zinc oxide, under the rotating speed of 3000rpm, stir 9min and promptly get rubber activator of the present invention.
Embodiment 16
Under the normal temperature condition, 22% para-phthalic sodium is mixed with 78% zinc oxide, under the rotating speed of 3000rpm, stir 10min and promptly get rubber activator of the present invention.
Embodiment 17
Under the normal temperature condition, 23% lead benzoate is mixed with 77% zinc oxide, under the rotating speed of 3000rpm, stir 11min and promptly get rubber activator of the present invention.
Embodiment 18
Under the normal temperature condition, 24% phthalic acid aluminium is mixed with 76% zinc oxide, under the rotating speed of 3000rpm, stir 12min and promptly get rubber activator of the present invention.
Embodiment 19
Under the normal temperature condition, with 51%1,2,3-benzene tricarboxylic acid calcium mixes with 49% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 3400rpm.
Embodiment 20
Under the normal temperature condition, with 26%1,2,4-benzene tricarboxylic acid magnesium mixes with 74% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 3300rpm.
Embodiment 21
Under the normal temperature condition, with 27%1,3,5-benzene tricarboxylic acid zinc mixes with 73% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 3200rpm.
Embodiment 22
Under the normal temperature condition, 28% m-phthalic acid aluminium is mixed with 72% zinc oxide, under the rotating speed of 3100rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 23
Under the normal temperature condition, 52% terephthalic acid iron is mixed with 48% zinc oxide, under the rotating speed of 2900rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 24
Under the normal temperature condition, 31% Barium dibenzoate is mixed with 69% zinc oxide, under the rotating speed of 2800rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 25
Under the normal temperature condition, 32% O-phthalic lead plumbate is mixed with 68% zinc oxide, under the rotating speed of 2700rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 26
Under the normal temperature condition, with 33%1,2,3-benzene tricarboxylic acid aluminium mixes with 67% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 2600rpm.
Embodiment 27
Under the normal temperature condition, with 34%1,2,4-benzene tricarboxylic acid potassium mixes with 66% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 2400rpm.
Embodiment 28
Under the normal temperature condition, with 53%1,3,5-benzene tricarboxylic acid calcium mixes with 47% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 2300rpm.
Embodiment 29
Under the normal temperature condition, 36% m-phthalic acid barium is mixed with 64% zinc oxide, under the rotating speed of 2200rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 30
Under the normal temperature condition, 37% terephthalic acid zinc is mixed with 63% zinc oxide, under the rotating speed of 3500rpm, stir 15min and promptly get rubber activator of the present invention.
Embodiment 31
Under the normal temperature condition, 38% potassium benzoate is mixed with 62% zinc oxide, under the rotating speed of 3500rpm, stir 14min and promptly get rubber activator of the present invention.
Embodiment 32
Under the normal temperature condition, 39% magnesium phthalate is mixed with 61% zinc oxide, under the rotating speed of 3500rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 33
Under the normal temperature condition, with 54%1,2,3-benzene tricarboxylic acid barium mixes with 46% zinc oxide, stirs 12min and promptly get rubber activator of the present invention under the rotating speed of 3500rpm.
Embodiment 34
Under the normal temperature condition, with 41%1,2, the plumbous zinc oxide with 59% of 4-benzene tricarboxylic acid mixes, and stirs 11min and promptly get rubber activator of the present invention under the rotating speed of 3500rpm.
Embodiment 35
Under the normal temperature condition, with 42%1,3,5-benzene tricarboxylic acid aluminium mixes with 58% zinc oxide, stirs 10min and promptly get rubber activator of the present invention under the rotating speed of 3500rpm.
Embodiment 36
Under the normal temperature condition, 43% m-phthalic acid iron is mixed with 57% zinc oxide, under the rotating speed of 3500rpm, stir 9min and promptly get rubber activator of the present invention.
Embodiment 37
Under the normal temperature condition, 44% terephthaldehyde's lead plumbate is mixed with 56% zinc oxide, under the rotating speed of 3500rpm, stir 8min and promptly get rubber activator of the present invention.
Embodiment 38
Under the normal temperature condition, 56% magnesium benzoate is mixed with 44% zinc oxide, under the rotating speed of 3500rpm, stir 7min and promptly get rubber activator of the present invention.
Embodiment 39
Under the normal temperature condition, 46% zinc phthalate is mixed with 54% zinc oxide, under the rotating speed of 3500rpm, stir 6min and promptly get rubber activator of the present invention.
Embodiment 40
Under the normal temperature condition, with 47%1,2,3-benzene tricarboxylic acid sodium mixes with 53% zinc oxide, stirs 5min and promptly get rubber activator of the present invention under the rotating speed of 3500rpm.
Embodiment 41
Under the normal temperature condition, with 48%1,2,4-benzene tricarboxylic acid sodium mixes with 52% zinc oxide, stirs 15min and promptly get rubber activator of the present invention under the rotating speed of 2000rpm.
Embodiment 42
Under the normal temperature condition, with 49%1,3,5-benzene tricarboxylic acid sodium mixes with 51% zinc oxide, stirs 14min and promptly get rubber activator of the present invention under the rotating speed of 2000rpm.
Embodiment 43
Under the normal temperature condition, the plumbous zinc oxide with 43% of 57% m-phthalic acid is mixed, under the rotating speed of 2000rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 44
Under the normal temperature condition, 58% terephthalic acid aluminium is mixed with 42% zinc oxide, under the rotating speed of 2000rpm, stir 12min and promptly get rubber activator of the present invention.
Embodiment 45
Under the normal temperature condition, 59% phenylformic acid iron is mixed with 41% zinc oxide, under the rotating speed of 2000rpm, stir 11min and promptly get rubber activator of the present invention.
Embodiment 46
Under the normal temperature condition, 61% calcium phthalate is mixed with 39% zinc oxide, under the rotating speed of 2000rpm, stir 10min and promptly get rubber activator of the present invention.
Embodiment 47
Under the normal temperature condition, with 62%1,2,3-benzene tricarboxylic acid magnesium mixes with 38% zinc oxide, stirs 9min and promptly get rubber activator of the present invention under the rotating speed of 2000rpm.
Embodiment 48
Under the normal temperature condition, with 63%1,2,4-benzene tricarboxylic acid zinc mixes with 37% zinc oxide, stirs 8min and promptly get rubber activator of the present invention under the rotating speed of 2000rpm.
Embodiment 49
Under the normal temperature condition, with 64%1,3,5-benzene tricarboxylic acid potassium mixes with 36% zinc oxide, stirs 7min and promptly get rubber activator of the present invention under the rotating speed of 2000rpm.
Embodiment 50
Under the normal temperature condition, 66% m-phthalic acid sodium is mixed with 34% zinc oxide, under the rotating speed of 2000rpm, stir 6min and promptly get rubber activator of the present invention.
Embodiment 51
Under the normal temperature condition, 67% terephthalic acid barium is mixed with 33% zinc oxide, under the rotating speed of 2000rpm, stir 5min and promptly get rubber activator of the present invention.
Embodiment 52
Under the normal temperature condition, 68% calcium benzoate is mixed with 32% zinc oxide, under the rotating speed of 3000rpm, stir 9min and promptly get rubber activator of the present invention.
Embodiment 53
Under the normal temperature condition, 69% phthalic acid potassium is mixed with 31% zinc oxide, under the rotating speed of 3000rpm, stir 8min and promptly get rubber activator of the present invention.
Embodiment 54
Under the normal temperature condition, with 71%1,2,3-benzene tricarboxylic acid iron mixes with 29% zinc oxide, stirs 7min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 55
Under the normal temperature condition, with 72%1,2,4-benzene tricarboxylic acid calcium mixes with 28% zinc oxide, stirs 6min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 56
Under the normal temperature condition, with 73%1,3,5-benzene tricarboxylic acid magnesium mixes with 27% zinc oxide, stirs 5min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 57
Under the normal temperature condition, 74% m-phthalic acid zinc is mixed with 26% zinc oxide, under the rotating speed of 3000rpm, stir 15min and promptly get rubber activator of the present invention.
Embodiment 58
Under the normal temperature condition, 76% potassium terephthalate is mixed with 24% zinc oxide, under the rotating speed of 3000rpm, stir 14min and promptly get rubber activator of the present invention.
Embodiment 59
Under the normal temperature condition, 77% Sodium Benzoate is mixed with 23% zinc oxide, under the rotating speed of 3000rpm, stir 13min and promptly get rubber activator of the present invention.
Embodiment 60
Under the normal temperature condition, 78% phthalic acid barium is mixed with 22% zinc oxide, under the rotating speed of 3000rpm, stir 12min and promptly get rubber activator of the present invention.
Embodiment 61
Under the normal temperature condition, with 79%1,2, the plumbous zinc oxide with 21% of 3-benzene tricarboxylic acid mixes, and stirs 11min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 62
Under the normal temperature condition, with 20%1,2,4-benzene tricarboxylic acid aluminium mixes with 80% zinc oxide, stirs 13min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Embodiment 63
Under the normal temperature condition, with 80%1,3,5-benzene tricarboxylic acid iron mixes with 20% zinc oxide, stirs 10min and promptly get rubber activator of the present invention under the rotating speed of 3000rpm.
Claims (3)
1. new type rubber activator, it is characterized in that consisting of: 20%-80% contains the formic acid metalloid salt of aromatic group and the zinc oxide of 20%-80%.
2. new type rubber activator according to claim 1, it is characterized in that: the formic acid metalloid salt that contains aromatic group can be calcium benzoate, magnesium benzoate, Zinc dibenzoate, potassium benzoate, Sodium Benzoate, Barium dibenzoate, lead benzoate, aluminum benzoate, phenylformic acid iron, calcium phthalate, magnesium phthalate, zinc phthalate, phthalic acid potassium, sodium phthalate, phthalic acid barium, the O-phthalic lead plumbate, phthalic acid aluminium, phthalic acid iron, m-phthalic acid calcium, m-phthalic acid magnesium, m-phthalic acid zinc, m-phthalic acid potassium, m-phthalic acid sodium, m-phthalic acid barium, m-phthalic acid iron, m-phthalic acid lead, m-phthalic acid aluminium, terephthalic acid calcium, terephthalic acid magnesium, terephthalic acid zinc, potassium terephthalate, para-phthalic sodium, terephthalic acid barium, terephthaldehyde's lead plumbate, terephthalic acid aluminium, terephthalic acid iron, 1,2,3-benzene tricarboxylic acid calcium, 1,2,3-benzene tricarboxylic acid magnesium, 1,2,3-benzene tricarboxylic acid zinc, 1,2,3-benzene tricarboxylic acid potassium, 1,2,3-benzene tricarboxylic acid sodium, 1,2,3-benzene tricarboxylic acid barium, 1,2,3-benzene tricarboxylic acid lead, 1,2,3-benzene tricarboxylic acid aluminium, 1,2,3-benzene tricarboxylic acid iron, 1,2,4-benzene tricarboxylic acid calcium, 1,2,4-benzene tricarboxylic acid magnesium, 1,2,4-benzene tricarboxylic acid zinc, 1,2,4-benzene tricarboxylic acid potassium, 1,2,4-benzene tricarboxylic acid sodium, 1,2,4-benzene tricarboxylic acid barium, 1,2,4-benzene tricarboxylic acid lead, 1,2,4-benzene tricarboxylic acid aluminium, 1,2,4-benzene tricarboxylic acid iron, 1,3,5-benzene tricarboxylic acid calcium, 1,3,5-benzene tricarboxylic acid magnesium, 1,3,5-benzene tricarboxylic acid zinc, 1,3,5-benzene tricarboxylic acid potassium, 1,3,5-benzene tricarboxylic acid sodium, 1,3,5-benzene tricarboxylic acid barium, 1,3,5-benzene tricarboxylic acid lead, 1,3,5-benzene tricarboxylic acid aluminium or 1,3,5-benzene tricarboxylic acid iron.
3. method for preparing the described new type rubber activator of claim 1, it is characterized in that: under the normal temperature condition, the formic acid metalloid salt that will contain aromatic group mixes with zinc oxide, stirs 5min-15min under the rotating speed of 2000rpm-3500rpm.