CN102060454A - 一种轻烧白云石水泥 - Google Patents
一种轻烧白云石水泥 Download PDFInfo
- Publication number
- CN102060454A CN102060454A CN201010551895XA CN201010551895A CN102060454A CN 102060454 A CN102060454 A CN 102060454A CN 201010551895X A CN201010551895X A CN 201010551895XA CN 201010551895 A CN201010551895 A CN 201010551895A CN 102060454 A CN102060454 A CN 102060454A
- Authority
- CN
- China
- Prior art keywords
- parts
- light dolomite
- light
- cement
- phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种轻烧白云石水泥，其包括如下重量份组份：轻烧白云石100份、工业废渣10～50份、增强增稠剂10～40份和抗水外加剂0.5～15份。本发明的优点在于，轻烧白云石水泥具有快凝、早强、高强、抗水性好和抗冻的优点，大量消耗工业废渣，符合环保要求，原料来源广泛。
Description
技术领域
本发明涉及一种水泥，特别是涉及一种具有快凝、早强、高强、抗水性好、抗冻的轻烧白云石水泥。
背景技术
普通硅酸盐水泥是目前广泛使用的胶凝材料，但是烧成硅酸盐水泥熟料的温度高达1450℃以上，大量消耗优质石灰石、粘土、铁粉等原料，而且每生产1吨水泥要排放1吨二氧化碳气体，加剧了地球的温室气体效应，因而属于一种高消耗、高能耗、高污染的不可持续发展的胶凝材料。为了降低能耗，采用其他的低消耗、低能耗、低污染的胶凝材料如石膏、轻烧氧化镁水泥等，具有重要的社会意义和现实意义。但是，石膏胶凝材料的强度低、抗水性差，难以真正替代现有的普通硅酸盐水泥，而以轻烧氧化镁水泥采用氯化镁或者硫酸镁溶液拌和，则具有巨大的应用价值和市场前景。中国发明专利ZL00122936.2公开了一种铝硅镁水泥，由氧化镁100份、粉煤灰80份、河砂60份、25度氯化镁溶液80份、硅酸钠4.4份、硅酸溶胶4.4份(溶液)、18度硫酸铝8.8份(溶液)、28度硫酸镁88份(溶液)、30度硫酸8.8份(溶液)混合配制而成，但是该专利产品的组成中既有粉料、又有溶液、同时还含有砂子，而且只能在施工现场或者工厂车间现拌现用，实际上属于一种氧化镁水泥湿拌砂浆，不属于严格意义上的水泥胶凝材料，更不能包装成一种现代意义上的水泥产品。此外，上述专利产品中的氧化镁来源集中于我国的辽宁省海城市和大石桥市以及山东省莱州市，由菱镁矿煅烧得到，一方面大量消耗了我国宝贵的菱镁矿资源，另一方面受到地域所限，难以在全国范围内推广应用。
发明内容
本发明的目的在于提供一种完全由粉料包装而成的轻烧白云石水泥，该水泥具有快凝、早强、高强、抗水性好、抗冻、大量消耗工业废渣、符合环保要求、原料来源广泛。
本发明的目的由如下技术方案实施，一种轻烧白云石水泥，包括如下重量份的组分：轻烧白云石粉100份和抗水外加剂0.5～15份。
其还包括有如下重量份数的原料：工业废渣1～60份。
其还包括有如下重量份数的原料：增强增稠剂1～50份。
各组分重量份数比优选为：轻烧白云石粉100份、工业废渣10～50份、增强增稠剂10～40份和抗水外加剂1～10份。
各组分重量份数比进一步优选为：轻烧白云石粉100份、工业废渣20～40份、增强增稠剂15～30份和抗水外加剂2～8份。
所述轻烧白云石粉为白云石经过煅烧之后得到的含有活性氧化镁和碳酸钙的粉末材料。
所述工业废渣为粉煤灰、炉渣、矿渣、钢渣、脱硫石膏中的任意一种或一种以上的混合物。
所述增强增稠剂为氧化镁、硅酸镁中的任意一种或两种的混合物。
所述抗水外加剂为磷酸钠、磷酸钾、磷酸铵、磷酸钙、磷酸二氢钠、磷酸二氢钾、磷酸二氢铵、磷酸二氢钙、偏磷酸钠、硫酸亚铁、石膏和硅灰中的任意一种或一种以上的混合物。
本发明所述的轻烧白云石水泥，其配制方法包括以下步骤：
(1)原料计量：将轻烧白云石粉、工业废渣、增强增稠剂、抗水外加剂按照上述的配方，分别计量；
(2)混合磨细：将计量好的所述原材料混合均匀，搅拌制成轻烧白云石水泥；
(3)防潮包装：用纸袋或内衬塑料膜的编制袋包装，出厂。
该水泥采用调和剂溶液拌和，在自然条件下既能发生凝结硬化。
所述调和剂溶液是波美度为18～35°Bé的氯化镁溶液、波美度为20～35°Bé的硫酸镁溶液中的任意一种或两种的混合物。
本发明轻烧白云石水泥可替代普通硅酸盐水泥，与骨料、纤维等材料一起配制成各种墙体材料、屋面材料、装饰材料等建筑材料制品，如砂浆、保温砂浆、砂石混凝土、轻骨料混凝土、砖、砌块、轻质隔墙板、屋面瓦等。
本发明的优点在于：1、具有常温固化反应快凝、早强、高强、抗水性好、抗冻的优点，生产过程中无三废排放，属清洁生产，符合新型墙体材料对建筑功能和建筑节能的要求，具有较好的社会经济效益；2、加入了抗水外加剂，提高了产品的抗水性，可用作潮湿环境下的建筑材料，扩大产品的应用范围；抗水性提高，延长产品的使用寿命，同时克服了产品吸潮、返卤和泛霜的缺点；3、大量采用粉煤灰、炉渣、矿渣、钢渣、脱硫石膏等工业废渣，促进了固体废弃物的资源化和综合利用，可减少对环境的污染，降低成本，并能使抗水性能大大提高；4、采用增强增稠剂，大大提高强度，改善和易性。本发明无毒、无味、无放射性，对人体无害，不污染环境，属于环保型新型胶凝材料。
具体实施方式
以下通过实施例进一步阐述本发明轻烧白云石水泥，这些实施例仅用于举例说明的目的，并没有限制本发明的范围。下列实施例中未注明具体条件的实验方法，通常按照常规条件。
实施例1：本发明所述的轻烧白云石水泥，其配制方法包括以下步骤：
(1)原料计量：将轻烧白云石粉、工业废渣、增强增稠剂、抗水外加剂按照实施例2-9的配方，分别计量；
(2)混合磨细：将计量好的所述原材料混合均匀，搅拌制成轻烧白云石水泥；
(3)防潮包装：用纸袋或内衬塑料膜的编制袋包装，出厂。
使用时采用波美度为18～35°Bé的氯化镁溶液、波美度为20～35°Bé的硫酸镁溶液中的任何一种或两种的混合溶液来拌和。
实施例2-9如表1所示：
实施例2-9中轻烧白云石水泥使用实施例1方法，按下表配方制备而成。
表1：实施例2-9配方列表
实施例10：对用实施例2-9配方制得的轻烧白云石水泥性能进行测试，结果如表2所示。
表2：按实施例2-9配方制得的轻烧白云石水泥的性能测试表
由表2数据可以看出，本发明具有快凝、早强、高强、抗水等特征。
Claims (9)
1.一种轻烧白云石水泥，其特征在于，包括如下重量份的组分：轻烧白云石粉100份和抗水外加剂0.5～15份。
2.根据权利要求1所述的一种轻烧白云石水泥，其特征在于，其还包括有如下重量份数的原料：工业废渣1～60份。
3.根据权利要求1或2所述的一种轻烧白云石水泥，其特征在于，其还包括有如下重量份数的原料：增强增稠剂1～50份。
4.根据权利要求1-3任意所述的一种轻烧白云石水泥，其特征在于，各组分重量份数比优选为：轻烧白云石粉100份、工业废渣10～50份、增强增稠剂10～40份和抗水外加剂1～10份。
5.根据权利要求4所述的一种轻烧白云石水泥，其特征在于，各组分重量份数比进一步优选为：轻烧白云石粉100份、工业废渣20～40份、增强增稠剂15～30份和抗水外加剂2～8份。
6.根据权利要求1所述的轻烧白云石水泥，其特征在于，所述轻烧白云石粉为白云石经过煅烧之后得到的含有活性氧化镁和碳酸钙的粉末材料。
7.根据权利要求2所述的轻烧白云石水泥，其特征在于，所述工业废渣为粉煤灰、炉渣、矿渣、钢渣、脱硫石膏中的任意一种或一种以上的混合物。
8.根据权利要求3所述的轻烧白云石水泥，其特征在于，所述增强增稠剂为氧化镁、硅酸镁中的任意一种或两种的混合物。
9.根据权利要求1所述的轻烧白云石水泥，其特征在于，所述抗水外加剂为磷酸钠、磷酸钾、磷酸铵、磷酸钙、磷酸二氢钠、磷酸二氢钾、磷酸二氢铵、磷酸二氢钙、偏磷酸钠、硫酸亚铁、石膏和硅灰中的任意一种或一种以上的混合物。