CN102020957B - 木材用环保无毒胶粘剂及其制备方法 - Google Patents

木材用环保无毒胶粘剂及其制备方法 Download PDF

Info

Publication number
CN102020957B
CN102020957B CN 200910092487 CN200910092487A CN102020957B CN 102020957 B CN102020957 B CN 102020957B CN 200910092487 CN200910092487 CN 200910092487 CN 200910092487 A CN200910092487 A CN 200910092487A CN 102020957 B CN102020957 B CN 102020957B
Authority
CN
China
Prior art keywords
adhesive
preparation
percent
tannin
tackiness agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 200910092487
Other languages
English (en)
Other versions
CN102020957A (zh
Inventor
冯流
陈大地
任鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing University of Chemical Technology
Original Assignee
Beijing University of Chemical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing University of Chemical Technology filed Critical Beijing University of Chemical Technology
Priority to CN 200910092487 priority Critical patent/CN102020957B/zh
Publication of CN102020957A publication Critical patent/CN102020957A/zh
Application granted granted Critical
Publication of CN102020957B publication Critical patent/CN102020957B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种环保无毒无甲醛木材胶粘剂及其制备方法，该胶粘剂所包括的原料重量配比为：软化水70％-80％；落叶松栲胶2％-20％；聚乙烯亚胺2％-20％；氢氧化钠1％-2％。本发明胶粘剂的制备方法简单快捷、制造成本低、胶黏性能强、使用方便，而且本发明制备的胶粘剂没有使用甲醛作为原料，所以不会释放出游离的甲醛，不会产生毒性而危害人类健康和环境。本发明解决了“醛类”胶粘剂人造板带来的室内空气中的甲醛污染等问题。

Description

木材用环保无毒胶粘剂及其制备方法
技术领域
本发明涉及一种胶粘剂及其制备，特别是一种家具木制品的专用胶粘剂及其制备工艺。
背景技术
21世纪以来，胶粘剂和粘接技术已经显示出无比的生机和活力，其重要性与日俱增，实用性令人瞩目，应用日益广泛。脲醛树脂胶黏剂是我国木材工业用量最大的合成树脂胶黏剂，占木材加工业胶黏剂总消耗量的60％多，占人造板用胶量的90％左右。随着人民生活水平的提高，居住条件的改善，大量的木材加工制品应用于室内装修，该类制品在使用过程中不断地释放出甲醛，污染环境，损坏人们的身体健康。石油资源的日益短缺，以及人们环保意识的不断增强，人类社会必须走可持续发展的道路。因此，寻找传统脲醛树脂胶粘剂的替代品已经成为了急需解决的问题。
单宁是一种含有多元酚基和羧基的有机物，它不是单一的化合物，而是类似化合物的混合物，主要来源于木材加工中树皮下脚料和单宁含量较高的植物，如金合欢树、黑荆树、落叶松等。单宁可分为两大类：水解类单宁和凝缩类单宁，又名缩合单宁，其中具有应用价值的为缩合单宁。多聚凝缩类单宁中含有大量儿茶酚，其环结构极易氧化形成邻苯醌。而邻苯醌及其加成产物均能与聚乙烯亚胺的氨基反应形成四种不同的吸附键。此外，邻苯醌与聚乙烯亚胺的氨基，以及它们与木材成分中的羟基都能形成较强的氢键，这些反应均有利于提高胶粘剂的胶合强度和耐水性。本发明利用缩合单宁和聚乙烯亚胺的这个特性，以聚乙烯亚胺和天然树皮中提取的落叶松栲胶单宁为原料，制备出环保无毒的胶粘剂，它不使用甲醛为原料，所以无甲醛释放，同时保持了胶粘剂较好的粘接强度和耐水性。
发明内容
本发明的目的是提供一种环保、无毒、无甲醛释放的胶粘剂及其制备方法。
单宁-聚乙烯亚胺胶粘剂以下述技术方案实现：
先将落叶松栲胶单宁溶于水中，用1mol/L的氢氧化钠溶液调节pH值到7.0。将溶于水的落叶松栲胶单宁缓慢加入聚乙烯亚胺溶液中，在一定温度下用电动搅拌器搅拌一定时间后，制得胶粘剂。
落叶松栲胶与聚乙烯亚胺的干固体质量比为1∶2。
聚乙烯亚胺分子量为10000～20000，质量分数为35％。
胶粘剂总固体含量为10～30％。
反应温度为15～60℃。
搅拌时间为10～60分钟。
本发明特点：本发明提供一种木材用环保胶粘剂的制备方法。该方法与以往方法相比具有粘接强度强、制备工艺简单、易于制备、无甲醛释放、方法简便可行、耐水性好、成本低等特点。
具体实施方式
以下结合具体实施方式对本发明作进一步详细说明：
实施例1
将13.3g落叶松栲胶单宁溶于123mL水中，用1mol/L的氢氧化钠溶液调节落叶松栲胶溶液pH值到7.0。称取76.3g质量分数为35％的聚乙烯亚胺溶液。将落叶松单宁溶液缓慢加入聚乙烯亚胺溶液中，恒温20℃，并用电动搅拌器搅拌15分钟，制得胶粘剂。
实施例2
将13.3g落叶松栲胶单宁溶于123mL水中，用1mol/L的氢氧化钠溶液调节落叶松栲胶溶液pH值到7.0。称取76.3g质量分数为35％的聚乙烯亚胺溶液。将落叶松单宁溶液缓慢加入聚乙烯亚胺溶液中，恒温20℃，并用电动搅拌器搅拌20分钟，制得胶粘剂。
实施例3
将13.3g落叶松栲胶单宁溶于123mL水中，用1mol/L的氢氧化钠溶液调节落叶松栲胶溶液pH值到7.0。称取76.3g质量分数为35％的聚乙烯亚胺溶液。将落叶松单宁溶液缓慢加入聚乙烯亚胺溶液中，恒温25℃，并用电动搅拌器搅拌15分钟，制得胶粘剂。
实施例4
将16.7g落叶松栲胶单宁溶于88mL水中，用1mol/L的氢氧化钠溶液调节落叶松栲胶溶液pH值到7.0。称取95.4g质量分数为35％的聚乙烯亚胺溶液。将落叶松单宁溶液缓慢加入聚乙烯亚胺溶液中，恒温25℃，并用电动搅拌器搅拌15分钟，制得胶粘剂。

Claims (1)

1.一种木材用胶粘剂的制备方法，其特征在于：先将落叶松栲胶单宁溶于水中，用1mol/L的氢氧化钠溶液调节pH值到7.0，将溶于水的落叶松栲胶单宁缓慢加入聚乙烯亚胺溶液中，在15～60℃的温度下用电动搅拌器搅拌10～60分钟，制得胶粘剂；其中，落叶松栲胶单宁与聚乙烯亚胺的干固体质量比为1∶2；聚乙烯亚胺分子量为10000～20000，聚乙烯亚胺溶液质量分数为35％；胶粘剂总固体含量为10％～30％。
CN 200910092487 2009-09-16 2009-09-16 木材用环保无毒胶粘剂及其制备方法 Expired - Fee Related CN102020957B (zh)