CN104287643B - A kind of egg McMuffin quick cooker ceramic heat dish and preparation method thereof - Google Patents
A kind of egg McMuffin quick cooker ceramic heat dish and preparation method thereof Download PDFInfo
- Publication number
- CN104287643B CN104287643B CN201410473850.3A CN201410473850A CN104287643B CN 104287643 B CN104287643 B CN 104287643B CN 201410473850 A CN201410473850 A CN 201410473850A CN 104287643 B CN104287643 B CN 104287643B
- Authority
- CN
- China
- Prior art keywords
- glaze
- ceramic body
- ceramic
- antiseized
- crystallite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of egg McMuffin quick cooker ceramic heat dish and preparation method thereof, including ceramic body, whole ceramic body raw materials are carried out ball mill pulverizing, add the additive sodium humate mixing of trace again, again the screen cloth through 300 mesh sieve, inhale ferrum, press filt, vacuum pugging, roller press roll forming, be dried, upper disk surface executes the high antiseized glaze of crystallite, 1320 ° of C base glaze of high temperature burn the most altogether, 1.5 2.5 hours, prepare ceramic body；Carrying out the polishing of ceramic body bottom surface again, install electrode after bottom surface plating stannum oxide heating film or carbon heating film, upper surface coating high temperature light oleoresin solidifies 2 hours in 180 degree；Product of the present invention i.e..Product surface of the present invention has high antiseized microcrystalline glaze to be coated with gloss oil high-temperature resin, durable in use, the most nontoxic, the viscous pot problem of the ordinary pan solved, also food is made more to complete, ceramic body is readily cleaned after a procedure, and economizes on water, and the most also solves the most aging problem and the harmful problem of coming off of " Teflon ".
Description
Technical field
The present invention relates to ceramic product, be specifically related to a kind of without contact heating and a kind of egg McMuffin quick cooker ceramic heat dish of direct-fired non-stick pan and preparation method thereof.
Background technology
Current egg McMuffin quick cooker mostly is metal pan, it is yielding that metal pan crosses thin heating, blocked up the heaviest, mode of heating mostly also is contact heating i.e. needs another independent heat generating components to heat metal pan, and pot surface non-stick pan to be reached mostly is coating non-adhesive material " Teflon ", this non-adhesive material is the most aging to come off, and this non-adhesive material has harmful composition；Pan-fried place egg mouthfeel out is the most bad.
Summary of the invention
For solving the problems referred to above, the invention provides ceramic heat dish of egg McMuffin quick cooker of a kind of direct-fired non-stick pan and preparation method thereof.
The ceramic heat dish of this egg McMuffin quick cooker, including ceramic body, it is characterised in that this ceramic body has highly thermally conductive and high heat stability performance, is provided with at ceramic body upper surface and does not glues glaze and coating, is provided with heating film in ceramic body bottom surface.
The manufacture method of the ceramic heat dish of this egg McMuffin quick cooker, it is characterized in that, described highly thermally conductive performance is to be added with silicon carbide powder in ceramic material, and described high heat stability performance is to be added with cordierite and spodumene composite ceramic material at ceramic material, sintered makes.
The described glaze that do not glues is the high antiseized glaze of crystallite.
The concrete components by weight of the high antiseized glaze of crystallite such as under: petalite 65-75%, Talcum 5-10 %, Zirconium orthosilicate. 1-5%, Suzhou soil 2-8%, quartz sand 12-18%, aluminium oxide 0-5%, additional microcrystalline glass powder 10-15 %.
By all of the above glaze raw material by ball: material: water=1.5:1:0.6 carries out obtaining after suction ferrum, the screen cloth of 300 mesh sieve after ball mill pulverizing reaches certain particle size the high antiseized glaze glaze water of crystallite again.
Described making microcrystalline glass powder is with following part by weight component: Talcum: 10% ~ 30%, quartz: 30 ~ 50%, aluminium oxide: 10% ~ 30%, calcium carbonate: 3 ~ 10%, brium carbonate: 5% ~ 10%, titanium dioxide 1% ~ 5% is pulverized after founding at 1550 DEG C ~ 1600 DEG C after being sufficiently mixed again and is formed.
Described coating is high temperature light oleoresin.
Described heating film can be stannum oxide heating film or carbon heating film.
The concrete components by weight of ceramic body such as under: cordierite 38-42, spodumene 12-14, Suzhou soil 8-12, black earth 13-17, corundum 8-12, carborundum 4-6, Talcum 4-6, petalite 1.5-2.5.
The ceramic heat dish specific make step of egg McMuffin quick cooker and technological parameter are as follows:
By all of the above ceramic body raw material by ball: material: water=1.7:1:1.2 carries out ball mill pulverizing, add the additive sodium humate mixing of trace again, again the screen cloth through 300 mesh sieve, inhale ferrum, press filt, vacuum pugging, roller press roll forming, be dried, upper disk surface executes the high antiseized glaze of crystallite, 1320 ° of C base glaze of high temperature burn the most altogether, 1.5-2.5 hour, prepare ceramic body；Carrying out the polishing of ceramic body bottom surface again, install electrode after bottom surface plating stannum oxide heating film or carbon heating film, upper surface coating high temperature light oleoresin solidifies 2 hours in 180 degree；Product of the present invention i.e..
The present invention finds through test of many times, cordierite, the composite ceramic material of spodumene take into account thermally-stabilised and conduction of heat advantage, after it adds a small amount of carborundum powder, after common sintering, can get the ceramic material of high thermal stability and highly thermally conductive speed, solve the problem that ceramic material high thermal stability can not be taken into account with high heat conductance.
Product of the present invention, its body surface first uses high antiseized microcrystalline glaze to be coated with gloss oil high-temperature resin, both materials can play antiseized dual fail-safe, glaze is the most durable in use, the most nontoxic, the viscous pot problem of the ordinary pan of solution, also food is made more to complete, ceramic body is readily cleaned after a procedure, and economizes on water, and the most also solves the most aging problem murder by poisoning problem with harmful composition that comes off of " Teflon ".
The product of the present invention, its ceramic body bottom surface uses the heating of silk-screen stannum oxide heating film, homogeneous heating, film silk-screen is in ceramic disk bottom surface, in hgher efficiency, and conduction is faster, start voltage lower, solve the problems such as electric-heating-wire-heating power is high, it is uneven to heat, conduct slowly, structure takes up space.Additionally this type of heating film can only attached on the insulating material, and the ceramic body material of the present invention has this advantage.Product of the present invention in use ceramic surface sends far infrared, the most useful to food mouthfeel and human body.
Accompanying drawing explanation
Fig. 1 is the structural representation of egg McMuffin quick cooker.
In figure: 1, ceramic heat dish, 2, disk cover, 3, mounting cylinder, 4, ceramic body, 5, the high antiseized glaze of crystallite, 6, high temperature light oleoresin, 7, stannum oxide heating film, 8, electrode, 9, wire, 10, plug, 11, annulus.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the structural principle of the present invention is described further.
The ceramic heat dish of this egg McMuffin quick cooker, including ceramic body, it is characterised in that this ceramic body has highly thermally conductive and high heat stability performance, is provided with at ceramic body upper surface and does not glues glaze and coating, is provided with heating film in ceramic body bottom surface.
The manufacture method of the ceramic heat dish of this egg McMuffin quick cooker, it is characterized in that, described highly thermally conductive performance is to be added with silicon carbide powder in ceramic material, and described high heat stability performance is to be added with cordierite and spodumene composite ceramic material at ceramic material, sintered makes.
The described glaze that do not glues is the high antiseized glaze of crystallite.
The concrete components by weight of the high antiseized glaze of crystallite such as under: petalite 69 %, Talcum 8 %, Zirconium orthosilicate. 3%, Suzhou soil 5%, quartz sand 14%, aluminium oxide 1%, additional microcrystalline glass powder 10 %.
By all of the above glaze raw material by ball: material: water=1.5:1:0.6 carries out obtaining after suction ferrum, the screen cloth of 300 mesh sieve after ball mill pulverizing reaches certain particle size the high antiseized glaze glaze water of crystallite again.
The concrete components by weight of described microcrystalline glass powder such as under: Talcum 25%, quartz 40%, aluminium oxide 20%, calcium carbonate 5%, brium carbonate 7%, titanium dioxide 3% is pulverized after founding at 1550 DEG C ~ 1600 DEG C after being sufficiently mixed again and is formed.
Described coating is high temperature light oleoresin.
Described heating film can be stannum oxide heating film or carbon heating film.
The concrete components by weight of ceramic body such as under: cordierite 40, spodumene 13, Suzhou soil 10, black earth 15, corundum 10, carborundum 5, Talcum 5, petalite 2.
Specific make step and technological parameter are as follows:
By all of the above ceramic body raw material by ball: material: water=1.7:1:1.2 carries out ball mill pulverizing, add the additive sodium humate mixing of trace again, again the screen cloth through 300 mesh sieve, inhale ferrum, press filt, vacuum pugging, roller press roll forming, be dried, upper disk surface executes the high antiseized glaze of crystallite, 1320 ° of C base glaze of high temperature burn the most altogether, 2 hours, prepare ceramic body；Carrying out the polishing of ceramic body bottom surface again, install electrode after bottom surface plating stannum oxide heating film, upper surface coating high temperature light oleoresin solidifies 2 hours in 180 degree；Product of the present invention i.e..
nullIn FIG: this egg McMuffin quick cooker includes ceramic heat dish (1)、Disk cover (2) and mounting cylinder (3)，It is characterized in that，Ceramic heat dish (1) is to sinter above at ceramic body (4) to have the high antiseized glaze (5) of crystallite，High temperature light oleoresin (6) is had at high antiseized glaze (5) applied atop of crystallite，Stannum oxide heating film (7) it is coated with below ceramic body (4)，Electrode (8) is installed on stannum oxide heating film (7)，Electrode (8) is connected by wire (9) plug (10)，Mounting cylinder (3) is a circular cylinder body，The internal diameter of mounting cylinder (3) is more than the external diameter 5-10mm of ceramic heat dish (1)，It is easy to ceramic heat dish (1) and puts into mounting cylinder (3)，Mounting cylinder (3) is suitable for reading an annulus (11)，It is easy to ceramic heat dish (1) lay on annulus (11)，The internal diameter of annulus (11) and the external diameter of disk cover (2) are equal.
This egg McMuffin quick cooker is easy to folding and unfolding after using in kitchen, does not takes up space, and is easy to carry in travelling.
Claims (2)
1. the manufacture method of the ceramic heat dish of an egg McMuffin quick cooker, the ceramic heat dish of this egg McMuffin quick cooker, including ceramic body, this ceramic body has highly thermally conductive and high heat stability performance, it is provided with at ceramic body upper surface and does not glues glaze and coating, be provided with heating film in ceramic body bottom surface；
Described highly thermally conductive performance is to be added with silicon carbide powder in ceramic material, and described high heat stability performance is to be added with cordierite and spodumene composite ceramic material at ceramic material, sintered makes；
The described glaze that do not glues is the high antiseized glaze of crystallite；The concrete components by weight of the high antiseized glaze of crystallite such as under: petalite 65-75%, Talcum 5-10 %, Zirconium orthosilicate. 1-5%, Suzhou soil 2-8%, quartz sand 12-18%, aluminium oxide 0-5%, additional microcrystalline glass powder 10-15 %；
The concrete components by weight of ceramic body such as under: cordierite 38-42, spodumene 12-14, Suzhou soil 8-12, black earth 13-17, corundum 8-12, carborundum 4-6, Talcum 4-6, petalite 1.5-2.5；
It is characterized in that, specific make step and technological parameter are as follows:
By all of the above ceramic body raw material by ball: material: water=1.7:1:1.2 carries out ball mill pulverizing, add the additive sodium humate mixing of trace again, again the screen cloth through 300 mesh sieve, inhale ferrum, press filt, vacuum pugging, roller press roll forming, be dried, upper disk surface executes the high antiseized glaze of crystallite, 1320 ° of C base glaze of high temperature burn the most altogether, 1.5-2.5 hour, prepare ceramic body；Carrying out the polishing of ceramic body bottom surface again, install electrode after bottom surface plating stannum oxide heating film or carbon heating film, upper surface coating high temperature light oleoresin solidifies 2 hours in 180 degree.
2. an egg McMuffin quick cooker, including ceramic heat dish (1), disk cover (2) and mounting cylinder (3), it is characterized in that, ceramic heat dish (1) is to sinter above at ceramic body (4) to have the high antiseized glaze (5) of crystallite, the concrete components by weight of the high antiseized glaze of crystallite such as under: petalite 65-75%, Talcum 5-10 %, Zirconium orthosilicate. 1-5%, Suzhou soil 2-8%, quartz sand 12-18%, aluminium oxide 0-5%, additional microcrystalline glass powder 10-15 %；
High temperature light oleoresin (6) is had at high antiseized glaze (5) applied atop of crystallite, stannum oxide heating film (7) it is coated with below ceramic body (4), electrode (8) is installed on stannum oxide heating film (7), electrode (8) is connected by wire (9) plug (10), mounting cylinder (3) is a circular cylinder body, the internal diameter of mounting cylinder (3) is more than the external diameter 5-10mm of ceramic heat dish (1), it is easy to ceramic heat dish (1) and puts into mounting cylinder (3), mounting cylinder (3) is suitable for reading an annulus (11), it is easy to ceramic heat dish (1) lay on annulus (11), the internal diameter of annulus (11) and the external diameter of disk cover (2) are equal.