Background technology:
What the cleaning of electronic circuit board was traditional in the surface mounting technology in electron trade is to adopt traditional halogenated hydrocarbon solvents such as freonll-11, trichloroethane, trieline, to have a cleansing power strong because of it, no flashing point, advantages such as the fast and retortable recovery of rate of drying and being widely used, but more there are many shortcomings in such ablution, to human body, environment be cleaned thing very big harm is all arranged.To human body: above-mentioned halogenated hydrocarbon solvent all has very big toxicity, and human body contacts or suck steam for a long time, causes liver, kidney, septicemia easily, cause dizziness, vomiting etc., under the effect of temperature and illumination, this kind solvent is decomposed to form height material phosgene easily, and carcinogenesis is arranged in addition.To environment: this types of solvents is difficult to biological degradation, and soil, water body are caused great harm, and they belong to the depletion of the ozone layer material.To being cleaned thing: the easy acidifying of halogenated hydrocarbon solvent, equipment and electronic circuit are produced corrosion, influence electric property, and the halohydrocarbon consistency is poor, most of rubber, plastics all there are swelling, corrosive nature, dissolving, distortion or embrittlement, its clean range is restricted, thereby can't satisfies the demand in market.
Summary of the invention:
Technical problem to be solved by this invention just is to overcome above-mentioned existing deficiency, provides a kind of electron surface to mount the environment protection water-based multifunction electronic ablution of industry.
For solving the problems of the technologies described above, the technical solution used in the present invention is: the formation raw material and the weight proportion of this environment protection water-based multifunction electronic ablution are:
Pure water 35-60 part;
Inhibiter 1-3 part;
Isomery alcohol ether phosphate 3-5 part;
Alkaline assistant 3-12 part;
Secondary alkyl sulfonate 7-12 part;
EO-PO multipolymer 3-8 part;
D-limonene 10-25 part;
Nonionic emulsifying agent 5-10 part.
In the technique scheme, the formation raw material and the weight proportion of described environment protection water-based multifunction electronic ablution are:
56 parts of pure water;
2.1 parts of inhibiter;
5 parts of isomery alcohol ether phosphates;
7 parts of alkaline assistants;
7 parts of secondary alkyl sulfonates;
3 parts of EO-PO multipolymers;
15 parts of D-limonene;
5 parts of nonionic emulsifying agents.
Or in the technique scheme, the formation raw material and the weight proportion of described environment protection water-based multifunction electronic ablution are:
46 parts of pure water;
3.1 parts of inhibiter;
3 parts of isomery alcohol ether phosphates;
7 parts of alkaline assistants;
10 parts of secondary alkyl sulfonates;
5 parts of EO-PO multipolymers;
20 parts of D-limonene;
6 parts of nonionic emulsifying agents.
In the technique scheme, described inhibiter is: one or more in Starso, 124 Triazole derivative, alkylolamide, the amino acid.
In the technique scheme, described isomery alcohol ether phosphate is C
6-C
10The fatty alcohol-ether phosphoric acid ester.
In the technique scheme, described alkaline assistant is: one or more in yellow soda ash, salt of wormwood, sodium hydroxide, potassium hydroxide, trolamine or the Yi Bingchunan.
In the technique scheme, described secondary alkyl sulfonate is: C
12-C
16Secondary alkylsulphonic acid amine or C
12-C
16Seconary Alkane Sulphonate Sodium.
In the technique scheme, described EO-PO multipolymer is the propylene glycol ethylene oxide-propylene oxide block copolymer, and its oxyethane contains 40%.
In the technique scheme, described nonionic emulsifying agent is C
10-C
13Aliphatic alcohol polyethenoxy 7 ethers, C
10-C
13A kind of in aliphatic alcohol polyethenoxy 10 ethers or two kinds.
The invention has the advantages that:
1, height concentrated product, only the dilution proportion that needs 5-10% can be brought into play good cleanup action in water;
2, adopt the environmental protection raw material, per os toxicity, skin contact, toxicity on inhalation are extremely low, to human body safety, are easy to biological degradation;
3, to being cleaned thing safety, can not produce corrosion to electronic circuit board, consistency is splendid, and the overwhelming majority's rubber, plastics are all had good consistency, can not cause swelling, corrosion etc., therefore can be widely used in the sanitising agent of electronic circuit board and five metals plastic cement;
4, can be used for soldering flux or remaining tin cream and other dirts that the normal temperature or the cleaning printed circuit board (PCBA) of heating are gone up remnants, also can be used for five metals or the dirt of plastic cement component heavy oil.
5, water-based concentrated product, Polyoxyethylene Lauryl Ether can keep the good electric property of PCBA, and is harmless, is to substitute the splendid selection of tradition to the very harmful ODSODS ablution of environment and human body.
Embodiment:
The present invention is further described below in conjunction with specific embodiment:
Embodiment one
Present embodiment one concrete raw material and weight are:
56 kilograms of pure water;
2 kilograms of Starsos;
0.1 kilogram in 124 Triazole derivative;
C
6-C
105 kilograms of fatty alcohol-ether phosphoric acid ester;
2 kilograms in potassium hydroxide;
5 kilograms of trolamines;
C
12-C
167 kilograms of Seconary Alkane Sulphonate Sodium;
3 kilograms of EO-PO multipolymers;
15 kilograms of D-limonene;
C
10-C
132 kilograms in aliphatic alcohol polyethenoxy 7 ethers;
C
10-C
133 kilograms in aliphatic alcohol polyethenoxy 10 ethers.
Embodiment two
Present embodiment two concrete raw materials and weight are:
46 kilograms of pure water;
2 kilograms of Starsos;
0.1 kilogram in 124 Triazole derivative;
1 kilogram of alkylolamide;
C
6-C
103 kilograms of fatty alcohol-ether phosphoric acid ester;
1 kilogram in potassium hydroxide;
6 kilograms of Yi Bingchunans;
C
12-C
1610 kilograms of Seconary Alkane Sulphonate Sodium;
5 kilograms of EO-PO multipolymers;
20 kilograms of D-limonene;
C
10-C
134 kilograms in aliphatic alcohol polyethenoxy 7 ethers;
C
10-C
132 kilograms in aliphatic alcohol polyethenoxy 10 ethers.
Certainly, the above only is several example of the present invention, be not to limit the scope of the present invention, all equivalences of doing according to the described structure of the present patent application claim, feature and principle change or modify, and all should be included in the present patent application claim.