CN102051709A - 一种夜光膜材料及其制备方法 - Google Patents
一种夜光膜材料及其制备方法 Download PDFInfo
- Publication number
- CN102051709A CN102051709A CN2009101985014A CN200910198501A CN102051709A CN 102051709 A CN102051709 A CN 102051709A CN 2009101985014 A CN2009101985014 A CN 2009101985014A CN 200910198501 A CN200910198501 A CN 200910198501A CN 102051709 A CN102051709 A CN 102051709A
- Authority
- CN
- China
- Prior art keywords
- noctilucence
- membrane material
- resin
- luminescent powder
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种夜光膜材料,包括:PET薄膜、夜光粉、树脂组成,所述的PET薄膜的厚度为0.008mm-0.025mm之间,所述的夜光粉是经过纳米技术处理的,都是通过选用意大利或者德国优质品牌,所述的树脂主要是选用德国的。本发明具有厚度超薄、极具柔软性、抗氧化及耐酸碱程度较高、抗拉性强的优点。
Description
技术领域
本发明是一种夜光膜材料及其制备方法,与其他产品组合成线类产品,主要用在纺织、织布、线带、抽纱、编织、绣品、商标、服饰、圣诞礼品、玩具零件、鞋帽等装饰行业。
背景技术
经有关资料反映,国内外的夜光膜材料厚度大于0.5MM,使得它的应用领域范围受到很大的限制,正因为它的厚度问题,造成难以切丝,而且又由于不够柔软,抗拉性抗氧化性不强,因而不能产生出能够应用于广泛领域和相关系列的产品,难以用于纺织、织布、线、薄型绸带、抽纱、薄型编织、刺绣、服饰、鞋帽、圣诞礼品等领域。
发明内容
本发明所要解决的技术问题是克服现有技术的难题,提供一种厚度超薄、极具柔软性、抗氧化及耐酸碱程度较高、抗拉性强的一种夜光膜材料及其制备方法。
为了解决上述技术问题,本发明提供了一种夜光膜材料,包括:PET薄膜、夜光粉、树脂组成,所述的PET薄膜的厚度为0.008MM-0.025MM之间,所述的夜光粉是经过纳米技术处理的,都是通过选用意大利或者德国优质品牌,所述的树脂主要是选用德国的。
本发明还提供了一种夜光膜材料的制备方法,其过程如下:首先将所述的夜光粉和树脂充分溶解,溶解完成后将其涂在PET薄膜上,然后将其在涂布机上进行烘烤,烘烤的温度设置在100℃-210℃之间,最后形成了夜光膜材料,再经过先进的机械和切割技术切割成0.15MM-5MM的宽度的丝,本发明的材料即完成,
本发明具有以下明显的优势和有益效果:
1)超薄,宽度在0.15MM-5MM之间;
2)具有抗氧化和耐酸碱性;
3)柔软性,抗拉性。
附图说明
图1是本发明一种夜光膜材料的M型的使用方式示意图;
图2是本发明一种夜光膜材料的MX型的使用方式示示意图;
图3是本发明一种夜光膜材料的MH型的使用方式示示意图;
图4是本发明一种夜光膜材料的MHX型的使用方式示示意图;
图5是本发明一种夜光膜材料的MS型的使用方式示示意图;
图6是本发明一种夜光膜材料的JB型的使用方式示示意图。
具体实施方式
如图1-6所示,本发明一种夜光膜材料,包括:PET薄膜、夜光粉、树脂组成,所述的PET薄膜的厚度为0.008MM-0.025MM之间,所述的夜光粉是经过纳米技术处理的,都是通过选用意大利或者德国优质品牌,所述的树脂主要是选用德国的,
一种夜光膜材料的制备方法,其过程如下:首先将所述的夜光粉树脂充分溶解,溶解完成后将其涂在PET薄膜上,然后将其在涂布机上进行烘烤,烘烤的温度设置在100℃-210℃之间,最后形成了夜光膜材料,再经过先进的机械和切割技术切割成0.15MM-5MM的宽度的丝,本发明的材料即完成,
以下举实施例对夜光膜材料的应用方法进行描述,
如图1所示为本发明一种夜光膜材料的M型示意图,M型是采用夜光膜切成0.15MM-5MM不同规格的丝,主要用于织布、编织、服饰和圣诞礼品等领域。
如图2所示为本发明一种夜光膜材料的MX型示意图,MX型是采用0.15MM-0.5MM的夜光丝与15D-50D的尼龙丝和涤纶丝交并而制成,将尼龙丝和涤纶围绕夜光丝形成的,主要适用于织布、编织、商标、服饰、线带和圣诞礼品领域。
如图3所示为本发明一种夜光膜材料的MH型示意图,MH型是采用0.15MM-1MM的夜光丝与15D-200D的尼龙丝或涤纶丝、人造丝等相互环绕而成,主要适用于编织、服饰、线带和圣诞礼品等领域。
如图4所示为本发明一种夜光膜材料的MHX型示意图,MHX型是采用0.15MM-0.5MM的夜光丝与15D-150D的尼龙丝和涤纶丝、人造丝等交并而制成,将人造丝、尼龙丝或者其中之一的两根围绕夜光丝绕动,成互相交织状态,主要适用于电脑绣花、服饰和圣诞礼品等领域。
如图5,图6所示为本发明一种夜光膜材料的MS和JB型示意图,MS和JB型是采用0.23MM-3MM的夜光丝与75D-3000D的各种线包覆而成,主要适用于织布、抽纱、绣品、编织、电脑绣花、商标、服饰、线带和圣诞礼品等领域。
最后应说明的是:以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案;因此,尽管本说明书参照上述的各个实施例对本发明已进行了详细的说明,但是,本领域的普通技术人员应当理解,仍然可以对本发明进行修改或等同替换;而一切不脱离发明的精神和范围的技术方案及其改进,其均应涵盖在本发明的权利要求范围当中。
Claims (2)
1.夜光膜材料,包括:PET薄膜、夜光粉、树脂组成,所述的PET薄膜的厚度为0.008MM-0.025MM之间,所述的夜光粉是经过纳米技术处理的,都是通过选用意大利或者德国优质品牌,所述的树脂主要是选用德国的。
2.根据权利要求1所述的一种夜光膜材料,其特征在于:其制作过程如下:首先将所述的夜光粉和树脂充分溶解,溶解完成后将其涂在PET薄膜上,然后将其在涂布机上进行烘烤,烘烤的温度设置在100℃-210℃之间,最后形成了夜光膜材料,再经过先进的机械和切割技术切割成0.15MM-5MM的宽度的丝,本发明的材料即完成。