CN101982601A - Preparation method of ecological non-iron cotton high-grade fabric - Google Patents
Preparation method of ecological non-iron cotton high-grade fabric Download PDFInfo
- Publication number
- CN101982601A CN101982601A CN 201010511235 CN201010511235A CN101982601A CN 101982601 A CN101982601 A CN 101982601A CN 201010511235 CN201010511235 CN 201010511235 CN 201010511235 A CN201010511235 A CN 201010511235A CN 101982601 A CN101982601 A CN 101982601A
- Authority
- CN
- China
- Prior art keywords
- preparation
- shitosan
- citric acid
- fibroin
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of an ecological non-iron cotton high-grade fabric. The method comprises the steps of preparation of fibroin/chitosan/citric acid anti-crease shrink-proof finishing agent, finishing and the like. In the invention, since waste silk, chitosan and citric acid, which are natural green healthy products, are utilized as raw materials, the ecological non-iron cotton high-grade fabric prepared by using the finishing agent conforms to the direction that the function classification of the textiles in the 21th century is required to be finished and processed on the premise of comfort, cleanness and safety. Since the fibroin finishing agent contains substantive fibroin proteins, the ecological non-iron cotton high-grade fabric has favorable skin affinity, and caters for the consumption concepts of environmental friendliness, health and fashion of people.
Description
Technical field:
The present invention designs the preparation method of the non-ironing cotton fabric of a kind of ecology
Background technology:
Cotton fiber is a kind of senior native cellulose fibre, is considered to " green fiber ".Its COTTON FABRIC quality is plentiful abundant, soft hand feeling, and good sucting wet air permeability and good wearing comfort always are subjected to people's favor, and market and development prospect are widely at home and abroad arranged.In various fabrics, textile clothes are one of most popular consumer goods of back to nature, but COTTON FABRIC is wrinkling serious in dress, need flatiron could recover original outward appearance after washing.For a long time, the anti-wrinkle shrink-proof finishing agent great majority that use are the formolation compound, can discharge ecological environment and the extremely harmful formaldehyde of human body in arrangement processing and wearing process.
And useless silk is as the main discarded object of Silk Industry, and shitosan is the second largest regenerated resources of nature as the discarded object of materials such as shrimp, crab, is only second to cotton fiber, but is not all effectively utilized.
Summary of the invention:
The object of the present invention is to provide a kind of preparation method of the cotton high-grade fabric with anti-wrinkle shrink-proof function of ecology.
Technical solution of the present invention is:
The non-ironing cotton high-grade fabric of a kind of ecology preparation method is characterized in that: adopt following method to make:
(1) preparation fibroin/shitosan/citric acid anti-wrinkle shrink-proof finishing agent
The preparation of A liquid: the silk alkaline washing that will give up, remove impurity such as its softener, adopt caustic soda hydrolysis waste silk again, filter through filter membrane, make the fibroin hydrolyzate that certain molecular weight distributes;
B finishing agent preparation: shitosan is adopted certain glacial acetic acid dissolving, handle and add hydrogen peroxide behind the certain hour and degrade, filter, the collecting precipitation thing makes the shitosan of degraded.
Composite: as B finishing agent and C citric acid slowly to be joined in the A liquid, add auxiliary reagents such as a certain amount of bleeding agent, softener again, fibroin/shitosan that must be stable/citric acid anti-wrinkle shrink-proof finishing agent.
(2) put in order: COTTON FABRIC is put in fibroin/shitosan/citric acid finishing padded, get product after oven dry bakes.
In the step (1), when A liquid prepared, the concentration of NaOH was 1～5mol/L, and the waste silk consumption is 1%～10%, and hydrolysis temperature is 100 ℃, and hydrolysis time is 30～120min; When B arrangement thing prepares, take by weighing certain amount of chitosan, it is added in the entry, add a certain amount of glacial acetic acid again, stir 24h down, shitosan fully is dissolved in the acetum at 30～60 ℃.Slowly add 30% hydrogen peroxide then at a certain temperature, behind reaction 1～3h, filter collecting precipitation; B finishing agent and C citric acid are joined in the A liquid, and A and B solid content ratio are 4: 1, and the citric acid consumption is 1%～10%
The concrete grammar of step (2) is: cotton fabric is put into fibroin/shitosan/citric acid finishing working solution pad, pick-up rate is 90%, and padding is two to soak two and roll; Then at 80 ℃ of following preliminary drying 5min, handle 3～5min down at 100～150 ℃ again, wash then, dry product.
Useless silk has a certain amount of free active group through washing the fibroin finishing agent that makes after the hydrolysis, as hydroxyl, phenolic hydroxyl group, amino etc., can form stable combining by covalent cross-linking or physical deposition with cotton fiber is intermolecular.Thereby improve the anti-wrinkle shrink-proof performance of cotton fiber.
The shitosan film forming is strong, and with the cellulose chemistry structural similarity, they have good absorption and compatibility, and the amino hydroxyl with fiber of the hydroxyl of shitosan and a part forms numerous intermolecular hydrogen bondings, add proper amount of cross-linking agent, make the shitosan arrangement can play certain anti-wrinkle shrink-proof wrinkle effect.
Citric acid has more reactive group, can form covalent cross-linking with hydroxyl on the COTTON FABRIC, simultaneously, and the crosslinking agent that can also close as other finishing agents and cotton knot.
Fibroin hydrolyzate, degradation of chitosan thing and citric acid under certain pH condition, are re-dubbed stable finishing agent by a certain percentage, have cooperative effect, and need not to add in addition crosslinking agent, make the all-cotton fabric after the arrangement have preferable anti-wrinkle shrink-proof effect.
The present invention is a raw material with useless silk, shitosan and citric acid, the three all belongs to the natural green health-oriented products, meeting the 21 century finishing functions of textile fabrics with the ecological non-ironing textile high-grade fabric of this finishing agent exploitation should be that keynote is carried out and put the direction of processing in order with comfortable, cleaning and safety, wherein contain a large amount of fibroin albumens in the fibroin finishing agent, have skin-friendly preferably, and catered to the consumption concept of people " environmental protection, health, fashion ".
The advantage that the present invention is compared with prior art had:
1, finishing agent adopted is product harmless, environmental protection.The consumption concept that meets " environmental protection, health, fashion ".
2, only contain hydroxyl on the all-cotton fabric, after arrangement, contain fibroin albumens such as part amino, phenolic hydroxyl group on the fabric, human body skin is had compatibility preferably.Can improve the sucting wet air permeability and the snugness of fit of cotton fiber.
3, do not add crosslinking agent, adopt citric acid as crosslinking agent, the fabric after the arrangement does not contain has the material that stimulation is toxic or ecological textile is forbidden to human body.
The invention will be further described below in conjunction with embodiment:
The specific embodiment:
The non-ironing cotton high-grade fabric of a kind of ecology preparation method, adopt following method to make:
(1) preparation fibroin/shitosan/citric acid anti-wrinkle shrink-proof finishing agent
The preparation of A liquid: the silk alkaline washing that will give up, remove impurity such as its softener, adopt caustic soda hydrolysis waste silk again, filter through filter membrane, make fibroin hydrolyzate (A liquid);
B finishing agent preparation: shitosan is adopted the glacial acetic acid dissolving, so add hydrogen peroxide and degrade, filter, the collecting precipitation thing makes the shitosan (B finishing agent) of degraded.
Composite: as B finishing agent and C citric acid slowly to be joined in the A liquid, can add (or not adding) bleeding agent, softener again, fibroin/shitosan that must be stable/citric acid anti-wrinkle shrink-proof finishing agent.
(2) put in order: COTTON FABRIC is put in fibroin/shitosan/citric acid finishing padded, get product after oven dry bakes.
In the step (1), when A liquid prepared, the concentration of NaOH was 1～5mol/L, and the waste silk consumption is 1%～10%, and hydrolysis temperature is 100 ℃, and hydrolysis time is 30～120min; When B arrangement thing prepares, take by weighing shitosan, it is added in the entry, add glacial acetic acid again, stir 24h down, shitosan fully is dissolved in the acetum at 30～60 ℃.Slowly add 30% hydrogen peroxide then, reaction 1～3h filters collecting precipitation; B finishing agent and C citric acid are joined in the A liquid, and A and B solid content ratio are 4: 1, and the citric acid consumption is 1%～10%;
The concrete grammar of step (2) is: cotton fabric is put into fibroin/shitosan/citric acid finishing working solution pad, pick-up rate is 90%, and padding is two to soak two and roll; Then at 80 ℃ of following preliminary drying 5min, handle 3～5min down at 100～150 ℃ again, wash then, dry product.
Claims (4)
1. the non-ironing cotton high-grade fabric of ecology preparation method is characterized in that: adopt following method to make:
(1) preparation fibroin/shitosan/citric acid anti-wrinkle shrink-proof finishing agent
The preparation of A liquid: the silk alkaline washing that will give up, remove impurity such as its softener, adopt caustic soda hydrolysis waste silk again, filter through filter membrane, make the fibroin hydrolyzate;
B finishing agent preparation: shitosan is adopted the glacial acetic acid dissolving, add hydrogen peroxide then and degrade, filter, the collecting precipitation thing makes the shitosan of degraded;
Composite: as B finishing agent and C citric acid slowly to be joined in the A liquid, add auxiliary reagents such as bleeding agent, softener again, fibroin/shitosan that must be stable/citric acid anti-wrinkle shrink-proof finishing agent.
(2) put in order: COTTON FABRIC is put in fibroin/shitosan/citric acid finishing padded, get product after oven dry bakes.
2. the non-ironing cotton high-grade fabric of ecology according to claim 1 preparation method is characterized in that: when A liquid and B finishing agent were composite in the step (1), the solid content ratio was 4: 1.
3. the preparation method of a kind of ecological full-cotton high-grade fabric according to claim 1 is characterized in that: in the step (1), when A liquid prepares, the concentration of NaOH is 1～5mol/L, the waste silk consumption is 1%～10%, and hydrolysis temperature is 100 ℃, and hydrolysis time is 30～120min; When B arrangement thing prepares, take by weighing certain amount of chitosan, it is added in the entry, add a certain amount of glacial acetic acid again, stir 24h down, shitosan fully is dissolved in the acetum at 30～60 ℃.Slowly add 30% hydrogen peroxide then at a certain temperature, behind reaction 1～3h, filter collecting precipitation; Put B in order thing and join in the A liquid, A and B solid content ratio are 4: 1, and the citric acid consumption is 1%～10%.
4. the preparation method of a kind of ecological full-cotton high-grade fabric according to claim 1, it is characterized in that: the concrete grammar of step (2) is: cotton fabric is put into fibroin/shitosan/citric acid finishing working solution pad, pick-up rate is 90%, and padding is two to soak two and roll; Then at 80 ℃ of following preliminary drying 5min, handle 3～5min down at 100～150 ℃ again, wash then, dry product.