CN102020461A - High-temperature bright red ceramic and preparation method thereof - Google Patents
High-temperature bright red ceramic and preparation method thereof Download PDFInfo
- Publication number
- CN102020461A CN102020461A CN2010105138912A CN201010513891A CN102020461A CN 102020461 A CN102020461 A CN 102020461A CN 2010105138912 A CN2010105138912 A CN 2010105138912A CN 201010513891 A CN201010513891 A CN 201010513891A CN 102020461 A CN102020461 A CN 102020461A
- Authority
- CN
- China
- Prior art keywords
- red
- glaze
- bright red
- biscuit
- cao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-temperature bright red ceramic and a preparation method thereof. The preparation method is as follows: preparing a ceramic blank body according to the conventional technique, calcining the ceramic blank body into a bisque, applying bright red glaze on the bisque, preparing a red blank by calcining, then applying transparent glaze on the red blank, and calcining to form the bright red ceramic. The ceramic blank body consists of the following components: SiO2, Al2O3, CaO, MgO, K2O, Na2O, Fe2O3, TiO, P2O5 and BaO; the bright red glaze consists of the following components: SiO2, Al2O3, CaO, MgO, K2O, Na2O, ZnO, BaO, Ba2O3, Fe2O3 and TiO2; and the transparent glaze comprises the following components: SiO2, Al2O3, CaO, MgO, K2O, Na2O, ZnO, Ba2O3, Fe2O3 and TiO2. The high-temperature bright red ceramic provided by the invention has unique components; secondary glaze firing is adopted, and the color-emitting red glaze is positioned at the bottom layer of a transparent glaze; and the high-temperature bright red ceramic has the advantages of stable color emitting, high glossiness, wear resistance, bright color formation, high glossiness, and no dissolving out of lead and cadmium, and can be used for manufacturing art ceramics and ceramics for daily use.
Description
Technical field the invention belongs to the ceramic production technology field, relates to a kind of high temperature scarlet pottery and preparation method thereof.
Background technology red glaze porcelain is exactly famous and precious artwork since ancient times, the Lang Hong of prior art, hold a memorial ceremony for red, chicken is blood red etc. all is famous and precious red glaze, but these red glaze color developments are dark partially, are not pure large reds.The red glaze product has been arranged on the market in recent years, but glaze smoothness degree is not high, color development is unstable and not bright-coloured, and the lead release height.Pure high temperature scarlet glaze pottery is one of difficult problem of Production of Ceramics always.
Summary of the invention the objective of the invention is to solve prior art and has that glaze smoothness degree is not high, color development is unstable and technical problem not bright-coloured, that lead release is high, provide stable and bright-coloured high temperature scarlet pottery of a kind of color development and preparation method thereof, to overcome the deficiencies in the prior art.
To achieve these goals, high temperature scarlet pottery of the present invention, the prepared ceramic body is made biscuit through calcining more routinely, imposes bright red glaze on biscuit, makes red base through calcining again, executes marzacotto then and calcine and form on red base; Its main points are:
Described ceramic body is made up of by the quality proportioning following material composition:
SiO
2?39.65 Al
2O
3?12.80 CaO?23.90 MgO?0.56 K
2O?1.77
Na
2O?0.54 Fe
2O
3?0.23 TiO
2?0.08 P
2O
5?20.21 BaO?0.02
Described bright red glaze is made up of by the quality proportioning following material composition:
SiO
2?69.35 Al
2O
3?11.61 CaO?9.62 MgO?0.81 K
2O?4.26 Na
2O?0.92
ZnO?1.12 BaO?0.80 B
2O
3?0.86 Fe
2O
3?0.16 TiO
2?0.13
Described marzacotto is made up of by the quality proportioning following material composition:
SiO
2?57.83 Al
2O
3?12.52 CaO?10.69 MgO?1.03 K
2O?2.32
Na
2O?5.42?ZnO?5.21 B
2O
3?4.12 Fe
2O
3?0.31 TiO
2?0.12
The preparation method of high temperature scarlet pottery of the present invention, its main points are undertaken by following processing step:
1), prepares bright red glaze slip: above-mentioned each component of bright red glaze is mixed, prepare glaze slip with the ball milling wet method, become basic powdered frit in 24 hours 200 ℃ of oven dry, more basic powdered frit, red stain and the water mass ratio by 1: 0.3: 0.9 is mixed, make red glaze slip;
2), prepare transparent glaze slip: above-mentioned marzacotto and the water mass ratio by 1: 1 is mixed, become transparent glaze slip with the ball milling wet grinding;
3), burning till of biscuit: ceramic body 1280～1310 ℃ of calcinings, is incubated 0.5 hour, and firing atmosphere is an oxydizing flame;
4), biscuit glazing: the biscuit surface after burning till sprays bright red glaze slip, and the glaze layer thickness is 0.15～0.20mm;
5), burning till of red base: the glazing biscuit 1260～1280 ℃ of calcinings, is incubated 0.5 hour, and firing atmosphere is an oxydizing flame;
6), red base glazing: the red base surface after burning till sprays transparent glaze slip, glaze layer thickness 0.12～0.15mm;
7), burning till of high temperature scarlet pottery: the red base of glazing is burnt till at 1150 ℃, be incubated 15 minutes, firing atmosphere is an oxydizing flame;
Described red stain is made up of by the quality proportioning following material composition:
ZrO
2?38.19 SO
2?6.62 CdO?20.28 SeO
2?7.8 SiO
2?27.11。
The invention provides stable and bright-coloured high temperature scarlet pottery of a kind of color development and preparation method thereof.This method not only can be produced art pottery product, but productive life porcelain also as tableware, tea set and coffee service, coffee set etc., has solved prior art and had that glaze smoothness degree is not high, color development is unstable and technical problem not bright-coloured, that lead release is high.
Embodiment high temperature scarlet pottery of the present invention at first prepares ceramic body, makes biscuit through calcining, imposes bright red glaze on biscuit, makes red base through calcining again, executes marzacotto then and calcine and form on red base;
It is formulated that ceramic body is pressed mass ratio by following compositions:
SiO
2?39.65 Al
2O
3?12.80 CaO?23.90 MgO?0.56 K
2O?1.77
Na
2O?0.54 Fe
2O
3?0.23 TiO
2?0.08 P
2O
5?20.21 BaO?0.02
It is formulated that bright red glaze is pressed mass ratio by following compositions:
SiO
2?69.35 Al
2O
3?11.61 CaO?9.62 MgO?0.81 K
2O?4.26 Na
2O?0.92
ZnO?1.12 BaO?0.80 B
2O
3?0.86 Fe
2O
3?0.16 TiO
2?0.13
It is formulated that marzacotto is pressed mass ratio by following compositions:
SiO
2?57.83 Al
2O
3?12.52 CaO?10.69 MgO?1.03 K
2O?2.32
Na
2O?5.42 ZnO?5.21 B
2O
3?4.12 Fe
2O
3?0.31 TiO
2?0.12
The preparation method of high temperature scarlet pottery of the present invention, undertaken by following processing step:
1), prepares bright red glaze slip: above-mentioned each component of bright red glaze is mixed, prepare glaze slip with the ball milling wet method, became basic powdered frit in 24 hours 200 ℃ of oven dry, basic powdered frit being added red stain and water mixes by 1: 0.3: 0.9 mass ratio again, make red glaze slip, it is formulated that red stain is pressed mass ratio by following compositions: ZrO
238.19 SO
26.62 CdO 20.28 SeO
27.8 SiO
227.11;
2), prepare transparent glaze slip: above-mentioned marzacotto and the water mass ratio by 1: 1 is mixed, become transparent glaze slip with the ball milling wet grinding;
3), burning till of biscuit: ceramic body 1300 ℃ of calcinings, is incubated 0.5 hour, and firing atmosphere is an oxydizing flame;
4), biscuit glazing: the biscuit surface after burning till sprays bright red glaze slip, and the glaze layer thickness is 0.18mm;
5), burning till of red base: the glazing biscuit 1270 ℃ of calcinings, is incubated 0.5 hour, and firing atmosphere is an oxydizing flame;
6), red base glazing: the red base surface after burning till sprays transparent glaze slip, glaze layer thickness 0.14mm;
7), burning till of high temperature scarlet pottery: the red base of glazing is burnt till at 1150 ℃, be incubated 15 minutes, firing atmosphere is an oxydizing flame.
Make the high temperature scarlet pottery by above processing step.
Main innovation characteristics of the present invention:
1, component uniqueness. Newly body recipe, red glaze prescription and the clear frit prescription of development have been used;
2, adopt the method for secondary glaze firing, the red glaze of color development is in the bottom of clear frit, thereby color development is stable, glossiness is high, wear-resistant;
3, the level and smooth light of product glaze, quality is bright-coloured, glossiness is high, the lead and cadmium free stripping, not only is used for the production art pottery, can also make life and using porcelain, has significantly promoted value-added content of product.
Claims (3)
1. high temperature scarlet pottery, biscuit is made in prepared ceramic body, calcining routinely, imposes bright red glaze on biscuit, makes red base through calcining again, executes marzacotto then and calcine and form on red base; It is characterized in that:
Described ceramic body is made up of by the quality proportioning following material composition:
SiO
2?39.65 Al
2O
3?12.80 CaO?23.90 MgO?0.56 K
2O?1.77
Na
2O?0.54 Fe
2O
3?0.23 TiO
2?0.08 P
2O
5?20.21 BaO?0.02
Described bright red glaze is made up of by the quality proportioning following material composition:
SiO
2?69.35 Al
2O
3?11.61 CaO?9.62 MgO?0.81 K
2O?4.26 Na
2O?0.92
ZnO?1.12 BaO?0.80 B
2O
3?0.86 Fe
2O
3?0.16 TiO
2?0.13
Described marzacotto is made up of by the quality proportioning following material composition:
SiO
2?57.83 Al
2O
3?12.52 CaO?10.69 MgO?1.03 K
2O?2.32
Na
2O?5.42 ZnO?5.21 B
2O
3?4.12 Fe
2O
3?0.31 TiO
2?0.12。
2. the preparation method of high temperature scarlet pottery according to claim 1 is characterized in that being undertaken by following processing step:
1), prepares bright red glaze slip: above-mentioned each component of bright red glaze is mixed, prepare glaze slip with the ball milling wet method, become basic powdered frit in 24 hours 200 ℃ of oven dry, more basic powdered frit, red stain and the water mass ratio by 1: 0.3: 0.9 is mixed, make red glaze slip;
2), prepare transparent glaze slip: above-mentioned marzacotto and the water mass ratio by 1: 1 is mixed, become transparent glaze slip with the ball milling wet grinding;
3), burning till of biscuit: ceramic body 1280～1310 ℃ of calcinings, is incubated 0.5 hour, and firing atmosphere is an oxydizing flame;
4), biscuit glazing: the biscuit surface after burning till sprays bright red glaze slip, and the glaze layer thickness is 0.15～0.20mm;
5), burning till of red base: the glazing biscuit 1260～1280 ℃ of calcinings, is incubated 0.5 hour, and firing atmosphere is an oxydizing flame;
6), red base glazing: the red base surface after burning till sprays transparent glaze slip, glaze layer thickness 0.12～0.15mm;
7), burning till of high temperature scarlet pottery: the red base of glazing is burnt till at 1150 ℃, be incubated 15 minutes, firing atmosphere is an oxydizing flame.
3. the preparation method of high temperature scarlet pottery according to claim 2 is characterized in that described red stain is made up of by the quality proportioning following material composition:
ZrO
2?38.19 SO
2?6.62 CdO?20.28 SeO
2?7.8 SiO
2?27.11。