CN102058159A - 一种选择性降低卷烟主流烟气中主要羰基化合物的卷烟滤嘴添加剂及制备和应用 - Google Patents
一种选择性降低卷烟主流烟气中主要羰基化合物的卷烟滤嘴添加剂及制备和应用 Download PDFInfo
- Publication number
- CN102058159A CN102058159A CN 201010564630 CN201010564630A CN102058159A CN 102058159 A CN102058159 A CN 102058159A CN 201010564630 CN201010564630 CN 201010564630 CN 201010564630 A CN201010564630 A CN 201010564630A CN 102058159 A CN102058159 A CN 102058159A
- Authority
- CN
- China
- Prior art keywords
- carrier
- additive
- cigarette
- temperature
- cuprous oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种选择性降低卷烟主流烟气中主要羰基化合物的卷烟滤嘴添加剂及制备和应用,所述添加剂以粒径为20-80目的活性炭为载体,在载体表面改性引入氧化亚铜这一活性反应层。本发明的添加剂对卷烟主流烟气中主要羰基化合物的选择性高,特别是对甲醛和巴豆醛,具有良好的降低效果;且本发明的添加剂稳定性非常好,不会掉粉尘而影响卷烟品质。本发明是通过浸制与煅烧,在载体表面引入氧化亚铜活性物质,工艺过程简单,所得到的氧化亚铜活性高。
Description
技术领域
本发明属于卷烟滤嘴除害技术领域,具体涉及一种选择性降低卷烟主流烟气中主要羰基化合物的添加剂及制备方法和应用。
背景技术
目前,在卷烟主流烟气中至少已发现20种醛和6种酮,其中含量高的七种是:甲醛、乙醛、丙醛、丙烯醛、巴豆醛、糠醛和丙酮等。特别是巴豆醛,是烟草行业重点关注的七种有害成分之一。
为了增加卷烟的安全性,可以采用多种方法降低卷烟主流烟气中的有害主要羰基化合物,如:采用滤嘴过滤卷烟主流烟气去除有害成分,普通滤嘴的过滤不仅去除掉了烟气中的有害成分,同时也截留了烟气中的有用成分,因此,有选择的进行过滤是国内外专家正在积极探索的课题。
以往的研究侧重于整体降焦,未有明显的选择性,如中国专利9010729.3,把活性炭加入嘴棒;中国专利CN1692848A(公开号),将TiO2-Pd-Cu基活性炭纤维制备复合嘴棒;中国专利CN101094598A(公开号),通过用表面改性活性炭加入嘴棒,制成复合嘴棒。但这些专利对主流烟气中主要羰基化合物没有选择性。目前,关于氧化亚铜的研究主要集中在其它化工行业如作为催化剂来深入研究等。
发明内容
本发明的目的旨在提供一种可选择性降低卷烟主流烟气中主要羰基化合物的卷烟滤嘴添加剂。
本发明的添加剂以粒径为20-80目的活性炭为载体,在载体表面改性引入氧化亚铜这一活性反应层。
所述的改性引入是将活化处理的载体浸渍于可分解成氧化亚铜的前驱物溶液中,经干燥煅烧而成。
所述的氧化亚铜的前驱物溶液最优选的是Cu(CH3COO)·2H2O溶液。所采用的Cu(CH3COO)·2H2O在物质分解后没有副产品,也没有残留,活性物质干净,不会带来新的分离困难等问题。
本发明添加剂的制备方法包括以下步骤:
1)载体的活化处理:
以20-80目的活性炭为载体,将活性炭加入到2-3mol/L的氨水或3-5mol/L硝酸溶液中,在40-60℃的温度下搅拌,抽滤并用蒸馏水洗涤至溶液PH值呈中性,然后烘干,待用;
2)载体的改性引入:
将活化处理后的载体在Cu(CH3COO)·2H2O水溶液中充分浸渍后,再取出干燥,得到负载有前驱物的载体,然后将其在N2气保护下于230-270℃温度下分解2-6h,冷却即得本发明的添加剂。
本发明通过1)步对活性炭表面处理,可以增加活性炭与后续活性物质的结合力。
本发明优选1)步中在40-60℃的温度下搅拌1-2h。1)步中烘干的优选温度为90-110℃。
2)步中优选的干燥温度为80-90℃。
Cu(CH3COO)·2H2O水溶液优选的配制质量百分比浓度为1.5-5.5%。
所述应用方式为:在每支卷烟中加入约30-50mg的本发明的添加剂,制备复合滤嘴棒;最后再卷接成烟支。
与现有技术的添加剂相比,本发明具有以下优势:
本发明的添加剂对卷烟主流烟气中主要羰基化合物的选择性高,特别是对甲醛和巴豆醛,在添加剂用量40mg/支卷烟的情况下,甲醛可以降低40%以上,巴豆醛降低效果接近50%;且本发明的添加剂稳定性非常好,不会掉粉尘而影响卷烟品质。
本发明是通过浸制与煅烧,在载体表面引入氧化亚铜活性物质,工艺过程简单,所得到的氧化亚铜活性高。
具体实施方式
以下实施例旨在说明本发明而不是对本发明的进一步限制。
实施例1:
称取20g的20-80目活性炭,将活性炭加入到2mol/L的氨水溶液中,在45℃的温度搅拌1h,抽滤并用蒸馏水洗涤至溶液PH值呈中性,然后放入105℃的烘箱中烘干,待用;将初步处理后的载体浸制在配制好50ml 2.5%左右的Cu(CH3COO)·2H2O溶液中,1h小时后,放入烘箱于85℃温度干燥,得到前驱物,然后将其在N2气保护下于240℃温度下分解4h,冷却。
所述应用方式为:在每支卷烟中加入约40mg的改性好的添加剂,制备复合棒,卷接成烟支。
实施例2:
称取20g的20-80目活性炭,将活性炭加入到3mol/L硝酸溶液中,在50℃的温度搅拌1h,抽滤并用蒸馏水洗涤至溶液PH值呈中性,然后放入105℃的烘箱中烘干,待用;将初步处理后的载体浸制在配制好50ml 3.5%左右的Cu(CH3COO)·2H2O溶液中,2h小时后,放入烘箱于85℃温度干燥,得到前驱物,然后将其在N2气保护下于250℃温度下分解4h,冷却。
所述应用方式为:在每支卷烟中加入约40mg的改性好的添加剂,制备复合棒,卷接成烟支。
测试结果见表1,结果显示使用添加剂后,复合滤嘴对卷烟主流烟气中主要羰基化合物选择性降低效率高。
表1
Claims (9)
1.一种选择性降低卷烟主流烟气中主要羰基化合物的卷烟滤嘴添加剂,所述添加剂以粒径为20-80目的活性炭为载体,在载体表面改性引入氧化亚铜这一活性反应层。
2.根据权利要求1所述的添加剂,所述的改性引入是将活化处理的载体浸渍于可分解成氧化亚铜的前驱物溶液中,经干燥煅烧而成。
3.根据权利要求1所述的添加剂,所述的氧化亚铜的前驱物水溶液为Cu(CH3COO)·2H2O水溶液。
4.一种选择性降低卷烟主流烟气中主要羰基化合物的卷烟滤嘴添加剂的制备方法,包括以下步骤:
1)、载体的活化处理:
以20-80目的活性炭为载体,将活性炭加入到2-3mol/L的氨水或3-5mol/L硝酸溶液中,在40-60℃的温度下搅拌,抽滤并用蒸馏水洗涤至溶液PH值呈中性,然后烘干,待用;
2)、载体的改性引入:
将活化处理后的载体在Cu(CH3COO)·2H2O水溶液中浸渍,再取出干燥,得到负载有前驱物的载体,然后将其在N2气保护下于230-270℃温度下分解2-6h,冷却即得。
5.根据权利要求4所述的方法,Cu(CH3COO)·2H2O水溶液的质量百分比浓度为1.5-5.5%。
6.根据权利要求4或5所述的方法,所述的1)步中在40-60℃的温度下搅拌1-2h。
7.根据权利要求4或5所述的方法,所述的1)步中烘干的温度为90-110℃。
8.根据权利要求4或5所述的方法,所述的2)步中干燥温度为80-90℃。
9.权利要求1-3任一项所述添加剂的应用:每支卷烟中加入约30-50mg所述添加剂,制备复合滤嘴棒。