CN101987789A - 一种相变储能保温调温建筑砂浆 - Google Patents

一种相变储能保温调温建筑砂浆 Download PDF

Info

Publication number
CN101987789A
CN101987789A CN2009101574708A CN200910157470A CN101987789A CN 101987789 A CN101987789 A CN 101987789A CN 2009101574708 A CN2009101574708 A CN 2009101574708A CN 200910157470 A CN200910157470 A CN 200910157470A CN 101987789 A CN101987789 A CN 101987789A
Authority
CN
China
Prior art keywords
parts
phase
agent
change accumulation
building mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009101574708A
Other languages
English (en)
Inventor
张世忠
张世永
张奕
张旭
Original Assignee
张世忠
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张世忠 filed Critical 张世忠
Priority to CN2009101574708A priority Critical patent/CN101987789A/zh
Publication of CN101987789A publication Critical patent/CN101987789A/zh
Pending legal-status Critical Current

Abstract

一种相变储能保温调温建筑砂浆，主要成分为：相变储能细骨料、粘结剂、发泡剂、防水剂、保水剂、增强防裂剂、超细填料等组成。相变储能保温调温建筑砂浆突破传统保温材料单一热阻性能，通过二元相变原理，可以吸收和释放热量，相变潜热值大，具有较高蓄热密度，蓄、放热过程近似等温的特点，在外部环境温度变化的情况下相对于普通材料具有优异的调温恒温效果，可以大幅度降低室内温度的波动，提高人体的舒适度，同时也具有显著的节能作用。

Description

一种相变储能保温调温建筑砂浆
技术领域
本发明涉及节能环保新材料技术领域，尤其涉及一种相变储能保温调温建筑砂浆。
背景技术
随着社会经济的发展和生活水平的提高，人们对室内环境舒适度的要求也越来越高，空调能耗随之大幅度增高，造成能源消耗过快、环境污染增加、电网负荷峰谷差过大、峰负荷时电力供应严重不足等问题。世界各国越来越重视节能环保工作，我国制定颁布了一系列节能环保政策，为节能环保新材料研制提供支持。传统保温材料只具有单一热阻性能，没有储能调温功能。由于相变材料在其形态的改变过程中具有吸收或释放热能的性能，被建筑节能、新能源利用、环境保护等领域广泛应用。相变储能保温调温建筑砂浆利用相变调温机理，通过储能介质的相态变化实现对热能储存和释放，从而改善室内热循环质量。当环境温度低于一定值时，相变材料由液态凝结为固态，释放热量；当环境温度高于一定值时，相变材料由固态熔化为液态，吸收热量，使室温相对平衡。相变材料可收集多余热量，适时平稳释放，梯度变化小，有效降低损耗量，室温可趋于稳定。相变储能保温调温建筑砂浆利用相变调温机理，可使电负荷“削峰平谷”，充分利用低谷电价，降低住户用能成本，减少能源浪费。相变储能保温调温建筑砂浆利用相变调温机理，对建筑分户采暖，具有广泛推动作用，特别是对首层、顶层、边角处居住环境的室温，夏季隔热、冬季保温均可起到平衡作用。在新楼装饰和旧楼改造中，相变储能保温调温建筑砂浆能够克服墙面裂缝、结露、发霉、起皮等先天不足弊病。相变储能保温调温建筑砂浆具有可观的社会效益和经济效益。
发明内容
本发明要解决的技术问题在于，提供一种能够根据环境温度的变化吸收或释放热量、自动调节室内温度、提高居住舒适度、健康、环保、节能的相变储能保温调温建筑砂浆。
具体实施方式
本发明一种相变储能保温调温建筑砂浆各组分的重量配比为：相变储能细骨料选用闭孔膨胀珍珠岩400份、松香50份、石蜡50份融化吸附混合均匀制得；粘结剂氯氧镁水泥选用无水氯化镁100份、氧化镁150份混合均匀制得；发泡剂选用表面活性剂十二烷基硫酸钠K12粉1份、碳酸钙50份、硫酸铝5份、松香皂粉3份混合均匀制得；防水剂选用甲基硅酸5份、皂粉1份、生石灰10份混合均匀制得；超细填料选用粉煤灰50份、硅灰微粉20份、硅藻土50份混合均匀制得；增强防裂剂选用无机纤维10份、合成纤维5份；保水剂选用羧甲基纤维素钠CMC 3份。把上述组分搅拌混合均匀即制得本发明相变储能保温调温建筑砂浆。
本发明相变储能保温调温建筑砂浆的相变温度为26-28℃，当室内温度高于这一温度范围时，相变储能保温调温建筑砂浆开始熔化吸收热量，降低室内温度；当室内温度低于这一温度范围时，相变储能保温调温建筑砂浆开始固化释放潜热，提高室内温度，从而达到调节室内温度的目的。
以上所述仅为本发明的实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的权利要求范围之内。

Claims (3)

1.一种相变储能保温调温建筑砂浆，其特征在于主要成分为：相变储能细骨料、粘结剂、发泡剂、防水剂、增强防裂剂、超细填料等组成。
2.如权利要求1所述的相变储能保温调温建筑砂浆，其特征在于相变储能细骨料选用闭孔膨胀珍珠岩400份、松香50份、石蜡50份均匀混合融化吸附制得。粘结剂氯氧镁水泥选用无水氯化镁100份、氧化镁150份均匀混合制得；发泡剂选用表面活性剂十二烷基硫酸钠K12粉1份、碳酸钙50份、硫酸铝5份、松香皂粉3份均匀混合制得；防水剂选用甲基硅酸5份、皂粉1份、生石灰10份均匀混合制得；超细填料选用粉煤灰50份、硅灰微粉20份、硅藻土50份均匀混合制得；增强防裂剂选用无机纤维纤10份、合成纤维5份；保水剂选用羧甲基纤维素钠CMC 3份。把上述组分搅拌混合均匀即制得本发明相变储能保温调温建筑砂浆。
3.如权利要求1-2所述的相变储能保温调温建筑砂浆，其特征在于：相变储能保温调温建筑砂浆相变温度为26-28℃，当室内温度高于这一温度范围时，相变储能保温调温建筑砂浆开始熔化吸收热量，降低室内温度；当室内温度低于这一温度范围时，相变储能保温调温建筑砂浆开始固化释放潜热，提高室内温度，从而达到调节室内温度的目的。
CN2009101574708A 2009-07-30 2009-07-30 一种相变储能保温调温建筑砂浆 Pending CN101987789A (zh)