CN102000893A - 一种led晶体微焊共晶方法 - Google Patents

一种led晶体微焊共晶方法 Download PDF

Info

Publication number
CN102000893A
CN102000893A CN 201010523777 CN201010523777A CN102000893A CN 102000893 A CN102000893 A CN 102000893A CN 201010523777 CN201010523777 CN 201010523777 CN 201010523777 A CN201010523777 A CN 201010523777A CN 102000893 A CN102000893 A CN 102000893A
Authority
CN
China
Prior art keywords
eutectic
led crystal
heating
microbonding
scolder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010523777
Other languages
English (en)
Other versions
CN102000893B (zh
Inventor
李启智
谭耀武
詹勋县
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUIZHOU CHI TAT OPTOELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
HUIZHOU CHI TAT OPTOELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUIZHOU CHI TAT OPTOELECTRONIC TECHNOLOGY Co Ltd filed Critical HUIZHOU CHI TAT OPTOELECTRONIC TECHNOLOGY Co Ltd
Priority to CN 201010523777 priority Critical patent/CN102000893B/zh
Publication of CN102000893A publication Critical patent/CN102000893A/zh
Application granted granted Critical
Publication of CN102000893B publication Critical patent/CN102000893B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种LED晶体微焊共晶方法,该方法步骤依次焊料涂布、助焊剂清除、真空蒸镀金保护层、共晶。与现有技术相比,采用本发明方法生产的LED灯具具有如下优点:1.具有高导电、高导热性能;2.设置了保护层,具有较高的抗氧化性能;3.具有较高的抗热冲击性;4.焊料渗透性(湿润性)良好;5.便于采用自动化设备作业,工作效率高,无需专用设备对成品进行检测。

Description

一种LED晶体微焊共晶方法
技术领域
本发明属于LED制作技术领域,具体地说是一种LED晶体微焊共晶方法。
背景技术
现有的LED晶体共晶过程中,一般是使用约3um~25um的金锡钎焊片,然后加热至300摄氏度使金锡合金融化将LED晶体焊接于固定支架上。另一方法是使用有助焊剂的锡金焊膏直接加热焊接晶片。实际使用中,该两种方法存在如下缺点:1.因LED晶体与支架接触表面粗糙度不一致,间接接触面积太少,在加热时也容易造成锡金氧化,形成假焊,造成导热不良;2.使用锡金焊膏时,助焊剂涂布不均匀或者助焊剂没有挥发赶紧残留于支架表面,也会形成假焊或导热不良;3.LED晶体固定后无法用普通显微镜检测芯片与之间间是否紧密焊接,只能用价格昂贵的X光设备用非破坏的方式检测,检测非常不便。
发明内容
本发明所要解决的技术问题是提供一种导热性能好、抗氧化性高的LED晶体微焊共晶方法。
为解决上述技术问题,本发明采用以下技术方案实现:
一种LED晶体微焊共晶方法,该方法步骤为:
1)、焊料涂布,将膏状锡金焊料涂布于固定支架上用于固定LED晶体位置,并通过助焊剂加热使焊料融化填充于支架LED晶体共晶位置上;
2)、助焊剂清除,在加热状态下,用纯水或皂化剂清洗清除助焊剂;
3)、镀保护层,在加热状态下,在氮气或氮氢混合气体或真空环境中在的焊料上镀金保护层。
其中,所述的保护层为金镀层,厚度约为0.1um~0.3um。
其中,所述的固定支架材料为氧化铝或硅或氮化铝或氮化硅或碳化硅。
其中,加热的方式为直接加热或超声波加热或点焊方式加热,加热温度为300±10摄氏度。
其中,加热时为氮气或氮氢混合气体或真空环境。
与现有技术相比,采用本发明方法生产的LED灯具具有如下优点:
1.具有高导电、高导热性能;
2.设置了保护层,具有较高的抗氧化性能;
3.具有较高的抗热冲击性;
4.焊料渗透性(湿润性)良好;
5.便于采用自动化设备作业,工作效率高,无需专用设备对成品进行检测。
具体实施方式
为了便于本领域技术人员的理解,下面将结合具体实施例对本发明结构原理作进一步详细描叙:
本发明实施例揭示的LED晶体微焊共晶方法采用如下步骤实现:
首先,焊料涂布,将膏状锡金焊料涂布于固定支架上用于固定LED晶体位置,并通过助焊剂加热至300±10摄氏度使焊料融化填充于支架LED晶体共晶位置;然后,在该加热状态下实施助焊剂清除,采用纯水或皂化剂清洗清除助焊剂,将助焊剂从融化的焊料上清除掉;最后镀保护层,同样在该加热状态下,在氮气或氮氢混合气体或真空环境中在融化的焊料上镀保护层,保护焊接部位不会直接暴露于外界空气中氧化。共晶时,再使用超声波或直接电加热微焊晶片。
本实施例中,保护层为金。
本实施例中,固定支架材料为氧化铝。此外,该固定支架材料也可以为氧化铝或硅或氮化铝或氮化硅。
本实施例中,加热的方式为直接家人。此外,该加热方式也可以为超声波加热或点焊方式加热。
本实施例中,加热时为氮气环境。此外,也可以为氮氢混合气体或真空环境。
本发明保证了LED晶体热量高效、迅速地传导散失,减少对LED晶体的损害,延长LED晶体的使用寿命。在本公司采用自动化设备批量实验来看,合格率已经可稳定在98%以上。
以上所述实施例仅表达了本发明的实施方式,其描述较为具体和详细,但并不能因此而理解为对本发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进。因此,本发明专利的保护范围应以所附权利要求为准。

Claims (5)

1.一种LED晶体微焊共晶方法,其特征在于,该方法步骤为:
1)、焊料涂布,将膏状锡金焊料涂布于固定支架上用于固定LED晶体位置,并通过助焊剂加热使焊料融化填充于支架LED共晶位置上;
2)、助焊剂清除,在加热状态下,用纯水或皂化剂清洗清除助焊剂;
3)、镀保护层,在加热状态下,在氮气或氮氢混合气体或真空环境中在融化的焊料上镀保护层;
4)、加热方法,程序。
2.根据权利要求1所述的LED晶体微焊共晶方法,其特征在于:所述的保护层为金。
3.根据权利要求1所述的LED晶体微焊共晶方法,其特征在于:所述的固定支架材料为氧化铝或硅或氮化铝或氮化硅。
4.根据权利要求1所述的LED晶体微焊共晶方法,其特征在于:加热的方式为直接加热或超声波加热或点焊方式加热,加热温度为300±10摄氏度。
5.根据权利要求1所述的LED晶体微焊共晶方法,其特征在于:加热时为氮气或氮氢混合气体或真空环境。
CN 201010523777 2010-10-25 2010-10-25 一种led晶体微焊共晶方法 Expired - Fee Related CN102000893B (zh)