CN102030558B - 一种混凝土保护材料及其制备方法 - Google Patents
一种混凝土保护材料及其制备方法 Download PDFInfo
- Publication number
- CN102030558B CN102030558B CN 201010553008 CN201010553008A CN102030558B CN 102030558 B CN102030558 B CN 102030558B CN 201010553008 CN201010553008 CN 201010553008 CN 201010553008 A CN201010553008 A CN 201010553008A CN 102030558 B CN102030558 B CN 102030558B
- Authority
- CN
- China
- Prior art keywords
- concrete protective
- agent
- concrete
- protective material
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明介绍了一种混凝土保护材料及其制备方法，该材料为质量组成为40%氯乙烯-乙烯基异丁基醚共聚物溶液50.0～55.0份、混凝土保护剂5.0～9.0份、溶剂10.0～15.0份、润湿分散剂0.2～0.5份、消泡剂0.1～0.3份、触变剂0.1～0.3份、颜填料20.0～25.0份的均匀分散体；制备方法是将原料依次混合、研磨、分装。本发明的材料具有良好的耐酸碱、耐盐雾、耐老化性，并可阻燃；对于水、氧气、氯气渗透率极低，耐紫外光稳定性优异；低温施工不受限制，漆膜层间互溶为一体，层间附着力好，重涂性良好；提供比单独使用混凝土保护剂或者单独使用防腐涂料更高的防腐性及耐久性,明显提高施工效率。
Description
技术领域
本发明涉及一种防腐涂料技术，特别是一种混凝土保护材料及其制备方法。
背景技术
众所周知，混凝土以其耐久性好、可塑性强、维修费用少的优点被广泛应用于道路、桥梁、码头、机场等建设工程领域，而其在使用过程受到强酸、强碱、氯离子等侵蚀性介质的渗透腐蚀，混凝土结出现开裂、脱落、膨胀变形等现象，严重影响了混凝土的使用性能和寿命。
目前，国内公知技术中混凝土保护材料比较多，且大多单独使用混凝土保护剂或者单独施工混凝土防腐涂料，当使用在混凝土混凝土强度、硬度不够或者腐蚀环境恶劣时，这些混凝土保护材料已经满足不了耐久性和耐腐蚀性要求。随着混凝土保护行业竞争日趋激烈，混凝土保护技术将会有更快的发展。
申请号为200910064673.2的中国专利公开的是一种海洋工程混凝土防腐涂料。该涂料以双酚A环氧树脂和胺类固化剂为基料，在冬季5℃以下无法使用且涂层的重涂效果也不尽理想，极大的限制了混凝土保护材料的施工。
申请号为200710189637.X的中国专利公开的是一种用于氯气环境下的长效防腐涂料。该涂料以高氯化聚乙烯树脂为基料，添加增塑剂来提高涂料的柔韧性，但增塑剂会迁移到涂层表面使漆膜变脆，影响了漆膜的耐久性。
发明内容
本发明所要解决的技术问题是提供一种混凝土保护材料及其制备方法，选用氯乙烯-乙烯基异丁基醚共聚物树脂为成膜物质，该树脂不含高毒性四氯化碳、不含易迁移增塑剂、具有良好的阻燃性、优异的耐氯离子渗透性，为混凝土表面提供良好的耐久性和耐腐蚀性要求；选用混凝土保护剂，该混凝土保护剂在混凝土保护材料施工时渗入混凝土内部与碱性物质发生化学反应，在孔隙以及毛细孔隙里产生致密结晶体，从而密封混凝土，增强了新旧混凝土的强度和硬度，为混凝土提供良好的耐腐蚀性和耐久性；选用氯乙烯-乙烯基异丁基醚共聚物树脂和混凝土增强剂的合理搭配，提供比单独使用混凝土保护剂或者单独使用防腐涂料更高的防腐性及耐久性，解决目前混凝土保护材料低温不能施工、维护成本高、维护困难以及阻燃性不佳等问题。
为了实现解决上述技术问题的目的，本发明采用了如下技术方案：
本发明的一种混凝土保护材料，该材料为质量组成为40%氯乙烯-乙烯基异丁基醚共聚物树脂溶液50.0～55.0份、混凝土增强剂5.0～9.0份、溶剂10.0～15.0份、润湿分散剂0.2～0.5份、消泡剂0.1～0.3份、触变剂0.1～0.3份、颜料和填料共20.0～25.0份的均匀分散体。
所述的40%氯乙烯-乙烯基异丁基醚共聚物树脂溶液为MP-15、MP-25 、MP-45、MP-60的任意一种。
所述的混凝土保护剂是DZ520混凝土保护剂、BD-002混凝土保护剂、SY-HG混凝土保护剂、ZWL-A混凝土保护剂中的任意一种。
所述的溶剂是二甲苯、醋酸丁酯、环己酮中的任意一种。
所述的润湿分散剂为中EFKA5065、EFKA4010中的任意一种。
所述消泡剂为徳谦6800、EFKA2035、EFKA2720、Tego-F.N中的任一种。
所述的触变剂是有机膨润土、氢化蓖麻油、气相二氧化硅中的任意一种。
所述的颜料为钛白粉、炭黑、酞青蓝、中铬黄、柠檬黄中的任意一种或是其中多种组合物。
所述的填料为滑石粉、云母粉、石英粉、沉淀硫酸钡、氧化锌中的任意一种或是其中多种组合物。
这些技术方案也可以互相组合或者结合，从而达到更好的技术效果。
本发明的混凝土保护材料的制备方法，具体操作步骤如下：
1）称取所需量的40%氯乙烯-乙烯基异丁基醚共聚物溶液、混凝土保护剂、润湿分散剂加入分散罐中，低速分散5-10分钟，得到混合物Ⅰ；
2）称取定量颜料和填料加入混合物Ⅰ，再高速分散15-20分钟，得到混合物Ⅱ；
3）称取定量的触变剂、消泡剂加入到混合物Ⅱ中，高速分散15-20分钟，分散完毕后，进入砂磨机研磨至细度≤40um,用溶剂调整粘度合格后80目筛网过滤即得该材料，按包装规格分装即可。
所述的低速分散，速度范围是300-500 r/min；所述的中速分散，速度范围是600-900 r/min；所述的高速分散，速度范围是1000-1500 r/min。
本发明材料的主要技术指标如表1所示。
表1
通过采用上述技术方案，本发明的混凝土保护材料具有以下的优异效果：
1、具有良好的耐强酸碱、耐盐雾、耐老化性，并具有一定的阻燃性；
2、对于水、氧气、氯气渗透率极低，具有优异的耐紫外光稳定性；
3、低温施工不受限制，具有优异的施工性能；
4、漆膜层间互溶为一体，有优异的层间附着力，重涂性良好；
5、施工1～2道，不仅增加混凝土的强度和硬度，还可满足混凝土内外防腐要求，明显提高施工效率；
6、满足当前国家的环保要求，可应用于各种混凝土防腐领域。
具体实施方式
下面结合具体实施例对本发明加以具体说明，但不局限于此特定实施例。实施例中的配比按重量份数计算。
实施例1
本发明的一种混凝土保护材料，具体配比如下：
40%MP-15树脂液 50.0
DZ520混凝土保护剂 5.0
二甲苯 10.0
EFKA-4010 0.2
有机膨润土 0.3
钛白粉 5.0
云母粉 5.0
石英粉 10.0
徳谦6800 0.3
称取所需量的40%MP-15树脂液、混凝土保护剂、润湿分散剂加入分散罐中，低速分散5-10分钟，得到混合物Ⅰ；然后称取定量的颜料和填料加入混合物Ⅰ中，再高速分散15-20分钟，得到混合物Ⅱ；再称取定量的触变剂、消泡剂加入到混合物Ⅱ中，高速分散20分钟，分散完毕后，进入砂磨机研磨至细度≤40um,用溶剂调整粘度合格后80目筛网过滤即得该材料，按包装规格分装即可。
所得材料性能如表2。
实施例2
配比如下，其他与实施例1相同。
40%MP-25 树脂液 55.0
BD-002混凝土保护剂 9.0
二甲苯 11.7
EFKA-5065 0.5
氢化蓖麻油 0.1
钛白粉 6.0
炭黑 0.2
沉淀硫酸钡 16.0
氧化锌 1.0
EFKA-2035 0.2
所得材料性能如表2。
实施例3
配比如下，其他与实施例1相同。
40%MP-45树脂液 52.5
SY-HG混凝土保护剂 6.0
二甲苯 13.0
EFKA-4010 0.3
白炭黑 0.2
酞青蓝 1.0
中铬黄 2.0
柠檬黄 3.0
滑石粉 9.0
石英粉 10.0
Tego-F N 0.1
所得材料性能如表2。
实施例4
配比如下，其他与实施例1相同。
40%MP-60树脂液 53.8
ZWL—A混凝土保护剂 7.4
二甲苯 15.0
EFKA-5065 0.4
有机膨润土 0.25
钛白粉 4.0
中铬黄 8.0
云母粉 9.0
氧化锌 1.2
EFKA-2720 0.15
所得材料性能如表2。
表2 实施例1-4材料性能。
Claims (2)
1.一种混凝土保护材料，其特征是：该材料为质量组成为40%氯乙烯-乙烯基异丁基醚共聚物树脂溶液50.0～55.0份、混凝土保护剂5.0～9.0份、溶剂10.0～15.0份、润湿分散剂0.2～0.5份、消泡剂0.1～0.3份、触变剂0.1～0.3份、颜料和填料共20.0～25.0份的均匀分散体。
2.根据权利要求1所述混凝土保护材料，其特征是：所述的40%氯乙烯-乙烯基异丁基醚共聚物溶液为MP-15、MP-25 、MP-45、MP-60的任意一种。
3.根据权利要求1所述混凝土保护材料，其特征是：所述的混凝土保护剂是DZ520混凝土保护剂、BD-002混凝土保护剂、SY-HG混凝土保护剂、ZWL—A混凝土保护剂中的任意一种。
4.根据权利要求1所述混凝土保护材料，其特征是：所述的溶剂是二甲苯、醋酸丁酯、环己酮中的任意一种。
5.根据权利要求1所述混凝土保护材料，其特征是：所述的润湿分散剂为中EFKA5065、EFKA4010中的任意一种。
6.根据权利要求1所述混凝土保护材料，其特征是：所述的触变剂是有机膨润土、氢化蓖麻油、气相二氧化硅中的任意一种。
7.根据权利要求1所述混凝土保护材料，其特征是：所述的颜料为钛白粉、炭黑、酞青蓝、中铬黄、柠檬黄中的任意一种或是多种组合物。
8.根据权利要求1所述混凝土保护材料，其特征是：所述的填料为滑石粉、云母粉、石英粉、沉淀硫酸钡、氧化锌中的任意一种或是多种组合物。
9.一种权利要求1所述混凝土保护材料的制备方法，其特征是：具体操作步骤如下：
1）称取所需量的40%氯乙烯-乙烯基异丁基醚共聚物溶液、混凝土保护剂、润湿分散剂加入分散罐中，低速分散5-10分钟，得到混合物Ⅰ；
2）称取定量的颜料和填料加入混合物Ⅰ中，再高速分散15-20分钟，得到混合物Ⅱ；
3）称取定量的触变剂、消泡剂加入到混合物Ⅱ中，高速分散15-20分钟，分散完毕后，进入砂磨机研磨至细度≤40um，用溶剂调整粘度合格后80目筛网过滤即得该材料，按包装规格分装即可。