CN101961203A - Environmental-friendly heat-resistant microcrystal color ceramic container and manufacturing method thereof - Google Patents
Environmental-friendly heat-resistant microcrystal color ceramic container and manufacturing method thereof Download PDFInfo
- Publication number
- CN101961203A CN101961203A CN2009101089346A CN200910108934A CN101961203A CN 101961203 A CN101961203 A CN 101961203A CN 2009101089346 A CN2009101089346 A CN 2009101089346A CN 200910108934 A CN200910108934 A CN 200910108934A CN 101961203 A CN101961203 A CN 101961203A
- Authority
- CN
- China
- Prior art keywords
- microcrystalline
- crystallite
- resistant
- faience
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an environmental-friendly heat-resistant microcrystal color ceramic container and a manufacturing method thereof. The ceramic container comprises a blank, an outer microcrystal glaze layer sintered on the outer surface of the blank, and an inner microcrystal glaze layer on the inner surface of the blank, wherein the outer surface of the outer microcrystal glaze layer also comprises a pattern layer formed by sintering patterned carbon fiber film decal attached to the outer surface of the outer microcrystal glaze layer. The environmental-friendly heat-resistant microcrystal color ceramic container is quick on heat conduction and uniform on heating, does not generate lampblack within 250 DEG C, has the advantages of good environmental protection performance, stable physical and chemical performance at high temperature, high surface density and poor viscosity to pans, does not decompose substances harmful to human health, and is superior to the traditional enamel pans on the properties of high density, wear resistance, heat-resistant stability, impact resistance, corrosion resistance and contamination resistance.
Description
Technical field
The present invention relates to a kind of kitchen utensils, more particularly, relate to a kind of environment-friendly heat-resistant crystallite faience vessel and manufacture method thereof.
Background technology
Though modern kitchen apparatus kind is a lot, the high-quality frying pan that is suitable for the Chinese cooking mode but seldom.The easy oil smoke that glues pot and can produce the people that chokes when traditional iron pan is cooked.And non-stick pan commonly used in recent years generally all is limited in 250 ℃ to use down owing to contain the Teflon material in the coating, is higher than this temperature, and coating can decomposite the material of harmful health.And Chinese cooking method major part is quick-fried, and temperature usually is higher than 250 ℃, should not use the non-stick pan of Teflon material.In addition, existing enamel ware since raw material and manufacturing process be prone in use and take off porcelain, crackle, cut etc., and heat-resistant stability, wear-resisting, impact resistance is poor.
Thereby, need a kind of heat-resistant stability of exploitation, shock-resistant, wear-resisting, fine corrosion resistance, be difficult for producing oil smoke, durable cooking ware.
Summary of the invention
The technical problem to be solved in the present invention is, at the existing defective of above-mentioned frying pan of prior art, provides a kind of environment-friendly heat-resistant crystallite faience vessel.The present invention also provides a kind of manufacture method of environment-friendly heat-resistant crystallite faience vessel.
The technical solution adopted for the present invention to solve the technical problems is: construct a kind of environment-friendly heat-resistant crystallite faience vessel, comprise base substrate, sintering at the outer microcrystalline glaze layer of described base substrate outer surface and the sintering interior microcrystalline glaze layer at described base substrate inner surface, described outer microcrystalline glaze layer and interior microcrystalline glaze layer mainly comprise the raw material of following parts by weight:
SiO
250-75 part;
B
2O
30-6 part;
Al
2O
30-20 part;
Na
2O and/or K
2O+Li
2O 8-23 part;
CaO and/or MgO 1-5 part;
P
2O
50.8-5.5 part;
TiO
22-15 part;
ZrO
20-8 part;
CeO
20-10 part;
CoO 0-1.25 part;
NiO 0-1.5 part;
MnO
20-1.5 part;
NaSiF
20-3 part.
In environment-friendly heat-resistant crystallite faience vessel of the present invention, described base substrate is made by the cold-rolled steel sheet material, and its thickness is 1.00~1.2mm.
In environment-friendly heat-resistant crystallite faience vessel of the present invention, described base substrate is made by cast iron materials, and its thickness is 2.5~5.0mm.
In environment-friendly heat-resistant crystallite faience vessel of the present invention, described outer microcrystalline glaze layer comprises that thickness is that outer ground-coat enamel microcrystalline coating of 150~200 μ m and thickness are 150~200 μ m cover-coat enamel microcrystalline coatings, and the thickness of described interior microcrystalline glaze layer is 150~200 μ m.
In environment-friendly heat-resistant crystallite faience vessel of the present invention, described outer microcrystalline glaze layer outer surface comprises that also one deck is pasted on the patterned layer that outer microcrystalline glaze layer outer surface forms through sintering by the carbon fiber film that has pattern.
The present invention solves another technical scheme that its technical problem adopts: a kind of manufacture method of environment-friendly heat-resistant crystallite faience vessel is provided, comprises;
The preparation base substrate;
Preparation microcrystalline glaze piece;
The heat-resisting glaze piece of interpolation, mill addition, water mixing and ball milling are made the crystallite glaze slip in the microcrystalline glaze piece;
Outer surface and inner surface coating crystallite glaze slip ground-coat enamel and sintering at described base substrate;
Coating crystallite glaze slip cover-coat enamel and sintering on the ground-coat enamel behind the sintering;
Wherein, described preparation microcrystalline glaze piece comprises:
Following raw materials by weight portion prepared burden and mix:
SiO
250-75 part;
B
2O
30-6 part;
Al
2O
30-20 part;
Na
2O and/or K
2O+Li
2O 8-23 part;
CaO+MgO 1-5 part;
P
2O
50.8-5.5 part;
TiO
22-15 part;
ZrO
20-8 part;
CeO
20-10 part;
CoO 0-1.25 part;
NiO 0-1.5 part;
MnO
20-1.5 part;
NaSiF
20-3 part;
With mixed raw materials at 1250-1350 ℃ of high temperature melting;
Quenching;
Oven dry;
Corase grind;
The crystal coring is handled the back and is become the microcrystalline glaze piece.
In the manufacture method of environment-friendly heat-resistant crystallite faience vessel of the present invention, the temperature that described crystal coring is handled is that 570 ± 10 ℃, time are 60-400 minute.
In the manufacture method of environment-friendly heat-resistant crystallite faience vessel of the present invention, described heat-resisting glaze piece comprises following compositions in portion by weight:
SiO
263-80 part;
Na
2O 8-17 part;
K
2O 0-7 part;
Li
2O 1-5 part;
CaO 0-2 part;
MgO 0-2 part;
TiO
20-2 part;
ZrO
20-8 part;
CoO 0-1.25 part;
NiO 0-1.50 part;
MnO
20-1.50 part;
NaSiF
20-3 part.
In the manufacture method of environment-friendly heat-resistant crystallite faience vessel of the present invention, described sintering temperature is 900 ± 10 ℃, sintering time 1-15 minute.
In the manufacture method of environment-friendly heat-resistant crystallite faience vessel of the present invention, the surface that is included in the outer microcrystalline glaze layer of described vessel attaches and has the carbon fiber film of pattern, and inserts in the sintering furnace at 800-900 ℃ of following decorated fire time 2-4 minute.
Implement environment-friendly heat-resistant crystallite faience vessel of the present invention, have following beneficial effect: heat conduction rapidly, be heated evenly, can not produce oil smoke, good environmental protection at 250 ℃ with interior; And at high temperature have stable physics, chemical property, can not decomposite the material of harmful health; The superficial density height is difficult for sticking pot.
In addition, environment-friendly heat-resistant crystallite faience vessel of the present invention have the mechanical performance higher than common enamel product, and density height, wear-resisting, heat-resistant stability, impact resistance, corrosion-resistant, antifouling property all are better than traditional enamel pan.Hardness: reach Mohs 8-9 level, anti-burning: dry combustion method is 300 ℃-400 ℃ on the electromagnetic oven, and flawless does not take off porcelain, the heatproof acute degeneration: product by heating swashs flawless suddenly with 20 ℃ of water and does not take off porcelain to 325-400 ℃.Product high temperature uses nondiscolouring, and is easy to clean.
Description of drawings
The invention will be further described below in conjunction with drawings and Examples, in the accompanying drawing:
Fig. 1 is the structural representation of environment-friendly heat-resistant crystallite faience vessel one embodiment according to the present invention;
Fig. 2 is the flow chart of environment-friendly heat-resistant crystallite faience vessel manufacture method of the present invention;
Fig. 3 is the flow chart of the microcrystalline glaze method for preparing raw material of the heat-resisting crystallite faience of guarantor's type of the present invention vessel.
The specific embodiment
In the embodiment shown in fig. 1, environment-friendly heat-resistant crystallite faience vessel of the present invention comprise three layers, and to be interior microcrystalline glaze layer 1, the second layer (being the intermediate layer) be outer microcrystalline glaze layer 3 for the green body layer 2 of vessel, the 3rd layer to ground floor.In another embodiment of the present invention, outer microcrystalline glaze layer 3 further comprises outer ground-coat enamel microcrystalline coating and cover-coat enamel microcrystalline coating (not shown).Wherein, the thickness of interior microcrystalline glaze layer can be that the thickness of 150~200 μ m, outer ground-coat enamel microcrystalline coating is that 150~200 μ m and cover-coat enamel microcrystalline coating thickness are 150~200 μ m.The purpose of control porcelain thickness is the physicochemical property that guarantees product, as: resistance to impact, anti-burning, heatproof acute degeneration.Improve adherence, promptly improve the combination degree between ground glaze layer and the metal level.
The intermediate layer base substrate can be made by steel plate materials, and its thickness can be chosen as 1.00~1.2mm.As another selection, the intermediate layer base substrate also can be made by cast iron materials, and thickness can be selected at 2.5~5.0mm as required.
In one embodiment of this invention, outer microcrystalline glaze layer outer surface also comprises a patterned layer, and this patterned layer is that the carbon fiber film that will have pattern is pasted on outer microcrystalline glaze layer outer surface after sintering and forming.
As shown in Figure 2, the flow process of environment-friendly heat-resistant crystallite faience vessel manufacture method of the present invention comprise body preparation 21, crystallite glaze slip preparation 30, be coated with glaze and sintering 22, operations such as design producing 23, the total inspection 24 of back dress.
Wherein:
Be coated with glaze and sintering 22 operations comprise: be coated with crystallite ground-coat enamel, ground-coat enamel oven dry, ground-coat enamel burn till, be coated with crystallite cover-coat enamel, cover-coat enamel oven dry, scrape mend powder, cover-coat enamel burns till and the plain color product inspection.In one embodiment of this invention, interior microcrystalline glaze layer 1 coating sintering one deck microcrystalline glaze and outer microcrystalline glaze layer 3 burns one deck cover-coat enamel that reburns behind one deck ground-coat enamels.As selection, interior microcrystalline glaze layer 1 of environment-friendly heat-resistant crystallite faience vessel of the present invention and outer microcrystalline glaze layer 3 be coating sintering one deck microcrystalline glaze all.As another selection, microcrystalline glaze layer 1 and outer microcrystalline glaze layer 3 in the environment-friendly heat-resistant crystallite faience vessel of the present invention all burn one deck cover-coat enamel that reburns behind one deck ground-coat enamel.
In actual fabrication, the composition of the crystallite glaze slip of ground-coat enamel and cover-coat enamel is slightly had any different.Generally, do not contain or only contain a spot of milkiness composition in the ground-coat enamel, like this with base substrate to combine firmness higher.
Design producing 23 operations comprise: applique, drying, decorated fire and check.
The back total inspection of dress 24 operations comprise: bound edge assembles, always examines and pack warehouse-in.
The crystallite glaze slip prepares 30 methods as shown in Figure 3, at first prepare the microcrystalline glaze piece, comprise: feedstock analysis, batching, mixing, the detection uniformity, found, the oven dry of discharging hardening, glaze piece, glaze piece corase grind, glaze piece crystallization are handled, cool off behind the crystallization, obtain the microcrystalline glaze piece.Then, preparation crystallite glaze slip, be included in the microcrystalline glaze piece and add mixing and ball milling after heat-resisting glaze piece, mill addition and the water (by weight umber: microcrystalline glaze piece 40-70 part, heat-resisting glaze piece 30-60 part, mill addition 1-20 part, water 40-60 part) and make the crystallite glaze slip, wherein the composition of microcrystalline glaze piece raw material contains (weight ratio):
SiO
250-75 part;
B
2O
30-6 part;
Al
2O
30-20 part;
Na
2O and/or K
2O+Li
2O 8-23 part;
CaO and/or MgO 1-5 part;
P
2O
50.8-5.5 part;
TiO
22-15 part;
ZrO
20-8 part;
CeO
20-10 part;
CoO 0-1.25 part;
NiO 0-1.5 part;
MnO
20-1.5 part;
NaSiF
20-3 part.
Wherein, heat-resisting glaze piece comprises following compositions in portion by weight:
SiO
263-80 part;
Na
2O 8-17 part;
K
2O 0-7 part;
Li
2O 1-5 part;
CaO 0-2 part;
MgO 0-2 part;
TiO
20-2 part;
ZrO
20-8 part;
CoO 0-1.25 part;
NiO 0-1.50 part;
MnO
20-1.50 part;
NaSiF
20-3 part.
In one embodiment of this invention, microcrystalline glaze piece raw material comprises following compositions in portion by weight:
SiO
250 parts;
B
2O
36 parts;
Al
2O
312 parts;
Na
2O+K
2O+Li
218 parts of O;
3 parts of CaO;
P
2O
54 parts;
ZrO
21 part;
0 part of CoO;
0 part of NiO;
MnO
21.5 part;
In one embodiment of this invention, microcrystalline glaze piece raw material comprises following compositions in portion by weight:
SiO
275 parts;
B
2O
32 parts;
Al
2O
30 part;
K
2O+Li
28 parts of O;
1 part of CaO+MgO;
P
2O
55.5 part;
TiO
210 parts;
ZrO
20 part;
CeO
210 parts;
1.25 parts of CoO;
1.5 parts of NiO;
MnO
20.5 part;
In one embodiment of this invention, microcrystalline glaze piece raw material comprises following compositions in portion by weight:
SiO
260 parts;
B
2O
30 part;
Al
2O
320 parts;
5 parts of MgO;
P
2O
50.8 part;
TiO
215 parts;
ZrO
28 parts;
CeO
20 part;
0.7 part of CoO;
0.9 part of NiO;
MnO
20 part;
F
20 part.
In one embodiment of this invention, heat-resisting glaze piece comprises following compositions in portion by weight:
SiO
263 parts;
Na
215 parts of O;
0 part of CaO;
2 parts of MgO;
TiO
21 part;
ZrO
20 part;
1 part of CoO;
0.5 part of NiO;
MnO
20.18 part;
NaSiF
21 part.
In one embodiment of this invention, heat-resisting glaze piece comprises following compositions in portion by weight:
SiO
270 parts;
Na
217 parts of O;
K
27 parts of O;
Li
21 part of O;
2 parts of CaO;
1 part of MgO;
TiO
20 part;
ZrO
28 parts;
0 part of CoO;
1.5 parts of NiO;
MnO
20 part;
In one embodiment of this invention, heat-resisting glaze piece comprises following compositions in portion by weight:
SiO
280 parts;
Na
28 parts of O;
K
20 part of O;
Li
25 parts of O;
1 part of CaO;
0 part of MgO;
ZrO
24 parts;
1.25 parts of CoO;
0 part of NiO;
MnO
21.5 part;
NaSiF
20 part.
Table one is three embodiment of the weight item ratio of various materials during with microcrystalline glaze piece, heat-resisting glaze piece, mill addition and water mixing and ball milling for preparation crystallite glaze slip.
Table one
Composition | First embodiment | Second embodiment | The 3rd embodiment |
The microcrystalline glaze piece | 40 | 55 | 70 |
Heat-resisting glaze piece | 50 | 60 | 30 |
Mill addition | 1 | 20 | 10 |
Water | 40 | 50 | 60 |
Among the present invention, produce a kind of crystallization glaze earlier, and make it crystallization and handle (the crystal nucleation temperature generally about 570 ℃, exceeding 35 ℃) and become the microcrystalline glaze piece, and then become the crystallite glaze slip of confession metal body blackening with another heat-resisting glaze piece mixed grinding than its softening point.Metal body can be that steel plate (for example cold-rolled steel sheet) material is made also and can be made by cast iron materials as previously mentioned.
" heat-resisting crystallite faience vessel " are meant with the crystallite glaze slip and are coated on the metal body, form through 900 ℃ of high-temperature firings.Can again on the crystallite porcelain facing, attach carbon fiber pattern marble paper in addition,, carbon fiber pattern and crystallite porcelain facing be fused into one, make the vessel that have different pattern through 800-900 ℃ of high temperature sintering.
The present invention has special character on prescription composition, manufacturing process:
(1) " heat-resisting microcrystalline glaze " is environment-friendly type high-tech enamel new product, and be with common enamel difference: the prescription and the treatment process of enamel are special.Its prescription of the present invention contains TiO in forming
2, ZrO
2, CeO
2, Li
2O, F
-Deng the nucleus agent, various composition raw materials mix after 1250-1350 ℃ of high temperature melting, and the oven dry corase grind is that 60-400 minute crystal coring is handled in 570 ± 10 ℃ of temperature, time in the coring stove again behind the quenching.The glaze slip made from heat-resisting microcrystalline glaze is coated on metal body, through 900 ℃ ± 10 ℃ high-temperature firing 1-15 minute (for example plate slab is that 1-3 minute, cast iron base are 4-15 minute), decorate with carbon fiber pattern marble paper again, form through 800-900 ℃ of high temperature, 2-4 branch clock time sintering.Because enamel has passed through coring (crystallization) and handled, vitreum becomes crystal, thereby wear-resisting, the hardness of enamel coating, heat-resistant stability, shock-resistant and decay resistance improve a lot.Hardness: reach Mohs 8-9 level; Anti-burning: dry combustion method is 300 ℃-400 ℃ on the electromagnetic oven, and flawless does not take off porcelain; The heatproof acute degeneration: product by heating swashs flawless suddenly with 20 ℃ of water and does not take off porcelain to 325-400 ℃.Product high temperature uses nondiscolouring, and is easy to clean.All kinds of pot such as available spades, plastic cement shovel, stainless steel shovel wooden dipper comes cooking, and does not stay cut.
(2) porcelain facing of product adopts carbon fiber graphics marble paper, enamel, the additive of environment-friendly type, and ornament materials meets standard, and is nontoxic to human body, adopts to add and sticks the novel uniqueness of flower process decorative effect.
(3) introduce reinforcing material such as alkali-free glass fiber powder in the microcrystalline glaze prescription, introduced good for health, the health environment-friendlies of trace element such as Fe, Se, Zn, Ca in the product internal layer glaze.
Adopt heat-resisting microcrystalline glaze among the present invention, mill addition adopts reinforcing materials such as alkali-free glass fiber powder, adopts environment-friendly type decal paper.The enamel manufacturing is adopted crystal nuclear metallization processes, product decoration to adopt and is sticked flower process.
From outside watch, the microcrystalline glaze layer evenly, continuously, the color and luster unanimity, no glaze knurl, do not have come off, no squama is quick-fried, edge dew is deceived less than 1.0mm.
Environment-friendly heat-resistant crystallite faience vessel base substrate of the present invention adopts steel plate or cast iron materials, in the middle of two-layer crystallite porcelain, form heat carrier, heat evenly is passed to the whole cooker body, the problem of Jiao that the inequality that keeps from heat is caused, burning, paste, oil smoke (can not produce oil smoke with interior) still less at 250 ℃, good environmental protection; And the superficial density height is difficult for sticking pot.And at high temperature have stable physics, chemical property, can not decomposite the material of harmful health.Adopt the present invention, because microcrystalline glaze layer heat conductivility is good, heat conduction is rapid, fully keeps the nutritional labeling of food.And the superficial density height, the superslide sense, high temperature resistant, difficult sticking, easy to clean.
Claims (10)
1. environment-friendly heat-resistant crystallite faience vessel, comprise that base substrate, sintering are at the outer microcrystalline glaze layer of described base substrate outer surface and the sintering interior microcrystalline glaze layer at described base substrate inner surface, it is characterized in that described outer microcrystalline glaze layer and interior microcrystalline glaze layer mainly comprise the raw material of following parts by weight:
SiO
250-75 part;
B
2O
30-6 part;
Al
2O
30-20 part;
Na
2O and/or K
2O+Li
2O 8-23 part;
CaO and/or MgO 1-5 part;
P
2O
50.8-5.5 part;
TiO
22-15 part;
ZrO
20-8 part;
CeO
20-10 part;
CoO 0-1.25 part;
NiO 0-1.5 part;
MnO
20-1.5 part;
NaSiF
20-3 part.
2. environment-friendly heat-resistant crystallite faience vessel according to claim 1 is characterized in that described base substrate is made by the cold-rolled steel sheet material, and its thickness is 1.00~1.2mm.
3. environment-friendly heat-resistant crystallite faience vessel according to claim 1 is characterized in that described base substrate is made by cast iron materials, and its thickness is 2.5~5.0mm.
4. according to claim 2 or 3 described environment-friendly heat-resistant crystallite faience vessel, it is characterized in that, described outer microcrystalline glaze layer comprises that thickness is that outer ground-coat enamel microcrystalline coating and the thickness of 150~200 μ m is 150~200 μ m cover-coat enamel microcrystalline coatings, described in the thickness of microcrystalline glaze layer be 150~200 μ m.
5. environment-friendly heat-resistant crystallite faience vessel according to claim 4 is characterized in that, described outer microcrystalline glaze layer outer surface comprises that also one deck is pasted on the patterned layer that outer microcrystalline glaze layer outer surface forms through sintering by the carbon fiber film that has pattern.
6. the manufacture method of environment-friendly heat-resistant crystallite faience vessel comprises;
The preparation base substrate;
Preparation microcrystalline glaze piece;
The heat-resisting glaze piece of interpolation, mill addition, water mixing and ball milling are made the crystallite glaze slip in the microcrystalline glaze piece;
Outer surface and inner surface coating crystallite glaze slip ground-coat enamel and sintering at described base substrate;
Coating crystallite glaze slip cover-coat enamel and sintering on the ground-coat enamel behind the sintering;
It is characterized in that described preparation microcrystalline glaze piece comprises:
Following raw materials by weight portion prepared burden and mix:
SiO
250-75 part;
B
2O
30-6 part;
Al
2O
30-20 part;
Na
2O and/or K
2O+Li
2O 8-23 part;
CaO+MgO 1-5 part;
P
2O
50.8-5.5 part;
TiO
22-15 part;
ZrO
20-8 part;
CeO
20-10 part;
CoO 0-1.25 part;
NiO 0-1.5 part;
MnO
20-1.5 part;
NaSiF
20-3 part;
With mixed raw materials at 1250-1350 ℃ of high temperature melting;
Quenching;
Oven dry;
Corase grind;
The crystal coring is handled the back and is become the microcrystalline glaze piece.
7. the manufacture method of environment-friendly heat-resistant crystallite faience vessel according to claim 6 is characterized in that, the temperature that described crystal coring is handled is that 570 ± 10 ℃, time are 60-400 minute.
8. the manufacture method of environment-friendly heat-resistant crystallite faience vessel according to claim 6 is characterized in that, described heat-resisting glaze piece comprises following compositions in portion by weight:
SiO
263-80 part;
Na
2O 8-17 part;
K
2O 0-7 part;
Li
2O 1-5 part;
CaO 0-2 part;
MgO 0-2 part;
TiO
20-2 part;
ZrO
20-8 part;
CoO 0-1.25 part;
NiO 0-1.50 part;
MnO
20-1.50 part;
NaSiF
20-3 part.
9. the manufacture method of environment-friendly heat-resistant crystallite faience vessel according to claim 6 is characterized in that, described sintering temperature is 900 ± 10 ℃, sintering time 1-15 minute.
10. the manufacture method of environment-friendly heat-resistant crystallite faience vessel according to claim 6, it is characterized in that, the surface that is included in the outer microcrystalline glaze layer of described vessel attaches and has the carbon fiber film of pattern, and inserts in the sintering furnace at 800-900 ℃ of following decorated fire time 2-4 minute.