CN101955331B - 一种混凝土固化剂 - Google Patents
一种混凝土固化剂 Download PDFInfo
- Publication number
- CN101955331B CN101955331B CN 201010284848 CN201010284848A CN101955331B CN 101955331 B CN101955331 B CN 101955331B CN 201010284848 CN201010284848 CN 201010284848 CN 201010284848 A CN201010284848 A CN 201010284848A CN 101955331 B CN101955331 B CN 101955331B
- Authority
- CN
- China
- Prior art keywords
- pure water
- caustic soda
- weight part
- parts
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及建材领域，具体涉及一种混凝土固化剂，由烧碱、EDTA二钠、硫磺粉、糖精钠、纯净水、红糖混合制成，其中烧碱含3-5重量份、EDTA二钠含10-20重量份、硫磺粉含8-15重量份、糖精钠含8-15重量份、纯净水含45-55重量份、红糖含8-15重量份，该固化剂可将垃圾残渣固结在一起成为建筑砖块，免烧结，也可将杂土、海泥、石粉、沙、红土、煤渣固化，使用方便。
Description
技术领域
本发明涉及建材领域，具体涉及一种混凝土固化剂及其生产工艺。
背景技术
粘土砖禁用后，墙材虽有材质轻且隔热保温性较佳的加气水泥砌块，但投资大而不易普及，特别是材质松化、挂浆易脱，做外墙易透水；强度低而保安性差；还有随着社会的发展，建材的需求越来越大，同时也产生了大量的垃圾，垃圾焚烧处理后，还会留下大量的残渣，必须作填埋处理，日积月累，填埋的残渣越来越多，占的地方也越来越多。
发明内容
本发明的目的是提供一种新型混凝土固化剂，该固化剂可将垃圾残渣固化为建筑砖块，免烧结，也可将杂土、海泥、石粉、沙、红土、煤渣固化。
一种混凝土固化剂，由烧碱、EDTA二钠、硫磺粉、糖精钠、纯净水、红糖混合制成，其中烧碱含3-5重量份、EDTA二钠含10-20重量份、硫磺粉含8-15重量份、糖精钠含8-15重量份、纯净水含45-55重量份、红糖含8-15重量份。
一种混凝土固化剂的生产工艺为：按重量称取烧碱、EDTA二钠、 硫磺粉、糖精钠、纯净水、红糖各物质，将烧碱加入20升的纯净水中，烧碱溶解发热，使纯净水温度升高到约50-60℃的时，再加入EDTA二钠，而后再加糖精钠，搅拌3-5分钟糖精钠溶解；加温，使溶液温度升到100℃，连续搅拌使溶液温度降至92℃±5℃，停止加热，再继续搅拌25-35分钟降至90℃再加入硫磺粉；而后再加水30升，再加温升到95±5℃，停止加热，再加红糖搅拌8-15分钟，完全溶解后，再加温升到100℃，停止加热，搅拌3-5分钟，得产品。
该固化剂可将垃圾残渣固结在一起成为建筑砖块，免烧结，也可将杂土、海泥、石粉、沙、红土、煤渣固化，使用方便，具有超强的防渗透力、有效的防冻融力，显著的防风化力。
具体实施方式
实施例1
一种混凝土固化剂的生产工艺为：按重量称取烧碱3.5kg、EDTA二钠15kg、硫磺粉10kg、糖精钠10kg、纯净水50升水、红糖10kg，将烧碱加入20升的纯净水中，烧碱溶解发热，使纯净水温度升高到约50-60℃的时，再加入EDTA二钠，而后再加糖精钠，搅拌3-5分钟糖精钠溶解；加温，使溶液温度升到100℃，连续搅拌使溶液温度降至92℃±5℃，停止加热，再继续搅拌25-35分钟降至90℃再加入硫磺粉；而后再加水30升，再加温升到95±5℃，停止加热，再加红糖搅拌8-15分钟，完全溶解后，再加温升到100℃，停止加热，搅拌3-5分钟，得98.5kg产品。使用时，按50kg的产品加入1200kg的水稀释，再把适量的稀释后的固化剂加入杂土、海泥、石粉、沙、 红土、煤渣中搅拌混合，再压制成型，凉干，得成型砖。
实施例2
一种混凝土固化剂的生产工艺为：按重量称取烧碱4kg、EDTA二钠14.5kg、硫磺粉11kg、糖精钠11kg、纯净水50升、红糖10kg，将烧碱加入20升的纯净水中，烧碱溶解发热，使纯净水温度升高到约50-60℃的时，再加入EDTA二钠，而后再加糖精钠，搅拌3-5分钟糖精钠溶解；加温，使溶液温度升到100℃，连续搅拌使溶液温度降至92℃±5℃，停止加热，再继续搅拌25-35分钟降至90℃再加入硫磺粉；而后再加水30升，再加温升到95±5℃，停止加热，再加红糖搅拌8-15分钟，完全溶解后，再加温升到100℃，停止加热，搅拌3-5分钟，得100kg产品。使用时，按50kg的产品加入1200kg的水稀释，再把适量的稀释后的固化剂加入杂土、海泥、石粉、沙、红土、煤渣中搅拌混合，再压制成型，凉干，得成型砖。本固化剂是一种由多个强离子组合而成的水溶剂，它与土壤混合后可以改变土壤的物理与化学性质，使土壤孔隙中所吸附的水离子变成可以被排出和蒸发的自由水，进而达到常规所不能达到的压实密度，极大地增强土壤的承载力和防渗性，改善土壤的湿胀干缩现象，对土壤具有永久性的强化作用。本固化剂还可渗透到混凝土中，与其中的碱性物质相互作用，生成胶状物，并向四周弥散，填充孔洞与缝隙。与此同时，胶状物将水、酸、碱、油、汁、污、藻等外来物质乳化，固化剂具有高渗透性。通过渗透，混凝土被由内而外永久封闭。而固化剂中水泥掺量使土颗粒胶结和孔隙填充对固化结构形成及强度增长的作用。
Claims (1)
1.一种混凝土固化剂，其特征在于：由烧碱、EDTA二钠、硫磺粉、糖精钠、纯净水、红糖混合制成，其中烧碱含3-5重量份、EDTA二钠含10-20重量份、硫磺粉含8-15重量份、糖精钠含8-15重量份、纯净水含45-55重量份、红糖含8-15重量份，其生产工艺为：按重量称取烧碱、EDTA二钠、硫磺粉、糖精钠、纯净水、红糖各物质，将烧碱加入20升的纯净水中，烧碱溶解发热，使纯净水温度升高到50-60℃时，再加入EDTA二钠，而后再加糖精钠，搅拌3-5分钟糖精钠溶解；加温，使溶液温度升到100℃，连续搅拌使溶液温度降至92℃，停止加热，再继续搅拌25-35分钟降至90℃再加入硫磺粉；而后再加水30升，再加温升到95℃，停止加热，再加红糖搅拌8-15分钟，完全溶解后，再加温升到100℃，停止加热，搅拌3-5分钟，得产品。