CN101961789A - 一种制造粉末冶金柱塞泵缸体毛坯的工艺 - Google Patents

一种制造粉末冶金柱塞泵缸体毛坯的工艺 Download PDF

Info

Publication number
CN101961789A
CN101961789A CN 201010507358 CN201010507358A CN101961789A CN 101961789 A CN101961789 A CN 101961789A CN 201010507358 CN201010507358 CN 201010507358 CN 201010507358 A CN201010507358 A CN 201010507358A CN 101961789 A CN101961789 A CN 101961789A
Authority
CN
China
Prior art keywords
plunger pump
powder
iron
green compact
carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010507358
Other languages
English (en)
Inventor
陆龙驹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Netshape Composite Materials Co Ltd
Original Assignee
Suzhou Netshape Composite Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Netshape Composite Materials Co Ltd filed Critical Suzhou Netshape Composite Materials Co Ltd
Priority to CN 201010507358 priority Critical patent/CN101961789A/zh
Publication of CN101961789A publication Critical patent/CN101961789A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种制造粉末冶金柱塞泵缸体毛坯的工艺，用于柱塞泵的缸体毛坯的制造。该粉末冶金材料的组成成分为铁、碳及铜，该粉末冶金柱塞泵缸体毛坯的制造工艺的步骤为：1)压制成形；2)烧结；3)机械加工。该制造工艺利用了粉末冶金代替了铸铁应用于该类零件的材料，成形复杂形状，尺寸精度高的工艺优点，大幅减少加工量，提高生产效率。

Description

一种制造粉末冶金柱塞泵缸体毛坯的工艺
技术领域
本发明涉及机械零件制造领域，具体的涉及一种制造粉末冶金柱塞泵缸体毛坯的工艺。
背景技术
现有的柱塞泵缸体毛坯的制造方法中采用铸铁为毛坯材料。这样铸造出来的毛坯精度低，且零件需经过车削、拉削、铣削、磨削等多个工序后才能进行精密加工，加工效率低，成本极高。
发明内容
为克服现有技术中的不足，本发明的目的在于提出一种制造粉末冶金柱塞泵缸体毛坯的工艺，该制造工艺利用了粉末冶金代替了铸铁应用于该类零件的材料，具有能够成形复杂形状、尺寸精度高的工艺优点，大幅减少加工量，提高生产效率。
为解决上述技术问题，达到上述技术目的，本发明采用如下技术方案：
一种制造粉末冶金柱塞泵缸体毛坯的工艺，其具体工艺步骤为：
1)压制成形：通过冷压的方法压制铁碳生坯及渗铜生坯；
2)烧结：将渗铜生坯与铁碳生坯组装后放入烧结电炉烧结，得到柱塞泵缸体毛坯，并以氮气保护；
3)机械加工：将烧结成的柱塞泵缸体毛坯进行后续机加工。
优选的，所述步骤1中，所述铁碳生坯由铁粉、碳粉及润滑剂加工而成，组成成分按重量百分比来表示为：铁粉为97％-99％、碳粉为0.6％-0.9％、润滑剂为0.8％-1.2％。
优选的，所述步骤2中，所述渗铜生坯由铜粉、铁粉、碳粉、锌、锰、碳及润滑剂加工而成，组成成分按重量百分比来表示为：铜粉为95％-98％、铁粉为1％-2％、润滑剂为0.2％-0.4％，其中，锌、锰、碳所占总重的重量百分比不大于3.8％。
优选的，所述步骤2中，所述烧结电炉中的最高温度为1121℃。
与现有技术相比，本发明的粉末冶金柱塞泵缸体毛坯的制造工艺具有如下优点：
1.通过对粉末冶金材料的研究，发明出适用于柱塞泵缸体毛坯的粉末冶金材料，替代原传统应用于该类零件的铸铁作为材料，从而可以成形复杂形状，提高尺寸精度。
2.本发明的粉末冶金制造该类毛坯的工艺方法，结合粉末冶金可成形复杂形、尺寸精度高的工艺优点，大幅减少加工量，提高生产效率。
具体实施方式
实施例1
本发明的一种制造粉末冶金柱塞泵缸体毛坯的工艺，具体步骤为：
1)压制成形：用98.2％的铁粉、0.8％的碳粉及1％的润滑剂通过冷压的方法压制铁碳生坯，用96.5％的铜、1.5％的铁、0.3％的润滑剂及1.7％的锌、锰、碳压制渗铜生坯；
2)烧结：将渗铜生坯与铁碳生坯组装后放入烧结电炉烧结，以氮气保护，高温区温度为1121℃；
3)机械加工：烧结后进行后续机加工。
实施例2
本发明的另一种制造粉末冶金柱塞泵缸体毛坯的工艺，具体步骤为：
1)压制成形：用98％的铁粉、0.8％的碳粉及1.2％的润滑剂通过冷压的方法压制铁碳生坯，用95％的铜、2％的铁、0.4％的润滑剂及3.6％的锌、锰、碳压制渗铜生坯；
2)烧结：将渗铜生坯与铁碳生坯组装后放入烧结电炉烧结，以氮气保护，高温区温度为1121℃；
3)机械加工：烧结后进行后续机加工。
实施例3
本发明的又一种制造粉末冶金柱塞泵缸体毛坯的工艺，具体步骤为：
1)压制成形：用98.6％的铁粉、0.6％的碳粉及0.8％的润滑剂通过冷压的方法压制铁碳生坯，用98％的铜、1％的铁、0.2％的润滑剂及0.8％的锌、锰、碳压制渗铜生坯；
2)烧结：将渗铜生坯与铁碳生坯组装后放入烧结电炉烧结，以氮气保护，高温区温度为1121℃；
3)机械加工：烧结后进行后续机加工。
本发明的粉末冶金柱塞泵缸体毛坯的制造工艺，是在对粉末冶金材料的研究基础上，发明出的可以替代传统应用于该类零件的铸铁作为材料，且发明出相应的粉末冶金制造该类毛坯的工艺方法，结合粉末冶金可成形复杂形状、尺寸精度高的工艺优点，大幅减少加工量，提高生产效率。

Claims (4)

1.一种制造粉末冶金柱塞泵缸体毛坯的工艺，其特征在于，具体工艺步骤为：
1)压制成形：通过冷压的方法压制铁碳生坯及渗铜生坯；
2)烧结：将渗铜生坯与铁碳生坯组装后放入烧结电炉烧结，得到柱塞泵缸体毛坯，并以氮气保护；
3)机械加工：将烧结成的柱塞泵缸体毛坯进行后续机加工。
2.如权利要求1所述的制造粉末冶金柱塞泵缸体毛坯的工艺，其特征在于，所述步骤1中，所述铁碳生坯由铁粉、碳粉及润滑剂加工而成，组成成分按重量百分比来表示为：铁粉为97％-99％、碳粉为0.6％-0.9％、润滑剂为0.8％-1.2％。
3.如权利要求1所述的制造粉末冶金柱塞泵缸体毛坯的工艺，其特征在于，所述步骤2中，所述渗铜生坯由铜粉、铁粉、碳粉、锌、锰、碳及润滑剂加工而成，组成成分按重量百分比来表示为：铜粉为95％-98％、铁粉为1％-2％、润滑剂为0.2％-0.4％，其中，锌、锰、碳所占总重的重量百分比不大于3.8％。
4.如权利要求1所述的制造粉末冶金柱塞泵缸体毛坯的工艺，其特征在于，所述步骤2中，所述烧结电炉中的最高温度为1121℃。
CN 201010507358 2010-10-15 2010-10-15 一种制造粉末冶金柱塞泵缸体毛坯的工艺 Pending CN101961789A (zh)